Facilitating Lithium-Ion Diffusion in Layered Cathode Materials by Introducing Li<sup>+</sup>/Ni<sup>2+</sup> Antisite Defects for High-Rate Li-Ion Batteries

Facilitating Lithium-Ion Diffusion in Layered Cathode Materials by Introducing Li⁺/Ni²⁺ Antisite Defects for High-Rate Li-Ion Batteries

PDF

Zhongfeng Tang¹, Sen Wang², Jiaying Liao¹, Shuo Wang¹, Xiaodong He¹, Bicai Pan², Haiyan He², Chunhua Chen¹

Research. Vol 2019 Article ID 2198906

Less

Research. Vol 2019 Article ID 2198906

• Research Article •

Facilitating Lithium-Ion Diffusion in Layered Cathode Materials by Introducing Li⁺/Ni²⁺ Antisite Defects for High-Rate Li-Ion Batteries

Full

Zhongfeng Tang¹, Sen Wang², Jiaying Liao¹, Shuo Wang¹, Xiaodong He¹, Bicai Pan², Haiyan He², Chunhua Chen¹

Affiliations

¹1 CAS Key Laboratory of Materials for Energy Conversions, Department of Materials Science and Engineering & Collaborative Innovation Center of Suzhou Nano Science and Technology, University of Science and Technology of China, Anhui Hefei 230026, China

²2 School of Physical Sciences, University of Science and Technology of China, Anhui Hefei 230026, China

About Author:

Authors’ Contributions

Zhongfeng Tang and Sen Wang contributed equally to this work.

Published: 2019-09-20 doi: 10.34133/2019/2198906

Outline

Abstract

Less

Li⁺/Ni²⁺ antisite defects mainly resulting from their similar ionic radii in the layered nickel-rich cathode materials belong to one of cation disordering scenarios. They are commonly considered harmful to the electrochemical properties, so a minimum degree of cation disordering is usually desired. However, this study indicates that LiNi_0.8Co_0.15Al_0.05O₂ as the key material for Tesla batteries possesses the highest rate capability when there is a minor degree (2.3%) of Li⁺/Ni²⁺ antisite defects existing in its layered structure. By combining a theoretical calculation, the improvement mechanism is attributed to two effects to decrease the activation barrier for lithium migration: (1) the anchoring of a low fraction of high-valence Ni²⁺ ions in the Li slab pushes uphill the nearest Li⁺ ions and (2) the same fraction of low-valence Li⁺ ions in the Ni slab weakens the repulsive interaction to the Li⁺ ions at the saddle point.

Cite this Article

Zhongfeng Tang, Sen Wang, Jiaying Liao, Shuo Wang, Xiaodong He, Bicai Pan, Haiyan He, Chunhua Chen. Facilitating Lithium-Ion Diffusion in Layered Cathode Materials by Introducing Li⁺/Ni²⁺ Antisite Defects for High-Rate Li-Ion Batteries[J]. Research, 2019 , 2019 (9) : 2198906 - . DOI: 10.34133/2019/2198906

Full Text

Less

1. Introduction

Less

Lithium-ion batteries are experiencing the large applications in mobile electronic devices and electric vehicles worldwide. High-energy density and high-power density are the two most important factors in a commercial lithium-ion battery. For the cathode materials, compared to the widely used LiFePO₄, LiMn₂O₄, and LiNi_1/3Co_1/3Mn_1/3O₂ [1–4], the layered nickel-rich materials with higher capacity (170-200 mAh g^-1) and appropriate working voltage (~3.75 V), such as LiNi_0.6Co_0.2Mn_0.2O₂, LiNi_0.8Co_0.1Mn_0.1O₂ (NCM811), and LiNi_0.8Co_0.15Al_0.05O₂ (NCA) [5–8], have attracted more and more attention.

One of the challenging problems of layered nickel-rich cathode materials is the Li⁺/Ni²⁺ antisite defects which result from their similar ionic radii (Li⁺: 0.072 nm, Ni²⁺: 0.069 nm) [9, 10]. It is very difficult to synthesize a pure LiNiO₂ phase because a high-temperature treatment leads to the phase transition from LiNiO₂ to

L i 1 ‐ x N i 1 + x O 2

which has a partially disordered cation distribution at the lithium layer, while a low-temperature treatment cannot bring sufficient crystallinity [11]. Although the cosubstitution of Co and Mn or Al for Ni can greatly inhibit the LiNiO₂ phase change, there is still some cation disordering in Ni-rich layered materials because Ni²⁺ ions cannot be completely oxidized to Ni³⁺ even under oxygen-rich atmospheres [12, 13]. If there are a lot of Ni²⁺ ions in the lithium layer (i.e., 3b sites), the diffusion of lithium ions is inevitably hindered in the two-dimensional channels, which is why the researchers desire to decrease the cation disordering in layered materials [14–16].

