Interface-to-Surface Transition Induced Topological Hall Effect in 2-Dimensional SrRuO<sub>3</sub> Integrated on Silicon

Interface-to-Surface Transition Induced Topological Hall Effect in 2-Dimensional SrRuO₃ Integrated on Silicon

PDF

Qinglong Wang¹, Bin He¹^,^*, Jinrui Guo¹, Jianping Zhang¹, Yue Han², Huan Liu², Weidong Wang¹, Shengshi Li¹^,^*, Weiming Lü¹^,²^,^*, Shishen Yan¹^,^*

Research. Vol 9 Article ID 1079

Less

Research. Vol 9 Article ID 1079

• RESEARCH ARTICLE •

Interface-to-Surface Transition Induced Topological Hall Effect in 2-Dimensional SrRuO₃ Integrated on Silicon

Full

Qinglong Wang¹, Bin He¹^,^*, Jinrui Guo¹, Jianping Zhang¹, Yue Han², Huan Liu², Weidong Wang¹, Shengshi Li¹^,^*, Weiming Lü¹^,²^,^*, Shishen Yan¹^,^*

Affiliations

¹Spintronics Institute, School of Physics and Technology, University of Jinan, Jinan 250022, China.

²School of Physics, Harbin Institute of Technology, Harbin 150001, China.

About Author:

^† These authors contributed equally to this work.

Published: 2026-01-20 doi: 10.34133/research.1079

Outline

Abstract

Less

The topological Hall effect (THE), a transport signature emerging from chiral spin textures induced by structural symmetry breaking and the Dzyaloshinskii–Moriya interaction (DMI), represents a rich frontier in condensed matter physics with promising applications in spintronic devices. To enhance the DMI and thereby induce THE in SrRuO₃ (SRO), we introduce a structural-symmetry-breaking strategy that disrupts the Ru–O termination at the rigid substrate interface. This disruption triggers a transition from a rigid epitaxial interface to a freestanding membrane with unsaturated surface bonds, resulting in asymmetric surface terminations (Sr–O on top and Ru–O at the bottom). Unlike its rigid counterpart, which shows no detectable THE, the freestanding SRO exhibits a pronounced THE signal, persisting up to 100 K while preserving high crystallinity and electronic coherence. The ability to generate robust THE in transferable oxide membranes has direct implications for next-generation spintronics, offering compelling prospects for creating low-power magnetic memory and logic devices based on chiral spin textures.

Cite this Article

Qinglong Wang, Bin He, Jinrui Guo, Jianping Zhang, Yue Han, Huan Liu, Weidong Wang, Shengshi Li, Weiming Lü, Shishen Yan. Interface-to-Surface Transition Induced Topological Hall Effect in 2-Dimensional SrRuO₃ Integrated on Silicon[J]. Research, 2026 , 9 (1) : 1079 - . DOI: 10.34133/research.1079

Full Text

Less

Introduction

Less

The topological Hall effect (THE), a hallmark of real-space Berry curvature effects [1–3], serves dual roles in modern condensed matter physics. Fundamentally, it provides critical insights into exotic topological phases, such as skyrmion lattices [4] and chiral spin liquids [5], that challenge conventional band theory. Technologically, THE enables transformative spintronic applications, including racetrack memories [6,7], spin–orbit torque oscillators [8,9], neuromorphic computing [10], etc., by permitting precise manipulation of chiral spin textures with exceptional energy efficiency and scalability. The emergence of THE requires a delicate balance between spatial inversion symmetry and time-reversal symmetry breakings for Dzyaloshinskii–Moriya interaction (DMI) and magnetic order [11–13], respectively. Theoretical frameworks posit an optimized DMI strength of D∼(JK)^1/2, where D, J, and K correspond to the DMI, Heisenberg exchange, and magnetic anisotropy energies. Thus, unit-cell-level strategies are always necessary, such as existing strain engineering, stoichiometric control, and heterointerface design in THE materials (e.g., SrRuO₃ [SRO] [14–16], Fe₃Sn₂ [17], and bilayer CrI₃ [18]).

Specifically, SRO, a THE pronounced complex oxide, inherently facilitates structural symmetry breaking due to the intrinsic interfacial and electronic asymmetries between Sr–O and Ru–O atomic layers at the subunit-cell level (Fig. 1A). In SRO, the Sr–O bonding is predominantly ionic, while Ru–O exhibits mixed covalent–ionic character, accompanied by a shorter Ru–O bond length compared to Sr–O [19]. These inherent differences make the RuO₆ octahedra highly susceptible to tilting and distortion, thereby promoting the emergence of THE. However, simultaneously exposing both Sr–O and Ru–O as surface terminations remains challenging, since high-quality low-dimensional SRO structures are typically epitaxial, requiring one of these planes to be clamped by the substrate. It is expected that overcoming this limitation enables the realization of SRO with spontaneous structural symmetry breaking while preserving high crystallinity and electronic coherence. Moreover, by circumventing interfacial defects, chemical interdiffusion, and magnetic dead layers in conventional heterostructures [20,21], the artifactual mimicry of topological Hall signatures can be avoided. It is noteworthy that SRO is highly sensitive to electronic phase homogeneity and that even minor inhomogeneities can introduce competing positive and negative contributions to the anomalous Hall effect (AHE), as previously reported [22–24]. Equally compelling is the transferability of these freestanding THE-active SRO layers, offering a critical capability for designing novel spin-electronic device paradigms.

In this study, we present the distinct THE in the freestanding SRO (FS-SRO) membrane that was released from epitaxial SRO/Sr₄Al₂O₇ (SAO)/SrTiO₃ (STO) by water dissolution of the sacrificial SAO interlayer. By disrupting the Ru–O termination at the SRO/SAO interface, the SRO transitions from a rigid heterostructure with mixed covalent–ionic bonds to a freestanding film with unsaturated dangling bonds. This process gives rise to exposed, asymmetric surface terminations, Sr–O on the top and Ru–O on the bottom, distinct from conventional approaches for tuning the THE. Notably, whereas epitaxially rigid SRO (RG-SRO) on STO exhibits no detectable THE, the FS-SRO transferred onto silicon demonstrates a pronounced THE that persists up to 100 K. We attribute this emergent THE to the asymmetric Ru–O- and Sr–O-terminated surfaces in FS-SRO, which enhance structural symmetry breaking, amplify the DMI, and thereby induce the observed topological Hall response. Our demonstration of a freestanding, flexible, and Si-compatible THE layer not only provides a versatile platform for fundamental research on strain-tunable topological spin textures but also establishes a direct pathway to integrate nonvolatile skyrmion-based logic and memory devices into mainstream silicon technology.

