Photoisomeric Molecule-Mediated Ion Anchoring and UV Resistance in Metal Halide Perovskites
收藏切换
PDF
Wenying Zhao1, Duo Qu1, Yongli Zhang2, 3, Chuanzhen Shang1, Xuewen Zhang1, Chenyun Wang1, Bin Zhou1, Jingyuan Qiao1, Ruilin Han1, Shasha Wang1, Yuyao Bi1, Siyu Wei1, Zheng Bao4, Fan Xu4, 5, Fengjun Ye4, Yongguang Tu1, *
Research. Vol 9 Article ID 1196
Less
收藏切换
Research. Vol 9 Article ID 1196
• RESEARCH ARTICLE •
Photoisomeric Molecule-Mediated Ion Anchoring and UV Resistance in Metal Halide Perovskites
Full
Wenying Zhao1, Duo Qu1, Yongli Zhang2, 3, Chuanzhen Shang1, Xuewen Zhang1, Chenyun Wang1, Bin Zhou1, Jingyuan Qiao1, Ruilin Han1, Shasha Wang1, Yuyao Bi1, Siyu Wei1, Zheng Bao4, Fan Xu4, 5, Fengjun Ye4, Yongguang Tu1, *
Affiliations
  • 1State Key Laboratory of Flexible Electronics (LOFE) and Institute of Flexible Electronics (IFE), Shaanxi Key Laboratory of Flexible Electronics, MIIT Key Laboratory of Flexible Electronics (KLOFE), Northwestern Polytechnical University, Xi’an 710072, China.
  • 2Harbin Institute of Technology, No. 92 Xidazhi Street, Nangang District, Harbin City, Heilongjiang Province 150001, China.
  • 3Shanghai Institute of Space Power-Sources, No. 2965 Dongchuan Road, Minhang District, Shanghai 200245, China.
  • 4Beijing Solarverse Optoelectronic Technology Co., Ltd, Beijing 100176, China.
  • 5Shenzhen Institute for Advanced Study, University of Electronic Science and Technology of China, Shenzhen 518110, China.
About Author:

† These authors contributed equally to this work.

Published: 2026-03-20 doi: 10.34133/research.1196
Outline
收藏切换

Halide perovskites are novel photovoltaic materials with soft ionic lattice that are continuously exposed to sunlight during operation. High-energy ultraviolet (UV) irradiation will cause halide ion oxidation within the perovskite layer, accelerating halide ion migration and component loss, which results in a marked degradation in the device’s photovoltaic performance. Here, we introduce a 2,3-bis(2,4,5-trimethyl-3-thienyl) maleimide (BTTM) molecule capable of interconversion between UV and visible light into the perovskite structure, intensifying the light stability of the perovskite layer via ion anchoring. Meanwhile, the incorporation of BTTM promotes the growth of perovskite crystals and efficiently passivates defects within the perovskite film, significantly boosting the open-circuit voltage of the perovskite solar cells. This results in a power conversion efficiency increase from 22.07% to 24.71%. Under UV irradiation (365 nm), BTTM molecules mitigate the degradation of perovskite by suppressing the ion migration of iodide ions. After cumulative exposure to 5 kWh/m2 of continuous UV irradiation, BTTM-based devices retain over 90% of their initial power conversion efficiency, demonstrating significantly enhanced UV stability. This study offers a straightforward approach to UV protection, providing novel insights for the environmental application of perovskite solar cells under intense UV irradiation.

Wenying Zhao, Duo Qu, Yongli Zhang, Chuanzhen Shang, Xuewen Zhang, Chenyun Wang, Bin Zhou, Jingyuan Qiao, Ruilin Han, Shasha Wang, Yuyao Bi, Siyu Wei, Zheng Bao, Fan Xu, Fengjun Ye, Yongguang Tu. Photoisomeric Molecule-Mediated Ion Anchoring and UV Resistance in Metal Halide Perovskites[J]. Research, 2026 , 9 (3) : 1196 - . DOI: 10.34133/research.1196
Full Text
Less
Introduction
Less
As one of the representatives of cutting-edge photovoltaic technologies, since the first report in 2009, perovskite solar cells (PSCs) have garnered widespread attention [1–6]. The outstanding physical characteristics of metal halide perovskite—such as broad absorption spectrum range [7–9], high optical absorption coefficient [10–12], high carrier mobility [12–14], and excellent defect tolerance [15–17]—underpin this growing interest. The power conversion efficiency (PCE) has improved rapidly, with laboratory-scale devices achieving efficiencies exceeding 27.0% [18]. However, compared to traditional crystalline silicon materials, metal halide perovskites exhibit notable inherent instability issue, hindering their large-scale application [19–21]. Notably, due to the unique soft ionic crystal property, perovskite materials are susceptible to photodegradation reactions under strong light irradiation, especially high-energy ultraviolet (UV) irradiation [22–26]. Specifically, I− and organic cations in perovskite will migrate, decompose, volatilize, and even escape from the film [27]. High-energy UV photons will accelerate the reduction of Pb2+ and oxidation of halogens, and the perovskite will be further degraded into I2 and Pb0 [28–31], leading to a sharp decline in photovoltaic performance. The formation of I2 means the generation of VI (iodine vacancy) defects within the perovskite crystal structure. This process triggers a cascade reaction: I2 combines with I− ions to form I3−, which further facilitates the migration and loss of halogen components, thereby accelerating the degradation of perovskite [32]. Meanwhile, the resulting Pb0 serves as a primary source of deep-level defects, aggravating nonradiative recombination processes and seriously affecting the photovoltaic characteristics and operational robustness of PSCs [33,34]. In addition, photoinduced defects will also decompose the organic transport layer and cause short circuits, forming escape channels for volatile components and leading to irreversible degradation of PSCs [35,36].
