Switching hydrogenation pathways of furfural via reduction-degree engineering of Ni-based catalysts
收藏切换
PDF
Xiaoqing CHANG1, 2, Lingyu JIA1, 2, Shanshan DANG1, 2, Tianliang LU3, *, Peng WANG4, *, Weifeng TU1, 2, *, Zhenzhou ZHANG1, 2, *
Journal of Fuel Chemistry and Technology | 2026, 54(8) : 20250159-1696 - 20250159-1707
Less
收藏切换
Journal of Fuel Chemistry and Technology | 2026, 54(8): 20250159-1696-20250159-1707
• RESEARCH PAPER •
Switching hydrogenation pathways of furfural via reduction-degree engineering of Ni-based catalysts
Full
Xiaoqing CHANG1, 2, Lingyu JIA1, 2, Shanshan DANG1, 2, Tianliang LU3, *, Peng WANG4, *, Weifeng TU1, 2, *, Zhenzhou ZHANG1, 2, *
Affiliations
  • 1State Key Laboratory of Coking Coal Resources Green Exploitation, Zhengzhou University, Zhengzhou 450001, China
  • 2Engineering Research Center of Advanced Functional Material Manufacturing of Ministry of Education, Zhengzhou University, Zhengzhou 450001, China
  • 3School of Chemical Engineering, Zhengzhou University, Zhengzhou 450001, China
  • 4School of Material and Chemical Engineering, Xuzhou University of Technology, Xuzhou 221018, China
About Author:

#

：These authors contributed equally to this work.

Published: 2026-08-10 doi: 10.1016/S1872-5813(26)60664-0
Outline
收藏切换

The selective hydrogenation of biomass-derived compounds is pivotal for the synthesis of high-value-added chemicals. The controllable hydrogenation in furfural for furfuryl alcohol or tetrahydrofurfuryl alcohol is highly desirable yet challenging. In this study, Ni2Al-LDO（layered double oxide） metal oxide catalyst featuring highly dispersed surface NiO was synthesized via a structural topological transformation using layered double hydroxides. The catalyst exhibited excellent performance in the hydrogenation of furfural, achieving 91.42% yield of furfuryl alcohol (FOL) at 160 °C and 1.4 MPa H2. Gradual reduction of Ni2Al-LDO produced Ni/NiO mixtures, enabling tunable shift from FOL to tetrahydrofurfuryl alcohol (HFOL) as the NiO content decreased and the Ni content increased. After a two-hour reduction at 700 °C, the HFOL yield reached 93.95%. CO2-TPD, NH3-TPD and FT-IR measurements revealed that variations in reduction degree on nickel influenced the adsorption behavior of furfural. NiO species could only adsorb the C=O group of furfural, isopropanol serves as the hydrogen source, and furfural undergoes hydrogenation to form furfuryl alcohol following the MPV conversion pathway. Whereas the flat adsorption mode on the metallic Ni surface facilitated the simultaneous adsorption and activation of both the furan ring and the carbonyl group of furfural. In addition, the hydrogen sources of the reaction systems also differ: the Ni2Al-LDO catalyst is only capable of activating isopropanol, with the reaction proceeding via the MPV mechanism; in contrast, Ni2Al-LDO-700 can activate both H2 and isopropanol, where H2 serves as the primary hydrogen source. This work elucidates a clear structure-activity relationship centered on the metal oxidation state and provides a practical reduction-engineering approach for designing adaptable catalysts in biomass upgrading.

furfural  /  selective hydrogenation  /  Ni-based catalysts  /  reduction degree  /  selectivity switching
常小庆, 贾玲玉, 党闪闪, 芦天亮, 王鹏, 涂维峰, 张振洲. 镍基催化剂表面氧覆盖度对糠醛选择性加氢路径的调控规律研究. 燃料化学学报（中英文）, 2026 , 54 (8) : 20250159-1696 -20250159-1707 . DOI: 10.1016/S1872-5813(26)60664-0
Xiaoqing CHANG, Lingyu JIA, Shanshan DANG, Tianliang LU, Peng WANG, Weifeng TU, Zhenzhou ZHANG. Switching hydrogenation pathways of furfural via reduction-degree engineering of Ni-based catalysts[J]. Journal of Fuel Chemistry and Technology, 2026 , 54 (8) : 20250159-1696 -20250159-1707 . DOI: 10.1016/S1872-5813(26)60664-0
Full Text
Less
With the rapid depletion of fossil energy sources and increasing environmental concerns, renewable biomass resources have attracted considerable attention as alternatives to traditional fossil fuels for the production of high-energy-density biofuels and high value-added chemicals[1−3]. Furfural (FAL) is one of the most important biomass-derived platform chemicals, owing to its wide range of high value-added derivatives. For instance, furfuryl alcohol (FOL), the partial hydrogenated product of FAL, is widely used in the production of resins, lysine, vitamins, and lubricants[4−5]. Tetrahydrofurfuryl alcohol (HFOL), a deep hydrogenation product of furfural, is in high demand as a key precursor and environmentally friendly solvent in industrial, agricultural, and automotive sectors[6−7]. However, controlling the selective hydrogenation of furfural toward either FOL or HFOL remains a significant challenge due to the complexity of parallel and sequential reaction networks[8−9].
Traditionally, HFOL has been produced through a two-step hydrogenation process using commercial Cu-Cr catalysts under harsh conditions (140−180 °C, >4 MPa H2), with FOL serving as an intermediate[10]. Currently, many transition metals, such as the noble metals Pt[11−12], Pd[13−14], have been employed for furfural hydrogenation to produce HFOL under mild conditions. However, these catalysts often induce side reactions, such as hydroxyl or furan ring hydrogenolysis, and their high cost also severely limits their applicability in large-scale industrial processes[15−16]. Consequently, research has increasingly focused on cost-effective non-precious metal catalysts, among which, nickel-based catalysts are highly attractive due to their proficient H2 activation capability. However, Ni strongly adsorbs both C=O and C=C bonds, leading to unselective hydrogenation[17−20].