Results

Less

High-quality FS-SRO membranes with crystalline integrity

As depicted in Fig. 1A, FS-SRO membranes of varying thicknesses were fabricated by dissolving a SAO sacrificial interlayer in SRO/SAO/STO heterostructures. During the etching process, the lower Sr–O termination layer was selectively removed (see Supplementary Note), after which the released FS-SRO membranes were transferred onto Si substrates using a high-precision transfer platform. This method ensured accurate alignment and preserved membrane integrity with minimal damage. The large-scale FS-SRO membrane (3.6 nm) exhibited no wrinkles or cracks, as illustrated in Fig. 1B, which is particularly advantageous for testing the structural information and ferromagnetic performance on Si substrates. The growth rate and layer-by-layer growth of the SAO sacrificial layer were monitored in situ via reflection high-energy electron diffraction (RHEED), as shown in Fig. 1C. The designed thickness of the SAO sacrificial layer in our work is about 12 nm, which can ensure the efficient large-area exfoliation of the ultrathin SRO membranes. Meanwhile, the SAO layer exhibits an exceptionally high dissolution rate [25,26], demonstrating the SRO layer to fully detach from the rigid substrate within 30 min. Figure 1D shows x-ray diffraction (XRD) patterns of the 2θ–ω scans of SRO/STO (001) films, SRO/SAO/STO (001) heterostructures, and FS-SRO on Si. On the basis of the position of the (0012) diffraction peak of the SAO layer and the (002) diffraction peaks of the SRO layers, we determined the out-of-plane lattice parameters c for SAO and SRO layers grown on the STO substrate. The calculated c of the SAO layer is approximately 25.743 Å, and the c of the SRO layer deposited on the STO and SAO/STO substrates is about 3.958 and 3.946 Å, respectively. Owing to the lattice mismatch between bulk SRO [19] and STO substrates, the in-plane compressive strain in SRO films will enlarge the c of SRO layers. The insertion of SAO layers will reduce compressive stress, thus decreasing the c of SRO layers. The dissolution of the SAO layer can result in the release of stress in the SRO layer imposed by the STO substrate. This is confirmed by XRD measurements, which reveal that the c of the FS-SRO membrane is about 3.928 Å. To thoroughly investigate the microstructural characteristics of the FS-SRO membrane, we conducted high-resolution transmission electron microscopy (HRTEM) analysis on both cross-sectional and plan-view samples (Fig. 1E and F). The HRTEM images of the FS-SRO (~4.8 nm) confirm their high crystallinity and the well-defined perovskite structure. Quantitative lattice analysis can confirm nearly identical in-plane (~3.922 Å) and out-of-plane (~3.932 Å) lattice parameters, closely matching the results obtained from XRD calculations (Fig. 1B). Combining the results from XRD and TEM, we demonstrated the successful preparation of high-quality single-crystal 2-dimensional FS-SRO membranes.

Enhanced ferromagnetism in FS-SRO membranes

To systematically investigate the evolution of magnetic and transport characteristics, we conducted comparative measurements across RG-SRO and FS-SRO membranes, including out-of-plane magnetic hysteresis (M–H) loops, field-cooled magnetization (M–T) curves, and temperature-dependent resistivity (ρ_xx–T) curves. Figure 2A to C shows the out-of-plane M–H loops of RG-SRO and FS-SRO with different thicknesses at 5 K. The RG-SRO and FS-SRO samples exhibit well-saturated M–H loops with an applied magnetic field of ±5 T. It is noteworthy that M–H curves (<12 nm) exhibit double-loop characteristics with distinct coercivities (H_c), demonstrating the magnetic phase existence (hard and soft magnetic phases). The emergence of double hysteresis loops in SRO originates from the oxygen vacancy during the growth process [27–30]. To further elucidate the origin of the double magnetic hysteresis loops in RG-SRO films, we systematically performed preannealing and postannealing treatments on substrates under controlled oxygen partial pressures, followed by comprehensive magnetic and transport characterizations (Fig. S5A to F). After oxygen annealing, the SRO films show only one ferromagnetic phase and a decreased saturation magnetization. This observation suggests that oxygen vacancies are responsible for the presence of dual magnetic phases. Meanwhile, the strong oxygen affinity of aluminum in the SAO/SRO heterostructure drives interfacial redox reactions, generating more oxygen vacancies in the FS-SRO membranes [31–33]. Therefore, the ultrathin (<12 nm) FS-SRO membranes exhibit larger magnetic moments than those of RG-SRO films. As illustrated in Fig. 2E, the saturation magnetization (M_s) of FS-SRO membranes increases rapidly with the decrease in thickness. The M_s of the RG-SRO films is nearly independent of thickness and is approximately 1.5 μ_B/Ru, consistent with reported values with low spin configuration of t_2g (3↑, 1↓) [19,34–36]. In particular, the M_s of the FS-SRO membrane with 3.6 nm is about 3.1 μ_B/Ru, indicating that the high-spin configuration is induced in our 2-dimensional SRO membrane [37].

The spin-state transition is not only related to oxygen vacancies but may also be associated with the unique interfacial crystal structure of the freestanding membrane. Figure 2D presents the M–T curves of the RG-SRO films and FS-SRO membranes with varying thicknesses. For all SRO samples, a decrease in magnetization is observed with increasing temperature, accompanied by a sharp transition from ferromagnetic to paramagnetic behavior. The Curie temperature (T_c) was determined via differentiation analysis of the M–T curves, specifically identified from the extremum point in the dM/dT versus T profile (Fig. S2). The T_c of the FS-SRO membranes and RG-SRO films exhibits a pronounced dependence on the modulation thickness. As the thickness of SRO films increases from 3.6 to 12 nm, the T_c of RG-SRO and FS-SRO exhibits a gradual increase from 138 to 146 K and 135 to 145 K, respectively. As displayed in Fig. 2F, the samples were further characterized by transport measurements of longitudinal resistivity. A characteristic thickness-dependent transition emerges, manifesting progressive suppression of both ferromagnetic ordering and metallic conduction characteristics with diminishing film thickness. Notably, FS-SRO membranes with thicknesses of 3.6 and 4.8 nm exhibit a metal–insulator transition temperature (<40 K), providing compelling evidence for progressive electron localization driving the system toward the insulating states [15]. Strong localization of 4d in FS-SRO membranes could increase the resistance and induce the metal–insulator transition. The distinct magnetic properties observed between FS-SRO and RG-SRO indicate fundamental differences in their electronic structure, originating from interfacial variations in spin configuration, chemical stoichiometry, and strain status.