Nevertheless, the Li⁺/Ni²⁺ antisite defects are not always detrimental to layered materials. Zheng et al. found that these defects benefit the thermal stability for Ni-rich NCM materials, because the Ni in the Li layer would form 180° Ni−O−Ni super exchange chains [17]. Moreover, it can partially relieve the magnetic frustration by forming a stable antiferromagnetic state in hexagonal sublattice with nonmagnetic ions located in centers of the hexagons [18]. Lee et al. have proved that a little amount of Ni²⁺ ions occupying Li⁺ (3b) sites is not a major obstacle to the diffusion of Li⁺ ions in the lithium layer [19]. In some cases, the substitution of inactive ions for Li⁺ or Na⁺ in the layered cathode materials can even improve the electrochemical properties due to the inhibition of phase transition and the enlargement of lattice parameters [20–22]. On the other hand, for the ions at 3a sites, Kang et al. indicated that [23] lower valence transition metal ions (Cu²⁺ or Ni²⁺ vs. Co³⁺ or Mn⁴⁺) can result in a weaker electrostatic interaction between Li⁺ in the activated state and the transition metal ions at 3a sites and thus substantially decrease the activation barrier for the migration of Li⁺ ions to the nearest vacancies. Hence, it is reasonable to speculate that the Li⁺ ions at 3a sites can further decrease the activation barrier for the diffusion of Li⁺ (3b) ions. Furthermore, a Ni²⁺ ion at 3b site in the lithium layer may also have a bigger electrostatic interaction (repulsion) with the nearest six Li⁺ ions, which can increase the energy of the activated lithium ions and thus decrease the activation barrier for lithium-ion migration.

Herein, taking NCA as an example of the Ni-rich cathode materials, we investigated the relationships between the rate capability and the Li⁺/Ni²⁺ antisite defects by combining experimental and theoretical calculations. Our experimental results indicate that the NCA sample with 2.3% Li⁺/Ni²⁺ exchange has the highest Li⁺ diffusion coefficient and exhibits the best rate capability, and our calculation results reveal that the activation barrier for the diffusion of Li⁺ ions significantly decreases when there is a minor degree of Li⁺/Ni²⁺ antisite defect in the Ni-rich layered oxides.

2. Materials and Methods

Less

2.1. Synthesis of NCA Materials

The NCA samples were synthesized by a thermal polymerization method as described in our previous studies [24]. Typically, lithium nitrate (LiNO₃), nickel nitrate (Ni(NO₃)₂·6H₂O), cobalt nitrate (Co(NO₃)₂·6H₂O), and aluminum nitrate (Al(NO₃)₃·9H₂O) were dissolved in deionized water to prepare the precursor solutions. The molar ratio of Li, Ni, Co, and Al was 1.00 : 0.8 : 0.15 : 0.05, and the metal (Li+Ni+Co+Al) concentration was 1.0 mol L^-1. Then, acrylic acid (AA, CH₂=CHCOOH) was added into the mixture as a complexing agent, and the volume ratio of AA and H₂O is 1 : 2. The mixed solution was kept at 160°C for 6 h to form xerogel, followed by thoroughly grinding and sintering at 500°C in air to remove the organics. The obtained precursor powders were again sintered at a tube furnace with flowing oxygen atmosphere for 12 h, and the sintering temperatures were set as 720°C, 735°C, 750°C, 765°C, and 780°C, respectively. For convenience, the prepared samples were denoted as NCA-720, NCA-735, NCA-750, NCA-765, and NCA-780, respectively.

2.2. Structure and Morphology Characterizations

Morphological studies were performed using scanning electron microscopy (SEM, JSM-6390LA, JEOL). The crystal structures of the prepared samples were measured by a theta/theta rotating anode X-ray diffractometer (XRD, Rigaku TTR-lll). The X-ray Rietveld refinement was performed by using a GSAS/EXPGUI package [25].

2.3. Electrochemical Analysis

Li-half 2032 coin cells were used to test the electrochemical properties. NCA powders (84 wt%), carbon black (8 wt%), and polyvinylidene fluoride (8 wt%) that dispersed in N-methyl-2-pyrrolidone were thoroughly mixed to make slurries. Then, the slurry was coated on an aluminum foil and dried at 80°C in an oven overnight. The laminates were punched into round disks with a diameter of 12 mm. A typical electrode disk contained 4 mg NCA. The coin cells were assembled in an Ar-filled glove box (MBraun Labmaster 130) with an electrolyte of 1 M LiPF₆ in ethylene carbonate (EC) and diethyl carbonate (DEC) (

EC : DEC = 1 : 1 V / V

) and a separator of Celgard 2400 porous membrane.

The cells were charged/discharged on a Neware BTS 610 multichannel battery cycler at a constant current (0.1C-10C,

1 C = 180 mA g − 1

) in the voltage range of 2.75-4.3 V for five cycles, respectively, to investigate the rate performance. In order to calculate the lithium-ion diffusion coefficient, the cyclic voltammograms (CV) were conducted on a CHI640 Electrochemical Workstation with a scan rate of 0.1, 0.3, 0.5, 0.8, and 1.0 mV s^-1, respectively, between 2.5 and 4.5 V. And the impedance measurement was also conducted, at a fully discharged state, using electrochemical impedance spectroscopy (EIS) in the frequency range of 0.01 Hz-100 kHz. The amplitude of the alternating current (AC) signal was 5 mV.

