Efficient and Stable Large-Area Perovskite Solar Cells with Inorganic Perovskite/Carbon Quantum Dot-Graded Heterojunction
收藏切换
PDF
Qiang Sun1, Cai Shen2, Deyu Wang2, Tao Zhang1, Huaxia Ban1, Yan Shen1, Zhipan Zhang3, Xiao-Li Zhang4, Guanjun Yang5, Mingkui Wang1
Research. Vol 2021 Article ID 9845067
Less
收藏切换
Research. Vol 2021 Article ID 9845067
• Research Article •
Efficient and Stable Large-Area Perovskite Solar Cells with Inorganic Perovskite/Carbon Quantum Dot-Graded Heterojunction
Full
Qiang Sun1, Cai Shen2, Deyu Wang2, Tao Zhang1, Huaxia Ban1, Yan Shen1, Zhipan Zhang3, Xiao-Li Zhang4, Guanjun Yang5, Mingkui Wang1
Affiliations
  • 1Wuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology, Wuhan, Hubei 430074, China
  • 2Ningbo Institute of Materials Technology & Engineering, Chinese Academy of Sciences, 1219 Zhongguan Road, Ningbo 315201, China
  • 3School of Chemistry, Beijing Institute of Technology, Beijing 102488, China
  • 4State Centre for International Cooperation on Designer Low-Carbon & Environmental Materials, School of Materials Science and Engineering, Zhengzhou University, 450001, China
  • 5State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China
About Author:

Authors’ Contributions

Q.S. and M.W. conceived the ideas. Q.S. conducted the device fabrication, performed the data analysis, and prepared the manuscript. C.S. and D.W. helped with the scanning KPFM characterization. Y.S. and X.Z helped with data analysis. T.Z. and H.B. helped with the device measurements. Z.Z. helped with the TOF-SIMS characterization. G.Y. provided the carbon paste. M.W. guided and supervised the whole study. All authors have given approval to the final version of the manuscript.

Published: 2021-07-20 doi: 10.34133/2021/9845067
Outline
收藏切换

This work reports on a compositionally graded heterojunction for photovoltaic application by cooperating fluorine-doped carbon quantum dots (FCQDs in short) into the CsPbI2.5Br0.5 inorganic perovskite layer. Using this CsPbI2.5Br0.5/FCQDs graded heterojunction in conjunction with low-temperature-processed carbon electrode, a power conversion efficiency of 13.53% for 1 cm2 all-inorganic perovskite solar cell can be achieved at AM 1.5G solar irradiation. To the best of our knowledge, this is one of the highest efficiency reported for carbon electrode based all-inorganic perovskite solar cells so far, and the first report of 1 cm2 carbon counter electrode based inorganic perovskite solar cell with PCE exceeding 13%. Moreover, the inorganic perovskite/carbon quantum dot graded heterojunction photovoltaics maintained over 90% of their initial efficiency after thermal aging at 85° for 1056 hours. This conception of constructing inorganic perovskite/FCQDs graded heterojunction offers a feasible pathway to develop efficient and stable photovoltaics for scale-up and practical applications.

Qiang Sun, Cai Shen, Deyu Wang, Tao Zhang, Huaxia Ban, Yan Shen, Zhipan Zhang, Xiao-Li Zhang, Guanjun Yang, Mingkui Wang. Efficient and Stable Large-Area Perovskite Solar Cells with Inorganic Perovskite/Carbon Quantum Dot-Graded Heterojunction[J]. Research, 2021 , 2021 (7) : 9845067 - . DOI: 10.34133/2021/9845067
Full Text
Less
1. Introduction
Less
Lead halide perovskites with the ABX3 formula (where X is halogen anion, A is monovalent cation (methylammonium (MA+), formamidinium (FA+) or Cs+), and B is Pb2+) have emerged as disruptive photovoltaic materials for solar energy conversion owning to a rapid increase in power conversion efficiency (PCE) [1–5]. However, the instability against thermal stress and humidity originated from the hygroscopic and volatile nature of organic cations (including MA+ and FA+) in these organic-inorganic hybrid perovskites as well as organic materials for collecting currents in a complete device has been the primary issue to hinder their commercialization [6–8]. Therefore, a solar cell free of organic components, which is constructed solely with inorganic perovskite compounds and inorganic functional materials including charge transport materials and contact electrode materials, offers great possibilities of enhancing solar cells performance with high stability.
In this regard, all-inorganic perovskite solar cells (PSCs) with carbon counter electrodes are thus developed in view of the structural stability and cost-effectiveness, and have become research interests arising from great prospect toward commercialization [9–14]. For example, an all-inorganic PSC with a structure of FTO/TiO2/CsPbIBr2/carbon has been reported by Zhu et al., which achieved a PCE over 9% and an open-circuit voltage (VOC) of 1.245 V [10]. Previously, we reported 10.8% efficient stable full-printable PSCs using an inorganic metal oxide framework of FTO/TiO2/Al2O3/NiO/carbon and inorganic perovskite CsPb0.98Mg0.02I2Br [15]. The inorganic perovskites featuring with excellent compositional and thermal stability offer promising potentials to process solar cells with high stability [16–18]. The utilization of moisture resistant carbon counter electrode offers additional advantages to inorganic PSCs, including good stability in ambient conditions and low-cost manufacture [19]. Moreover, the carbon electrode based PSCs can be fabricated with printing technology such as gravure printing and flexographic printing, which is beneficial for the scalable production of large modules [20]. Unfortunately, relatively lower PCE (typically 7%-11%) has been often observed for the inorganic PSCs using carbon counter electrode comparing to their counterparts that using 2,2′,7,7′-tetrakis(N,N-di-4-methoxyphenylamino)-9,9′-spiro-bifluorene (spiro-OMeTAD) as the hole-transport layer (HTL) and Au as the counter electrode [19, 21].
