TaO<sub>x</sub>-C supported ultra-small platinum nanoparticles as efficient and durable catalysts for PEMFCs

TaO_x-C supported ultra-small platinum nanoparticles as efficient and durable catalysts for PEMFCs

PDF

Nanshu Zhang^a^,^b^,^c^,^d, Liting Yang^a^,^b^,^c^,^d, Jingsen Bai^a^,^b^,^c^,^d, Chang Lan^a^,^b^,^c^,^d, Meiling Xiao^a^,^b^,^c^,^d^,^e, Wei Xing^a^,^b^,^c^,^d^,^e, Changpeng Liu^a^,^b^,^c^,^d^,^e

Chinese Chemical Letters | 2026, 37(6) : 111044

Less

Chinese Chemical Letters | 2026, 37(6): 111044

• Communication •

TaO_x-C supported ultra-small platinum nanoparticles as efficient and durable catalysts for PEMFCs

Full

Nanshu Zhang^a^,^b^,^c^,^d, Liting Yang^a^,^b^,^c^,^d, Jingsen Bai^a^,^b^,^c^,^d, Chang Lan^a^,^b^,^c^,^d, Meiling Xiao^a^,^b^,^c^,^d^,^e, Wei Xing^a^,^b^,^c^,^d^,^e, Changpeng Liu^a^,^b^,^c^,^d^,^e

Affiliations

^aLaboratory of Advanced Power Source, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China

^bSchool of Applied Chemistry and Engineering, University of Science and Technology of China, Hefei 230026, China

^cJilin Province Key Laboratory of Low Carbon Chemical Power Sources, Changchun 130022, China

^dState Key Laboratory of Electroanalytical Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China

^eCIAC – HKUST Joint Laboratory for Hydrogen Energy, Changchun 130022, China

About Author:

CRediT authorship contribution statement

Nanshu Zhang: Writing – original draft, Methodology, Investigation, Formal analysis, Data curation.

Liting Yang: Writing – review & editing, Methodology.

Jingsen Bai: Writing – review & editing, Methodology.

Chang Lan: Writing – review & editing, Investigation.

Meiling Xiao: Writing – review & editing, Investigation.

Wei Xing: Writing – review & editing, Funding acquisition, Formal analysis.

Changpeng Liu: Writing – review & editing, Investigation, Funding acquisition.

Published: 2026-06-15 doi: 10.1016/j.cclet.2025.111044

Outline

Abstract

Less

The limited stability of Pt-based catalysts as a result of irreversible support corrosion and Pt dissolution/aggregation remains a major barrier to the widespread deployment for Proton exchange membrane fuel cells. To overcome the issues, amorphous TaO_x with corrosion-resistance was introduced to stabilize Pt nanoparticles in this work. Benefiting from the strong metal-support interaction, Pt oxidation and dissolution is suppressed through efficient electron transfer from the support. Optimized Pt/TaO_x-C catalyst shows remarkable stability with voltage loss @0.8 A/cm² of only 29 mV after 50k cycles accelerated durability test, which is much lower than the goal for DOE 2025 (30 mV after 30k cycles). Besides, the strong anchoring effect of the amorphous TaO_x enables well dispersion of Pt with an ultra-small particle size of approximately 1.3 nm, reducing the local mass transfer resistance towards superior fuel cell performance of 2.29 W/cm², which is higher than the commercial Pt/C of 1.56 W/cm². This study offers a highly active and durable cathode electrocatalyst for fuel cells.

Key words

Oxygen reduction reaction / Pt-based catalyst / Metal oxides / High stability / Strong metal-support interaction

Cite this Article

Nanshu Zhang, Liting Yang, Jingsen Bai, Chang Lan, Meiling Xiao, Wei Xing, Changpeng Liu. TaO_x-C supported ultra-small platinum nanoparticles as efficient and durable catalysts for PEMFCs[J]. Chinese Chemical Letters, 2026 , 37 (6) : 111044 - . DOI: 10.1016/j.cclet.2025.111044