2.4. Computational Method

All calculations were performed by using a Vienna ab initio simulation package (VASP 5.3.3) based on the local density approximation [26]. The interaction between ions and valence electrons was described using projector augmented wave (PAW) potentials [27], and the on-site electron-electron interactions were taken into account by performing GGA+U level calculations with

U ‐ J = 4.91 eV

for Co-3d electrons and

U ‐ J = 6 eV

for Ni-3d electrons taken from the literatures [28–33]. A 120-atom supercell consisting of

2 × 5 × 1

primitive unit cells was employed, as shown in Figure 1, and all calculations were performed with a plane wave cutoff of 500 eV. In addition, we found a

k

-point sampling of

5 × 2 × 2

within the Monkhorst-Pack special

k

-point scheme in the Brillouin zone sufficiently dense for the bulk unit cell [34]. The energy relaxation iterates until the forces acting on all the atoms were less than 10^-2 eV/Å. The climbing image nudged elastic band (CI-NEB) method was used to determine the minimum energy paths for diffusion of Li atoms in LiNi_0.8Co_0.2O₂ [35–37]. With these settings, we obtained the optimal crystallographic parameters of LiNi_0.8Co_0.2O₂,

a = 2.79 Å

b = 2.95 Å

, and

c = 14.09 Å

, which are in good agreement with the experimental values (

a = 2.87 Å

b = 2.87 Å

, and

c = 14.13 Å

) [38].

3. Results

Less

3.1. Morphology and Structure Characterization

Figure S1 shows the SEM images of the NCA samples sintered at different temperatures, which consist of irregular particles around 700 nm-1 μm and without significant differences in the morphology and particle size. As indicated in Figures 2(a)–2(e), all their diffraction peaks can be well indexed in a hexagonal structure of α-NaFeO₂ type without any impurity [39, 40]. In order to reveal the detailed crystal information, the XRD data have been refined by the Rietveld method using GSAS software. In the refinement, Li₁/Ni₂ are set at 3b sites (0, 0, 0.5), Li₂/Ni₁/Co₁/Al₁ at 3a sites (0, 0, 0), and O at 6c sites (0, 0,

z

) where

z = 0.25

[41]. For the five samples, the average valences of transition metals (Ni and Co) are almost the same according to the semiquantitative analysis of X-ray photoelectron spectroscopy (XPS) (Figures S2 and S3). For the cation disordering, only Li⁺ and Ni²⁺ occupations are considered to be exchanged because Co³⁺ (0.061 nm) and Al³⁺ (0.054 nm) in the lithium layer would cause a drastically increased system energy due to the big differences in ionic radii and valences with Li⁺. The refinement results are given in Table 1 and Figure 2(f), according to which two crystal diagrams of the TM layer and the Li layer (seen from

c

-axis direction) for NCA-750 are given in Figure S4 to show the atom arrangements. It is quite clear that the ratio of Li⁺/Ni²⁺ exchange is highly related to the intensity ratio of

I 003 / I 104

that has been used to qualitatively analyze the degree of cation mixing in layered materials. It is widely believed that the lower the degree of cation disordering, the better the electrochemical properties [12, 14–16, 42]. NCA-720 has a relatively high degree of Li/Ni mixing because the temperature is not high enough to remove all of the lattice defects. The rest of the samples show an approximate linear relationship between the ratio of Li/Ni exchange and sintering temperature, which may be attributed to the phase transition of LiNiO₂ with increasing sintering temperature. It seems that NCA-735 which has the least Li/Ni exchange in the layered structure should have exhibited the best electrochemical properties. However, our electrochemical measurements give us some anomalous but interesting results as shown in the following part.

3.2. Electrochemistry

The electrochemical properties of NCA electrode materials are shown in Figure 3. In Figure 3(a), the charge/discharge profiles are obtained at 0.1C in the range of 2.75-4.3 V. Obviously, the discharge capacity depends highly on the sintering temperature. NCA-750 achieves the highest initial discharge capacity of 187.9 mAh g^-1 as well as the highest initial Coulombic efficiency of 89.5%. The CV curves with a scan rate of 0.1 mV s^-1 in Figure 3(b) show the redox behaviors of the transition metals as well as the phase transitions during the charging/discharging process. All the samples show the similar oxidation of Ni³⁺ to Ni⁴⁺ at around 3.8 V but with slight difference in the oxidation peaks which may be caused by the larger polarization for NCA-720 and NCA-765. It should also be noted that NCA-780 has another oxidation peak at around 4.5 V which mainly is attributed to the phase transition from H1 to O1 [43]. As mentioned before, the LiNiO₂-based materials decompose at high temperatures and form the nonstoichiometric

L i 1 ‐ x Ni O 2

phase. And that is the main reason for its lowest capacity in the voltage range of 2.75-4.3 V. As shown in Figure 3(c), the rate performances differ significantly with different sintering temperatures. NCA-750 shows the best rate capability even with a capacity of 129.8 mAh g^-1 at 10C rate while it is only 119.5 mAh g^-1 for NCA-735. And the EIS also shows the results consistent with the rate performance (Figure 3(d)). These results and the diffusion coefficient of lithium ions (see below) indicate that an appropriate amount of Li⁺/Ni²⁺ antisite defects in the layered structure is beneficial to the fast diffusion of Li⁺ in the lithium layer.