Several approaches have been explored in current research to reduce UV photodegradation and enhance the photostability of PSCs, including introduction of luminescent down-conversion materials [37,38], additive engineering for crystal stabilization [39], and application of UV absorption layers [40]. The luminescent down-conversion materials and UV absorption layer methods are fundamentally limited, as they merely shield the device from UV light rather than solving the instability issue of perovskite materials. On the other hand, additive engineering can effectively promote molecular interactions that passivate defects, anchor easily migratory ions, and increase the activation energy for degradation, thereby enhancing the UV photostability of the perovskites and solving the problem at the source [41]. For example, Li et al. [42] incorporated 2-(2-hydroxy-5-methylphenyl) benzotriazole into the perovskite layer, which not only passivated defects and reduced the nonradiative recombination but also absorbed UV light via the reversible ring-opening/closing reactions of its chelate ring, thus markedly improving the UV photostability. Similarly, the UV absorber, 2,2′-dihydroxy-4,4′-dimethoxybenzophenone, was demonstrated to absorb UV radiation through reversible keto-enol tautomerization under continuous intense UV irradiation, thereby delaying their photodegradation process [43]. Song et al. [44] proposed a [2+2] cycloaddition reaction using ethyl 6-bromocoumarin-3-carboxylate for incident UV radiation absorption and to suppress tensile strain, thus improving the efficiency and stability. Furthermore, the plant-derived l-theanine was employed to modulate the crystallization kinetics, successfully inhibiting the UV-induced α-to-δ phase transformation of formamidinium-based perovskite [45]. All the above methods propose additive strategies with both defect passivation effects and UV resistance in PSCs. However, the underlying evolution mechanism of the degradation behavior in perovskite materials under UV irradiation remains insufficiently explored.
Herein, we adopt a simple and efficient additive strategy by incorporating a 2,3-bis(2,4,5-trimethyl-3-thienyl) maleimide (BTTM) molecule into the perovskite. Photoisomerization occurs reversibly in this molecular system, driven by alternating UV and visible light exposure. The addition of BTTM serves to modulate residual stress within the perovskite film and help to inhibit the halogen components, thereby improving the stability of the perovskite lattice robustness and significantly increasing the open-circuit voltage (Voc) of PSCs, ultimately elevating the PCE of the device from 22.07% to 24.71%. Furthermore, under UV irradiation, the BTTM molecules can continuously suppress the ion migration of iodide ions through structural tautomerism, alleviating the UV-induced degradation process of the perovskite. After continuous UV irradiation with an irradiance of 5 kWh/m2, the BTTM device can still maintain over 90% of its initial PCE, far exceeding the control device that retains only 61.3%. This work provides a straightforward strategy for the long-term UV protection of the PSCs and offers new insights for the application of PSCs in extreme environments with intense UV irradiation.
Results
Less
As a photoisomeric molecule, BTTM can undergo isomerization between closed- and open-ring forms under UV light and visible light (Fig. 1A) [46,47]. First, we dissolved BTTM in an isopropyl alcohol solution and observed that its color deepened under 365-nm UV light irradiation. As shown in Fig. 1B, the absorption spectrum of the BTTM solution in the UV–visible range (300 to 600 nm) indicates a structural change. Meanwhile, it can be seen that the color of the BTTM solution that has changed after UV aging will return to the state before irradiation after the UV light is removed (inset in Fig. 1B), indicating the reversibility of its tautomeric reaction. Herein, we introduced the BTTM as an additive into the perovskite solution, allowing it to interact with the perovskite. Prior investigations have demonstrated that iodide ions in halide perovskite materials will migrate and form iodine vacancies under UV light irradiation, ultimately leading to the photodegradation of perovskite [48,49]. The C=O functional group in the BTTM molecule engages in a strong bond with Pb in the perovskite. Meanwhile, the N–H group coordinates with I (in the [PbI6]2− octahedron) through hydrogen bonding. These interactions will anchor the Pb–I octahedral structure of the perovskite, thereby effectively suppressing the migration of iodide ions and effectively passivating perovskite defects, as shown in Fig. 1C. To verify the interaction of BTTM molecules with iodide ions, we dissolved formamidinium iodide (FAI), BTTM, and FAI+BTTM in isopropyl alcohol, respectively, and irradiated under UV light (365 nm) for different periods of time. As shown in Fig. S1, it can be seen that the color of the FAI+BTTM solution is different from that of the BTTM solution after UV light irradiation. It is speculated that an interaction occurs between FAI and BTTM (Fig. S1B and C). Meanwhile, it can be seen that the FAI solution turned yellow after 4 h of UV light irradiation, indicating that iodide ions escape under UV light irradiation (Fig. S1C). After the FAI+BTTM solution irradiated with UV light for 4 h is placed in an environment without UV light for a period of time, a change in the solution color is also observed, indicating that there is still a certain tautomerism after the interaction between the BTTM and FAI (Fig. S1D). To further verify the interaction between BTTM and the perovskite, we carried out Fourier transform infrared spectroscopy (FTIR) and x-ray photoelectron spectroscopy (XPS) tests. The FTIR results show that the BTTM with –C=O and –N–H groups interacts with FAI and with PbI2, as shown in Fig. 1D and Fig. S2. After the interaction between the –C=O in the BTTM and PbI2, the observed downward shift of the –C=O symmetric stretching band is from 1,643 to 1,637 cm−1, indicating a strong interaction between PbI2 and –C=O. Meanwhile, the stretching vibration of N–H also shifts notably, indicating an obvious interaction between the N–H group and I−, which further indicates that the BTTM is beneficial for passivating defects in the perovskite film. Figure 1E and F shows the XPS Pb 4f spectra and I 3d spectra of the control and BTTM perovskite films (denoted as control and BTTM, respectively). The XPS spectrum of Pb 4f in the BTTM perovskite film shows that the peak positions of the 2 main peaks, Pb 4f 7/2 and Pb 4f 5/2, are 138.2 and 143.1 eV, respectively, while those of the control perovskite film are located at 138.5 and 143.3 eV. This observation signifies a robust interfacial interaction between the perovskite and BTTM, driven by electron cloud redistribution-induced shifts in binding energy. Meanwhile, the shifts of the I 3d and N 1s peak positions (Fig. S3) further indicate that the N–H group in the BTTM perovskite film interacts with I− to form hydrogen bonds. The results of FTIR and XPS indicate that BTTM would passivate defects in the perovskite film and achieve an anchoring effect on Pb–I, reducing the migration of halide ions, which is expected to improve the photoelectric properties and UV stability of the perovskite film.