Full Text

Less

As a clean and efficient energy conversion technology, proton exchange membrane fuel cells (PEMFCs) are capable of converting the chemical energy stored in hydrogen into electrical energy directly without carbon emissions, bypassing the limitations imposed by the Carnot cycle [1–4]. As a result, PEMFCs have shown significant application potential in transportation, household power supply, and portable devices [5]. One of the key reactions in fuel cell technology is the sluggish oxygen reduction reaction (ORR) at cathode [6,7]. Commonly, platinum (Pt) and its alloys have been the primary catalysts for ORR in fuel cells. However, the high cost and limited availability of Pt hampered the widespread commercialization of PEMFCs. Consequently, reducing the reliance on Pt-based catalysts is essential to making PEMFCs more economically viable and accelerating their large-scale deployment [8–11]. In this regard, a variety of strategies, including reducing size [12,13], alloying [14,15] and morphology modulation [16–18] have been employed to increase the activity of Pt-based catalysts towards reduced Pt loading. Huang et al. [19] devised a PtCo nanocatalyst for ORR comprising membrane electrodes with high power density up to 13.2 W/mg_Pt, which far exceeds the current target proposed by the United States Department of Energy (DOE) (8 W/mg_Pt). The activity of Pt-based catalysts has been significantly enhanced, thereby necessitating the attainment of a balance between high activity and long-lasting stability at low loading for the commercialization of fuel cells. The carbon support corrosion and oxidation/dissolution of Pt nanoparticles are regarded as the two major degradation mechanisms [20]. And agglomeration and Ostwald ripening of the catalyst is another significant contributor to performance loss [21].

Targeting the durability challenge Pt-based catalyst faced with, researchers have developed numerous structural regulations, such as intermetallic compound formation [22–25], construction of core-shell structure [26–30], introducing inert metals [31] and support materials modification [32–34]. Among them, developing corrosion-resistant supports is more appealing as it can address the carbon corrosion issue fundamentally [35–37]. Various support materials, including metal oxides (e.g., SnO_x, TiO_x) [38–41], nitrides (e.g., TiN, VN) [42,43] and carbides (e.g., WC, MoC) [44–47] have demonstrated capable of enhancing the stability of Pt-based electrocatalysts. However, the poor electrical conductivity of the supports restricts the full expression of the catalyst performance. Despite the fact that studies have also combined them with carbon materials, the Pt nanoparticles could not be uniformly distributed and were observed heavily agglomerated. The interfacial interaction between Pt and support was insufficient and prone to particles aggregation [48].

Herein, to strengthen the interfacial interaction and alleviate the agglomeration, amorphous TaO_x with abundant oxygen vacancies was utilized for anchoring Pt nanoparticles tightly, enabling the uniform growth of ultra-small Pt clusters with 1.3 nm. Besides, the strengthened metal-support interaction inhibited over-oxidation and dissolution of Pt through electron transfer from TaO_x to Pt nanoparticles. Owing to these attributes, the as-developed catalyst showed outstanding stability with a negligible half-wave potential decay after 90k cycles between 0.6 V and 1.0 V in three-electrode system. When integrated into membrane electrode assembly (MEA), the catalyst exhibited a retention rate of 90% for power density following 50k accelerated durability tests (ADT) cycles at both H₂/O₂ and H₂/Air condition. This study not only addressed the stability issues of Pt-based catalysts for PEMFCs, but also offered a promising avenue for designing ultra-small nanoparticles supported on metal oxide.

The synthetic procedure of the Pt/TaO_x-C catalysts is schematically illustrated in Fig. S1 (Supporting information). Firstly, the support was obtained by thermal reduction. And the catalyst was achieved through pH-based reflux reduction of ethylene glycol (EG). To be specific, a solution of prepared TaO_x-C in ethylene glycol was sonicated for 2 h, H₂PtCl₆ (7.4 mg/mL) was added and stirred. And then the pH of solution was adjusted by 0.1 mol/L NaOH. Subsequently, the resulting solution was refluxed at 130 ℃ for 3 h. Once the temperature had cooled to room temperature, the product was filtered and washed.