The lithium-ion diffusion coefficient was calculated based on the CV curves with different scan rates (Figure 4) [44]. In a diffusion controlled process, the peak current is proportional to the square root of the scanning rates, which is in line with the Randles-Sevcik equation:

(1) i p = 2.69 ∗ 105 ∗ n 3 / 2 C Li A v 1 / 2 D Li 1 / 2,

where

i p

is the peak current,

n

is the number of the electrons transferred,

C Li

is the concentration of Li⁺,

A

is the surface area of the electrode,

v

is the scan rate, and

D Li

is the diffusion coefficient of lithium ions. As shown in Figures 4(a)–4(e), the deintercalation

O ‐ D Li

and intercalation

R ‐ D Li

are calculated from the oxidation peak and reduction peak, respectively, and the data are summarized in Table 2. The slope of the linear fit of each peak, as shown in Figure 4(f), is positively proportional to the diffusion coefficient of lithium ions. Clearly, the diffusion coefficient of the deintercalation process has a higher dependence on temperature, which is consistent with the rate performance, than that of the intercalation process.

3.3. Calculation Results

In order to understand the anomalous experimental result that NCA-750 with higher Li/Ni antisite defects show better electrochemical properties, especially the rate capability, than that of NCA-735 which contains the lowest antisite defects, we perform the calculations from the perspective of activation barrier which strongly affects the diffusion of lithium ions in electrode materials. However, due to the limited calculation abilities, we can only build a 120-atom supercell consisting of

2 × 5 × 1

LiNi_0.8Co_0.2O₂ primitive unit cells as mentioned before but not a LiNi_0.8Co_0.15Al_0.05O₂ supercell in which the five percent aluminum ions would need a huge amount of computations.

In a typical layered structure as shown in Figure 5(a), the lithium ions and transition metal ions alternately occupy a layer of octahedron sites, which means that there is a two-dimensional transfer pathway for lithium ions. When a lithium ion migrates to the nearest lithium vacancy, it has to pass through the adjacent tetrahedron sites, in which the neighboring transition metal ion hinders the Li⁺ diffusion because of the strong electrostatic repulsion (Figure 5(b)) [23]. And that is the main reason for the activation barrier in layered electrode materials. If the high-valence TM ions are replaced by the Li⁺ ions, the activation barrier for Li⁺ diffusion decreases due to the weaker electrostatic repulsion (Figure 5(c)). On the other hand, when a high-valence TM ion occupies Li⁺ sites, i.e., Li/Ni exchange (Figures 5(d) and 5(e)), it should also have some effect on the activation barrier for the six nearest lithium ions’ diffusion, which will be discussed in the following part in detail.

We then calculate the activation barriers in lithium vacancy environments, i.e., a lithium ion migrates to occupy its nearest lithium vacancy in Li slab, as shown in Figure 6. This is similar to the Li diffusion in LiCoO₂ [45]. Firstly, we explore Li diffusion in LiNi_0.8Co_0.2O₂ without Li-Ni exchange and find that the activation barriers are approximately 0.69 eV, as shown in Figure 6(a). Then, we consider the Li diffusion in LiNi_0.8Co_0.2O₂ with 4.17% Li-Ni exchange, i.e., one Ni for one Li in the 120-atom supercell. The initial site of a Li ion is adjacent to a Ni ion in the Li slab, and the diffusion path is under the Ni ion in Ni(Co) slab, as shown in Figure 6(b). The calculated activation barriers decrease to be 0.45 eV, indicating that Li-Ni exchange favors the diffusion of Li. For this ratio of Li-Ni exchange, we also concern another case of Li diffusion path; that is, a diffusing Li ion is under an exchanged Li ion in the Ni(Co) slab, as shown in Figure 6(c). Surprisingly, the activation barrier decreases to 0.25 eV. Moreover, we further investigate diffusion of Li at the next neighboring Ni ion in the Li slab and find that the activation barriers are almost the same as those in LiNi_0.8Co_0.2O₂ without Li-Ni exchange. This means that the Ni ions in the Li slab just influence the diffusion of Li ions within the scope of the neighboring region.

Then, we focus on Li diffusion in LiNi_0.8Co_0.2O₂ with different ratios of Li-Ni exchange. Our calculations reveal that the activation barrier further decreases with the increase of the ratio of Li-Ni exchange, as depicted in Figure 7(a). From Figure 7(a), we can see that for each concerned ratio of Li-Ni exchange, the activation barrier decreases by 0.2 eV at least when the diffusion path is under a Ni ion, as compared to that under a Li ion. Therefore, we can conclude that Li-Ni exchange promotes the diffusion possibilities of Li in LiNi_0.8Co_0.2O_2.

To understand this interesting phenomenon above, we investigate the electronic properties of the system. The charge distribution for the states at the saddle points of the diffusion paths for the typical cases is displayed in Figures 7(b)–7(d). We can see clearly from Figure 7(b) that the interactions between Li and O ions are weak while the interactions between Ni and O ions are strong in LiNi_0.8Co_0.2O₂. When Li-Ni exchange occurs with a Ni ion appearing in the Li slab, stronger interactions between Ni ion in the Li slab and O ions drive Li ions near this Ni ion diffuse to its neighboring vacancies, and it reduces the activation barriers of Li diffusion around the Ni ion. This is why the Ni ions in Li slab can only alter the diffusion of Li ions within the scope of the neighboring region. For the same reason, when the Li diffusion path is under a Li ion, the above Li ion will reduce the interactions with surrounding O ions and then the distance between O ions and Li diffusion path, which results in the further decrease of activation barriers.