Emergent THE in FS-SRO membranes

To further systematically probe thickness-dependent transport evolution, we performed Hall resistivity measurements on RG-SRO and FS-SRO membranes to examine the electrical transport properties. Figure 3A and B shows the schematic and optical microscopy image of the typical Hall bar devices with platinum electrodes. The Hall resistivity of SRO can be expressed as

ρ xy = R 0 H + R S M + ρ xy T

, where first term on the right side represents the ordinary Hall effect, which is proportional to out-of-plane magnetic field H. The negative ordinary Hall backgrounds provide evidence that the carriers are n type. The second term corresponds to the AHE, where R_S and M are the anomalous Hall coefficient and out-of-plane magnetization. The third term

ρ xy T

denotes the topological Hall resistivity that is typically associated with originates from magnetic skyrmions, chiral domain walls, or other noncollinear spin textures with chirality [38,39]. As shown in Fig. 3C to H, after subtracting the linear ordinary Hall term, all samples exhibit sign-reversed hysteresis loops in Hall resistivity ρ_xy, confirming the existence of a negative R_s. AHE hysteresis loops are observed in RG-SRO films at all thicknesses, consistent with previous literature [19]. In particular, as shown in Fig. 3D and F, distinct Hall anomalies emerge near ±H_c at 5 K for FS-SRO membranes with thicknesses of 3.6 and 4.8 nm. The observed hump signatures could be attributed to the term

ρ xy T

. In addition, as the thickness of the FS-SRO membrane increases, the intensity of the Hall anomalies decreases monotonically, vanishing completely at 12 nm. To further validate the reproducibility of the Hall anomalies, we measured the Hall resistance as a function of magnetic field for 3 devices on the FS-SRO with 4.8 nm (Fig. S3). The consistent observation of emergent THE-like behavior in all devices implies that the freestanding state and its associated lattice structure can stabilize magnetic domain configurations in the ultrathin SRO membranes (Fig. S4A to C). More interestingly, these electrical/magnetic properties are exhibited in an isolated single-layer SRO without clamping or proximity effect from substrate or superlattice [16,40].

An alternative theoretical framework proposes a 2-channel AHE mechanism involving the superposition of opposite Hall polarities to explain the observed transport anomalies [22–24,41]. While our FS-SRO membranes exhibit M–H loops with 2 distinct magnetic orders, the pronounced hump in the ρ_xy–H loops would seem to be attributed to a 2-channel AHE mechanism (Fig. 3D and F). However, rigid samples with very similar M–H loop profiles show no such anomalies in their ρ_xy–H loops (Fig. 3C, E, and G). This discrepancy indicates that the 2-channel model cannot fully explain the topological Hall-like behavior. To investigate the origin of Hall anomalies, Fig. 4 presents the thickness- and temperature-dependent Hall resistivity hysteresis for RG-SRO and FS-SRO, with blue arrows indicating magnetic field sweep direction. For rigid samples, the Hall resistivity exhibited conventional AHE behavior without hump-like features. In contrast, freestanding samples demonstrated a distinct hump superimposed on the AHE hysteresis loop over a broad temperature range from 5 to 100 K (Fig. 4C). Notably, Hall anomalies consistently emerge below the AHE sign-reversal temperature in FS-SRO membranes (Fig. 4C and D). This contrasts with reported 2-channel AHE behavior in other SRO systems, where anomalies appear only in a narrow temperature window between the AHE sign-reversal temperature and T_c [42–44]. The Hall anomalies observed in FS-SRO recall the characteristic signatures of the intrinsic THE previously reported in ultrathin SRO films and SRO-based heterostructures [14–16].

Manipulation of the THE by current and field orientation

On the other hand, as illustrated in Fig. 5A and B, the

ρ xy T

exhibit a progressive suppression with increasing longitudinal current density j_x between 2.78 × 10⁶ and 5.55 × 10⁸ A/m². Figure 5C shows inverse proportionality between the

ρ xy T

and j_x, described by the scaling relation:

ρ xy T j ∝ 1 / j x

. To explain this current-dependent THE, we first provide a concise overview of skyrmion dynamics. Spin-polarized current applies a force on the magnetic spin structure via the spin–transfer torque mechanism, a phenomenon that has been widely studied in ferromagnetic systems [45,46]. Moving skyrmions can generate emergent electric fields [47]:

E = − P e q e v s × b e

, where P_e signifies the degree of spin polarization of the charge carriers, q^e represents the emergent charge that arises from the spin configurations of these charge carriers, including spin-up and spin-down, v_s is the drift velocity of skyrmions, and b_e is the emergent magnetic field generated by skyrmions. This transverse emergent electric field counteracts the additional Hall voltage, thereby suppressing the topological Hall resistivity, a hallmark manifestation of the skyrmion Hall effect (SkHE) [48,49]. Subsequently, the functional relationship between current density and topological Hall resistivity can be established through the constitutive relation [50]:

ρ xy T j = E y / j x,

where E_y denotes the net transverse emergent electric field arising from skyrmions [47]. At sufficiently high j_x, the back action of the current becomes strong enough to overcome the pinning force of the skyrmion domains, causing the skyrmions to begin to move [4,47]. Meanwhile, high j_x may destroy skyrmions by driving them toward nanotracks edges [51,52]. Our results are consistent with the proposed mechanism of current-driven skyrmion motion, suppressing the THE as discussed.

In materials with pronounced magnetic skyrmions,

ρ xy T

should be strongly dependent on the canting angle of the magnetic field [53,54]. Figure 5D to F systematically demonstrates the angular dependence of THE under magnetic field inclinations ranging from out-of-plane (θ = 0°) to in-plane (θ = 90°). Both

ρ xy T

and the H_c exhibit strong angular dependence:

ρ xy T

decreases progressively with increasing canting angle θ and disappears at θ = 80°, while H_c follows characteristic 1/cos(θ) scaling (Fig. 5F). Furthermore, this suppression is consistent with skyrmion systems such as La_0.825Sr_0.175MnO₃ [55] and CaMnO₃/CaIrO₃/CaMnO₃ [56] trilayer structure, and the topological charge (Q) of skyrmions was transformed into zero when the magnetic field is tilted toward the in-plane orientation. Following the established relationship [56]:

ρ xy T ∝ Q

, this phase transition consequently diminishes the THE. Our FS-SRO shows a wide phase diagram region of the THE signatures under the field tilting up to θ = 80°. In addition, as shown in Fig. S7, AHE loops of RG-SRO (3.6 nm) measured under varying current densities and magnetic field orientations exhibit robustness of maximum ρ_xy, providing further evidence that the THE observed in FS-SRO originates from skyrmions, rather than the artifact of 2-channel AHE.