To address this, modifying the catalyst surface structure to regulate the substrate adsorption configuration has emerged as a promising strategy for enhancing selectivity[21−23]. For instance, Meng et al.[24] demonstrated that different exposed facets of Ni, derived from hydrotalcite precursors, could direct furfural hydrogenation toward either FOL or HFOL with high selectivity. Similarly, Fu et al.[25] achieved an exceptional HFOL yield over a Ni/C catalyst featuring abundant NiO species and exposed Ni(200) facets, highlighting the critical role of surface composition and microstructure. These findings confirm that tuning the microstructure of nickel particles can significantly influence their adsorption behavior.
Despite the remarkable advances achieved in the research of nickel-based catalysts, the hydrogenation of furfural still suffers from harsh reaction conditions and the preparation of such catalysts remains rather complicated[26−28]. The rational design and development of novel catalysts with tunable selectivity toward a broad spectrum of high value-added hydrogenation products within a single catalytic system remains a considerable challenge. Furthermore, detailed mechanistic insights into how the catalyst structure influences the adsorption conformation of the substrate, such as the modulation of the reduction degree of nickel, are still lacking.
Herein, we report an approach to achieve switchable selectivity in furfural hydrogenation by precisely controlling the reduction degree of a flower-like Ni2Al hydrotalcite-derived catalyst and Ni/NiO metal mixtures with different ratios were obtained by controlling the reduction time and temperature. The influence of nickel reduction degree on the adsorption configuration of furfural and the activation pathway of the hydrogen donor was systematically investigated. Notably, Ni2Al-LDO exhibited high selectivity for FOL (91.42%), while Ni2Al-LDO-700 showed excellent selectivity for HFOL (93.95%). Based on structural characterization using XRD, CO2-TPD and in situ FT-IR measurements, it was confirmed that variations in the reduction degree of nickel affect the adsorption sites of the substrate. This finding demonstrates that the Ni microstructure can be finely tuned within a single catalyst system to enable facile switching between the two target products. This work provides fundamental insights into the structure-activity relationship governed by metal oxidation state and offers a straightforward design principle for tunable catalysts in biomass upgrading.
1　Experimental
Less
1.1　Materials
Nickel nitrate (II) hydrate (Ni(NO3)2·6H2O), aluminum nitrate nonahydrate (Al(NO3)3·9H2O, AR), urea (CH4N2O, 99.5%), furfural (FAL, AR, 99%), furfuryl alcohol (FOL, AR, 98%), tetrahydrofurfuryl alcohol (HFOL, AR, 98%), isopropyl alcohol (C3H8O2, AR, 98%.) and n-octanol (C8H18O, 99.5%) were purchased from Shanghai Aladdin Biochemical Technology Co., Ltd. All the chemicals were used as received and did not need to be further purified.
1.2　Catalyst synthesis
A series of nickel-aluminum hydrotalcite catalysts were prepared using the hydrothermal method, with Ni2Al-LDH (layered double hydroxides) as an example. A solution containing 0.01 mol of aluminum nitrate, 0.02 mol of nickel nitrate, and 0.084 mol of urea was dissolved in 60 mL of deionized water, stirred at room temperature for 1 h until a homogeneous solution was obtained, and then transferred to the liner of a hydrothermal autoclave. The mixture was aged at 140 °C for 7 h, naturally cooled to room temperature, and subsequently rinsed repeatedly with deionized water until the supernatant reached a pH value of 7. The resulting green precipitate was dispersed in 200 mL of methanol and stirred at room temperature for 2 h to effectively remove the residual ions. Methanol was used due to its lower surface tension, which helps mitigate structural aggregation during subsequent drying (24 h). The obtained hydrotalcite precursor was calcined at 500 °C in an argon gas stream (60 mL/min) for 2 h, yielding a gray-green solid catalyst. The catalyst was then reduced at different temperatures and then passivated in 1% O2/Ar at room temperature. The resulting samples were named as Ni2Al-LDO-T-t, where T represents the reduction temperature and t denotes the reduction duration.
1.3　Characterization
The morphology of the catalysts was analyzed using a JSM-7401F scanning electron microscope (SEM). X-ray diffraction (XRD) patterns were recorded using a Bruker X-ray powder diffractometer (Germany) equipped with a Cu Kα radiation source (λ = 1.5418 Å), operating at 40 kV and 40 mA, with a scanning step size of 0.02(°)/s and a scanning range of 10°−80°. Prior to testing, the catalysts were ground into a fine powder and placed in a ceramic sample holder (inner diameter: 10 mm).
Nitrogen physisorption experiments were conducted on the reduced catalysts at −196 °C using a fully automated gas adsorption analyzer (ASAP-2460, Micromeritics). Before measurements, 200 mg of the sample was dehydrated under vacuum at 200 °C for 6 h. The specific surface area was calculated using the multi-point Brunauer-Emmett-Teller (BET) method (p/p0= 0−1), while the pore size distribution was determined by the Barrett-Joyner-Halenda (BJH) method.
X-ray photoelectron spectroscopy (XPS) was performed using an ESCALAB 250Xi spectrometer (Thermo Fisher) with an Al Kα X-ray source (hv = 1486.6 eV). The X-ray source operated at an accelerating voltage of 15 kV and a power of 80 W.
High-resolution XPS spectra were recorded with a step size of 0.05 eV and a pass energy of 25 eV. All binding energies were calibrated to the C 1s peak of adventitious carbon at 284.6 eV, and the spectra were analyzed using CasaXPS software.