The carbon source was selected to be KJ-300 with numerous mesopores. These nanopores were able to regulate the growth of TaO_x through space-confinement effect, thus facilitating the formation of amorphous TaO_x with small particle size. Both the X-ray diffraction (XRD) spectra and transmission electron microscopy (TEM) images confirmed the successful preparation of amorphous TaO_x nanoparticles embedded into the pores of carbon matrix (Figs. S2-S4 in Supporting information). Amorphous TaO_x provided considerable nucleation sites for the uniform deposition of Pt nanoparticles with ultra-small size of about 1.3 nm, much smaller than that of Pt/KJ (2.3 nm) and Pt/Ta₂O₅ (3.9 nm), suggesting a higher atomic utilization for Pt/TaO_x-C (Fig. 1a and Figs. S5-S7 in Supporting information). As shown in high resolution TEM (HRTEM), the majority Pt nanoparticles are located on the amorphous TaO_x, and lattice fringes of 0.221 nm were attributed to the (111) plane of Pt nanoparticles (Figs. 1b and c). The overlapping distribution of Pt and Ta from the energy-dispersive X-ray spectroscopy (EDS) results (Fig. 1d) further confirmed that Pt nanoparticles were predominantly deposited on TaO_x.

X-ray photoelectron spectroscopy (XPS) and X-ray absorption near edge structure (XANES) were used to check the interaction between Pt nanoparticles and TaO_x-C support. As shown in Fig. S8 (Supporting information), Ta 4f peak for TaO_x-C (26 eV) exhibited a negative shift of 0.7 eV compared with that of Ta₂O₅ (26.7 eV), demonstrating a lower valence state of Ta in the TaO_x-C. In line with the XPS analysis, the Ta L₃-edge XANES spectra revealed that the adsorption edge of Ta in TaO_x-C situated between the TaO (+2) and the Ta₂O₅ (+5) (Fig. 2a, Fig. S9 and Table S1 in Supporting information), and the valence state of Ta could be obtained by the first derivative of normalized XANES spectra [49]. The average extrapolated valence of Ta was calculated to be 2.98 for TaO_x-C (Fig. 2b), implying the presence of oxygen vacancy. It is noteworthy that TaO_x-C exhibited a more pronounced O 1s XPS peak at 532.4 eV (peak area increased from 20.5% to 24.8%), which is ascribed to the presence of low oxygen coordination defects (Fig. 2c). Besides, electron paramagnetic resonance (EPR) presented in Fig. 2d also showed higher concentration of oxygen vacancies in TaO_x-C. These results indicated that TaO_x-C is in electron-rich and has capacity to offer electron to Pt particles. Notably, the 4f binding energy of Ta in Pt/TaO_x-C shifted positively relative to that in TaO_x-C, indicating electron transfer from TaO_x-C to Pt, or in other words, a strong metal-support interaction (SMSI) (Fig. S10 in Supporting information). Accordingly, the Pt 4f peaks for Pt/TaO_x-C (71.40 eV) shifted negatively compared to commercial Pt/C (71.96 eV) (Fig. 2e). The presence of SMSI in the Pt/TaO_x-C catalyst was further verified by conducting Pt L₃ edge XANES spectroscopy. As illustrated in Fig. 2f, the Pt L₃ edge white line intensity in Pt/TaO_x-C was lower than those of Pt/KJ and JM-Pt/C. The above results strongly proved that the amorphous TaO_x support can donate electron to the deposited Pt nanoparticles, contributing to the higher anti-oxidation capacity, which is crucial for achieving superior catalytic stability. Besides, the enrichment of low-valence Pt species was favorable for catalyst to express higher performance.

A series of electrochemical tests were performed to evaluate the oxygen reduction performance of the Pt/TaO_x-C catalyst. These tests include cyclic voltammetry (CV) and linear sweep voltammetry (LSV), which were carried out using a rotating disk electrode in a standard three-electrode system (Figs. 3a and b). The electrochemical surface area (ECSA) of the catalyst was determined using the H_upd method, yielding a value of 72.5 m²/g for Pt/TaO_x-C, much bigger than those of Pt/KJ (54.3 m²/g) and Pt/Ta₂O₅ (21.2m²/g), indicating more accessible active sites and higher Pt utilization efficiency in Pt/TaO_x-C. The ORR polarization curve revealed that the half-wave potential (E_1/2) of Pt/TaO_x-C was 0.885 V. To assess the activity of catalyst, the kinetic current density was normalized by both the Pt loading mass and the ECSA at 0.9 V. The mass activity (MA) and specific activity (SA) of Pt/TaO_x-C were calculated to be 0.22 A/mg_Pt and 0.28 mA/cm², respectively, higher than those of the JM-Pt/C catalyst (0.15 A/mg_Pt and 0.22 mA/cm²) (Fig. 3c and Table S2 in Supporting information). These results suggested that the activity of Pt in Pt/TaO_x-C is enhanced, likely due to electron transfer between Pt and TaO_x, which effectively modulates the electronic structure of Pt surface. Notably, Pt/TaO_x-C exhibited the smallest Tafel slope, demonstrating its superior catalytic activity (Fig. S11 in Supporting information). To further investigate the reaction mechanism, LSV tests were conducted at varying rotational speeds to determine the electron transfer number (Fig. S12 in Supporting information). The electron transfer number for Pt/TaO_x-C was calculated to be 4, which is consistent with the expected direct four-electron reaction mechanism.