Discussion

Less

Structural origin of THE in FS-SRO membranes

In summary, the observed THE in FS-SRO, including its characteristic hump, current-dependent suppression, and sensitivity to field orientation, provides strong evidence for stabilizing current-sensitive chiral spin textures such as skyrmions. To elucidate the connection between THE and magnetic spin texture, we investigate the microscopic origin of the DMI in the FS-SRO membranes. The stabilization of chiral spin textures in the strongly correlated oxide systems typically requires strong DMI from spin–orbit coupling (SOC) and inversion symmetry breaking [12,13]. The ρ_xy–H loops of the RG-SRO layer with the varying concentration of oxygen defects (Fig. S6) indicate that, in our SRO, oxygen defects alone are insufficient to induce measurable THE. In FS-SRO membranes, a selective etching of Sr–O layers during sacrificial layer dissolution creates asymmetric Ru–O-terminated surfaces (Fig. 6A). This lattice distortion naturally breaks inversion symmetry, providing a possible way to generate the DMI. The Hamiltonian of the DMI is defined as follows: H_DMI = D₀₁ · (S₀ × S₁), where the DMI vector is given by D₀₁ = Dr₀₁ × z. Here, r₀₁ and z respectively represent pointing from S₀ to S₁ and unit vectors along the [001] axis. As shown in Fig. 6B, D₀₁ should be perpendicular to the Ru–O–Ru chains [11,13]. DMI stabilizes skyrmions in the FS-SRO, leading to the observations of the THE and SkHE. The evolution of skyrmion density (d_sk) with sample thicknesses provides important information about the origin of skyrmions. Because of the strong interaction between local M in skyrmions and spin of charge carriers, the skyrmion density can be expressed as follows:

d sk = e ρ xy T / R 0 h P e

, where e and h denote elementary charge and Planck constant, respectively. For SRO, we estimate P_e = −10 ± 5% according to previous reports [15,19]. The

ρ xy T

and d_sk reaches maximum at 5 K and decreases gradually with the increasing temperature (Fig. 6C), indicating that thermal fluctuations suppress skyrmion stability. Furthermore, the marked decay of d_sk with increasing FS-SRO thickness suggests that the skyrmions stabilization mechanism originates near the lower surface.

On this basis, we conducted density functional theory (DFT) 0o988calculations comparing lattice and electronic structures of RG-SRO and FS-SRO. The structural schematic diagrams and computational details are presented in Fig. S8 and Materials and Methods. It can be observed that the RG-SRO films greatly retain the structural features of bulk SRO, except for a buckling distortion in the surface Sr_II–O_II layer, with the Sr_II atoms displaced downward, while the RuO₆ octahedra remain intact. In contrast, FS-SRO undergoes more pronounced structural symmetry breaking, wherein the original RuO₆ octahedra are transformed into RuO₅ square pyramids due to the removal of the underlying Sr–O layer (Fig. S8). As listed in Table S1, compared to the RG-SRO, the difference between Ru_I–O_I and Ru_II–O_I bond lengths in FS-SRO is notably increased (δ = 0.29Å), and the diagonal Sr_I–O_I–Sr_I angle is concurrently decreased to 165.28°. As shown in Fig. 6D, DFT calculations revealed that the FS-SRO with the Ru–O-terminated surfaces shows larger degree of lattice distortion than the RG-SRO. Meanwhile, the DMI strength (|D|) of FS-SRO is about 1.53 meV/Ru, approximately 5 times larger than RG-SRO (0.34 meV/Ru). The enhanced |D| in FS-SRO membranes directly stabilize magnetic skyrmions, accounting for the observed THE. To further investigate the role of oxygen vacancies, as illustrated in Fig. S3A. The calculated DMI strength |D| for this defective structure, shown in Fig. S3B, increases to 2.00 meV/Ru. This enhancement can be attributed to the additional lattice distortion induced by oxygen vacancies at the bottom surface (Fig. S10). These results suggest that while oxygen vacancies alone are insufficient to trigger THE, appropriate concentration can further enhance the DMI strength in FS-SRO.

This structural symmetry breaking profoundly alters the magnetic properties of SRO. The magnetic moment calculated by DFT (Table S1) reveals that localized moments for Ru_I and Ru_II atoms in FS-SRO (RG-SRO) are found to be 2.58 μ_B (1.36 μ_B) and 1.77 μ_B (1.43 μ_B), respectively. In FS-SRO, the formation of RuO₅ square pyramids crystal field at the Ru–O-terminated surface results in the splitting of the e_g orbitals into d_x2−y2 and d_z2. Projected density of states (PDOS) in Fig. 6E and F shows that the energy of d_z2 orbital of Ru_I at Ru–O-terminated surfaces is lowered below the Fermi level, falling even below the d_yz level. Moreover, in the absence of the Sr–O termination, the spin-down electron from the d_yz orbital of Ru_II, previously located near the Fermi level and involved in conduction, becomes transferred to the lower d_z2 orbital of Ru_I. Furthermore, because of the close energy proximity between the d_z2 and d_xy/d_xz orbitals, the 3 electrons now preferentially align their spins parallel. This stabilizing high-spin configuration of Ru_I (d⁵, S = 3/2) and Ru_II (d³, S = 3/2), confirming the existence of high-spin states in FS-SRO compared to low-spin states of RG-SRO (d⁴, S = 1) in Fig. S11. This electronic reconstruction substantially enhances the M_s in the FS-SRO, which is consistent with our experimental results (Fig. 2). The Ru_I magnetic moment is slightly lower than expected 3.00 μ_B. This discrepancy arises from the hybridization between the Ru_I d and O p orbitals, which induces a localized magnetic moment of ~0.30 μ_B on the oxygen atom. Furthermore, by analyzing the layer-resolved SOC energy difference (E_SOC), as illustrated in Fig. S12A, b, we find that the DMI in both systems primarily originates from the Ru_I atom, since the E_SOC of O atoms is negligible. We have compared our system with SRO-based materials in Table S2. Most reported systems exhibit relatively low saturation magnetization, suggesting that conventional tuning approaches have limited influence on the spin state. In contrast, our method not only achieves a high saturation magnetization of up to 3.1 μB/Ru but also yields a substantial DMI strength. Meanwhile, the freestanding structure allows for seamless integration with silicon-based technologies, facilitating the development of next-generation spintronic devices.