However, as shown in Figure 8, if there are too many Li-Ni antisite defects in Ni-rich layered materials, the total system energy drastically increases, which means that the layered structure becomes quite unstable with the increasing Li/Ni antisite defects. Therefore, it seems impossible to synthesize the layered structure materials with so many defects under the mentioned experimental conditions. On the other hand, the excessive inactive TM ions in Li slab would inevitably cause a longer diffusion path for lithium ions. Therefore, the highest rate of Li⁺ diffusion can be achieved when the benefit from the decrease of activation barriers and hindrance reach a balance, which corresponds to the experimental result of 2.39% for NCA-750 in our study.

4. Discussion

Less

In this work, our experimental results show that, unlike the widely assumed, the layered Ni-rich material with an appropriate amount of Li/Ni antisite defects exhibits the best electrochemical properties. By building a 120-atom supercell consisting of

2 × 5 × 1

LiNi_0.8Co_0.2O₂ primitive unit cells, we have investigated the relationships between the Li/Ni antisite defects and activation barrier for lithium ions’ diffusion. When a Ni²⁺ ion occupies a Li⁺ site, the stronger interactions between Ni and O drive the nearest Li⁺ ion diffuse to the neighboring vacancies. In other words, high-valence TM ions can decrease the activation barrier for the diffusion of lithium ions, resulting in the improved rate capabilities. And the activation barrier can be further decreased when there is a synergy between Ni (3b sites) and Li (3a sites), i.e., Li/Ni exchange. However, a large amount of Li/Ni antisite defects cause the drastic increase of system energy and make the layered structure unstable. We expect that these interesting findings offer some opportunities to design the layered cathode materials for advanced lithium-ion batteries.

Funding

Less

National Natural Science Foundation of China(51577175)
National Key R&D Program of China(2018YFB0905400)

References

Less

Amisse

, Sougrati

M. T.

, Stievano

, Davoisne

, Dražič

, Budič

, Dominko

, and Masquelier

, “Singular structural and electrochemical properties in highly defective LiFePO₄ powders,” Chemistry of Materials, vol. 27, no. 12, pp. 4261–4273, 2015

, Liu

, Zhang

, Cui

, and Chen

, “Strategies for improving the cyclability and thermo-stability of LiMn₂O₄-based batteries at elevated temperatures,” Journal of Materials Chemistry A, vol. 3, no. 8, pp. 4092–4123, 2015

Rao

C. V.

, Reddy

A. L. M.

, Ishikawa

, and Ajayan

P. M.

, “LiNi_1/3Co_1/3Mn_1/3O₂–graphene composite as a promising cathode for lithium-ion batteries,” ACS Applied Materials & Interfaces, vol. 3, no. 8, pp. 2966–2972, 2011

, Yao

, and Cao

, “LiNi_1/3Co_1/3Mn_1/3O₂ nanoplates with {010} active planes exposing prepared in polyol medium as a high-performance cathode for Li-ion battery,” ACS Applied Materials & Interfaces, vol. 6, no. 7, pp. 5075–5082, 2014

Kim

, Kim

M. G.

, Jeong

H. Y.

, Nam

, and Cho

, “A new coating method for alleviating surface degradation of LiNi_0.6Co_0.2Mn_0.2O₂ cathode material: nanoscale surface treatment of primary particles,” Nano Letters, vol. 15, no. 3, pp. 2111–2119, 2015

Lee

J. H.

, Yoon

C. S.

, Hwang

J. Y.

, Kim

S. J.

, Maglia

, Lamp

, Myung

S. T.

, and Sun

Y. K.

, “High-energy-density lithium-ion battery using a carbon-nanotube–Si composite anode and a compositionally graded Li[Ni_0.85Co_0.05Mn_0.10]O₂ cathode,” Energy & Environmental Science, vol. 9, no. 6, pp. 2152–2158, 2016

Zhou

, Meng

, Zhang

, Chen

, Lu

, Cao

, Cheng

, and Chen

, “Stable layered Ni-rich LiNi_0.9Co_0.07Al_0.03O₂ microspheres assembled with nanoparticles as high-performance cathode materials for lithium-ion batteries,” Journal of Materials Chemistry A, vol. 5, no. 6, pp. 2724–2731, 2017

Tang

, Bao

, Du

, Shao

, Gao

, Zou

, and Chen

, “Surface surgery of the nickel-rich cathode material LiNi_0.815Co_0.15Al_0.035O₂: toward a complete and ordered surface layered structure and better electrochemical properties,” ACS Applied Materials & Interfaces, vol. 8, no. 50, pp. 34879–34887, 2016

, Tian

, Su

, Wang

, Zhang

, Bao

, He

, Li

, and Chen

, “Effect of Ni²⁺ content on lithium/nickel disorder for Ni-rich cathode materials,” ACS Applied Materials & Interfaces, vol. 7, no. 14, pp. 7702–7708, 2015

, Li

, Luo

, Li

, Fan

, and Li

, “Nickel-rich layered microspheres cathodes: lithium/nickel disordering and electrochemical performance,” ACS Applied Materials & Interfaces, vol. 6, no. 18, pp. 15822–15831, 2014

Hiranoa

, Kannoa

, Kawamotoa

, Takedab

, Yamaurac

, Takanoc

, Ohyamad

, Ohashid

, and Yamaguchi

, “Relationship between non-stoichiometry and physical properties in LiNiO₂,” Solid State Ionics, vol. 78, no. 1-2, pp. 123–131, 1995