The interface between perovskite layer and carbon electrode is crucial to the photovoltaic performance of carbon electrode based PSCs. A poor interfacial contact as well as mismatched energy level alignment between perovskite layer and carbon electrode significantly induces undesirable charge recombination [22–25]. This also explains the widely observed large VOC loss (defined as Eg/q−VOC, where Eg is the bandgap of the absorption material, q is elementary charge), as well as low fill factor (FF) for carbon electrode based PSCs [9–14]. Considering the big resistance of carbon counter electrode (~20-40  Ω/□) with large-sized particles of high porosity, indeed, minimization of the interfacial recombination kinetics gives a good shot of enhancing VOC along with FF. Therefore, in aim to enhance the photovoltaic performance of carbon electrode based all-inorganic PSCs, it is of fundamental importance to overcome the limits through the formation of intimate contact at the perovskite/carbon electrode interface and tailoring the interfacial energy-band alignment.
Graded-heterojunction (GHJ) engineering can be an effective method to facilitate the separation of photo-generated charge carriers and their transport in photovoltaic devices [26–30]. For example, an organic-inorganic hybrid perovskite-fullerene graded-heterojunction structure has been proposed by Wu and coworkers for the inverted-structured planar PSCs, which enabled the fabrication of centimeter-scale PSC device with a certified PCE exceeding 18% [26]. The carbon electrode-based PSCs with MAPbI3-PTAA gradient heterojunction also achieved a PCE of 13.0% in active area of 1 cm2 [29]. The graded-heterojunction architecture combines the advantage of short charge travel distance with the merit of introducing band slope at the heterojunction interface for transport of photo-generated charge carriers. Consequently, charge recombination loss can be minimized and thus augments the open-circuit voltage.
This work for the first time reports on compositionally graded heterojunction for photovoltaic application by injecting fluorine-doped carbon quantum dots (FCQDs in short) into inorganic CsPbI2.5Br0.5 perovskite via the antisolvent method. Because of the excellent optoelectronic properties together with high chemical stability, carbon quantum dots have shown significant potential as charge transport material or surface passivating agent in photovoltaic devices [31–34]. In this case, due to its small size and high polarization property, FCQDs carried by antisolvent (chlorobenzene) can be deposited into the CsPbI2.5Br0.5 perovskite layer before perovskite crystallization, forming a perovskite/FCQDs graded heterojunction with increasing FCQDs percentage along the vertical direction. The results indicate that the FCQDs interact strongly with CsPbI2.5Br0.5 perovskite and efficiently passivate the uncoordinated Pb ions defects. Moreover, the CsPbI2.5Br0.5/FCQDs graded heterojunction selectively promotes photo-generated charge separation and extraction, resulting in improved photovoltaic performance. The CsPbI2.5Br0.5/FCQD-graded heterojunction in conjunction with low-temperature-processed carbon electrode achieved an impressive power conversion efficiency of 13.53% in a 1 cm2 device at AM 1.5G solar irradiation. More importantly, the solar cells based on CsPbI2.5Br0.5/FCQDs GHJ in combination with low-temperature processed carbon electrode exhibited excellent long-term stability. The unencapsulated devices maintained over 90% of their initial efficiency under thermal aging at 85°С for 1056 h.
2. Results
Less
The CsPbI2.5Br0.5/FCQDs graded heterojunction was fabricated by injecting FCQDs into inorganic CsPbI2.5Br0.5 perovskite layer via antisolvent method during perovskite precursor spin-coating process as illustrated in Figure 1(a). In this case, partial FCQDs in a size of about 3-7 nm (characterized with transmission electron microscopy, Figure S1) carried by antisolvent chlorobenzene (CB) can be deposited into the upper layer of CsPbI2.5Br0.5 perovskite film before crystallization, while most of FCQDs maintain on perovskite layer surface, forming a CsPbI2.5Br0.5/FCQDs graded heterojunction structure with increasing FCQDs percentage along the vertical direction. This GHJ conception was verified by time-of-flight secondary-ion mass spectrometry (TOF-SIMS) characterization as shown in Figure 1(b) [15, 35]. When sputtering through the CsPbI2.5Br0.5/FCQDs GHJ thin film by using Bi3+ ion beam, the SIMS characterization detects the signals of Pb, I, Br, and C in negative mass detection mode, in which C was used as an indicator of FCQDs. Obviously, the C depth profile (blue line) shows a steep decline at the perovskite/FCQDs GHJ film surface and negligible counting amount in the bulk. The decrease of carbon content along the vertical direction verifies a graded distribution of FCQDs in the CsPbI2.5Br0.5 perovskite absorption layer.
The interfacial band alignment around CsPbI2.5Br0.5 and FCQDs was estimated by ultraviolet photoelectron spectroscopy (UPS) and UV-visible absorption spectroscopy characterization (Figure S2a-S2c). The Fermi energy level (EF) of CsPbI2.5Br0.5 and FCQDs was calculated to be −4.36 and −4.74 eV, respectively (Figure S2d). The corresponding valence band maximum (EVB) of CsPbI2.5Br0.5 and FCQDs was further evaluated to be −5.61 eV and −5.37 eV, respectively. By taking into account of the valance band maximum, the conduction band minimum, and the Fermi level of both CsPbI2.5Br0.5 and FCQDs, upon contact, electron is depleted from CsPbI2.5Br0.5 to FCQDs, causing an upward band bending at the CsPbI2.5Br0.5/FCQDs interface. Base on this understanding, we built up an energy-level diagram for the perovskite/FCQDs GHJ in Figure 1(c), which schematically illustrates the upper shift valance band of CsPbI2.5Br0.5 at the heterojunction interface. In addition to concentration gradient, this kind of band bending supplies additional driving force for photogenerated hole extraction and restrains electron flowing back.