In this work, we have successfully fabricated large-area 2-dimensional SRO membranes of varying thickness using a water-soluble SAO sacrificial layer from epitaxial SRO/SAO/STO heterostructures. We demonstrate that the ultrathin FS-SRO membranes integrated on silicon exhibit a pronounced THE over wide temperature range and under tilted magnetic field, which is attributed to the emergence of the noncollinear skyrmions. This phenomenon originates from the asymmetric Ru–O-terminated surface in the FS-SRO membrane, which substantially enhances structural symmetry breaking and the DMI strength, thereby inducing the THE. Furthermore, compared with rigid films, ultrathin FS-SRO membranes (<12 nm) stabilize high spin states with a large magnetic moment. These findings not only provide critical insights into the THE properties of 2-dimensional SRO materials but also establish a foundation for the development of next-generation spintronic devices based on silicon-integrated oxide membranes.

Materials and Methods

Less

Preparation of epitaxial SRO films

The series of SRO films and SRO/SAO heterostructures was epitaxially grown on STO (001) single-crystal substrates by pulsed laser deposition (PLD) using a KrF excimer laser (λ = 248 nm). The STO substrates were subjected to an etching process utilizing buffered hydrofluoric acid and annealed in an ambient atmosphere at 1,000 °C for 90 min to achieve an atomically flat and TiO₂-terminated surface. All SRO films were grown under an oxygen partial pressure of 1 × 10⁻¹ torr at a temperature of 700 °C, and the laser repetition rate was set at 2 Hz. The water-soluble sacrificial SAO layers (~12 nm) were grown in an oxygen atmosphere of 5 × 10⁻⁵ torr at a temperature of 700 °C using a 2-Hz laser frequency, and growth was monitored via RHEED. After deposition, all samples were postannealed at growth temperature for 15 min under an oxygen pressure of 1 × 10⁻¹ torr.

Fabrication of FS-SRO membranes and structural characterizations

To fabricate highly crystalline FS-SRO membranes, the sacrificial SAO layer in the epitaxial heterostructures was selectively etched with deionized water. Upon the complete dissolution of the sacrificial layer, the film was exfoliated and adhered to polydimethylsiloxane (PDMS). FS-SRO membranes were transferred on Si substrate using the transfer stage with heating and a precise displacement controller (E1-T, Metatest Corporation, China). The crystal structures of the rigid, FS-SRO membranes and SRO/SAO heterostructures were investigated by XRD (Rigaku, SmartLab 3KW). The thickness, morphology, and crystal structures of FS-SRO membranes are characterized by TEM (F20, Tecnai) and atomic force microscopy (MFP-3D Origin+).

Electrical transport and magnetic measurements

Longitudinal and transverse transport data at low temperature were measured using a Physical Properties Measurement System (PPMS; Quantum Design) on standard Hall bars. Photolithography and Ar ion milling were used to pattern the SRO films into the Hall bar geometry. The Pt films were deposited onto the Hall bar as contact electrodes via PLD. Transport characterizations, M–H loops, and M–T curves were measured using PPMS. The magnetic field was applied along the out-of-plane direction. Hall measurements were performed with the magnetic field sweeping up to ±5 T. M–H loops were obtained by sweeping the magnetic field up to ±5 T.

DFT calculations

First-principles calculations were performed using the projected augmented wave method, as implemented in the Vienna ab initio simulation package (VASP) [57–59]. The generalized gradient approximation (GGA) in the form of Perdew–Burke–Ernzerhof (PBE) functional was adopted to describe the exchange–correlation interaction [60]. To treat the strong correlations of the Ru 4d orbitals, the GGA + U scheme was used, with the Hubbard parameters U and J set to 2.5 and 0.4 eV, respectively [61–63]. All structures were optimized until the force on each atom was less than 0.001 eV/Å, and the convergence criterion for energy was 10⁻⁶ eV. The plane-wave cutoff energy was set to 500 eV. To sample the Brillouin zone, Γ-centered k meshes of 19 × 19 × 1 for both RG-SRO and FS-SRO, respectively. A vacuum space of >20 Å was applied along the z direction to eliminate interactions between periodic images. The DMI strength was calculated on the basis of the chirality-dependent total energy difference approach in the presence of SOC using noncollinear calculations in VASP [64]. The 4 × 1 × 1 supercell was constructed for the RG-SRO and FS-SRO systems. The clockwise (CW) and anticlockwise (ACW) spin configurations of Ru atoms in various SRO films are illustrated in Fig. S9. The DMI energy is defined as H_DMI = D_ij · (S_i × S_j). The DMI strength was then calculated via the energy difference between CW and ACW spin configurations, expressed as D = (H_CW − H_ACW)/n. In our systems, n equals 8.

References

Less

Nagaosa

, Tokura

. Topological properties and dynamics of magnetic skyrmions. Nat Nanotechnol. 2013;8(12):899–911.

Fert

, Reyren

, Cros

. Magnetic skyrmions: Advances in physics and potential applications. Nat Rev Mater. 2017;2(7):17031.

Verma

, Addison

, Randeria

. Unified theory of the anomalous and topological Hall effects with phase-space Berry curvatures. Sci Adv. 2022;8(45):Article eabq2765.

Birch

, Belopolski

, Fujishiro

, Kawamura

, Kikkawa

, Taguchi

, Hirschberger

, Nagaosa

, Tokura

. Dynamic transition and Galilean relativity of current-driven skyrmions. Nature. 2024;633(8030):554–559.

Lozano-Gomez

, Iqbal

, Vojta

. A classical chiral spin liquid from chiral interactions on the pyrochlore lattice. Nat Commun. 2024;15(1):10162.

Tomasello

, Martinez

, Zivieri

, Torres

, Carpentieri

, Finocchio

. A strategy for the design of skyrmion racetrack memories. Sci Rep. 2014;4(1):6784.

, Upadhyaya

, Shao

, Wu

, Yin

, Li

, He

, Jiang

, Han

, Amiri

, et al.Room-temperature skyrmion shift device for memory application. Nano Lett. 2017;17(1):261–268.

Garcia-Sanchez

, Sampaio

, Reyren

, Cros

, Kim

. A skyrmion-based spin-torque nano-oscillator. New J Phys. 2016;18(7):Article 075011.

Liang

, Shen

, Xing

, Zhou

. Elongated skyrmion as spin torque nano-oscillator and magnonic waveguide. Commun Phys. 2022;5(1):310.

10.