Next, we screened the optimal introduction content of BTTM in the perovskite precursor solution. Herein, 0, 0.05, 0.1, 0.25, 0.5, and 1 wt% of BTTM were added to the perovskite precursor solution, respectively. The photos of the films before and after UV light are shown in Fig. S4. It can be seen that the morphology of the 0.1-wt% BTTM film remains relatively good. In addition, to evaluate the impact of BTTM incorporation on film morphology, scanning electron microscopy (SEM) was employed, and images for films with different BTTM contents are displayed in Fig. S5. It can be seen that the perovskite film without BTTM has smaller grains and a large amount of PbI2, while the perovskite films with 0.05% and 0.1% BTTM have larger grains and a reduced PbI2 content. However, when the added content of BTTM is too high, the morphology of the perovskite film deteriorates, and many voids appear on the surface. Simultaneous x-ray diffraction (XRD) testing (Fig. S6) and time-resolved photoluminescence (PL) testing (Fig. S7) revealed that perovskite films containing 0.1-wt% BTTM exhibited superior crystalline quality and longer carrier lifetime. Compared to the control films, the carrier lifetime increased from 126.41 to 340.82 ns. Finally, we prepared PSCs with varying BTTM concentrations and conducted J-V testing (Fig. S8). Comparisons revealed that adding BTTM significantly increased Voc across all samples, with the 0.1-wt% BTTM group exhibiting that the PCE has been significantly improved. Based on these results, we determined that 0.1 wt% represents the optimal BTTM concentration.
To assess the impact of BTTM on the carrier dynamics of perovskite films, steady-state PL and time-resolved PL measurements were performed on films from different groups [50]. In subsequent multiple tests, the addition amount of BTTM in the BTTM group was 0.1 wt%. First, in the PL spectrum of the perovskite film (Fig. 2A), it can be seen that the PL intensity is markedly enhanced after adding BTTM. Meanwhile, the PL emission peak of the control film is centered at 792 nm, whereas that of the BTTM-modified film shifts to 786 nm, indicating a 6-nm blueshift relative to the control. This indicates that nonradiative recombination losses are effectively suppressed and that the defects in the film are reduced. Meanwhile, as shown in Fig. 2B, the BTTM film exhibits a longer carrier lifetime than the control film. A longer carrier lifetime means fewer nonradiative recombination paths.
To further investigate the crystallinity and micro-nano morphology of the perovskite films, we compared the XRD patterns of the control and BTTM perovskite (Fig. 2C). Upon introducing BTTM, the diffraction intensity of the (001) plane increased, indicating that BTTM promotes more oriented crystal growth. Notably, the characteristic PbI2 peak at 12.7° observed in the control film disappears in the BTTM-treated film, demonstrating that BTTM interacts with PbI2 during crystallization and suppresses excess PbI2 formation, thereby enhancing film stability. Contact-angle measurements of the pristine and BTTM-modified films (Fig. S9) show only negligible changes, suggesting that BTTM has minimal influence on surface wettability and does not affect subsequent solution-processing steps. Next, SEM and atomic force microscopy analyses were then performed to investigate the impact of BTTM on the micro/nanostructure of the films. [51]. Comparing the surface and cross-sectional SEM images of the control perovskite film (Fig. 2D), it can be seen that after the addition of BTTM, the grain size of perovskite becomes larger and shows a tendency of vertical growth, which is more conducive to the reduction of defects at the grain boundaries and the efficient transport of carriers. Atomic force microscopy images of the control and the BTTM film reveal (Fig. 2E) that the incorporation of BTTM reduces the film’s roughness, with Rq decreasing from 25.3 to 21.0 nm and Ra decreasing from 20.0 to 16.5 nm. Residual stress in halide perovskites induces significant lattice distortion, serving as a key factor contributing to material instability [52,53]. To quantify this effect, we conducted grazing-incidence XRD using the 2θ-sin2ψ method, with residual stress determined through linear fitting analysis of the diffraction intensity on the (012) plane (Fig. S10) [54]. The slope decreases from 0.57 (control) to 0.39 (BTTM), indicating that BTTM effectively releases residual tensile stress and modulates the crystallization kinetics of the perovskite film.