Hydrogen temperature-programmed reduction (H2-TPR), carbon dioxide temperature-programmed desorption (CO2-TPD), ammonia temperature-programmed desorption (NH3-TPD), and hydrogen temperature-programmed desorption (H2-TPD) experiments were conducted using a microreactor system (CATLAB, Hiden Analytical Ltd.), coupled with a quadrupole mass spectrometer (QIC20, Hiden Analytical Ltd.). For the H2-TPR experiments, 30 mg of catalyst was weighed and dehydrated under an Ar atmosphere (30 mL/min) at 200 °C for 2 h. The catalyst was then cooled to 50 °C, the atmosphere was switched to 10% H2, and the temperature was ramped to 800 °C at a rate of 5 °C/min, while the exhaust gases were analyzed by mass spectrometry. For the CO2-TPD, NH3-TPD and H2-TPD experiments, 30 mg of catalyst was pretreated by reduction or dehydration, cooled to 50 °C, purged with 10% CO2/Ar, 10% NH3/Ar or 10% H2/Ar for 1 h, followed by purging with Ar (50 mL/min) for 1 h. The temperature was then increased to 800 °C at a rate of 5 °C/min, and the exhaust gases were analyzed by a quadrupole mass spectrometer.
In situ diffuse reflectance Fourier transform infrared spectroscopy (DRIFTS) experiments were conducted using a Thermo iS50 spectrometer equipped with an MCT liquid nitrogen-cooled detector and an in situ reaction cell. The catalyst samples were reduced under an H2 atmosphere at 500 °C (30 mL/min) for 2 h (heating rate: 10 °C/min), followed by cooling in an Ar flow (30 mL/min) to 30 °C, and background spectra were collected. Pyridine (probe molecule) or substrates (furfural, isopropanol) were introduced into the reaction cell using Ar (30 mL/min) at 30 °C. After saturation of adsorption, Ar was passed through to remove physically adsorbed substances, followed by the collection of successive in situ FT-IR spectra. After collecting the background spectrum, CO (probe molecule, 10 mL/min) was introduced to achieve saturation adsorption on the catalyst surface, followed by purging with Ar to remove physically adsorbed CO. Continuous in situ FT-IR spectra were collected throughout the process. The FT-IR spectra were recorded within the range of 1900−2200 cm−1 with 64 scans and a resolution of 4 cm−1.
1.4　Hydrogenation experiments
Selective hydrogenation of furfural was conducted in a 10 mL micromagnetic heating reactor (Haian Huawei Scientific Research Instrument). Furfural (FAL, 0.6 mmol), catalyst (30 mg) and isopropanol (3 mL) were added to a 10 mL autoclave. The autoclave was purged five times with H2 (by pressurizing to 1 MPa and then venting to atmospheric pressure) to ensure complete removal of air, then filled with hydrogen to the specified pressure. The reactor was subsequently heated to the required reaction temperature, and the reaction was carried out at 1000 r/min (time). After the reaction was completed, the reactor was rapidly cooled in an ice-water bath. The reaction mixture was then separated and diluted with isopropanol, followed by the addition of n-octanol as an internal standard for further analysis. All key catalytic experiments were repeated at least twice under the same conditions, with the error of the experimental results within ±3%.
1.5　Product analysis
The separated liquid samples were quantitatively analyzed by gas chromatography (SHIMADZU GC-2018, flame ionization detector, equipped with HP-5 column), and all products were qualitatively analyzed by gas chromatography-mass spectrometry (GC-MS, Agilent 8860-8977B). The standard curves of reactants and products were plotted by internal standard method, and the substrate conversion and product selectivity were calculated by the following equations.
$ {\mathrm{Conv.}}_{\text{FAL}}=\frac{n_{\text{FAL initial}}-{n}_{\text{FAL final}}}{{n}_{\text{FAL initial}}}\times 100\% $
$ {\mathrm{Sel.}}_{\text{FOL}}=\frac{{n}_{\text{FOL}}}{n_{\text{FAL initial}}-{n}_{\text{FAL final}}} \times 100\% $
$ {\mathrm{Sel.}}_{\text{HFOL}}=\frac{{n}_{\text{HFOL}}}{n_{\text{FAL initial}}-{n}_{\text{FAL final}}} \times 100\% $
In equations (1)−(3), where nFAL initial and nFAL final are the initial and final molar amounts of furfural, respectively; nFOL and nHFOL are the molar amounts of the corresponding products formed.
2　Results and discussion
Less
2.1　Catalyst characterizations
Three-dimensional (3D) flower-like Ni2Al-LDO precursors with uniform morphology were synthesized via the urea decomposition method, as shown in Figure 1(a), (b)[29]. After reduction, the flower-like morphology of the precursor was well preserved, and distinct open spaces between adjacent nanolayers were observed, as shown in the enlarged illustrations (Figure 1(c), (d)). Upon reduction, the surface roughness of the nanosheets increased, as shown in Figure1(f), but the overall 3D hierarchical structure did not collapse. This preserved 3D layered hydrotalcite structure provides an effective contact area between the reaction substrate and hydrogen throughout the reaction system[30], is expected to sufficient active sites to optimize hydrogenation performance.
The crystal structures of the synthesized samples were characterized using XRD. As shown in Figure 2(a), the Ni2Al-LDO catalyst exhibited patterns corresponding to the NiO crystal planes ((200) and (220))[31]. No characteristic diffraction patterns of Al2O3 were found, implying an amorphous phase. For samples reduced at 700 °C，the intensity of the Ni diffraction patterns (2θ = 44.5°, 51.8°, 76.3°) increased, whereas the NiO diffraction patterns disappeared completely after 2 h of reduction at 700 °C. This indicates that an increase in reduction temperature promotes the reduction of more Ni2+ to Ni0[32]. The average crystallite sizes of NiO in Ni2Al-LDO and Ni0 in Ni2Al-LDO-700 were estimated using the Scherrer equation based on the NiO(200) and Ni(111) peaks, respectively (Table 1). The NiO crystallite size was calculated to be 4.04 nm. After reduction at 700 °C, the metallic Ni crystallite size increased to 8.46 nm, indicating the occurrence of metal particle sintering under severe reduction conditions[17].