Lone

, Zou

, Das

, Fong

, Setti

, Fariborzi

. Anomalous Hall and skyrmion topological Hall resistivity in magnetic heterostructures for the neuromorphic computing applications. NPJ Spintronics. 2024;2(1):3.

11.

Dzyaloshinsky

. A thermodynamic theory of “weak” ferromagnetism of antiferromagnetics. J Phys Chem Solids. 1958;4(4):241–255.

12.

Manchon

, Koo

, Nitta

, Frolov

, Duine

. New perspectives for Rashba spin-orbit coupling. Nat Mater. 2015;14(9):871–882.

13.

Moriya

. Anisotropic superexchange interaction and weak ferromagnetism. Phys Rev. 1960;120(1):91–98.

14.

Qin

, Liu

, Lin

, Shu

, Xie

, Lim

, Li

, He

, Chow

, Chen

. Emergence of topological Hall effect in a SrRuO₃ single layer. Adv Mater. 2019;31(8):1807008.

15.

Matsuno

, Ogawa

, Yasuda

, Kagawa

, Koshibae

, Nagaosa

, Tokura

, Kawasaki

. Interface-driven topological Hall effect in SrRuO₃-SrIrO₃ bilayer. Sci Adv. 2016;2(7):Article e1600304.

16.

Wang

, Feng

, Kim

, Lee

, Pollard

, Shin

, Zhou

, Peng

, Lee

, et al.Ferroelectrically tunable magnetic skyrmions in ultrathin oxide heterostructures. Nat Mater. 2018;17(12):1087–1094.

17.

, Han

, Liu

, Ren

, Zhu

, Petrovic

. Room-temperature skyrmion thermopower in Fe₃Sn₂. Adv Quantum Technol. 2020;3(10):2000058.

18.

Akram

, LaBollita

, Dey

, Kapeghian

, Erten

, Botana

. Moire skyrmions and chiral magnetic phases in twisted CrX₃ (X = I, Br, and cl) bilayers. Nano Lett. 2021;21(15):6633–6639.

19.

Koster

, Klein

, Siemons

, Rijnders

, Dodge

, Eom

C-B

, Blank

DHA

, Beasley

. Structure, physical properties, and applications of SrRuO₃ thin films. Rev Mod Phys. 2012;84(1):253–298.

20.

Niu

, Chen

, Zhong

, Xiang

, Duan

. Topological Hall effect in SrRuO₃ thin films and heterostructures. J Phys Condens Matter. 2022;34(24):Article 244001.

21.

, Wang

, Hu

, Liu

, Zhang

, Pan

, Song

. An overview of SrRuO₃-based heterostructures for spintronic and topological phenomena. J Phys D Appl Phys. 2022;55(23):Article 233001.

22.

Wang

, Feng

, Lee

, Ko

, Lu

, Noh

. Controllable thickness inhomogeneity and berry curvature engineering of anomalous Hall effect in SrRuO₃ ultrathin films. Nano Lett. 2020;20(4):2468–2477.

23.

Zheng

, Fang

, Zhang

, Li

, Wen

, Fang

, He

, Li

, Zhang

, Tong

, et al.Berry phase engineering in SrRuO₃/SrIrO₃/SrTiO₃ superlattices induced by band structure reconstruction. ACS Nano. 2021;15(3):5086–5095.

24.

Kimbell

, Sass

, Woltjes

, Ko

, Noh

, Wu

, Robinson

JWA

. Two-channel anomalous Hall effect in SrRuO₃. Phys Rev Mater. 2020;4(5):Article 054414.

25.

Zhang

, Lin

, Wang

, He

, Ye

, Lu

, Wang

, Liang

, Jin

, et al.Super-tetragonal Sr₄Al₂O₇ as a sacrificial layer for high-integrity freestanding oxide membranes. Science. 2024;383(6681):388–394.

26.

Nian

, Sun

, Wang

, Xu

, Hao

, Yan

, Li

, Zhou

, Deng

, Hao

, et al.Sr₄Al₂O₇: A new sacrificial layer with high water dissolution rate for the synthesis of freestanding oxide membranes. Adv Mater. 2024;36(15):Article e2307682.

27.

Liu

, Feng

, Tang

, Zhao

, Gao

, Shi

, Yang

. Mechanically tunable magnetic properties of flexible SrRuO₃ epitaxial thin films on mica substrates. Adv Electron Mater. 2018;4(4):1700522.

28.

, Si

, Zhang

, Tian

, Liu

, Song

, Dong

, Wang

, Cheng

, Qu

, et al.Defect-engineered Dzyaloshinskii-Moriya interaction and electric-field-switchable topological spin texture in SrRuO₃. Adv Mater. 2021;33(33):Article e2102525.

29.

Kim

, Jung

, Lee

. Single-crystalline-level properties of ultrathin SrRuO₃ flexible membranes with wide and clean surface. NPJ Flexible Electron. 2022;6(1):24.

30.

, Si

, Yao

, Tian

, Wang

, Zhang

, Lai

, Malik

, Liu

, Jiang

, et al.Electric field controllable high-spin SrRuO₃ driven by a solid ionic junction. Phys Rev B. 2020;101(21):Article 214401.

31.

Wang

, He

, Guo

, Wang

, Shi

, Han

, Fang

, Wang

, Zhang

, et al.High-temperature ferromagnetic metallic phase in LaMnO₃/Sr₃Al₂O₆ heterostructure. J Mater Sci Technol. 2022;119:69–74.

32.

Lee

, Liu

, Heo

, Gordon

. Creation and control of two-dimensional electron gas using Al-based amorphous oxides/SrTiO₃ heterostructures grown by atomic layer deposition. Nano Lett. 2012;12(9):4775–4783.

33.

, Kang

, Liu

, Wang

, Miao

, Zhang

, Wu

, Ren

, Meng

, Chen

, et al.Strain- and oxygen-modulated anomalous Hall effect in the SrRuO₃/Sr₃Al₂O₆ heterostructure. J Phys Chem C. 2023;127(47):23044–23052.

34.

Grutter

, Wong

, Arenholz

, Liberati

, Vailionis

, Suzuki

. Enhanced magnetism in epitaxial SrRuO₃ thin films. Appl Phys Lett. 2010;96(8):Article 082509.

35.

Wang

, Liu

, He

, Qi

, Wang

, Xu

, Zhang

, Wang

, Chen

, Wang

, et al.Enhanced oxygen evolution reaction by stacking single-crystalline freestanding SrRuO₃. Appl Catal B. 2022;317(15):Article 121781.

36.