Based on previous studies, high-energy UV radiation induces the oxidation of halide anions in perovskites. These I2 react with I− to form I3−, followed by ion migration, and this process would lead to progressive degradation and loss of components within the perovskite structure [49,55]. The incorporation of BTTM into perovskite structures enables the absorption of UV radiation and continuous passivation of defects, thereby anchoring I− ions and reducing the production of I2 to mitigate UV irradiation damage to perovskite. To validate the anchoring effect of the BTTM on iodine, we immersed both control and BTTM perovskite films in chlorobenzene (CB). It is because CB exhibits low solubility in perovskite films but good solubility in iodine, allowing the degradation reaction of perovskite to be verified by measuring the iodine content in the solution. The samples were then exposed to 365-nm UV irradiation at 200 mW/cm2 for 10 h, followed by continuous solution absorbance measurements. The results are shown in Fig. 3A and D. The control film exhibited noticeable color changes, with some samples turning from black to yellow. This transformation likely resulted from the collapse of the perovskite octahedral structure due to iodine ion migration, leading to the loss of A-site organic cations and the formation of PbI2. Subsequent UV–visible measurements of the control film’s aged CB solution revealed a distinct I₂ characteristic absorption peak around 500 nm. In contrast, no such specific absorption peak was ever observed in the CB of the BTTM perovskite film. This phenomenon indicates that the introduction of BTTM can reduce the diffusion of iodine in perovskite films during UV aging, which may be due to BTTM stabilizing I−, inhibiting its oxidation reaction, and further preventing the photodegradation of perovskite. This directly enhances the stability of the perovskite film components. Additionally, to evaluate ion migration within the thin film, we investigated device behavior at different J-V scan rates, with particular focus on low scan rates. This is because at slower scan rates, ions have sufficient time to respond to electric field changes, potentially leading to an increase in the hysteresis index (HI) as ion migration activity intensifies. As shown in Fig. S11 and Tables S3 and S4, the HI of the control device increased from 0.009 to 0.014 upon reducing the scan rate. In contrast, the HI of the BTTM device at the low scan rate of 20 mV/s only rose to 0.008—significantly lower than the control device. The observed decrease in HI provides indirect evidence for suppressed ion migration, supporting the “ion-anchoring” hypothesis. For metal halide perovskites, their fluorescence properties can effectively validate and evaluate their optoelectronic performance. We conducted PL testing to examine the evolution of fluorescence characteristics in perovskite films subjected to UV aging, and both control and BTTM perovskite films were exposed to 365-nm UV irradiation at an irradiance of 200 mW/cm2. As shown in Fig. 3B and E, the PL intensity of control perovskite films decreases to varying degrees after UV aging. In contrast, BTTM films maintain relatively strong PL intensity even after 1 h of UV irradiation, indicating that the anchoring effect of BTTM preserves the fluorescence properties of perovskite films and reduces defect generation even after UV aging. Additionally, we performed the photoluminescence quantum yield (PLQY) measurements to evaluate nonradiative recombination in perovskite films and tested the films before and after UV aging (Fig. S12). The perovskite film incorporating BTTM exhibited a slight improvement in PLQY compared to the control group. Notably, after 60 min of UV aging at 200 mW/cm2, the PLQY of the BTTM film significantly increased to 3.13%, whereas the control film remained at only 1.60%. These results collectively support that nonradiative recombination within the BTTM film has been suppressed.
To verify the stability of perovskite crystals under UV irradiation, we conducted XRD testing on control and BTTM perovskite films exposed to UV light, as shown in Fig. 3C and F. The XRD analysis reveals a substantial decrease in the intensity of diffraction peaks for the control perovskite film as UV exposure time increases. In contrast, the peak intensity of the BTTM perovskite film remains relatively stable, indicating that BTTM effectively mitigates UV-induced structural degradation of the perovskite. Concurrently, as UV irradiation accumulated, a distinct PbI2 diffraction peak emerged at 12.7° in the control film. The photostability of this excess PbI2 significantly accelerates perovskite degradation, severely compromising crystal stability. To compare the evolution of PbI2 generated during decomposition across different film groups over irradiation time, we calculated the integral areas of the PbI2 and perovskite (001) crystal plane diffraction peaks. Figure 3G shows the comparison of the ratio of the integrated area of their diffraction peaks to the duration of UV irradiation. The control film exhibits a higher integral area ratio than the BTTM perovskite film. Moreover, the area ratio of the BTTM film remains relatively stable after aging, indicating that BTTM effectively mitigates UV-induced degradation of the perovskite structure. Additionally, UV–visible spectroscopy measurements were performed on both the control group and the BTTM perovskite films, and tauc plots were fitted (Fig. S13), and the introduction of BTTM did not alter the optical bandgap of the perovskite film. Moreover, the BTTM perovskite film exhibits better retention of absorbance after UV irradiation, further demonstrating the UV-protective effect of BTTM. Subsequently, SEM images were used to observe morphological changes in both control and BTTM perovskite films after exposure to 365-nm UV light (Fig. 3H). Interestingly, the SEM images of the films became blurred after UV irradiation, potentially related to changes in surface conductivity. Simultaneously, noticeable gaps appeared at grain boundaries, indicating that UV irradiation primarily affects grain boundaries, subsequently triggering perovskite degradation.