An accelerated stability test (AST) was conducted to evaluate the durability of the Pt/TaO_x-C electrocatalyst. After 90k cycles within the potential range of 0.6–1.0 V, the Pt/TaO_x-C catalyst exhibited negligible decay (only 2 mV) in its half-wave potential (Fig. 3d), which significantly outperforms JM-Pt/C, Pt/KJC, and Pt/Ta₂O₅ (54, 30 and 50 mV, respectively, after 50k cycles) (Fig. 3e, Figs. S13 and S14, Table S3 in Supporting information). Moreover, the Pt/TaO_x-C electrocatalyst retained 77% of its initial mass activity after AST, while Pt/KJC, JM-Pt/C and Pt/Ta₂O₅ catalysts retained only 39%, 40% and 42%, respectively (Fig. 3f). The superior stability of Pt/TaO_x-C could be ascribable to the increased electron density at Pt sites as a result of electron transfer from TaO_x-C support to Pt, which inhibits the oxidation of active Pt, accelerates desorption of oxygen species and consequently lowers the coverage. Further physical characterization of catalyst confirmed the high structural stability of Pt/TaO_x-C. XRD patterns display that the crystalline structure remained intact, implying no distinct structure reconstruction (Fig. 3g). The higher stability of the Pt/TaO_x-C catalysts was further corroborated by slight aggregation after AST (Fig. S15 in Supporting information). XPS analysis before and after the stability test revealed that the binding energy of Pt in Pt/TaOx-C remained unchanged and the Ta 4f peak exhibited a positive shift, suggesting the electron transfer from support to Pt nanoparticles towards inhibited oxidation of Pt (Fig. 3h and Fig. S16 in Supporting information). In contrast, the Pt 4f peak of Pt/KJC shifted to a higher binding energy, corresponding to the oxidized species (Fig. S17 in Supporting information). Meanwhile, the dissolution of the Pt/TaO_x-C was significantly lower than that of the Pt/KJ, indicating that the Pt/TaO_x-C composite exhibits superior antioxidant dissolution properties (Fig. 3i and Fig. S18 in Supporting information). In order to verify the antioxidant ability of TaO_x-C further, AST was carried out on Pt/TaOx-C and Pt/KJ, respectively, between 1.0–1.5 V. Impressively, the half-wave potential of Pt/TaO_x-C only diminishes by 4 mV after 20,000 cycles operation, whereas Pt/KJ shows performance degradation of 13 mV (Figs. S19 and S20 in Supporting information). This suggests that TaOx-C exhibits enhanced corrosion resistance and mitigates the catalytic loss due to carbon corrosion at high potentials. In a short, oxidation resistance of Pt was improved because of electron transfer from /TaO_x-C.