The textural properties of the catalysts were investigated by N2 physisorption. Both Ni2Al-LDO and Ni2Al-LDO-700 exhibit type IV isotherms with an H3-type hysteresis loop (Figure 2(b)), which is characteristic of mesoporous materials with slit-shaped pores. The corresponding pore size distribution curves (Figure 2(c)) show a unimodal peak centered in the mesoporous region, confirming the presence of uniform mesopores[33]. The specific surface area of Ni2Al-LDO was measured to be 173.3 m2/g, which decreased to 160.2 m2/g after reduction (Table 1). The layered structure of the catalysts contributed to their relatively high specific surface area[34−35]. Additionally, the pore volume was calculated to be 0.6 cm3/g for both samples. The high surface area and well-developed meso-porosity are beneficial for the diffusion of reactant molecules, such as furfural, in liquid-phase reactions[36].
The electronic valence state of Ni in the different samples was investigated using (XPS), as depicted in Figure 3(a)−(h). According to the literature, the composite peaks obtained were deconvoluted into several peaks, which are summarized in Table S1. These results indicate that tuning the reduction parameters can effectively modulate the surface reduction degree Table S1 of nickel[37]. It is important to note that even in the sample reduced at 700 °C, a significant portion of Ni2+ remains. This is attributed to the surface re-oxidation during the passivation step prior to XPS measurement and the possible presence of a thin oxidized layer upon air exposure[38].
2.2　Catalytic performance
The catalytic hydrogenation of furfural over a series of hydrotalcite-derived catalysts with varying Ni/Al ratios was first investigated. In the case of the Ni2Al-LDO catalyst (Figure 4(a)), FOL was the dominant product regardless of the Ni/Al ratio, achieving a yield of over 90% at complete conversion. This suggests that the NiO sites in these catalysts are highly active and selective for the partial hydrogenation of the carbonyl group. In contrast, the fully reduced Ni2Al-LDO-700 catalysts exhibited a strong dependence on nickel loading (Figure 4(b)). At a low Ni/Al ratio (e.g., 1∶2), the primary product remained FOL. However, as the Ni/Al ratio increased to 2∶1, the yield of tetrahydrofurfuryl HFOL dramatically rose to 93.95% at full conversion. This indicates that a sufficient density of reduced metallic Ni0 sites is crucial for driving the deep hydrogenation of the furan ring. Based on these results, the catalyst with a Ni/Al ratio of 2∶1, which displayed the highest HFOL yield, was selected for subsequent studies on the effect of reduction degree.
To systematically tune the reduction degree, the Ni2Al-LDO catalyst was subjected to reduction at varying temperatures and durations, guided by H2-TPR analysis (Figure S1) which indicated a main reduction onset around 400 °C. The catalytic performance as a function of reduction temperature and duration is summarized in Figure 5.
Therefore, Ni2Al-LDO catalysts were subjected to reduction at various temperatures and durations, starting from 400 °C, to systematically examine the influence of reduction degree. According to Figure 5, the unreduced catalyst exhibited a single activity toward furfuryl alcohol with a yield of 91.42%. As the reduction time increased from 400 °C, the selectivity for furfuryl alcohol decreased while that for tetrahydrofurfuryl alcohol increased, reaching a yield of 77.96% after 90 min of reduction. When the reduction time was extended to 2 h and the temperature increased from 400 to 700 °C, NiO was completely reduced (as confirmed by XRD), the HFOL yield was further optimized to 93.95% at 100% conversion. These results demonstrate a clear correlation between the catalyst reduction degree (Ni0/NiO ratio) and the hydrogenation pathway: NiO-rich surfaces favor carbonyl hydrogenation to FOL, while Ni0-rich surfaces promote subsequent furan ring hydrogenation to HFOL.
The distinct catalytic behaviors of Ni2Al-LDO (FOL-selective) and Ni2Al-LDO-700 (HFOL-selective) were further compared under different reaction conditions (Figure 6). For the Ni2Al-LDO catalyst, the complete furfural conversion required relatively harsh conditions. In contrast, the fully reduced Ni2Al-LDO-700 catalyst achieved 100% conversion under much milder conditions, and the HFOL yield remained consistently high (>90%) across a wide range of temperatures, pressures, and reaction times. This highlights the superior activity and outstanding performance of the metallic Ni0 sites for the deep hydrogenation reaction
Finally, the stability of the two catalysts was evaluated over five continuous reaction cycles (Figure 7). At the end of each reaction cycle, the liquid phase was separated from the catalyst by centrifugation, followed by rinsing the catalyst three times with ethanol and water, and drying it at 40 °C for 12 h before reuse. Each experiment ensured the use of 30 mg of catalyst, with any loss supplemented by fresh catalyst. The recovery rate was calculated based on the ratio of fresh catalyst to used catalyst. As shown in Figure 7, the furfural conversion of the Ni2Al-LDO catalyst remained above 93.8% over five cycles, while the selectivity for furfuryl alcohol slightly decreased from 87.79% to 82.09%, with minimal loss of activity. Compared to the fresh catalyst, the used Ni2Al-LDO catalyst exhibited a similar crystal structure (Figure S2), and the NiO grain size, calculated to be 4.89 nm (Table S2), was negligible increase to that of the fresh catalyst, suggesting that Table S2 Ni2Al-LDO demonstrated good stability in liquid-phase reactions. In contrast, the Ni2Al-LDO-700 catalyst maintained a 100% conversion rate after five cycles; however, its HFOL selectivity decreased from 91.14% to 81.04%. Significantly, this selectivity could be largely restored to 89% upon re-reduction of the spent catalyst, suggesting that the deactivation is primarily due to the oxidation of metallic Ni0 during the reaction/repeat cycle rather than permanent structural degradation. XRD of the spent Ni2Al-LDO-700 (Figure S3) confirmed a decrease in metallic Ni peak intensity and a slight increase in Ni0 crystallite size (to 10.35 nm, Table S2), indicating some surface oxidation and mild particle sintering. Overall, both catalysts demonstrated satisfactory recyclability, which can be attributed to the flower-like structure of layered double hydroxides.