The heterogeneity of halide perovskites severely limits the development of device optoelectronic performance and stability, particularly during UV aging processes. Therefore, we further investigated the effect of BTTM on the homogeneity of perovskite films after UV aging. Here, both control and BTTM perovskite films were exposed to 365-nm UV light at an irradiance of 200 mW/cm2, and their PL mapping images were measured as shown in Fig. 4A to F and Figs. S14 and S15. The results reveal that the BTTM film exhibits enhanced homogeneity after UV irradiation, whereas the control perovskite film shows deteriorated PL peak position uniformity and a tendency toward blueshift, consistent with the findings in Fig. 3B. Additionally, Fig. S14 shows an increase in the PL intensity of the perovskite film after UV irradiation, which may be attributed to the high energy provided by UV irradiation compensating for defects. Furthermore, Fig. S15 indicates that the half-width of the perovskite film’s peak position broadens after UV irradiation. To further elucidate the effect of UV irradiation on perovskite film uniformity, Kelvin probe force microscopy measurements were performed on both control and BTTM films before and after UV irradiation, as shown in Fig. 4G and H, with a cumulative irradiation dose of 2 kWh/m2. It can be observed that the surface potential of the control perovskite film decreased significantly from −0.166 to −0.433 V after UV irradiation, while the surface potential of the BTTM perovskite film showed no marked change, increasing only slightly from −0.468 to −0.450 V. This indicates that after UV irradiation, the anchoring of BTTM to the components within the perovskite film effectively maintains the uniformity.
PSCs with the structure of F-doped tin oxide (FTO)/NiOx/MeO-2PACz/perovskite/2-phenylethylamine hydroiodide (PEAI)/(6,6)-phenyl-C61-butyric acid methyl ester (PCBM)/bathocuproine (BCP)/Ag were fabricated, as shown in Fig. 5A, to investigate the effect of BTTM on PSC performance. Figure 5B displays the J-V curves of the optimal control and BTTM devices, where the optimal BTTM PSCs exhibit a Voc of 1.16 V, a short-circuit current density (Jsc) of 26.03 mA/cm2, a fill factor (FF) of 81.67%, and a PCE of 24.71%, while the control device shows a lower PCE of 22.07%. Box plots of PCE and J-V parameter distributions for control and BTTM devices are shown in Fig. 5C and Fig. S16, demonstrating improved performance parameters across all devices. Additionally, forward and reverse scan tests were conducted on a BTTM device, as shown in Fig. 5D, revealing minimal hysteresis between forward and reverse scans. In order to explore the applicability of this method in other perovskite compositions, we prepared wide-bandgap PSCs. The best PCE of the BTTM device increased from 22.02% in the reference device to 23.50% (Fig. S17). To understand the impact of BTTM adding on charge recombination dynamics in the devices, we measured dark current curves for both control and BTTM devices (Fig. 5E). Compared to the control device, the BTTM device shows a lower saturation current density, indicating reduced charge recombination and thus higher Voc. Figure 5F displays the steady-state power output of PSCs biased at the maximum power point voltage for both control and BTTM devices, showing a stabilized PCE of 24.12% for BTTM devices. When unencapsulated PSCs were stored in a nitrogen environment for 1,000 h, the PCE changes are shown in Fig. 5G. The BTTM device maintained 96.9% of its initial PCE after 1,000 h, while the control device retained only 54.3%, indicating better long-term stability for BTTM devices. To evaluate the protective effect of BTTM against UV irradiation in PSCs, we subjected both control and BTTM devices to UV irradiation in a N2 glovebox. During the test, it was found that the NiOx layer and the PCBM layer have a notable impact on the UV stability of the device [56,57]. Under UV irradiation, the PCE of the device drops rapidly, as shown in Figs. S18 and S19. Therefore, we chose FTO/MeO-2PACz/perovskite/PEAI/C60/BCP/Ag device structure for UV stability test, as shown in Fig. 5H, with a total UV dose of 5 kWh/m2. Throughout the UV aging test, the control device’s PCE gradually degraded to only 60% of its initial value, while the BTTM device maintained 90% of its initial PCE, demonstrating the significant role of BTTM in enhancing the UV stability of perovskite devices.
Conclusion
Less
In this study, we incorporated the photoisomeric BTTM molecule capable of interconverting between UV and visible light into perovskite. This enhanced the photovoltaic performance of PSCs while simultaneously improving their UV stability. The incorporation of BTTM promotes perovskite crystal growth and passivates defects within the film, significantly increasing the Voc of PSCs. This results in a PCE improvement from 22.07% to 24.71%. Under UV irradiation, BTTM mitigate perovskite degradation by suppressing halide ion migration. After cumulative exposure to 5 kWh/m2 of continuous UV radiation, BTTM PSCs retained 90% of initial PCE, whereas unmodified PSCs exhibited gradual degradation to only 60% of their initial PCE, demonstrating markedly enhanced UV stability. This study provides deeper insights into perovskite aging under UV irradiation and offers a simple additive engineering approach for UV protection in halide perovskites, presenting novel strategies for PSCs in environments with intense UV exposure.
Materials and Methods
Less
Comprehensive materials and methods can be found in the Supplementary Materials.
References
Less
1.
Tan S, Shih M-C, Lu Y, Choi S-G, Dong Y, Lee J-H, Yavuz I, Larson BW, Park SY, Kodalle T, et al.Spontaneous formation of robust two-dimensional perovskite phases. Science. 2025;388(6747):639–645.
2.
Shang C, Qu D, Bao Z, Wang C, Zhao Q, Li C, Zhou B, Wang X, Han R, Wang S, et al.Reducing energetic disorder for high-efficiency perovskite solar cells with low urbach energy by in situ NH3 generation. Angew Chem Int Ed Engl. 2025;64(48):Article e202516464.
3.
Wang C, Qu D, Zhou B, Shang C, Zhang X, Tu Y, Huang W. Self-healing behavior of the metal halide perovskites and photovoltaics. Small. 2023;20(6):2307645.
4.
Yan C, Yu J, Li Y, Fong PWK, Ding R, Liu K, Xia H, Ren Z, Lu X, Hao J, et al.Ambipolar-transport wide-bandgap perovskite interlayer for organic photovoltaics with over 18% efficiency. Matter. 2022;5(7):2238–2250.
5.