To further assess the potential practicability of Pt/TaO_x-C catalysts in fuel cell applications, we assembled membrane electrode assembly (MEA) with Pt/TaO_x-C as the cathode and commercial Pt/C as the anode (Fig. 4a). The Pt loading was kept to be 0.10 mg/cm² in both cathode and anode. Additionally, Pt/KJ and JM-Pt/C MEA with the same Pt loading were also prepared for comparative analysis [50]. As shown in Fig. 4b, the Pt/TaO_x-C cathode achieved a peak power density of 2.29 W/cm² under H₂-O₂ conditions, far superior to the JM-Pt/C (1.56 W/cm²) and Pt/KJ (1.8 W/cm²). The polarization curves of Pt/TaO_x-C under H₂-O₂ conditions exhibited higher current densities across the entire voltage range, particularly in the high voltage region (>0.7 V). To better simulate real operating conditions, the MEA performance was evaluated under H₂/Air conditions. As shown in Fig. 4c, Pt/TaO_x-C delivered peak power densities of 1.06 W/cm² at 100 kPa and 1.28 W/cm² at 200 kPa, surpassing the performance of commercial Pt/C (0.72 W/cm² at 100 kPa, 0.86 W/cm² at 200 kPa) and Pt/KJ (0.69 W/cm² at 100 kPa, 0.85 W/cm² at 200 kPa). Notably, the cell with commercial Pt/C and Pt/KJ as cathode, demonstrated pronounced mass transfer polarization in the high current density region, resulting in decreased performance with current density of <3000 mA/cm². While the Pt/TaO_x-C-assembled MEA exhibited negligible mass transfer resistance, delivering high current density beyond 4000 mA/cm². This is because that the Pt loading drops below 0.12 mg_Pt/cm², the localized mass transfer resistance becomes the main cause of performance degradation, which can be effectively improved by increasing the active site density via reducing particle size [51,52]. Pt/TaO_x-C catalyst comprises ultra-small Pt particles with high atom utilization, and the effective mass transfer space is fully employed, which is helpful to fully increase the distribution density of active sites in the catalytic layer, drastically reduce the local mass transfer demand of each particle, and facilitate the reaction of oxygen on the Pt surface, contributed to the improvement of the performance of the precious metal catalysts with low loading of PEMFC at high current densities [53,54].

Further analysis of the power output at 0.67 V, a voltage relevant for practical fuel cell operation, was conducted to assess the performance under realistic conditions. As shown in Fig. 4d, Pt/TaO_x-C demonstrated current density of 224 mA/cm² and power density of 554 mW/cm² at 0.67 V, which is significantly higher than the values for commercial Pt/C (189 mA/cm², 396.7 mW/cm²) and Pt/KJ (177 mA/cm², 396.5 mW/cm²). After normalizing the performance to the cathode Pt loading, Pt/TaO_x-C was rated at 22.9 W/mg_Pt, surpassing most of the state-of-art Pt-based catalysts (Fig. 4e and Table S4 in Supporting information), further emphasizing its exceptional catalytic efficiency.

To further assess the long-term stability of Pt/TaO_x-C, which was subjected to AST with 50k potential cycles in the 0.6–0.95 V range, simulating the practical operation. As shown in Figs. 4f and g, the power density of Pt/TaO_x-C under both H₂/Air and H₂/O₂ conditions showed minimal decrease after AST, in comparison to JM-Pt/C and Pt/KJ, demonstrating superior MEA stability (Figs. S21–S24 in Supporting information). Furthermore, Pt/TaO_x-C retained >80% of its initial power at 0.67 V and exhibited only 29 mV voltage loss at 0.8 A/cm², meeting the DOE 2025 target for this condition (Fig. 4h). In contrast, Pt/KJ showed >40% power loss at 0.67 V and approximately 60 mV voltage drop at 0.8 A/cm² (Fig. S25 and Table S5 in Supporting information). Both the initial and post-aging performance of Pt/TaO_x-C remained at high levels. In conclusion, AST results demonstrate that the introduction of amorphous TaO_x support can effectively stabilize Pt nanoparticles and greatly prolong the performance of the lifespan, providing evidence of its practical application in fuel cells.

In this study, amorphous TaO_x has been developed by confinement effect of porous carbon to stabilize Pt nanoparticles. The strong interaction between TaO_x-C and Pt nanoparticles enables electron transfer from support to Pt, inhibiting the dissolution and oxidation of Pt nanoparticles. After 50k AST cycles in MEA, the voltage loss at 0.8 A/cm² is only 29 mV. Besides, amorphous TaO_x with abundant oxygen vacancies facilitates the nanoscale dispersion of Pt nanoparticles with an ultra-small particle size of approximately 1.3 nm, achieving high atomic efficiency and alleviating the problem of local mass transfer, which enables the catalyst express impressive activity of normalized power up to 22.9 W/mg_Pt, surpassing the DOE targets. This strategy presents a novel and promising approach to develop metal oxides as support, offering significant potential for practical fuel cell applications.