2.3　The activation of hydrogen and isopropanol
Since isopropanol is used as the solvent and the reaction atmosphere consists of H2, it is essential to first determine the hydrogen donor for the reaction to elucidate the hydrogenation mechanism. As shown in Figure 8(a), control experiments were conducted under a N2 atmosphere (1.4 MPa) at 160 °C for 3 h. In contrast, the catalytic activity of Ni2Al-LDO under a hydrogen atmosphere showed no significant difference compared to that under a nitrogen atmosphere. This indicates that the two catalysts exhibit different hydrogenation behaviors. Furthermore, the two catalysts exhibit different hydrogen consumption behaviors. As shown in the H2-TPD profile in Figure 8(b), Ni2Al-LDO-700 exhibits two strong hydrogen adsorption peaks: one in the low-temperature region (centered at 119.2 °C) and the other in the high-temperature region (centered at 196.3 °C). These peaks are attributed to the dissociation of H−H bonds on metallic Ni particles[39]. In contrast, Ni2Al-LDO shows no detectable H2 adsorption, indicating its inability to dissociate hydrogen. This result is consistent with its inactivity under pure H2 atmosphere in the control experiment.
The adsorption behavior of isopropanol on the catalyst was investigated using in situ FT-IR and CO2-TPD. As shown in Figure 9, three C−H stretching vibration peaks were observed after isopropanol adsorption on the catalyst: ν (CH3), ν (CH2), ν (CH), corresponding to 2970.4, 2935.1 and 2868.4 cm−1, respectively. These results indicate that the prepared catalysts effectively adsorb isopropanol.
To assess the catalysts' ability to abstract hydride from isopropanol (a key step in the MPV mechanism), their surface basicity were evaluated via CO2-TPD (Figure 9(b)) Furthermore, the acidic nature of the C−H bond in isopropanol was confirmed by CO2-TPD analysis, as shown in Figure 9(b).
Both catalysts exhibit CO2 desorption peaks, with three distinct peak regions centered at 100.3, 302.2 and 470.9 °C, corresponding to weak, medium, and strong basic sites, respectively[40]. According to previous studies, weak, medium, and strong basic sites originate from hydroxyl groups, M+−O− species, and low-coordinated oxygen anions, respectively[41]. It is evident that the Ni2Al-LDO catalyst possesses a higher density of basic sites compared to Ni2Al-LDO-700, resulting in stronger C−H adsorption of isopropanol. However, isopropanol binding to the basic sites occurs in both catalysts. Based on these results, for the unreduced catalyst, it cannot dissociate hydrogen but exhibits basicity. The furfural hydrogenation process follows the Meerwein-Ponndorf-Verley (MPV) pathway, with isopropanol serving as the hydrogen donor and the basic sites facilitating hydrogen transfer. In contrast, for the reduced catalyst, Ni enables hydrogen dissociation, and H2 acts as the primary hydrogen source[42].
2.4　Adsorption configuration of furfural and reaction mechanism
The adsorption configuration of the substrate plays a crucial role in determining the hydrogenation reaction pathway and selectivity. The acid sites on the catalyst surface were initially characterized using pyridine infrared spectroscopy (Py-FTIR, Figure 10(a)) and temperature-programmed desorption of ammonia (NH3-TPD, Figure 10(b)). As shown in Figure 10(a), both samples exhibit a distinct characteristic band of pyridine adsorption at 1445.9 cm−1, which is attributed to the Lewis acid sites of the metal oxides (NiO and Al2O3)[43]. As presented in Figure 10(b), the NH3 desorption peaks at 100.7 and 500.2 °C correspond to two broad peaks, which are associated with weak (W) and strong (S) acid sites, respectively. A comparative analysis indicates that the unreduced Ni2Al-LDO possesses a higher overall acidity, particularly in the strong acid region, than the reduced Ni2Al-LDO-700.
The adsorption behavior of furfural on the catalyst was further investigated (Figure 10(d)), and the surface electron density of Ni along with the bonding state of CO was analyzed using in situ FT-IR (Figure 10(c)). As shown in Figure 10(c), for the Ni2Al-LDO-700 catalyst, CO is adsorbed on monometallic Ni in both linear (2074.4 and 2046.8 cm−1) and bridge (1960.3 cm−1) configurations[44].
These frequencies correspond to CO adsorption on metallic Ni, confirming that the catalyst possesses both low and high coordination adsorption sites, which are capable of adsorbing the furan ring and carbonyl group of furfural on the catalyst surface[45]. In contrast, for the Ni2Al-LDO catalyst, no significant CO adsorption is observed, as the chemical state of nickel is predominantly NiO.
As shown in Figure 10(d), gas-phase furfural adsorbed on Al2O3 exhibits a distinct Lewis acid adsorption peak for ν (C=O) at 1678.3 cm−1, while ν (C=C) and furan ring vibrations appear at 1586.8 and 1466.7 cm−1, respectively[46]. Notably, the chemisorption of furan rings on the catalyst surface leads to the disappearance of the ν (C=C) and furan ring vibration peaks[47]. As depicted in the figure, both Ni2Al-LDO and Ni2Al-LDO-700 catalysts exhibit corresponding adsorption peaks at 1671.2 and 1664.5 cm−1, which are red-shifted compared to Al2O3, indicating that the C=O group undergoes activated adsorption on both catalysts. Moreover, the Ni2Al-LDO catalyst displays characteristic furan ring bands at 1586.8 and 1466.7 cm−1, suggesting that only the C=O group of furfural is adsorbed on the catalyst surface. In contrast, the spectral bands of ν (C=C) and furan ring vibrations on Ni2Al-LDO-700 are negligible, indicating that furfural is adsorbed in a parallel configuration on the catalyst surface[48]. These findings demonstrate that Ni2Al-LDO-700 exhibits a stronger adsorption capacity for both the furan ring and the C=O group compared to Ni2Al-LDO, making it more favorable for the complete hydrogenation of furfural molecules. Conversely, the Ni2Al-LDO catalyst primarily facilitates the chemisorption of the C=O group, which may hinder the hydrogenation of the furan ring.