Tu Y, Wu J, He X, Guo P, Wu T, Luo H, Liu Q, Wu Q, Lin J, Huang M, et al.A gradient engineered hole-transporting material for monolithic series-type large-area perovskite solar cells. J Mater Chem A. 2017;5(40):21161–21168.
6.
Yi Z, Li X, Xiong Y, Shen G, Zhang W, Huang Y, Jiang Q, Ng XR, Luo Y, Zheng J, et al.Self-assembled monolayers (SAMs) in inverted perovskite solar cells and their tandem photovoltaics application. Interdiscip Mater. 2024;3(2):203–244.
7.
Luo D, Yang W, Wang Z, Sadhanala A, Hu Q, Su R, Shivanna R, Trindade GF, Watts JF, Xu Z, et al.Enhanced photovoltage for inverted planar heterojunction perovskite solar cells. Science. 2018;360(6396):1442–1446.
8.
Zhang Y, Tu Y, Yang X, Su R, Yang W, Yu M, Wang Y, Huang W, Gong Q, Zhu R. Green solution-bathing process for efficient large-area planar perovskite solar cells. ACS Appl Mater Interfaces. 2020;12(22):24905–24912.
9.
Wang Y, Wang X, Wang C, Cheng R, Zhao L, Wang X, Zhang X, Shang J, Zhang H, Zhao L, et al.Defect suppression and energy level alignment in formamidinium-based perovskite solar cells. J Energy Chem. 2022;67:65–72.
10.
Wang S, Cao Y, Peng Q, Huang W, Wang J. Carrier dynamics determines the optimization strategies of perovskite leds and pvs. Research. 2023;2023(4):2096–5168.
11.
Sun Q, Zhao C, Yin Z, Wang S, Leng J, Tian W, Jin S. Ultrafast and high-yield polaronic exciton dissociation in two-dimensional perovskites. J Am Chem Soc. 2021;143(45):19128–19136.
12.
Wang C, Wang X, He Z, Zhou B, Qu D, Wang Y, Hu H, Hu Q, Tu Y. Minimizing voltage deficit in methylammonium-free perovskite solar cells via surface reconstruction. Chem Eng J. 2022;444:Article 136622.
13.
Yoo JJ, Seo G, Chua MR, Park TG, Lu Y, Rotermund F, Kim Y-K, Moon CS, Jeon NJ, Correa-Baena J-P, et al.Efficient perovskite solar cells via improved carrier management. Nature. 2021;590(7847):587–593.
14.
Tu Y, Xu G, Yang X, Zhang Y, Li Z, Su R, Luo D, Yang W, Miao Y, Cai R, et al.Mixed-cation perovskite solar cells in space. Sci China Phys Mech Astron. 2019;62(7):Article 974221.
15.
Lee MM, Teuscher J, Miyasaka T, Murakami TN, Snaith HJ. Efficient hybrid solar cells based on meso-superstructured organometal halide perovskites. Science. 2012;338(6107):643–647.
16.
Tu Y, Wu J, He X, Guo P, Luo H, Liu Q, Lin J, Huang M, Huang Y, Fan L, et al.Controlled growth of CH3NH3PBI3 films towards efficient perovskite solar cells by varied-stoichiometric intermediate adduct. Appl Surf Sci. 2017;403:572–577.
17.
Wu T, Wu J, Tu Y, He X, Lan Z, Huang M, Lin J. Solvent engineering for high-quality perovskite solar cell with an efficiency approaching 20%. J Power Sources. 2017;365:1–6.
18.
Best research-cell efficiency chart. [accessed September 2025] https://www.Nrel.Gov/pv/cell-efficiency.Html
19.
Ma C, Park N-G. A realistic methodology for 30% efficient perovskite solar cells. Chem. 2020;6(6):1254–1264.
20.
Chai W, Li L, Zhu W, Chen D, Zhou L, Xi H, Zhang J, Zhang C, Hao Y. Graded heterojunction improves wide-bandgap perovskite for highly efficient 4-terminal perovskite/silicon tandem solar cells. Research. 2023;6:0196.
21.
Yang X, Li Q, Zheng Y, Luo D, Zhang Y, Tu Y, Zhao L, Wang Y, Xu F, Gong Q, et al.Perovskite hetero-bilayer for efficient charge-transport-layer-free solar cells. Joule. 2022;6(6):1277–1289.
22.
Jena AK, Kulkarni A, Miyasaka T. Halide perovskite photovoltaics: Background, status, and future prospects. Chem Rev. 2019;119(5):3036–3103.
23.
Lee D-K, Park N-G. Additive engineering for highly efficient and stable perovskite solar cells. Appl Phys Rev. 2023;10:Article 011308.
24.
Xue J, Wang R, Yang Y. The surface of halide perovskites from nano to bulk. Nat Rev Mater. 2020;5(11):809–827.
25.
Azpiroz JM, Mosconi E, Bisquert J, De Angelis F. Defect migration in methylammonium lead iodide and its role in perovskite solar cell operation. Energy Environ Sci. 2015;8(7):2118–2127.
26.
Zheng C, He Y, Li Y, Gao A, Liu Z, Chen L, Wang D, Liu S. Oxidation stability of perovskite solar cells reinforced by punicalagin to resist UV damage. Adv Funct Mater. 2025;35(40):2502232.
27.
Fei C, Kuvayskaya A, Shi X, Wang M, Shi Z, Jiao H, Silverman TJ, Owen-Bellini M, Dong Y, Xian Y, et al.Strong-bonding hole-transport layers reduce ultraviolet degradation of perovskite solar cells. Science. 2024;384(6700):1126–1134.
28.