References

Less

H. Cruz-Martínez, H. Rojas-Chávez, P.T. Matadamas-Ortiz, et al., Mater. Today Phys. 19 (2021) 100406.

Z. Ma, Z.P. Cano, A. Yu, et al., Angew. Chem. Int. Ed. 59 (2020) 18334–18348.

D. Zhang, Y. Zhang, Y. Huang, et al., Inorg. Chem. 61 (2022) 12023–12032.

X. Wang, L. Zhang, M. Xiao, et al., Chin. Chem. Lett. 34 (2023) 107455.

J. Wang, W. Ding, Z. Wei, Acta Phys. Chim. Sin. 37 (2021) 2009094.

J. Zhang, Y. Yuan, L. Gao, et al., Adv. Mater. 33 (2021) 2006494.

J. Chen, Z. Ou, H. Chen, et al., Chin. J. Catal. 42 (2021) 1297–1326.

Q. Gong, H. Zhang, H. Yu, et al., Matter 6 (2023) 963–982.

L. Bu, J. Liang, F. Ning, et al., Adv. Mater. 35 (2023) 202208672.

L. Gao, T. Sun, X. Tan, et al., Appl. Catal. B: Environ. 303 (2022) 120918.

Y. Hu, X. Guo, T. Shen, et al., ACS Catal. 12 (2022) 5380–5387.

X. Feng, Y. Bai, W. Zhang, et al., ACS Energy Lett. 8 (2022) 628–636.

H. Cheng, R. Gui, H. Yu, et al., Proc. Nat. Acad. Sci. U. S. A. 118 (2021) e2104026118.

W. Guo, X. Gao, M. Zhu, et al., Energy Environ. Sci. 16 (2023) 148–156.

J. Lai, S. Chen, X. Liu, et al., ACS Catal. 13 (2023) 11996–12006.

Y. Chen, T. Cheng, W.A. Goddard Iii, J. Am. Chem. Soc. 142 (2020) 8625–8632.

J. Chang; T.J. Ko, M. Je, et al., ACS Energy Lett. 6 (2021) 3481–3487.

X. Huang, Z. Zhao, Y. Chen, et al., Energy Environ. Sci. 7 (2014) 2957–2962.

Z. Zhao, Z. Liu, A. Zhang, et al., Nat. Nanotechnol. 17 (2022) 968–975.

S. Cherevko, N. Kulyk, K.J.J. Mayrhofer, Nano Energy 29 (2016) 275–298.

P. Parthasarathy, A.V. Virkar, J. Power Sources 234 (2013) 82–90.

P. Xiong, H. Niu, Z. Zhu, et al., Nano Lett. 24 (2024) 3961–3970.

H. Lv, Y. Zheng, Y. Wang, et al., Angew. Chem. Int. Ed. 62 (2023) e202304420.

J. Wang, F. Pan, W. Chen, et al., Electrochem. Energy Rev. 6 (2023) 6.

E. Wang, L. Luo, Y. Feng, et al., J. Energy Chem. 93 (2024) 157–165.

H. Jin, Z. Xu, Z.Y. Hu, et al., Nat. Commun. 14 (2023) 1518.

X. Zhao, K. Sasaki, Acc. Chem. Res. 55 (2022) 1226–1236.

A.C. Foucher, D.J. Rosen, L.K. Decker, et al., Chem. Mater. 35 (2023) 8758–8764.

L. Luo, F. Zhu, R. Tian, et al., ACS Catal. 7 (2017) 5420–5430.

L. Luo, C. Fu, A. Wu, et al., Nano Res. 15 (2022) 1892–1900.

P.P. Lopes, D. Li, H. Lv, et al., Nat. Mater. 19 (2020) 1207–1214.

N. Tachibana, Y. Yukawa, K. Morikawa, et al., SN Appl. Sci. 3 (2021) 338.

D. Liu, S. Gao, J. Xu, et al., Appl. Surf. Sci. 604 (2022) 154466.

Y. Chen, X. Zheng, J. Cai, et al., ACS Catal. 12 (2022) 7406–7414.

Z. Wang, W. Wu, H. Jiang, et al., Adv. Funct. Mater. 34 (2024) 2406347.

Z. Wang, S. Chen, W. Wu, et al., Adv. Mater. 35 (2023) 2301310.

H. Jiang, Z. Wang, S. Chen, et al., J. Mater. Sci. Technol. 205 (2025) 212–220.

Z. Lin, J. Liu, S. Li, et al., Adv. Funct. Mater. 33 (2023) 2211638.

T.H. Huang, D. Bhalothia, S. Dai, et al., Sustain. Energy Fuels 5 (2021) 2960–2971.