Figure S3 shows scanning electron microscopy (SEM) image of surface morphology of the as-prepared perovskite/FCQDs GHJ thin film. The corresponding films are very dense and smooth with few aggregates and pinholes. The X-ray photoelectron spectroscopy (XPS) characterization in Figure S4 presents the chemical states of the as-fabricated films. The binding energies of Pb(4f7/2) and Pb(4f5/2) at 138.2 eV and 143.05 eV for CsPbI2.5Br0.5 sample positively shift to higher values by 0.015 eV for CsPbI2.5Br0.5/FCQDs GHJ sample. This is usually caused with the existence of additional negative charges surrounding Pb ions [36–38]. In this work, we attributed this to the presence of fluorine in FCQDs, which provides extra electrons toward uncoordinated Pb ions at the perovskite film surface and grain boundaries, forming strong Pb-F ionic bonds, therefore efficiently passivating the widespread uncoordinated Pb ions defects. Recently, Li et al. employed fluoride to simultaneously passivate both anion and cation vacancies of halide perovskites, by taking the advantage of its high electronegativity [39]. This conclusion agrees well with our previous reports that the incorporation of fluorine-containing functional groups at the perovskite/HTL interface can efficiently passivate the interfacial defects and boost the photovoltaic performances of PSCs [40]. Figure 1(d) presents the results of steady-state photoluminescence (PL) characterization of the deposited CsPbI2.5Br0.5 thin film and CsPbI2.5Br0.5/FCQDs GHJ thin films on glass substrates. By formation of graded heterojunction, the PL emission peak changed from ~1.81 eV to ~1.82 eV for the CsPbI2.5Br0.5 perovskite thin film. A blue-shifted PL emission peak can be correlated with filling of the trap states on CsPbI2.5Br0.5 layers’ surface or along the grain boundaries by injection of FCQDs [40]. Moreover, a strong photoluminescence quenching of ~60% was observed in the CsPbI2.5Br0.5/FCQDs GHJ thin film as a result of charge transfer from CsPbI2.5Br0.5 to FCQDs. This was further confirmed by time-resolved PL decay characterization, Figure 1(e). A considerably reduced PL decay lifetime (from ~21 to 11 ns) for the CsPbI2.5Br0.5/FCQDs GHJ sample demonstrates substantial photogenerated charge carriers transfer from CsPbI2.5Br0.5 to FCQDs.
To gain more insight about the construction of CsPbI2.5Br0.5/FCQDs GHJ on charge transfer, we investigated the electrical potential distribution across the GHJ structure by performing scanning Kevin probe force microscopy (KPFM) characterization on cross-section of the FTO/TiO2/CsPbI2.5Br0.5/Au and the FTO/TiO2/CsPbI2.5Br0.5/FCQDs GHJ/Au samples in dark condition as shown in Figure S5 [41–44]. To exclude the interference of surface charges on the cleaved surface, the potential distribution measurements were performed at different biases voltage (0 V, −0.5 V, and −1.0 V) [42]. Figures 2(a) and 2(b) present the averaged potential profiles across the two samples. In contrast to the FTO/TiO2/CsPbI2.5Br0.5/Au sample which exhibited a relatively constant potential distribution across the perovskite absorption layer, a potential drop of about 120 mV was observed at the perovskite/FCQDs graded heterojunction area at −1.0 V bias voltage in the FTO/TiO2/CsPbI2.5Br0.5/FCQDs GHJ/Au sample. This obvious potential drop can be caused by charge diffusion motion at the perovskite/FCQDs interface, which also demonstrates the existence of depletion region at the perovskite/FCQDs heterojunction interface. The electric field distribution profiles can be determined as shown in Figures 2(c) and 2(d) by taking the first derivative of the potential differences (Figure S6) for the samples. For the control sample, the electric field at the perovskite/Au interface is quite weak, which implies no obvious depletion region at the interface. Therefore, the photo-generated holes need to diffuse through the whole perovskite absorption layer to be collected by the Au electrode. In contrast, a strong and wide nonzero electric field was identified at the perovskite/FCQDs graded heterojunction area, indicating the formation of a wide depletion region with strong built-in electric field across the junction. This wide depletion region across the perovskite/FCQDs graded heterojunction is expected to facilitate photogenerated hole extraction and thus decrease charge carrier recombination loss.
We further fabricated CsPbI2.5Br0.5/FCQDs GHJ PSCs using low-temperature processed carbon electrode as current collector. With the merit of low-temperature large-area processability and low manufacture cost, the carbon electrode based CsPbI2.5Br0.5/FCQDs GHJ PSCs can be easily scaled up for practical applications. Figure 3(a) presents the cross-sectional SEM image of a completed perovskite/FCQDs GHJ device, from which a dense and uniform CsPbI2.5Br0.5/FCQDs film can be clearly observed. Figure 3(b) presents photocurrent density-voltage (J−V) measurement curves of the optimized 1.0 cm2 PSC devices. We observed that the PSC device (device B) based on perovskite/FCQDs GHJ exhibited improved photovoltaic performance. The champion device showed a VOC of 1.12 V, a JSC of 16.87 mA cm−2, a FF of 71.6%, yielding an impressive PCE of 13.53%. This is one of the highest PCE among carbon electrode-based inorganic PSCs reported so far. In contrast, the control device (device A) showed a total PCE of 10.70%, with a VOC of 1.05 V, a JSC of 15.97 mA cm−2, and a FF of 63.8%. Figure 3(c) presents the plot of PCE versus VOC loss for currently reported PSCs (detail data can be found in Table S1) that using inorganic perovskites (CsPbI3, CsPbI2Br, CsPbIBr2, and CsPbBr3) as light absorber and carbon counter electrode as current collector. Apparently, our present fabricated CsPbI2.5Br0.5/FCQDs GHJ device exhibited both high PCE and low VOC loss. This result substantiates the promising potential for constructing perovskite/FCQDs GHJ toward highly efficient PSCs. To the most of our knowledge, this is the first report of 1 cm2 carbon counter electrode based inorganic PSC with PCE exceeding 13%. Figure 3(d) compares the results of external quantum efficiency (EQE) characterization of the aforementioned PSC devices. Device A exhibited obvious EQE drop in long wavelength region (>600 nm), implying inefficient collection of charge carriers generated in the region close to the back contact of the absorber layer [45–47]. For the HTL-free PSCs, severe charge transfer barrier usually exists at the perovskite/counter electrode interface, thus decreasing charge collection efficiency in such region of the devices [45]. Impressively, device B based on perovskite/FCQDs GHJ exhibited much-improved EQE response in the long wavelength region, which confirms the augmented charge collection efficiency. The integrated JSC calculated from the EQE spectra for devices A and B were estimated to be 15.40 and 16.19 mA cm−2, respectively.