In summary, the comprehensive reaction mechanism dictated by the nickel reduction degree for the two catalysts are illustrated in Figure 11. For the Ni2Al-LDO catalyst, NiO functions as a Lewis acid site that adsorbs the C=O group of furfural, while basic sites in the catalyst adsorb the α-hydrogen from isopropanol. This interaction facilitates the transfer of proton hydrogen from the hydrogen donor to the acceptor, resulting in the formation of furfuryl alcohol.
In contrast, for the Ni2Al-LDO-700 catalyst, the NiO reduction degree is negligible, the primary active sites are metallic Ni, which enable simultaneous adsorption on both the furan ring and the C=O group of furfural. Additionally, Ni facilitates the dissociation of H2 into H−H, leading to the complete hydrogenation of furfural to tetrahydrofurfuryl alcohol. The influence of Ni reduction degree on product selectivity is attributed to the adsorption capability of NiO. NiO can adsorb only the C=O group of furfural as a Lewis acid site, and the hydrogenation pathway follows the MPV mechanism. In contrast, when NiO is fully reduced to metallic Ni, multiple adsorption sites are exposed, enabling simultaneous interaction with both the furan ring and the C=O group. Thus, variations in Ni reduction degree directly modulate the adsorption configuration of the catalyst on the substrate, thereby influencing the reaction pathway and product distribution.
3　Conclusion
Less
In summary, the hydrogenation selectivity of furfural can be precisely switched between FOL and HFOL by controlling the reduction degree of a flower-like Ni2Al hydrotalcite-derived catalyst. The Ni2Al-LDO catalyst, rich in NiO, exhibited high selectivity (91.42%) towards FOL at 160 °C and 1.4 MPa H2. Upon reduction at 700 °C for 2 h, the catalyst transformed into a Ni0-dominant state, which exclusively produced HFOL with a yield of 93.95% under identical conditions. Experimental and theoretical analyses revealed that the switchable selectivity originates from the distinct adsorption configurations of furfural dictated by the catalyst's composition. On the NiO-rich catalyst, Lewis acidic Ni2+ sites selectively adsorb and activate the carbonyl group of furfural and adjacent basic sites cooperate to facilitate a hydride transfer from isopropanol via the MPV mechanism, yielding FOL. In contrast, on the metallic Ni0 surface, furfural enables simultaneous interaction with both the carbonyl group and the furan ring. This configuration, coupled with efficient H2 dissociation on Ni0, drives the complete hydrogenation to HFOL. This work provides fundamental insight into how the oxidation state of a non-precious metal catalyst governs substrate adsorption and reaction pathways. The strategy of tuning the metal/oxide ratio through controlled reduction offers a general approach for designing selective catalysts for biomass upgrading.
References
Less
1
MANDALIKA A, QIN L, SATO T K, et al. Integrated biorefinery model based on production of furans using open-ended high yield processes[J]. Green Chem, 2014, 16: 2480−2489.
2
ROCNIK T, LIKOZAR B, JASIUKAITYTE-GROJZDEK E, et al. Catalytic lignin valorisation by depolymerisation, hydrogenation, demethylation and hydrodeoxygenation: Mechanism, chemical reaction kinetics and transport phenomena[J]. Chem Eng J, 2022, 448: 137309.
3
VINOD N, DUTTA S. Energy densification of biomass-derived furfurals to furanic biofuels by catalytic hydrogenation and hydrodeoxygenation reactions[J]. Sustainable Chem, 2021, 2: 521−549.
4
GUO H, ZHANG H, ZHANG L, et al. Selective hydrogenation of furfural to furfuryl alcohol over acid-activated attapulgite-supported NiCoB amorphous alloy catalyst[J]. Ind Eng Chem Res, 2018, 57: 498−511.
5
LIN Z, WAN W, YAO S, et al. Cobalt-modified molybdenum carbide as a selective catalyst for hydrodeoxygenation of furfural[J]. Appl Catal B: Environ, 2018, 233: 160−166.
6
GUPTA K, RAI R K, SINGH S K. Metal catalysts for the efficient transformation of biomass-derived HMF and furfural to value added chemicals[J]. ChemCatChem, 2018, 10: 2326−2349.
7
IAHIKAWA H, SHENG M, NAKATA A, et al. Air-stable and reusable cobalt phosphide nanoalloy catalyst for selective hydrogenation of furfural derivatives[J]. ACS Catal, 2021, 11: 750−757.
8
XU C, PAONE E, LUQUE R, et al. Recent catalytic routes for the preparation and the upgrading of biomass derived furfural and 5-hydroxymethylfurfural[J]. Chem Soc Rev, 2020, 49: 4273−4306.
9
MARISCAL R, MAIRELES-TORRES P, OJEDA M, et al. Furfural: a renewable and versatile platform molecule for the synthesis of chemicals and fuels[J]. Energy Environ Sci, 2016, 9: 1144−1189.
10
LI S, WANG Y, GAO L, et al. Short channeled Ni-Co/SBA-15 catalysts for highly selective hydrogenation of biomass-derived furfural to tetrahydrofurfuryl alcohol[J]. Microporous Mesoporous Mater, 2018, 262: 154−165.
11
O'DRISCOLL A, LEAHY J J, CURTIN T. The influence of metal selection on catalyst activity for the liquid phase hydrogenation of furfural to furfuryl alcohol[J]. Catal Today, 2017, 279: 194−201.