X. Shen, T. Nagai, F. Yang, et al., J. Am. Chem. Soc. 141 (2019) 9463–9467.

F. Xu, Q. Zou, G. Xiong, et al. Chem. Eur. J. 28 (2022) e202202580.

R. Kumar, S. Pasupathi, B.G. Pollet, K. Scott, Electrochim. Acta 109 (2013) 365–369.

N.Y. Kim, J.H. Lee, J.A. Kwon, et al., J. Ind. Engin. Chem. 46 (2017) 298–303.

O. Lori, S. Gonen, O. Kapon, L. Elbaz, ACS Appl. Mater. Interfaces 13 (2021) 8315–8323.

M. Nie, S. Du, Q. Li, et al., J. Electrochem. Soc. 167 (2020) 044510.

L. Elbaz, C.R. Kreller, N.J. Henson, E.L. Brosha, J. Electroanal. Chem. 720-721 (2014) 34–40.

Z. Yan, J. Xie, P.K. Shen, J. Power Sources 286 (2015) 239–246.

O.A. Baturina, Y. Garsany, T.J. Zega, et al., J. Electrochem. Soc. 155 (2008) B1314.

Q. Jia, S. Ghoshal, J. Li, et al., J. Am. Chem. Soc. 139 (2017) 7893–7903.

D.A. Cullen, K.C. Neyerlin, R.K. Ahluwalia, et al., Nat. Energy 6 (2021) 462–474.

A. Kongkanand, K. Tvrdy; K. Takechi, et al., J. Am. Chem. Soc. 130 (2008) 4007–4015.

Y. Ono, T. Mashio, S. Takaichi, et al., ECS Trans. 28 (2010) 69.

A. Kongkanand, M.F. Mathias, J. Phys. Chem. Lett. 7 (2016) 1127–1137.

V. Yarlagadda, M.K. Carpenter, T.E. Moylan, et al., ACS Energy Lett. 3 (2018) 618–621.

Appendix

Less

Year 2026 volume 37 Issue 6

PDF

Cite this Article

BibTeX

Article Info

doi: 10.1016/j.cclet.2025.111044

Receive Date：2025-01-02
Online Date：2026-10-27
Published：2026-06-15

Article Data

Affiliations

History

Received：2025-01-02
Revised：2025-02-27
Accepted：2025-03-05

Affiliations

^aLaboratory of Advanced Power Source, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China

^bSchool of Applied Chemistry and Engineering, University of Science and Technology of China, Hefei 230026, China

^cJilin Province Key Laboratory of Low Carbon Chemical Power Sources, Changchun 130022, China

^dState Key Laboratory of Electroanalytical Chemistry, Changchun Institute of Applied Chemistry, Chinese Academy of Sciences, Changchun 130022, China

^eCIAC – HKUST Joint Laboratory for Hydrogen Energy, Changchun 130022, China

Corresponding:

E-mail addresses: mlxiao@ciac.ac.cn (M. Xiao)

xingwei@ciac.ac.cn (W. Xing)

liuchp@ciac.ac.cn (C. Liu)

References

Share

https://castjournals.cast.org.cn/joweb/ccl/EN/10.1016/j.cclet.2025.111044

Share to

Scan QR to access full text

Cite this article

BibTeX

Citations

表12种不同金属材料的力学参数

科 Family	属数 Number of genus	种数 Number of species	占总种数比例 Percentage of total species (%)	属 Genus	种数 Number of species	占总种数比例 Percentage of total species (%)
鹅膏菌科Amanitaceae	2	11	5.26	鹅膏菌属 Amanita	10	4.78
小菇科 Mycenaceae	2	12	5.74	丝盖伞属 Inocybe	5	2.39
多孔菌科 Polyporaceae	8	14	6.70	蜡蘑属 Laccaria	5	2.39
红菇科 Russulaceae	3	23	11.00	小皮伞属 Marasmius	6	2.87
				小菇属 Mycena	11	5.26
				光柄菇属 Pluteus	5	2.39
				红菇属 Russula	17	8.13
				栓菌属 Trametes	5	2.39

关闭全屏

BibTeX
EndNote
RefWorks
TxT

Fig.1 (a) XRD patterns of Pt/KJ, Pt/TaO_x-C and Pt/Ta₂O₅. (b) HRTEM images of Pt/TaO_x-C. (c) Enlargement (top) and intensity profiles (bottom) of Pt (111) in the yellow dotted line frame of Fig. 2b. (d) EDS mapping of Pt/TaO_x-C.