Electronic impedance spectroscopy (EIS) measurements were conducted to understand the effect of perovskite/FCQDs GHJ on electronic processes at the perovskite/carbon electrode interface. The measurements were performed by connecting the FTO glass as working electrode and carbon electrode as counter electrode and reference electrode [48–52]. Figure 4(a) presents the result of EIS characterization in the form of Nyquist plots when the devices were biased at 0.9 V under 10 mW cm−2 illumination. Two semicircles were observed in the frequency analysis. The first arc corresponds to charge transport processes in the charge transport layers or at the charge transport layer/counter-electrode interfaces in the high-frequency region, i.e., fast charge transport processes. The second arc can be assigned to charge recombination processes at the perovskite layer/charge selective contact interfaces in the intermediate frequency region, i.e., relative slow charge transport processes [49]. We fitted the EIS plots with equivalent circuit exhibited in the inset of Figure 4(a). Figure 4(b) shows that device B presents smaller charge-transfer resistance (RCE) at the perovskite layer/counter-electrode interface, which indicates faster transport of holes from the perovskite absorber to the carbon electrode. Figure 4(c) presents the fitted interfacial charge recombination resistance (RCT) as a function of bias voltage. Apparently, device B exhibits larger RCT under a series of bias voltage, indicating a slower interfacial charge recombination process. Moreover, a relatively smaller capacitance was calculated for device B from the response in the intermediate frequency region (Figure S7), implying less charge carrier accumulation at the perovskite layer/carbon electrode interface and thus the restrain of interfacial charge recombination [52].
To examine the effect of perovskite/FCQDs GHJ on dynamics of charge carrier transfer and recombination, the PSC devices were further characterized with transient photocurrent/photovoltage decay (TPC/TPV) measurements at various bias light intensities (Figure S8). The working principles for measurements of the TPC/TPV have been described in our previous reports [53–55]. By varying the bias light intensity, the corresponding recombination lifetime (τre) at a different open-circuit voltage (or quasi-Fermi level) can be obtained in the model of TPV. Similarly, the apparent transport lifetime (τtr) is collected at short circuit conditions in TPC measurements. The transport/recombination kinetics in PSCs are frequently modeled with biphasic decay (Figure S8), corresponding to the dynamics of electron and hole, respectively. Figure 4(d) exhibits the carrier transport lifetime as a function of VOC (determined by the incident light intensity) for the devices by fitting the TPC curves. Notably, both electron and hole transport lifetimes of device B are significantly shorter than that of device A. At an identical voltage of ~0.9 V, the transport lifetime of electron (τtr,e) of device B is approximately 6  μs, being shorter than that of device A (~8  μs). Similarly, the transport lifetime of hole (τtr,h) of device B is approximately 1.5  μs, being shorter than that of device A (~2.6  μs). This result can be attributed to the CsPbI2.5Br0.5/FCQDs GHJ, which introduces additional driving force for hole transfer, therefore an enhanced charge carrier transport. This result also indicates an imbalanced charge transport in both devices. A similar behavior has been found in the TPV measurements (Figure 4(e)), showing that device B exhibited a longer carrier recombination lifetime (τre) of electron and hole compared to device A. At an identical voltage of ~0.9 V, the recombination lifetime of electron (τre,e) of device B is approximately 31.5  μs, being longer than that of device A (~23  μs). Similarly, the recombination lifetime of the hole (τre,h) of device B is approximately 7  μs, being longer than that of device A (~2.9  μs). A long interfacial recombination lifetime guarantees efficient charge collection and thus enhancing the device output photovoltage. The diffusion length (L) of charge carriers in CsPbI2.5Br0.5 PSCs was further evaluated by the ratio of recombination lifetime and transport lifetime, as given by the expression L=D×τre1/2, where D is the charge carrier diffusion coefficient obtained from charge transport time τtr. As shown in Figure 4(f), device B has a longer charge diffusion length (L). At an identical voltage of ~0.9 V, the diffusion length of electron (Le) of device B is approximately 1.46  μm, being longer than that of device A (~1.06  μm). The diffusion length of the hole (Lh) of device B is approximately 617 nm, being longer than that of device A (~303 nm). In comparison with previous report on CsPbI2Br-based inorganic PSC showing diffusion length of 463 nm for electrons and 202 nm for holes, in this study, the CsPbI2.5Br0.5/FCQDs GHJ device exhibited much longer diffusion length for both electrons and holes [55]. Especially, such a greatly increased hole diffusion length indicates effective hole collection efficiency, which principally delivers higher output photocurrent. This result also well explains the increased EQE value observed for device B in long wavelength region (Figure 3(d)), which can be ascribed to the better charge carrier collection efficiency. The negative slope of the EQE curve for both devices towards longer wavelengths could be due to the loss of carriers by recombination in the bulk of the perovskite layer. Clearly, we should concern to increase the hole diffusion length along with a reduced interfacial charge recombination with the aim to a balanced charge transport and further improvement in device performace.
Long-term stability is another momentous metrics for the practical application of PSCs [56]. To estimate long-term stability of the carbon electrode-based CsPbI2.5Br0.5 perovskite/FCQDs GHJ PSCs, the unencapsulated CsPbI2.5Br0.5 devices (control) and CsPbI2.5Br0.5/FCQDs GHJ devices were measured under 85°C thermal-aging condition in argon-filled glove box. Herein, 85°C was selected for thermal-aging according to the standard IEC 61215-1 : 2016 [57], and the inert atmosphere (argon) was chosen to investigate the intrinsic stability of PSCs by eliminating the interference of other stresses from the ambient [58, 59]. The PSC device based on commonly used spiro-OMeTAD as HTL and Au as counter-electrode was measured under identical conditions as a reference. As shown in Figure 5, after thermal aging at 85°С for 1056 hours, the carbon electrode-based CsPbI2.5Br0.5 devices (control) maintained 84.3% of the initial efficiency, while the CsPbI2.5Br0.5/FCQDs GHJ device maintained 90.7% of the initial efficiency. In contrast, the PSC device using spiro-OMeTAD as HTL and Au as counter-electrode almost lose 100% of the initial efficiency within 200 hours. The considerable improvement in long-term thermal stability of the carbon electrode-based CsPbI2.5Br0.5/FCQD GHJ devices can be attributed to the elimination of organic HTL and metal-electrode, as well as the robust shielding effect of FCQDs. These results demonstrate the significance of constructing carbon electrode-based inorganic perovskite/FCQDs GHJ PSCs for achieving long-term stability and provide important direction to realize low cost and highly stable inorganic PSCs toward commercialization.