, Liu

, Peng

, Du

, and Cao

, “Synthesis and electrochemical properties of LiNi_0.8Co_0.15Al_0.05O₂ prepared from the precursor Ni_0.8Co_0.15Al_0.05OOH,” Journal of Power Sources, vol. 198, pp. 258–263, 2012

Bianchi

, Bach

, Belhomme

, Farcy

, Pereira-Ramos

J. P.

, Caurant

, Baffier

, and Willmann

, “Electrochemical investigation of the Li insertion–extraction reaction as a function of lithium deficiency in Li_1−xNi_1+xO₂,” Electrochimica Acta, vol. 46, no. 7, pp. 999–1011, 2001

Ding

, Mu

, Wu

, Wang

, Zhao

, and Wu

, “Recent progresses on nickel-rich layered oxide positive electrode materials used in lithium-ion batteries for electric vehicles,” Applied Energy, vol. 195, pp. 586–599, 2017

Manthiram

, Knight

J. C.

, Myung

S. T.

, Oh

S. M.

, and Sun

Y. K.

, “Nickel-rich and lithium-rich layered oxide cathodes: progress and perspectives,” Advanced Energy Materials, vol. 6, no. 1, article 1501010, 2016

Schipper

, Erickson

E. M.

, Erk

, Shin

J. Y.

, Chesneau

F. F.

, and Aurbach

, “Review—Recent advances and remaining challenges for lithium ion battery cathodes I. nickel-rich, LiNi_xCo_yMn_zO₂,” Journal of the Electrochemical Society, vol. 164, no. 1, pp. A6220–A6228, 2017

Zheng

, Liu

, Hu

, Wei

, Song

, Ren

, Wang

, Rao

, Lin

, Chen

, Lu

, Wang

, Amine

, and Pan

, “Tuning of thermal stability in layered Li(Ni_xMn_yCo_z)O₂,” Journal of the American Chemical Society, vol. 138, no. 40, pp. 13326–13334, 2016

Xiao

, Liu

, He

, Chen

, Zhang

, Luo

, Lu

, Wang

, Zhu

, Hu

, Teng

, Xin

, Zheng

, Liang

, Wang

, Chen

, Huang

, Pan

, and Chen

, “Insight into the origin of lithium/nickel ions exchange in layered Li(Ni_xMn_yCo_z)O₂ cathode materials,” Nano Energy, vol. 49, pp. 77–85, 2018

Lee

, Muhammad

, Kim

, Lee

, Jeong

, Son

, Ryou

J. H.

, and Yoon

W. S.

, “New insight into Ni-rich layered structure for next-generation Li rechargeable batteries,” Advanced Energy Materials, vol. 8, no. 4, article 1701788, 2018

Xie

, Du

, Hu

, Peng

, and Cao

, “The role of sodium in LiNi_0.8Co_0.15Al_0.05O₂ cathode material and its electrochemical behaviors,” The Journal of Physical Chemistry C, vol. 120, no. 6, pp. 3235–3241, 2016

Z. Y.

, Gao

, Zhang

, Hu

, and Liu

, “New insights into designing high-rate performance cathode materials for sodium ion batteries by enlarging the slab-spacing of the Na-ion diffusion layer,” Journal of Materials Chemistry A, vol. 4, no. 9, pp. 3453–3461, 2016

Huang

, Wang

, Jing

, Guo

, Li

, and Yang

, “Investigation on the effect of Na doping on structure and Li-ion kinetics of layered LiNi_0.6Co_0.2Mn_0.2O₂ cathode material,” Electrochimica Acta, vol. 192, pp. 120–126, 2016

Kang

, Meng

Y. S.

, Bréger

, Grey

C. P.

, and Ceder

, “Electrodes with high power and high capacity for rechargeable lithium batteries,” Science, vol. 311, no. 5763, pp. 977–980, 2006

Q.-X.

, Tang

Z.-F.

, Ma

X.-H.

, Zang

, Sun

, Shao

, Wen

Z.-Y.

, and Chen

C.-H.

, “Improving the electrochemical properties of high-energy cathode material LiNi_0.5Co_0.2Mn_0.3O₂ by Zr doping and sintering in oxygen,” Solid State Ionics, vol. 279, pp. 11–17, 2015

Toby

B. H.

, “EXPGUI, a graphical user interface for GSAS,” Journal of Applied Crystallography, vol. 34, no. 2, pp. 210–213, 2001

Kresse

, and Furthmüller

, “Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set,” Physical Review B, vol. 54, no. 16, pp. 11169–11186, 1996

Blöchl

P. E.

, “Projector augmented-wave method,” Physical Review B, vol. 50, no. 24, pp. 17953–17979, 1994

Perdew

J. P.

, Burke

, and Ernzerhof

, “Generalized gradient approximation made simple,” Physical Review Letters, vol. 77, no. 18, pp. 3865–3868, 1996

Dudarev

S. L.

, Botton

G. A.

, Savrasov

S. Y.

, Humphreys

C. J.

, and Sutton

A. P.

, “Electron-energy-loss spectra and the structural stability of nickel oxide: an LSDA+U study,” Physical Review B, vol. 57, no. 3, pp. 1505–1509, 1998

Kramer

, and Ceder

, “Tailoring the morphology of LiCoO₂: a first principles study,” Chemistry of Materials, vol. 21, no. 16, pp. 3799–3809, 2009