Fig.2 (a) Ta L₃-edge for Ta foil, TaO, TaO_x-C and Ta₂O₅. (b) Extrapolate the valence state of Ta. White line position as a function of the oxidation states of Ta for Pt/TaO_x-C, with metallic Ta foil (0) and Ta₂O₅ (+5) as standard. (c) High resolution XPS spectra O 1s for Ta₂O₅ and TaO_x-C. (d) EPR spectra of Ta₂O₅ and TaO_x-C. (e) Pt 4f for Pt/Ta₂O₅ and Pt/TaO_x-C. (f) Pt L₃-edge for Pt foil, PtO₂, Pt/TaO_x-C, Pt/KJ, and JM-Pt/C.

Fig.3 (a) Cyclic voltammetry curves and (b) ORR polarization curves of JM-Pt/C, Pt/KJC, Pt/TaO_x-C and Pt/Ta₂O₅.(c) Comparison of mass activity and specific activity for Pt–TaO_x-C, Pt/KJ, JM-Pt/C and Pt/Ta₂O₅ at 0.9 V. (d) Pt/TaO_x-C and (e) JM-Pt/C O₂ LSV curves before and after stability tests between 0.6–1.0 V. (f) Change and retention of mass activity before and after stability testing of JM-Pt/C, Pt/KJ, Pt/TaO_x-C and Pt/Ta₂O₅. (g) Changes in XRD spectra of Pt/TaO_x-C before and after stability tests. (h) Changes in XPS spectra of Pt for Pt/TaO_x-C before and after stability tests. (i) Dissolution concentration of Pt during stability testing.

Fig.4 (a) PEMFCs sketch. (b) Polarization and power density curves of Pt/TaO_x-C, JM-Pt/C and Pt/KJ in H₂−Air fuel cells at 80 ℃ with 100 and 200 kPa back pressure and 100% RH with the cathode metal loading of 0.1 mg_Pt/cm². (c) Polarization and power density curves of Pt/TaO_x-C, JM-Pt/C, Pt/KJ in H₂−O₂ fuel cells at 80 ℃ with 100 and 200 kPa back pressure and 100% RH with the cathode metal loading of 0.1 mg_Pt/cm². (d) The comparison of the current density at 0.8 V and the power density at 0.67 V for Pt/TaO_x-C, JM-Pt/C and Pt/KJ in H₂-Air mode. (e) Comparison of peak power density between Pt/TaO_x-C with the state-of-art in the literature. (f) Polarization and power density curves of Pt/TaO_x-C in H₂−Air fuel cells at 80 ℃ with 200 kPa back pressure and 100% RH with the cathode metal loading of 0.1 mg_Pt/cm² after 10k, 20k, 30k, 40k and 50k potential cycles. (g) Polarization and power density curves of Pt/TaO_x-C in H₂−O₂ fuel cells at 80 ℃ with 200 kPa back pressure and 100% RH with the cathode metal loading of 0.1 mg_Pt/cm² after 10k, 20k, 30k, 40k and 50k potential cycles. (h) Power density at 0.67 V and voltage loss at 0.8 A/cm² at the begin of life (BOL), 10k and 50k. Note: The yellow dashed line indicates the DOE target for voltage drop at 0.8 A/cm² after 30k potential cycles.

Articles: Latest Articles; Most Read; Collections

Updates: Events; News; Multimedia

About: About Us

Contact

No. 86 Xueyuan South Road, Haidian District, Beijing

100081

010-62662699(Operation and Technical Support)

qkjq@cast.org.cn

Copyright © 2025 China Association for Science and Technology. All rights reserved. For all open access content, the relevant licensing terms apply.
Sponsored by the Office of the Leading Group for Cybersecurity and Informatization of CAST, and supported by Science and Technology Review Publishing House