3. Discussion
Less
In summary, we first present a compositionally graded heterojunction structure for photovoltaic application by injecting fluorine-doped carbon quantum dots into inorganic perovskite CsPbI2.5Br0.5. This CsPbI2.5Br0.5/FCQDs GHJ can effectively facilitate the separation of photo-generated charge carriers and their transport in photovoltaic devices. Using this novel inorganic perovskite/FCQDs graded heterojunction in conjunction with low-temperature processed carbon electrode, a PCE of 13.53% can be achieved over 1 cm2 device. Moreover, the carbon electrode based CsPbI2.5Br0.5/FCQDs GHJ PSCs exhibited excellent long-term stability, maintaining 90.7% of the initial efficiency under 85°С thermal aging for 1056 hours. This inorganic perovskite/FCQDs graded heterojunction offers a visible pathway to solve charge extraction obstacle in large-area carbon electrode based inorganic PSCs and provides an important direction to realize low-cost and highly stable inorganic PSCs toward commercialization.
4. Materials and Methods
Less
Synthesis of fluorine-doped carbon quantum dots (FCQDs): a one-step hydrothermal method was adapted to prepare FCQDs [60]. Briefly, 360 mg of citric acid, 1080 mg of urea, and 200 mg of sodium fluoride were added in 20 mL deionized water. The mixture was sonicated for about 30 min and transferred into a Teflon-lined autoclave. After heating at 180°C for 10 h and naturally cooling, the obtained FCQDs were purified by dialysis against distilled water. Then, the solution was centrifuged at 10000 rpm, and the obtained FCQDs were dispersed in chlorobenzene for use.
PSC devices fabrication: the compact TiO2 layer was prepared by spray pyrolysis deposition of titanium isopropoxide ethyl alcohol solution, followed by annealing at 100°C for 10 min and 450°C for 30 min. The mesoporous TiO2 layer was prepared by spin-coating of 18 nm particle size paste (Dyesol 18 NR-D) diluted in ethanol at 3000 for rpm 30 s, then sintered at 100°C for 10 min and 450°C for 1 hour. The 0.8 M CsPbI2.5Br0.5 perovskite precursor solution was made by dissolving CsI, CsBr, and PbI2 (molar ratio 1 : 1 : 2) in a mixture of DMF and DMSO (v/v, 4 : 1) and stirred overnight. For the graded heterojunction device, 2 mg/mL FCQDs were added into chlorobenzene antisolvent and stirred overnight. The perovskite solution was spin-coated onto FTO/TiO2 substrates at 2000 rpm for 10 s and 6000 rpm 30 s, and chlorobenzene with or without FCQDs was dropped onto the film at the last 23 s during the second step. Subsequently, the spin-coated perovskite films were dried for 5 min, then thermally annealed at 70°C for 3 min and 300°C for 10 min. Finally, the carbon paste was coated by the doctor-blade method and annealed at 100°C for 30 min [61].
Other experimental details and characterizations are shown in the Supporting Information.
Funding
Less
  • National Natural Science Foundation of China(51961165106; 21975088)
  • National Key Research and Development Program of China(2019YFE0101300; 2018YFB1502900)
References
Less
1
Yang W., Park B., Jung E., Jeon N., Kim Y., Lee D., Shin S., Seo J., Kim E., Noh J., and Il Seok S., “Iodide management in formamidinium-lead-halide-based perovskite layers for efficient solar cells,” Science, vol. 356, no. 6345, pp. 1376–1379, 2017
2
Jiang Q., Zhao Y., Zhang X., Yang X., Chen Y., Chu Z., Ye Q., Li X., Yin Z., and You J., “Surface passivation of perovskite film for efficient solar cells,” Nature Photonics, vol. 13, no. 7, pp. 460–466, 2019
3
Min H., Kim M., Lee S., Kim H., Kim G., Choi K., Lee J., and Il Seok S., “Efficient, stable solar cells by using inherent bandgap of α-phase formamidinium lead iodide,” Science, vol. 366, no. 6466, pp. 749–753, 2019
4
Alharbi E., Dar M., Arora N., Alotaibi M., Alzhrani Y., Yadav P., Tress W., Alyamani A., Albadri A., Zakeeruddin S., and Grätzel M., “Perovskite solar cells yielding reproducible photovoltage of 1.20 V,” Research, vol. 2019, article 8474698, –9, 2019
5
Yoo J., Seo G., Chua M., Park T., Lu Y., Rotermund F., Kim Y., Moon C., Jeon N., Correa-Baena J., Bulović V., Shin S., Bawendi M., and Seo J., “Efficient perovskite solar cells via improved carrier management,” Nature, vol. 590, pp. 587–593, 2021
6
Wang Z., Shi Z., Li T., Chen Y., and Huang W., “Stability of perovskite solar cells: a prospective on the substitution of the A cation and X anion,” Angewandte Chemie International Edition, vol. 56, no. 5, pp. 1190–1212, 2017
7
Chao L., Niu T., Gu H., Yang Y., Wei Q., Xia Y., Hui W., Zuo S., Zhu Z., Pei C., Li X., Zhang J., Fang J., Xing G., Li H., Huang X., Gao X., Ran C., Song L., Fu L., Chen Y., and Huang W., “Origin of high efficiency and long-term stability in ionic liquid perovskite photovoltaic,” Research, vol. 2020, article 2616345, –13, 2020
8
Miyasaka T., Kulkarni A., Kim G., Öz S., and Jena A., “Perovskite solar cells: can we go organic-free, lead-free, and dopant-free?,” Advanced Energy Materials, vol. 10, no. 13, article 1902500, 2020
9
Liang J., Liu Z., Qiu L., Hawash Z., Meng L., Wu Z., Jiang Y., Ono L., and Qi Y., “Enhancing optical, electronic, crystalline, and morphological properties of cesium lead halide by Mn substitution for high-stability all-inorganic perovskite solar cells with carbon electrodes,” Advanced Energy Materials, vol. 8, no. 20, article 1800504, 2018