Zhang

, He

, Guo

, Wang

, Han

, Shi

, Chen

, Fang

, Wang

, Yan

, et al.Extreme enhanced curie temperature and perpendicular exchange bias in freestanding ferromagnetic superlattices. ACS Appl Mater Interfaces. 2023;15(13):17309–17316.

37.

Ning

, Wang

, Zhang

. Anisotropy of electrical and magnetic transport properties of epitaxial SrRuO₃ thin films. J Appl Phys. 2015;117(9):Article 093907.

38.

Neubauer

, Pfleiderer

, Binz

, Rosch

, Ritz

, Niklowitz

, Boni

. Topological Hall effect in the a phase of MnSi. Phys Rev Lett. 2009;102(18):Article 186602.

39.

Vistoli

, Wang

, Sander

, Zhu

, Casals

, Cichelero

, Barthélémy

, Fusil

, Herranz

, Valencia

, et al.Giant topological Hall effect in correlated oxide thin films. Nat Phys. 2018;15(1):67–72.

40.

Zhang

, Liu

, Dong

, Wu

, Zhang

, Wang

, Lu

, Ruckriegel

, Wang

, Duine

, et al.Strain-driven Dzyaloshinskii-Moriya interaction for room-temperature magnetic skyrmions. Phys Rev Lett. 2021;127(11):Article 117204.

41.

Groenendijk

, Autieri

, van Thiel

, Brzezicki

, Hortensius

, Afanasiev

, Gauquelin

, Barone

, van den Bos

KHW

, van Aert

, et al.Berry phase engineering at oxide interfaces. Phys Rev Res. 2020;2(2):Article 023404.

42.

Miao

, Schreiber

, Nair

, Goodge

, Jiang

, Ruf

, Lee

, Fu

, Tsang

, Li

, et al.Strain relaxation induced transverse resistivity anomalies in SrRuO₃ thin films. Phys Rev B. 2020;102(6):Article 064406.

43.

Kan

, Moriyama

, Kobayashi

, Shimakawa

. Alternative to the topological interpretation of the transverse resistivity anomalies in SrRuO₃. Phys Rev B. 2018;98(18):Article 180408.

44.

Wang

, Dai

, Liu

, Xie

, Liu

, Lin

, Liu

, Yang

, Wang

, Venkatesan

, et al. Adv Mater. 2020;32(14):1904415.

45.

Iwasaki

, Mochizuki

, Nagaosa

. Universal current-velocity relation of skyrmion motion in chiral magnets. Nat Commun. 2012;4:1463.

46.

Žutić

, Fabian

, Sarma

. Spintronics: Fundamentals and applications. Rev Mod Phys. 2004;76:323–410.

47.

Liang

, DeGrave

, Stolt

, Tokura

, Jin

. Current-driven dynamics of skyrmions stabilized in MnSi nanowires revealed by topological Hall effect. Nat Commun. 2015;6(1):8217.

48.

Jiang

, Zhang

, Yu

, Zhang

, Wang

, Benjamin Jungfleisch

, Pearson John

, Cheng

, Heinonen

, Wang

, et al.Direct observation of the skyrmion Hall effect. Nat Phys. 2016;13(2):162–169.

49.

Litzius

, Lemesh

, Krueger

, Bassirian

, Caretta

, Richter

, Buttner

, Sato

, Tretiakov

, Forster

, et al.Skyrmion Hall effect revealed by direct time-resolved x-ray microscopy. Nat Phys. 2016;13(2):170–175.

50.

Schulz

, Ritz

, Bauer

, Halder

, Wagner

, Franz

, Pfleiderer

, Everschor

, Garst

, Rosch

. Emergent electrodynamics of skyrmions in a chiral magnet. Nat Phys. 2012;8(4):301–304.

51.

Purnama

, Gan

, Wong

, Lew

. Guided current-induced skyrmion motion in 1D potential well. Sci Rep. 2015;5(1):10620.

52.

Zhang

, Zhao

, Fangohr

, Liu

, Xia

, Morvan

. Skyrmion-skyrmion and skyrmion-edge repulsions in skyrmion-based racetrack memory. Sci Rep. 2015;5(1):7643.

53.

Ohuchi

, Kozuka

, Uchida

, Ueno

, Tsukazaki

, Kawasaki

. Topological Hall effect in thin films of the Heisenberg ferromagnet EuO. Phys Rev B. 2015;91(24):Article 245115.

54.

Yan

, Jiang

, Xiao

, Lu

, Song

, Zhu

, Luo

, Sun

, Yamashita

. Field-induced topological Hall effect in antiferromagnetic axion insulator candidate EuIn₂As₂. Phys Rev Res. 2022;4(1):Article 013163.

55.

Kotani

, Nakajima

, Ishii

, Harada

, Mori

. Observation of spin textures in La_1−xSr_xMnO₃ (x = 0.175). AIP Adv. 2016;6(5):Article 056403.

56.

Lim

, Li

, Huang

, Chi

, Zhou

, Zeng

, Omar

, Feng

, Rusydi

, Pennycook

, et al.Emergent topological Hall effect at a charge-transfer interface. Small. 2020;16(50):Article e2004683.

57.

Kohn

, Sham

. Self-consistent equations including exchange and correlation effects. Phys Rev. 1965;140(4A):A1133–A1138.

58.

Blochl

. Projector augmented-wave method. Phys Rev B. 1994;50(24):17953–17979.

59.

Kresse

, Furthmuller

. Efficient iterative schemes for ab initio total-energy calculations using a plane-wave basis set. Phys Rev B. 1996;54(16):11169–11186.

60.

Perdew

, Burke

, Ernzerhof

. Generalized gradient approximation made simple. Phys Rev Lett. 1996;77(18):3865–3868.

61.

Anisimov

, Zaanen

, Andersen

. Band theory and Mott insulators: Hubbard U instead of stoner I. Phys Rev B. 1991;44(3):943–954.

62.

Dudarev

, Botton

, Savrasov

, Humphreys

, Sutton

. Electron-energy-loss spectra and the structural stability of nickel oxide: An LSDA+U study. Phys Rev B. 1998;57(3):1505–1509.

63.

Gupta

, Mandal

, Mahadevan

. Strain-induced metal-insulator transition in ultrathin films of SrRuO₃. Phys Rev B. 2014;90(12):Article 125109.

64.

Yang

, Thiaville

, Rohart

, Fert

, Chshiev

. Anatomy of Dzyaloshinskii-Moriya interaction at Co/Pt interfaces. Phys Rev Lett. 2015;115(26):Article 267210.