Zhou

, Cococcioni

, Marianetti

C. A.

, Morgan

, and Ceder

, “First-principles prediction of redox potentials in transition-metal compounds with LDA+U,” Physical Review B, vol. 70, no. 23, article 235121, 2004

Moriwake

, Kuwabara

, Fisher

C. A. J.

, Huang

, Hitosugi

, Ikuhara

Y. H.

, Oki

, and Ikuhara

, “First-principles calculations of lithium-ion migration at a coherent grain boundary in a cathode material, LiCoO₂,” Advanced Materials, vol. 25, no. 4, pp. 618–622, 2013

Kim

, Lee

, and Kang

, “First-principles and experimental investigation of the morphology of layer-structured LiNiO₂ and LiCoO₂,” Journal of Materials Chemistry, vol. 22, no. 25, pp. 12874–12881, 2012

Monkhorst

H. J.

, and Pack

J. D.

, “Special points for brillouin-zone integrations,” Physical Review B, vol. 13, no. 12, pp. 5188–5192, 1976

Mills

, Jónsson

, and Schenter

G. K.

, “Reversible work transition state theory: application to dissociative adsorption of hydrogen,” Surface Science, vol. 324, no. 2-3, pp. 305–337, 1995

Henkelman

, Uberuaga

B. P.

, and Jonsson

, “A climbing image nudged elastic band method for finding saddle points and minimum energy paths,” The Journal of Chemical Physics, vol. 113, no. 22, pp. 9901–9904, 2000

Henkelman

, and Jonsson

, “Improved tangent estimate in the nudged elastic band method for finding minimum energy paths and saddle points,” The Journal of Chemical Physics, vol. 113, no. 22, pp. 9978–9985, 2000

Xiao

, Yang

, Zhao

, Ai

, Yang

, and Cao

, “Synthesis and electrochemical properties of submicron LiNi_0.8Co_0.2O₂ by a polymer-pyrolysis method,” Electrochimica Acta, vol. 53, no. 6, pp. 3007–3012, 2008

Makimura

, Sasaki

, Nonaka

, Nishimura

Y. F.

, Uyama

, Okuda

, Itou

, and Takeuchi

, “Factors affecting cycling life of LiNi_0.8Co_0.15Al_0.05O₂ for lithium-ion batteries,” Journal of Materials Chemistry A, vol. 4, no. 21, pp. 8350–8358, 2016

Zhang

H. Z.

, Liu

, Song

D. W.

, Zhang

L. Q.

, and Bie

L. J.

, “A new synthesis strategy towards enhancing the structure and cycle stabilities of the LiNi_0.80Co_0.15Al_0.05O₂ cathode material,” Journal of Materials Chemistry A, vol. 5, no. 2, pp. 835–841, 2017

Schipper

, Dixit

, Kovacheva

, Talianker

, Haik

, Grinblat

, Erickson

E. M.

, Ghanty

, Major

D. T.

, Markovsky

, and Aurbach

, “Stabilizing nickel-rich layered cathode materials by a high-charge cation doping strategy: zirconium-doped LiNi_0.6Co_0.2Mn_0.2O₂,” Journal of Materials Chemistry A, vol. 4, no. 41, pp. 16073–16084, 2016

Liu

, Oh

, Liu

, Lee

M. J.

, Cho

, Chae

, Kim

, and Cho

, “Nickel-rich layered lithium transition-metal oxide for high-energy lithium-ion batteries,” Angewandte Chemie International Edition, vol. 54, no. 15, pp. 4440–4457, 2015

Chang

, Hallstedt

, and Music

, “Thermodynamic description of the LiNiO₂–NiO₂ pseudo-binary system and extrapolation to the Li(Co,Ni)O₂–(Co,Ni)O₂ system,” Calphad, vol. 37, pp. 100–107, 2012

Zou

B. K.

, Wang

H. Y.

, Qiang

Z. Y.

, Shao

, Sun

, Wen

Z. Y.

, and Chen

C. H.

, “Mixed-carbon-coated LiMn_0.4Fe_0.6PO₄ nanopowders with excellent high rate and low temperature performances for lithium-ion batteries,” Electrochimica Acta, vol. 196, pp. 377–385, 2016

van der Ven

, Ceder

, Asta

, and Tepesch

P. D.

, “First-principles theory of ionic diffusion with nondilute carriers,” Physical Review B, vol. 64, no. 18, article 184307, 2001

Appendix

Less

Year 2019 volume 2019 Issue 9

PDF

Cite this Article

BibTeX

Article Info

doi: 10.34133/2019/2198906

Receive Date：2019-04-21
Online Date：2026-10-27
Published：2019-09-20

Article Data

Affiliations

History

Received：2019-04-21
Accepted：2019-07-28

Funding

National Natural Science Foundation of China(51577175)

National Key R&D Program of China(2018YFB0905400)

Affiliations

²2 School of Physical Sciences, University of Science and Technology of China, Anhui Hefei 230026, China

References

Share

https://castjournals.cast.org.cn/joweb/research/EN/10.34133/2019/2198906

Share to

Scan QR to access full text

Cite this article

BibTeX

Citations

表12种不同金属材料的力学参数

科 Family	属数 Number of genus	种数 Number of species	占总种数比例 Percentage of total species (%)	属 Genus	种数 Number of species	占总种数比例 Percentage of total species (%)
鹅膏菌科Amanitaceae	2	11	5.26	鹅膏菌属 Amanita	10	4.78
小菇科 Mycenaceae	2	12	5.74	丝盖伞属 Inocybe	5	2.39
多孔菌科 Polyporaceae	8	14	6.70	蜡蘑属 Laccaria	5	2.39
红菇科 Russulaceae	3	23	11.00	小皮伞属 Marasmius	6	2.87
				小菇属 Mycena	11	5.26
				光柄菇属 Pluteus	5	2.39
				红菇属 Russula	17	8.13
				栓菌属 Trametes	5	2.39

关闭全屏

BibTeX
EndNote
RefWorks
TxT

Table 1 Summary of the Rietveld result of the five NCA samples based on the space group of R-3m.