10
Zhu W., Zhang Q., Chen D., Zhang Z., Lin Z., Chang J., Zhang J., Zhang C., and Hao Y., “Intermolecular exchange boosts efficiency of air-stable, carbon-based all-inorganic planar CsPbIBr2 Perovskite solar cells to over 9%,” Advanced Energy Materials, vol. 8, no. 30, article 1802080, 2018
11
Dong C., Han X., Li W., Qiu Q., and Wang J., “Anti-solvent assisted multi-step deposition for efficient and stable carbon- based CsPbI2Br all-inorganic perovskite solar cell,” Nano Energy, vol. 59, pp. 553–559, 2019
12
Guo Z., Teo S., Xu Z., Zhang C., Kamata Y., Hayase S., and Ma T., “Achievable high Voc of carbon based all-inorganic CsPbIBr2 perovskite solar cells through interface engineering,” Journal of Materials Chemistry A, vol. 7, no. 3, pp. 1227–1232, 2019
13
Liang J., Han X., Yang J., Zhang B., Fang Q., Zhang J., Ai Q., Ogle M., Terlier T., Martí A., and Lou J., “Defect-engineering-enabled high-efficiency all-inorganic perovskite solar cells,” Advanced Materials, vol. 31, no. 51, article 1903448, 2019
14
Wang H., Liu H., Dong Z., Li W., Zhu L., and Chen H., “Composition manipulation boosts the efficiency of carbon-based CsPbI3 perovskite solar cells to beyond 14%,” Nano Energy, vol. 84, article 105881, 2021
15
Liu S., Guan L., Zhang T., Gong X., Zhao X., Sun Q., Shai X., Zhang X., Xiao X., Shen Y., and Wang M., “Stable and efficient full-printable solar cells using inorganic metal oxide framework and inorganic perovskites,” Applied Materials Today, vol. 20, article 100644, 2020
16
Zhang J., Hodes G., Jin Z., and Liu S., “All-inorganic CsPbX3 Perovskite solar cells: progress and prospects,” Angewandte Chemie International Edition, vol. 58, no. 44, pp. 15596–15618, 2019
17
Chen W., Zhang S., Liu Z., Wu S., Chen R., Pan M., Yang Z., Zhu H., Liu S., Tang J., Li J., and Chen W., “A tailored nickel oxide hole-transporting layer to improve the long-term thermal stability of inorganic perovskite solar cells,” Solar RRL, vol. 3, no. 11, article 1900346, 2019
18
Sun Q., Liang G., Zhang X., and Wang M., “Sn/Pb binary metal inorganic perovskite: a true material worthy of trust for efficient and stable photovoltaic application,” Science Bulletin, vol. 65, no. 16, pp. 1330–1333, 2020
19
Wang H., Liu H., Li W., Zhu L., and Chen H., “Inorganic perovskite solar cells based on carbon electrodes,” Nano Energy, vol. 77, article 105160, 2020
20
He S., Qiu L., Son D., Liu Z., Juarez-Perez E., Ono L., Stecker C., and Qi Y., “Carbon-based electrode engineering boosts the efficiency of all low-temperature-processed perovskite solar cells,” ACS Energy Letters, vol. 4, no. 9, pp. 2032–2039, 2019
21
Yoon S., Min H., Kim J., Kim G., Lee K., and Seok S., “Surface engineering of ambient-air-processed cesium lead triiodide layers for efficient solar cells,” Joule, vol. 5, no. 1, pp. 183–196, 2021
22
Cao K., Zuo Z., Cui J., Shen Y., Moehl T., Zakeeruddin S., Grätzel M., and Wang M., “Efficient screen printed perovskite solar cells based on mesoscopic TiO2/Al2O3/NiO/carbon architecture,” Nano Energy, vol. 17, pp. 171–179, 2015
23
Xu X., Liu Z., Zuo Z., Zhang M., Zhao Z., Shen Y., Zhou H., Chen Q., Yang Y., and Wang M., “Hole selective NiO contact for efficient perovskite solar cells with carbon electrode,” Nano Letters, vol. 15, no. 4, pp. 2402–2408, 2015
24
Meng F., Liu A., Gao L., Cao J., Yan Y., Wang N., Fan M., Wei G., and Ma T., “Current progress in interfacial engineering of carbon-based perovskite solar cells,” Journal of Materials Chemistry A, vol. 7, no. 15, pp. 8690–8699, 2019
25
Wu Z., Liu Z., Hu Z., Hawash Z., Qiu L., Jiang Y., Ono L., and Qi Y., “Highly efficient and stable perovskite solar cells via modification of energy levels at the perovskite/carbon electrode interface,” Advanced Materials, vol. 31, no. 11, article 1804284, 2019
26
Wu Y., Yang X., Chen W., Yue Y., Cai M., Xie F., Bi E., Islam A., and Han L., “Perovskite solar cells with 18.21% efficiency and area over 1 cm2 fabricated by heterojunction engineering,” Nature Energy, vol. 1, no. 11, article 16148, 2016
27
Rajagopal A., Liang P., Chueh C., Yang Z., and Jen A., “Defect passivation via a graded fullerene heterojunction in low-bandgap Pb-Sn binary perovskite photovoltaics,” ACS Energy Letters, vol. 2, no. 11, pp. 2531–2539, 2017
28
Li B., Zhang Y., Zhang L., and Yin L., “Graded heterojunction engineering for hole-conductor-free perovskite solar cells with high hole extraction efficiency and conductivity,” Advanced Materials, vol. 29, no. 39, article 1701221, 2017
29
Han J., Yin X., Zhou Y., Nan H., Gu Y., Tai M., Li J., and Lin H., “Perovskite/poly[bis(4-phenyl)(2,4,6-trimethylphenyl)amine] bulk heterojunction for high-efficient carbon-based large-area solar cells by gradient engineering,” ACS Applied Materials & Interfaces, vol. 10, no. 49, pp. 42328–42334, 2018
30
Zhao Q., Hazarika A., Chen X., Harvey S., Larson B., Teeter G., Liu J., Song T., Xiao C., Shaw L., Zhang M., Li G., Beard M., and Luther J., “High efficiency perovskite quantum dot solar cells with charge separating heterostructure,” Nature Communications, vol. 10, no. 1, p. 2842, 2019