Bischak CG, Hetherington CL, Wu H, Aloni S, Ogletree DF, Limmer DT, Ginsberg NS. Origin of reversible photoinduced phase separation in hybrid perovskites. Nano Lett. 2017;17(2):1028–1033.
29.
Tress W, Marinova N, Moehl T, Zakeeruddin SM, Nazeeruddin MK, Grätzel M. Understanding the rate-dependent J–V hysteresis, slow time component, and aging in CH3NH3PBI3 perovskite solar cells: The role of a compensated electric field. Energy Environ Sci. 2015;8(3):995–1004.
30.
Hang P, Xie J, Li G, Wang Y, Fang D, Yao Y, Xie D, Cui C, Yan K, Xu J, et al.An interlayer with strong Pb-Cl bond delivers ultraviolet-filter-free, efficient, and photostable perovskite solar cells. iScience. 2019;21:217–227.
31.
Li Y, Xu X, Wang C, Ecker B, Yang J, Huang J, Gao Y. Light-induced degradation of CH3NH3PBI3 hybrid perovskite thin film. J Phys Chem C. 2017;121(7):3904–3910.
32.
Wang C, Qu D, Han R, Zhang X, Shang C, Zhou B, Wang S, Hu H, Zhao W, Qin Q, et al.Dipole molecule-mediated modulating residual PbI2 clusters in two-step-processing inverted perovskite photovoltaics. Nano Lett. 2024;24(49):15912–15920.
33.
Luo D, Su R, Zhang W, Gong Q, Zhu R. Minimizing non-radiative recombination losses in perovskite solar cells. Nat Rev Mater. 2019;5(1):44–60.
34.
Zhou J, Li M, Wang S, Tan L, Liu Y, Jiang C, Zhao X, Ding L, Yi C. 2-CF3-PEAI to eliminate Pb0 traps and form a 2D perovskite layer to enhance the performance and stability of perovskite solar cells. Nano Energy. 2022;95:Article 107036.
35.
Liang Q, Liu J, Han Y. Optimizing film morphology and crystal orientation of perovskite for efficient planar-heterojunction solar cells by slowing crystallization process. Org Electron. 2018;62:26–34.
36.
Petrović M, Maksudov T, Panagiotopoulos A, Serpetzoglou E, Konidakis I, Stylianakis MM, Stratakis E, Kymakis E. Limitations of a polymer-based hole transporting layer for application in planar inverted perovskite solar cells. Nanoscale Adv. 2019;1(8):3107–3118.
37.
Chander N, Khan AF, Chandrasekhar PS, Thouti E, Swami SK, Dutta V, Komarala VK. Reduced ultraviolet light induced degradation and enhanced light harvesting using YVO4:Eu3+ down-shifting nano-phosphor layer in organometal halide perovskite solar cells. Appl Phys Lett. 2014;105(3):Article 033904.
38.
Chen T, Xie J, Gao P. Ultraviolet photocatalytic degradation of perovskite solar cells: Progress, challenges, and strategies. Adv Energy Sustain Res. 2022;3(6):2100218.
39.
Wang Y, Zhang Z, Lan Y, Song Q, Li M, Song Y. Tautomeric molecule acts as a “sunscreen” for metal halide perovskite solar cells. Angew Chem Int Ed Engl. 2021;60(16):8673–8677.
40.
Jeong J, Seo J, Nam S, Han H, Kim H, Anthopoulos TD, Bradley DDC, Kim Y. Significant stability enhancement in high-efficiency polymer: Fullerene bulk heterojunction solar cells by blocking ultraviolet photons from solar light. Adv Sci. 2015;3(4):1500269.
41.
Chen Y, Wang Q, Yao Y, Yang J, Tang W, Qiu W, Wu Y, Peng Q. Synergistic transition metal ion co-doping and multiple functional additive passivation for realizing 25.30% efficiency perovskite solar cells. Energy Environ Sci. 2023;16(11):5243–5254.
42.
Li J, Qi W, Li Y, Jiao S, Ling H, Wang P, Zhou X, Sohail K, Wang G, Hou G, et al.UV light absorbers executing synergistic effects of passivating defects and improving photostability for efficient perovskite photovoltaics. J Energy Chem. 2021;67:138–146.
43.
Li Y, Li J, Qi W, Jiao S, Ling H, Sohail K, Li X, Zhang X. 2,2′-Dihydroxy-4,4′-dimethoxy-benzophenon as bifunctional additives for passivated defects and improved photostability of efficient perovskite photovoltaics. ACS Appl Mater Interfaces. 2022;14(32):36602–36610.
44.
Tao M, Wang Y, Zhang K, Song Z, Lan Y, Guo H, Guo L, Zhang X, Wei J, Cao D, et al.Molecule-triggered strain regulation and interfacial passivation for efficient inverted perovskite solar cells. Joule. 2024;8(11):3142–3152.
45.
Li Y, Liu L, Zheng C, Liu Z, Chen L, Yuan N, Ding J, Wang D, Liu S. Plant-derived l-theanine for ultraviolet/ozone resistant perovskite photovoltaics. Adv Energy Mater. 2022;13(3):2203190.
46.
Asai K, Koshimizu M, Fujimoto Y, Asai K. Radiochromic properties of organic films based on a diarylethene molecule. Nucl Instrum Methods Phys Res A. 2020;954:Article 161828.
47.
Irie M, Sayo K. Solvent effects on the photochromic reactions of diarylethene derivatives. J Phys Chem. 1992;96(19):7671–7674.
48.
Cai S, Gao J, Wu Y, Zou Y, Liang J, Li Y, He X, Cai Q, Wang M, Huang X, et al.Rational tailored polyfluorosubstituted amide molecule for stabilizing PBI6 framework and inhibiting ion migration toward highly efficient and stable perovskite solar cells. Adv Funct Mater. 2024;34(52):2411014.