Samples	$a$ (Å)	$c$ (Å)	$c / a$	$χ 2$	Rwp%	Rp%	$I 003 / I 104$	Li/Ni exchange
NCA-720	2.8615 (4)	14.1738 (6)	4.9533	6.11	9.6	7.6	1.37131	3.19%
NCA-735	2.8614 (8)	14.1756 (4)	4.9541	7.629	10.3	7.6	1.45642	1.69%
NCA-750	2.8619 (3)	14.1776 (5)	4.9539	7.394	10.4	7.9	1.44492	2.39%
NCA-765	2.8628 (3)	14.1776 (3)	4.9539	9.188	11.4	8.5	1.41527	3.20%
NCA-780	2.8632 (1)	14.1781 (2)	4.9518	8.351	11	8.1	1.31637	3.82%

Table 2 The calculated diffusion coefficient of Li⁺ for deintercalation and intercalation processes.

Samples	$O ‐ D Li$ (cm² s^-1)	$R ‐ D Li$ (cm² s^-1)
NCA-720	$5.79 ∗ 10 ‐ 11$	$2.49 ∗ 10 ‐ 11$
NCA-735	$1.08 ∗ 10 ‐ 10$	$3.63 ∗ 10 ‐ 11$
NCA-750	$1.45 ∗ 10 ‐ 10$	$3.66 ∗ 10 ‐ 11$
NCA-765	$6.54 ∗ 10 ‐ 11$	$3.26 ∗ 10 ‐ 11$
NCA-780	$5.51 ∗ 10 ‐ 11$	$2.16 ∗ 10 ‐ 11$

Figure 1 The structure of a 120-atom supercell consisting of $2 × 5 × 1$ LiNi_0.8Co_0.2O₂ primitive unit cells.

Figure 2 Rietveld refinement of XRD. (a–e) Rietveld analysis of NCA-720, NCA-735, NCA-750, NCA-765, and NCA-780, respectively. (f) The refinement results of the ratio of Li/Ni exchange and the peak intensity ratio of (003)/(104).

Figure 3 Electrochemical measurements and characterization: (a) the initial charge-discharge profiles; (b) the initial CV curves; (c) rate capabilities; and (d) Nyquist plots of Li/NCA half cells for the five samples.

Figure 4 CV measurements. (a–e) CV curves of NCA-720, NCA-735, NCA-750, NCA-765, and NCA-780, respectively; (f) linear fit of the peak currents and the square root of scanning rates for the five samples.

Figure 5 Structure and diffusion path of Li⁺ ions of the Ni-rich cathode materials. (a) Layered structure of the Ni-rich cathode materials; the diffusion of Li⁺ ions under different conditions: (b) without Li/Ni antisite defects, (c) Li ion occupies TM ion sites, (d) Ni²⁺ occupies Li⁺ sites; (e) simultaneously with two defects near the diffusion pathway.

Figure 6 Calculation results of the activation barriers in lithium vacancy environments. (a) Energy profiles for Li diffusion and diffusion path in LiNi_0.8Co_0.2O₂, (b) energy profiles for Li diffusion in LiNi_0.8Co_0.2O₂ with 4.17% Li-Ni exchange and diffusion path under Ni ion, (c) energy profiles for Li diffusion in LiNi_0.8Co_0.2O₂ with 4.17% Li-Ni exchange and diffusion path under Li ion. Squares are lithium vacancies, black arrows represent diffusion path, and the blue double-sided arrows represent Li-Ni exchange.

Figure 7 Calculation results of the activation barriers in Li-Ni exchange environments. (a) Calculated activation barrier for Li migration with different Li-Ni exchanges under Li or Ni ion, (b) charge distribution for Li diffusion in LiNi_0.8Co_0.2O₂ without Li-Ni exchange, (c) charge distribution for Li diffusion in LiNi_0.8Co_0.2O₂ with 4.17% Li-Ni exchange and diffusion path under Ni ion, and (d) charge distribution for Li diffusion in LiNi_0.8Co_0.2O₂ with 4.17% Li-Ni exchange and diffusion path under Li ion.

Figure 8 Change of total energy with different amounts of Li-Ni exchange in the supercell.

Articles: Latest Articles; Most Read; Collections

Updates: Events; News; Multimedia

About: About Us

Contact

No. 86 Xueyuan South Road, Haidian District, Beijing

100081

010-62662699(Operation and Technical Support)

qkjq@cast.org.cn

Copyright © 2025 China Association for Science and Technology. All rights reserved. For all open access content, the relevant licensing terms apply.
Sponsored by the Office of the Leading Group for Cybersecurity and Informatization of CAST, and supported by Science and Technology Review Publishing House