31
Paulo S., Stoica G., Cambarau W., Martinez-Ferrero E., and Palomares E., “Carbon quantum dots as new hole transport material for perovskite solar cells,” Synthetic Metals, vol. 222, pp. 17–22, 2016
32
Zhou S., Tang R., and Yin L., “Slow-photon-effect-induced photoelectrical-conversion efficiency enhancement for carbon-quantum-dot-sensitized inorganic CsPbBr3Inverse opal perovskite solar cells,” Advanced Materials, vol. 29, no. 43, article 1703682, 2017
33
Hsu H., Hsiao H., Juang T., Jiang B., Chen S., Jeng R., and Chen C., “Carbon nanodot additives realize high-performance air-stable p-i-n perovskite solar cells providing efficiencies of up to 20.2%,” Advanced Energy Materials, vol. 8, no. 34, article 1802323, 2018
34
Ma Y., Zhang H., Zhang Y., Hu R., Jiang M., Zhang R., Lv H., Tian J., Chu L., Zhang J., Xue Q., Yip H., Xia R., Li X., and Huang W., “Enhancing the performance of inverted perovskite solar cells via grain boundary passivation with carbon quantum dots,” ACS Applied Materials & Interfaces, vol. 11, no. 3, pp. 3044–3052, 2019
35
Bai S., Da P., Li C., Wang Z., Yuan Z., Fu F., Kawecki M., Liu X., Sakai N., Wang J., Huettner S., Buecheler S., Fahlman M., Gao F., and Snaith H. J., “Planar perovskite solar cells with long-term stability using ionic liquid additives,” Nature, vol. 571, no. 7764, pp. 245–250, 2019
36
Liu K., Chen S., Wu J., Zhang H., Qin M., Lu X., Tu Y., Meng Q., and Zhan X., “Fullerene derivative anchored SnO2 for high-performance perovskite solar cells,” Energy & Environmental Science, vol. 11, no. 12, pp. 3463–3471, 2018
37
Sun Q., Li H., Gong X., Ban H., Shen Y., and Wang M., “Interconnected SnO2Nanocrystals electron transport layer for highly efficient flexible perovskite solar cells,” Solar RRL, vol. 4, no. 2, article 1900229, 2020
38
Lv Y., Zhang H., Wang J., Chen L., Bian L., An Z., Qian Z., Ren G., Wu J., Nüesch F., and Huang W., “All-in-one deposition to synergistically manipulate perovskite growth for high-performance solar cell,” Research, vol. 2020, article 2763409, –10, 2020
39
Li N., Tao S., Chen Y., Niu X., Onwudinanti C., Hu C., Qiu Z., Xu Z., Zheng G., Wang L., Zhang Y., Li L., Liu H., Lun Y., Hong J., Wang X., Liu Y., Xie H., Gao Y., Bai Y., Yang S., Brocks G., Chen Q., and Zhou H., “Cation and anion immobilization through chemical bonding enhancement with fluorides for stable halide perovskite solar cells,” Nature Energy, vol. 4, no. 5, pp. 408–415, 2019
40
Li H., Tao L., Huang F., Sun Q., Zhao X., Han J., Shen Y., and Wang M., “Enhancing efficiency of perovskite solar cells via surface passivation with graphene oxide interlayer,” ACS Applied Materials & Interfaces, vol. 9, no. 44, pp. 38967–38976, 2017
41
Dänekamp B., Müller C., Sendner M., Boix P., Sessolo M., Lovrincic R., and Bolink H., “Perovskite–perovskite homojunctions via compositional doping,” Journal of Physical Chemistry Letters, vol. 9, no. 11, pp. 2770–2775, 2018
42
Cui P., Wei D., Ji J., Huang H., Jia E., Dou S., Wang T., Wang W., and Li M., “Planar p-n homojunction perovskite solar cells with efficiency exceeding 21.3%,” Nature Energy, vol. 4, no. 2, pp. 150–159, 2019
43
Hou Y., Aydin E., de Bastiani M., Xiao C., Isikgor F., Xue D., Chen B., Chen H., Bahrami B., Chowdhury A., Johnston A., Baek S., Huang Z., Wei M., Dong Y., Troughton J., Jalmood R., Mirabelli A., Allen T., van Kerschaver E., Saidaminov M., Baran D., Qiao Q., Zhu K., de Wolf S., and Sargent E., “Efficient tandem solar cells with solution-processed perovskite on textured crystalline silicon,” Science, vol. 367, no. 6482, pp. 1135–1140, 2020
44
Xiao C., Zhao Q., Jiang C., Sun Y., al-Jassim M. M., Nanayakkara S., and Luther J., “Perovskite quantum dot solar cells: mapping interfacial energetics for improving charge separation,” Nano Energy, vol. 78, article 105319, 2020
45
Wei H., Shi J., Xu X., Xiao J., Luo J., Dong J., Lv S., Zhu L., Wu H., Li D., Luo Y., Meng Q., and Chen Q., “Enhanced charge collection with ultrathin AlOx electron blocking layer for hole-transporting material-free perovskite solar cell,” Physical Chemistry Chemical Physics, vol. 17, no. 7, pp. 4937–4944, 2015
46
Yu Y., Wang C., Grice C., Shrestha N., Zhao D., Liao W., Guan L., Awni R., Meng W., Cimaroli A., Zhu K., Ellingson R., and Yan Y., “Synergistic effects of lead thiocyanate additive and solvent annealing on the performance of wide-bandgap perovskite solar cells,” ACS Energy Letters, vol. 2, no. 5, pp. 1177–1182, 2017
47
Sun Q., Gong X., Li H., Liu S., Zhao X., Shen Y., and Wang M., “Direct formation of I3- ions in organic cation solution for efficient perovskite solar cells,” Solar Energy Materials & Solar Cells, vol. 185, pp. 111–116, 2018
48
Wang M., Chen P., Humphry-Baker R., Zakeeruddin S., and Grätzel M., “The influence of charge transport and recombination on the performance of dye-sensitized solar cells,” ChemPhysChem, vol. 10, no. 1, pp. 290–299, 2009
49
Zuo L., Guo H., deQuilettes D., Jariwala S., de Marco N., Dong S., DeBlock R., Ginger D., Dunn B., Wang M., and Yang Y., “Polymer-modified halide perovskite films for efficient and stable planar heterojunction solar cells,” Science Advances, vol. 3, no. 8, article e1700106, 2017