12
DAI S, YOU Y, ZHANG S, et al. In situ atomic-scale observation of oxygen-driven core-shell formation in Pt3Co nanoparticles[J]. Nat Commun, 2017, 8: 204.
13
MIRONENKO R M, BELSKAYA O B, TALSI V P, et al. Mechanism of Pd/C-catalyzed hydrogenation of furfural under hydrothermal conditions[J]. J Catal, 2020, 389: 721−734.
14
YUAN E, WANG C, WU C, et al. Constructing hierarchical structures of Pd catalysts to realize reaction pathway regulation of furfural hydroconversion[J]. J Catal, 2023, 421: 30−44.
15
ZHANG S, XIA Z, ZOU Y, et al. Spatial intimacy of binary active-sites for selective sequential hydrogenation-condensation of nitriles into secondary imines[J]. Nat Commun, 2021, 12: 3382.
16
LIU W, MAGNIN Y, FORSTER D, et al. Size-dependent hydrogen trapping in palladium nanoparticles[J]. J Mater Chem A, 2021, 9: 10354−10363.
17
TANG F, WANG L, WALLE M D, et al. An alloy chemistry strategy to tailoring the d-band center of Ni by Cu for efficient and selective catalytic hydrogenation of furfural[J]. J Catal, 2020, 383: 172−180.
18
FANG W, LIU S, STEFFENSEN A K, et al. On the role of Cu+ and CuNi alloy phases in mesoporous CuNi catalyst for furfural hydrogenation[J]. ACS Catal, 2023, 13: 8437−8444.
19
JASWAL A, SINGH P P, KAR A K, et al. Production of 2-methyl furan, a promising 2nd generation biofuel, by the vapor phase hydrodeoxygenation of biomass-derived furfural over TiO2 supported CuNi bimetallic catalysts[J]. Fuel, 2023, 245: 107726.
20
CUI H, LIAO X, REN Y, et al. Highly selective transfer hydrogenation of α, β-unsaturated aldehydes by frustrated Lewis pairs (FLPs) on oxygen-defect-rich Co3O4@NC[J]. J Catal, 2023, 428: 115126.
21
CHEN L, YE J, YANG Y, et al. Catalytic conversion furfuryl alcohol to tetrahydrofurfuryl alcohol and 2-methylfuran at terrace, step, and corner sites on Ni[J]. ACS Catal, 2020, 10: 7240−7249.
22
JIANG M, LIAN H. Enhancing low-temperature CO2 methanation performance by selectively covering Ni with CeO2 to form Ni-O-Ce interface active sites[J]. J Catal, 2024, 438: 115716.
23
ZOU Y, LIU Y, ZHANG S, et al. Dual active-sites of Co and oxygen vacancies in Co-doped CeO2-catalyzed toluene oxidation for the subsequent Knoevenagel condensation process[J]. Green Chem, 2023, 25: 7673−7681.
24
MENG X, YANG Y, CHEN L, et al. A control over hydrogenation selectivity of furfural via tuning exposed facet of Ni catalysts[J]. ACS Catal, 2019, 9: 4226−4235.
25
FU Q, YAN L, LIU D, et al. Highly-dispersed surface NiO species and exposed Ni (200) facets facilitating activation of furan ring for high-efficiency total hydrogenation of furfural[J]. Appl Catal B: Environ, 2024, 343: 123501.
26
YANG Y, WANG Y, LI S, et al. Selective hydrogenation of aromatic furfurals into aliphatic tetrahydrofurfural derivatives[J]. Green Chem, 2020, 22: 4937−4942.
27
SUNYOL C, OWEN R E, GINZALEZ M D, et al. Catalytic hydrogenation of furfural to tetrahydrofurfuryl alcohol using competitive nickel catalysts supported on mesoporous clays[J]. Appl Catal A: Gen, 2021, 611: 117903.
28
LIN W, ZHANG Y, MA Z, et al. Synergy between Ni3Sn2 alloy and Lewis acidic ReOx enables selectivity control of furfural hydrogenation to cyclopentanone[J]. Appl Catal B: Environ, 2024, 340: 123191.
29
MENG X, WANG L, CHEN L, et al. Charge-separated metal-couple-site in NiZn alloy catalysts towards furfural hydrodeoxygenation reaction[J]. J Catal, 2020, 392: 69−79.
30
YANG Y, CHEN L, CHEN Y, et al. The selective hydrogenation of furfural over intermetallic compounds with outstanding catalytic performance[J]. Green Chem, 2019, 21: 5352−5362.
31
WU Y, CAI S, WANG D, et al. Syntheses of water-soluble octahedral, truncated octahedral, and cubic Pt-Ni nanocrystals and their structure-activity study in model hydrogenation reactions[J]. J Am Chem Soc, 2012, 134: 8975−8981.
32
LI Z, YANG H, FENG S, et al. Selective hydrogenation of furfural to tetrahydrofurfuryl alcohol in isopropanol over hydrotalcite-derived nickel-based catalyst[J]. Chem Eng J, 2024, 482: 149044.
33
PANIEGO A R. Reporting physisorption data for gas/solid systems with special reference to the determination of surface area and porosity[J]. An Quim Ser A: Quim Fis Quim Tec, 1989, 85: 386−399.
34
REN Y, ZHANG M, PANG D, et al. Acid-base synergistic effect towards catalytic transfer hydrogenation reactions[J]. Chem Eng J, 2024, 495: 153618.
35
ZHANG Y, YONG C, YAN Z, et al. Influence of hydrothermal treatment on structural property of NiZrAl mixed-metal oxides and on catalytic steam reforming of glycerol for hydrogen production[J]. Int J Hydrogen Energy, 2020, 45: 22448−22458.