49.
Ren X, Wang J, Lin Y, Wang Y, Xie H, Huang H, Yang B, Yan Y, Gao Y, He J, et al.Mobile iodides capture for highly photolysis- and reverse-bias-stable perovskite solar cells. Nat Mater. 2024;23(6):810–817.
50.
Zhu H, Tong G, Li J, Tao X, Shen Y, Sheng Y, Shi L, Xie F, Tang J, Jiang Y. Acid-etching induced metal cation competitive lattice occupancy of perovskite quantum dots for efficient pure-blue qleds. Interdiscip Mater. 2024;3(3):437–447.
51.
Jiang R, Pu J, Wang Y, Chen J, Fu G, Chen X, Yang J, Shen J, Sun X, Ding J, et al.Tailored wrinkles for tunable sensing performance by stereolithography. Interdiscip Mater. 2024;3(3):414–424.
52.
Wang C, Shang C, Feng H, Lei Y, Qu D, Zhou B, Zhang X, Hu H, Zhang Y, Zhang Z, et al.Synergistic toughening and strain releasing strategy in metal halide perovskite photovoltaics. Adv Funct Mater. 2024;34(52):2410621.
53.
Zhou B, Shang C, Wang C, Qu D, Qiao J, Zhang X, Zhao W, Han R, Dong S, Xue Y, et al.Strain engineering and halogen compensation of buried interface in polycrystalline halide perovskites. Research. 2024;7(2):0309.
54.
Zhang X, Shang C, Wang C, Zhao W, Tao C, Wang S, Zhang X, Han R, Zhou B, Qu D, et al.Preferred crystallographic orientation via solution bathing for high-performance inverted perovskite photovoltaics. Adv Funct Mater. 2024;34(46):2407732.
55.
Zhu H, Teale S, Lintangpradipto MN, Mahesh S, Chen B, McGehee MD, Sargent EH, Bakr OM. Long-term operating stability in perovskite photovoltaics. Nat Rev Mater. 2023;8(9):569–586.
56.
You S, Zhu H, Shen Z, Wang X, Shao B, Wang Q, Lu J, Yuan Y, Dou BD, Sanehira EM, et al.C60-based ionic salt electron shuttle for high-performance inverted perovskite solar modules. Science. 2025;388(6750):964–968.
57.
He X, Chen H, Yang J, Wang T, Pu X, Feng G, Jia S, Bai Y, Zhou Z, Cao Q, et al.Enhancing hole transport uniformity for efficient inverted perovskite solar cells through optimizing buried interface contacts and suppressing interface recombination. Angew Chem Int Ed Engl. 2024;63(52):Article e202412601.
Appendix
Less
Year 2026 volume 9 Issue 3
PDF
121
66
Cite this Article
BibTeX
Article Info
doi: 10.34133/research.1196
  • Receive Date：2025-12-03
  • Online Date：2026-10-16
  • Published：2026-03-20
Article Data
Affiliations
History
  • Received：2025-12-03
  • Revised：2026-02-07
  • Accepted：2026-02-25
Affiliations
    1State Key Laboratory of Flexible Electronics (LOFE) and Institute of Flexible Electronics (IFE), Shaanxi Key Laboratory of Flexible Electronics, MIIT Key Laboratory of Flexible Electronics (KLOFE), Northwestern Polytechnical University, Xi’an 710072, China.
    2Harbin Institute of Technology, No. 92 Xidazhi Street, Nangang District, Harbin City, Heilongjiang Province 150001, China.
    3Shanghai Institute of Space Power-Sources, No. 2965 Dongchuan Road, Minhang District, Shanghai 200245, China.
    4Beijing Solarverse Optoelectronic Technology Co., Ltd, Beijing 100176, China.
    5Shenzhen Institute for Advanced Study, University of Electronic Science and Technology of China, Shenzhen 518110, China.

Corresponding:

* Address correspondence to:
References
Share
https://castjournals.cast.org.cn/joweb/research/EN/10.34133/research.1196
Share to
QR

Scan QR to access full text

Cite this article
BibTeX
Citations
表12种不同金属材料的力学参数
科
Family		 属数
Number of
genus		 种数
Number of
species		 占总种数比例
Percentage of
total species (%)		 属
Genus		 种数
Number of
species		 占总种数比例
Percentage of total
species (%)
鹅膏菌科Amanitaceae 2 11 5.26 鹅膏菌属 Amanita 10 4.78
小菇科 Mycenaceae 2 12 5.74 丝盖伞属 Inocybe 5 2.39
多孔菌科 Polyporaceae 8 14 6.70 蜡蘑属 Laccaria 5 2.39
红菇科 Russulaceae 3 23 11.00 小皮伞属 Marasmius 6 2.87
小菇属 Mycena 11 5.26
光柄菇属 Pluteus 5 2.39
红菇属 Russula 17 8.13
栓菌属 Trametes 5 2.39
关闭全屏
  • BibTeX
  • EndNote
  • RefWorks
  • TxT
Links
Articles
Latest Articles
Most Read
Collections
Updates
Events
News
Multimedia
About
About Us
Contact
No. 86 Xueyuan South Road, Haidian District, Beijing
100081
010-62662699(Operation and Technical Support)
qkjq@cast.org.cn

Copyright © 2025 China Association for Science and Technology. All rights reserved. For all open access content, the relevant licensing terms apply.
Sponsored by the Office of the Leading Group for Cybersecurity and Informatization of CAST, and supported by Science and Technology Review Publishing House