50
Gong X., Sun Q., Liu S., Liao P., Shen Y., Grätzel C., Zakeeruddin S., Grätzel M., and Wang M., “Highly efficient perovskite solar cells with gradient bilayer electron transport materials,” Nano Letters, vol. 18, no. 6, pp. 3969–3977, 2018
51
Shai X., Zuo L., Sun P., Liao P., Huang W., Yao E., Li H., Liu S., Shen Y., Yang Y., and Wang M., “Efficient planar perovskite solar cells using halide Sr-substituted Pb perovskite,” Nano Energy, vol. 36, pp. 213–222, 2017
52
Li H., Lu J., Zhang T., Shen Y., and Wang M., “Cation-assisted restraint of a wide quantum well and interfacial charge accumulation in two-dimensional perovskites,” ACS Energy Letters, vol. 3, no. 8, pp. 1815–1823, 2018
53
Zhao X., Liu S., Zhang H., Chang S.-Y., Huang W., Zhu B., Shen Y., Shen C., Wang D., Yang Y., and Wang M., “20% efficient perovskite solar cells with 2D electron transporting layer,” Advanced Functional Materials, vol. 29, no. 4, article 1805168, 2019
54
Pan H., Zhao X., Xiu G., Li H., Zhang X., Liang G., Shen Y., and Wang M., “Controlling layered Ruddlesden-Popper perovskites via solvent additives,” Nanoscale, vol. 12, no. 13, pp. 7330–7338, 2020
55
Gong X., Guan L., Li Q., Li Y., Zhang T., Pan H., Sun Q., Shen Y., Grätzel C., Zakeeruddin S., Grätzel M., and Wang M., “Black phosphorus quantum dots in inorganic perovskite thin films for efficient photovoltaic application,” Science Advances, vol. 6, no. 15, 2020
56
Guo Q., Wu J., Yang Y., Liu X., Lan Z., Lin J., Huang M., Wei Y., Dong J., Jia J., and Huang Y., “High-performance and hysteresis-free perovskite solar cells based on rare-earth-doped SnO2 Mesoporous scaffold,” Research, vol. 2019, article 4049793, –13, 2019
57
, “Terrestrial Photovoltaic (PV) Modules Design Qualification and Type Approval-Part 1: Test Requirements (IEC, 2016),” , IEC 61215-1:2016.
58
Snaith H., and Hacke P., “Enabling reliability assessments of pre-commercial perovskite photovoltaics with lessons learned from industrial standards,” Nature Energy, vol. 3, no. 6, pp. 459–465, 2018
59
Wu S., Chen R., Zhang S., Babu B., Yue Y., Zhu H., Yang Z., Chen C., Chen W., Huang Y., Fang S., Liu T., Han L., and Chen W., “A chemically inert bismuth interlayer enhances long-term stability of inverted perovskite solar cells,” Nature Communications, vol. 10, no. 1, 2019
60
Yang W., Zhang H., Lai J., Peng X., Hu Y., Gu W., and Ye L., “Carbon dots with red-shifted photoluminescence by fluorine doping for optical bio-imaging,” Carbon, vol. 128, pp. 78–85, 2018
61
Chu Q., Ding B., Peng J., Shen H., Li X., Liu Y., Li C., Li C., Yang G., White T., and Catchpole K., “Highly stable carbon-based perovskite solar cell with a record efficiency of over 18% via hole transport engineering,” Journal of Materials Science and Technology, vol. 35, no. 6, pp. 987–993, 2019
Appendix
Less
Year 2021 volume 2021 Issue 7
PDF
60
34
Cite this Article
BibTeX
Article Info
doi: 10.34133/2021/9845067
  • Receive Date：2021-03-27
  • Online Date：2026-10-27
  • Published：2021-07-20
Article Data
Affiliations
History
  • Received：2021-03-27
  • Accepted：2021-06-04
Funding
National Natural Science Foundation of China(51961165106; 21975088)
National Key Research and Development Program of China(2019YFE0101300; 2018YFB1502900)
Affiliations
    1Wuhan National Laboratory for Optoelectronics, Huazhong University of Science and Technology, Wuhan, Hubei 430074, China
    2Ningbo Institute of Materials Technology & Engineering, Chinese Academy of Sciences, 1219 Zhongguan Road, Ningbo 315201, China
    3School of Chemistry, Beijing Institute of Technology, Beijing 102488, China
    4State Centre for International Cooperation on Designer Low-Carbon & Environmental Materials, School of Materials Science and Engineering, Zhengzhou University, 450001, China
    5State Key Laboratory for Mechanical Behavior of Materials, Xi’an Jiaotong University, Xi’an 710049, China
References
Share
https://castjournals.cast.org.cn/joweb/research/EN/10.34133/2021/9845067
Share to
QR

Scan QR to access full text

Cite this article
BibTeX
Citations
表12种不同金属材料的力学参数
科
Family		 属数
Number of
genus		 种数
Number of
species		 占总种数比例
Percentage of
total species (%)		 属
Genus		 种数
Number of
species		 占总种数比例
Percentage of total
species (%)
鹅膏菌科Amanitaceae 2 11 5.26 鹅膏菌属 Amanita 10 4.78
小菇科 Mycenaceae 2 12 5.74 丝盖伞属 Inocybe 5 2.39
多孔菌科 Polyporaceae 8 14 6.70 蜡蘑属 Laccaria 5 2.39
红菇科 Russulaceae 3 23 11.00 小皮伞属 Marasmius 6 2.87
小菇属 Mycena 11 5.26
光柄菇属 Pluteus 5 2.39
红菇属 Russula 17 8.13
栓菌属 Trametes 5 2.39
关闭全屏
  • BibTeX
  • EndNote
  • RefWorks
  • TxT
Links
Articles
Latest Articles
Most Read
Collections
Updates
Events
News
Multimedia
About
About Us
Contact
No. 86 Xueyuan South Road, Haidian District, Beijing
100081
010-62662699(Operation and Technical Support)
qkjq@cast.org.cn

Copyright © 2025 China Association for Science and Technology. All rights reserved. For all open access content, the relevant licensing terms apply.
Sponsored by the Office of the Leading Group for Cybersecurity and Informatization of CAST, and supported by Science and Technology Review Publishing House