Appendix

Less

Year 2026 volume 9 Issue 1

PDF

Cite this Article

BibTeX

Article Info

doi: 10.34133/research.1079

Receive Date：2025-10-15
Online Date：2026-10-16
Published：2026-01-20

Article Data

Affiliations

History

Received：2025-10-15
Revised：2025-11-30
Accepted：2025-12-15

Affiliations

¹Spintronics Institute, School of Physics and Technology, University of Jinan, Jinan 250022, China.

²School of Physics, Harbin Institute of Technology, Harbin 150001, China.

Corresponding:

^* Address correspondence to: sdy_heb@ujn.edu.cn (B.H.);

^* Address correspondence to: sdy_liss@ujn.edu.cn (S.L.);

^* Address correspondence to: weiminglv@hit.edu.cn (W.L.);

^* Address correspondence to: shishenyan@sdu.edu.cn (S.Y.)

References

Share

https://castjournals.cast.org.cn/joweb/research/EN/10.34133/research.1079

Share to

Scan QR to access full text

Cite this article

BibTeX

Citations

表12种不同金属材料的力学参数

科 Family	属数 Number of genus	种数 Number of species	占总种数比例 Percentage of total species (%)	属 Genus	种数 Number of species	占总种数比例 Percentage of total species (%)
鹅膏菌科Amanitaceae	2	11	5.26	鹅膏菌属 Amanita	10	4.78
小菇科 Mycenaceae	2	12	5.74	丝盖伞属 Inocybe	5	2.39
多孔菌科 Polyporaceae	8	14	6.70	蜡蘑属 Laccaria	5	2.39
红菇科 Russulaceae	3	23	11.00	小皮伞属 Marasmius	6	2.87
				小菇属 Mycena	11	5.26
				光柄菇属 Pluteus	5	2.39
				红菇属 Russula	17	8.13
				栓菌属 Trametes	5	2.39

关闭全屏

BibTeX
EndNote
RefWorks
TxT

Fig. 1. Preparation and structural characterization of FS-SRO membranes. (A) Schematic illustration of the fabrication of FS-SRO membranes. The sacrificial SAO layer is dissolved in deionized water to release the SRO films with the support of PDMS. FS-SRO membranes are transferred onto the Si substrate. (B) Optical microscopy image of FS-SRO (3.6 nm) on a Si substrate. (C) Time-dependent RHEED intensity oscillation profiles during the growth of SAO films. A period of three oscillation peaks indicates the deposition of 1/2 unit cell (u. c.). (D) XRD 2θ–ω scans of SRO (12 nm) films, SRO (12 nm)/SAO (12 nm) heterostructures on STO (001), and FS-SRO (12 nm) on Si substrate. (E) Plan-view HRTEM image of FS-SRO membrane. The inset shows the fast Fourier transformation of FS-SRO. (F) Cross-sectional HRTEM image of FS-SRO membrane on Si.

Fig. 2. Magnetic and transport properties of RG-SRO and FS-SRO membranes. (A to C) The M–H of RG-SRO and FS-SRO are presented for 3 different thicknesses: 3.6, 4.8, and 12 nm at 5 K. Magnetic fields were applied along the out-of-plane direction. (D) Normalized M–T curves of RG-SRO and FS-SRO with various thicknesses: 3.6, 4.8, and 12 nm. The M–T curves were measured with an out-of-plane magnetic field of 1,000 Oe. (E) Variation of M_s and T_c with SRO thickness for RG-SRO films and FS-SRO membranes. (F) Comparison of temperature-dependent longitudinal resistivity ρ_xx for RG-SRO and corresponding FS-SRO membranes.

Fig. 3. Hall transport properties of RG-SRO films and FS-SRO membranes. (A) Schematic of the Hall bar device for an FS-SRO film. I₊ and I₋ represent the applied current. V_xx and V_xy represent the measured longitudinal and transverse voltages, respectively. (B) Optical image of a Hall bar device for an FS-SRO membrane on the Si substrate. (C to H) Magnetic-field-dependent Hall resistivity ρ_xy of RG-SRO and FS-SRO membranes with various thicknesses at 5 K. The H is applied along the out-of-plane direction. The ordinary Hall components (R₀H) were subtracted.

Fig. 4. Hall resistivity of RG-SRO films and FS-SRO membranes. Magnetic field dependence of the Hall resistivity ρ_xy of the RG-SRO films with 3.6 nm (A) and 4.8 nm (B) at various temperatures. Magnetic field dependence of the Hall resistivity ρ_xy of the FS-SRO membranes with 3.6 nm (C) and 4.8 nm (D) at various temperatures. Blue arrows represent sweeping directions of the magnetic field. The ordinary Hall term was subtracted.

Fig. 5. Current- and field-orientation dependence of THE in FS-SRO membranes. (A) Magnetic-field-dependent ρ_xy of FS-SRO membranes (3.6 nm) at 60 K under various current density and (B) topological Hall resistivity $ρ xy T$ versus μ₀H. (C) $ρ xy T$ as a function of increasing current density j_x. The red solid line represents nonlinear fitting based on equation 1/j_x. (D) $ρ xy$ versus μ₀H of the FS-SRO membranes (3.6 nm) at 60 K under various magnetic field canting angles θ and (E) topological Hall resistivity $ρ xy T$ versus μ₀H. (F) $ρ xy T$ and H_c as a function of various field canting angles θ. The yellow solid curve represents nonlinear fitting based on equation 1/cos(θ).

Fig. 6. The generation of Ru–O-terminated surfaces and the emergence of DMI in FS-SRO membranes. (A) Schematic of the magnetic structure in the FS-SRO membrane. The etching of the Sr–O termination layer induces inversion symmetry breaking. (B) The DMI vector D₀₁ is perpendicular to the plane defined by Ru–O–Ru. (C) Temperature dependence of $ρ xy T$ and d_sk for FS-SRO membranes. (D) DFT calculations of DMI strength (|D|) for the RG-SRO (SRO/STO) and FS-SRO. Calculated PDOS of the Ru_I (E) and Ru_II (F) atoms in the FS-SRO. The inset is a schematic diagram of the electron configuration of the d orbital of the Ru atom.

Articles: Latest Articles; Most Read; Collections

Updates: Events; News; Multimedia

About: About Us

Contact

No. 86 Xueyuan South Road, Haidian District, Beijing

100081

010-62662699(Operation and Technical Support)

qkjq@cast.org.cn

Copyright © 2025 China Association for Science and Technology. All rights reserved. For all open access content, the relevant licensing terms apply.
Sponsored by the Office of the Leading Group for Cybersecurity and Informatization of CAST, and supported by Science and Technology Review Publishing House