36
ZHENG Y, ZHANG R, ZHANG L, et al. A resol-assisted cationic coordinative Co-assembly approach to mesoporous ABO3 perovskite oxides with rich oxygen vacancy for enhanced hydrogenation of furfural to furfuryl alcohol[J]. Angew Chem Int Ed, 2021, 60: 4774−4781.
37
GIL A, DIAZ A, MONTES M. Passion and reactivation of nickle-catalysts[J]. J Chem Soc, Faraday Trans, 1991, 87: 791−795.
38
MORALES M, CONESA J, GUERRERO-RUIZ A, Rodriguez-Ramos I. Tunable selectivity of Ni catalysts in the hydrogenation reaction of 5-hydroxymethylfurfural in aqueous media: Role of the carbon supports[J]. Carbon, 2021, 182: 265−275.
39
ZHENG Y, ZHAO N, CHEN J. Enhanced direct deoxygenation of anisole to benzene on SiO2-supported NiGa alloy and intermetallic compound[J]. Appl Catal B: Environ, 2019, 250: 280−291.
40
GAO Z, LI C, FAN G, et al. Nitrogen-doped carbon-decorated copper catalyst for highly efficient transfer hydrogenolysis of 5-hydroxymethylfurfural to convertibly produce 2, 5-dimethylfuran or 2, 5-dimethyltetrahydrofuran[J]. Appl Catal B: Environ, 2018, 226: 523−533.
41
YAN T, BING W, XU M, et al. Acid-base sites synergistic catalysis over Mg-Zr-Al mixed metal oxide toward synthesis of diethyl carbonate[J]. RSC Adv, 2018, 8: 4695−4702.
42
GILKEY M J, PANAGiIOTOPOULOU P, MIRONENKO A V, et al. Mechanistic insights into metal lewis acid-mediated catalytic transfer hydrogenation of furfural to 2-Methylfuran[J]. ACS Catal, 2015, 5: 3988−3994.
43
CHEN H, HE S, XU M, et al. Promoted synergic catalysis between metal Ni and acid-base sites toward oxidant-free dehydrogenation of alcohols[J]. ACS Catal, 2017, 7: 2735−2743.
44
PRIETO G, MARTÍNET A, CONCEPCIÓB P, et al. Cobalt particle size effects in Fischer-Tropsch synthesis: Structural and in situ spectroscopic characterisation on reverse micelle-synthesised Co/ITQ-2 model catalysts[J]. J Catal, 2009, 266: 129−144.
45
ZHANG H, ZHOU X, LIU L, et al. Assembling Co clusters via nanosized ZIF-67 sprouted from CoAl-LDH nanoflower for selective hydrogenation[J]. Appl Catal B: Environ, 2023, 338: 123026.
46
ZHANG H, YANG J, ZHAO T, et al. In situ constructing ultrafine NiCo alloy confined in LDH nanoflower for efficient selective hydrogenation of furfural[J]. Chem Eng J, 2024, 494: 152881.
47
QIAN M, XU M, ZHOU S, et al. Template synthesis of two-dimensional ternary nickel-cobalt-nitrogen co-doped porous carbon film: Promoting the conductivity and more active sites for oxygen reduction[J]. J Colloid Interface Sci, 2020, 564: 276−285.
48
YU W, XIONG K, JI N, et al. Theoretical and experimental studies of the adsorption geometry and reaction pathways of furfural over FeNi bimetallic model surfaces and supported catalysts[J]. J Catal, 2014, 317: 253−262.
Appendix
Less
Year 2026 volume 54 Issue 8
PDF
129
52
Cite this Article
BibTeX
Article Info
doi: 10.1016/S1872-5813(26)60664-0
  • Receive Date：2025-06-28
  • Online Date：2026-09-23
  • Published：2026-08-10
Article Data
Affiliations
History
  • Received：2025-06-28
  • Revised：2025-11-09
  • Accepted：2025-12-01
Affiliations
    1State Key Laboratory of Coking Coal Resources Green Exploitation, Zhengzhou University, Zhengzhou 450001, China
    2Engineering Research Center of Advanced Functional Material Manufacturing of Ministry of Education, Zhengzhou University, Zhengzhou 450001, China
    3School of Chemical Engineering, Zhengzhou University, Zhengzhou 450001, China
    4School of Material and Chemical Engineering, Xuzhou University of Technology, Xuzhou 221018, China

Corresponding:

References
Share
https://castjournals.cast.org.cn/joweb/rlhxxb/EN/10.1016/S1872-5813(26)60664-0
Share to
QR

Scan QR to access full text

Cite this article
BibTeX
Citations
表12种不同金属材料的力学参数
科
Family		 属数
Number of
genus		 种数
Number of
species		 占总种数比例
Percentage of
total species (%)		 属
Genus		 种数
Number of
species		 占总种数比例
Percentage of total
species (%)
鹅膏菌科Amanitaceae 2 11 5.26 鹅膏菌属 Amanita 10 4.78
小菇科 Mycenaceae 2 12 5.74 丝盖伞属 Inocybe 5 2.39
多孔菌科 Polyporaceae 8 14 6.70 蜡蘑属 Laccaria 5 2.39
红菇科 Russulaceae 3 23 11.00 小皮伞属 Marasmius 6 2.87
小菇属 Mycena 11 5.26
光柄菇属 Pluteus 5 2.39
红菇属 Russula 17 8.13
栓菌属 Trametes 5 2.39
关闭全屏
  • BibTeX
  • EndNote
  • RefWorks
  • TxT
Links
Articles
Latest Articles
Most Read
Collections
Updates
Events
News
Multimedia
About
About Us
Contact
No. 86 Xueyuan South Road, Haidian District, Beijing
100081
010-62662699(Operation and Technical Support)
qkjq@cast.org.cn

Copyright © 2025 China Association for Science and Technology. All rights reserved. For all open access content, the relevant licensing terms apply.
Sponsored by the Office of the Leading Group for Cybersecurity and Informatization of CAST, and supported by Science and Technology Review Publishing House