Synthesis and structure of Au19Ag4(S-Adm)15 nanocluster: Polymorphs and optical properties

Synthesis and structure of Au₁₉Ag₄(S-Adm)₁₅ nanocluster: Polymorphs and optical properties

PDF

Xuemei Fu^a^,^b, Xinzhang Lin^a^,^b, Xiuqing Ren^a, Hengjiang Cong^c, Chao Liu^a^,^*, Jiahui Huang^a^,^*

Chinese Chemical Letters | 2021, 32(1) : 565 - 568

Less

Chinese Chemical Letters | 2021, 32(1): 565-568

• Communication •

Synthesis and structure of Au₁₉Ag₄(S-Adm)₁₅ nanocluster: Polymorphs and optical properties

Full

Xuemei Fu^a^,^b, Xinzhang Lin^a^,^b, Xiuqing Ren^a, Hengjiang Cong^c, Chao Liu^a^,^*, Jiahui Huang^a^,^*

Affiliations

^a Gold Catalysis Research Center, State Key Laboratory of Catalysis, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023, China

^b University of Chinese Academy of Sciences, Beijing 100049, China

^c College of Chemistry and Molecular Sciences, Engineering Research Center of Organosilicon Compounds & Materials, Ministry of Education, Wuhan University, Wuhan 430072, China

Published: 2021-01-15 doi: 10.1016/j.cclet.2020.02.041

Outline

Abstract

Less

Polymorphism is a common phenomenon in nature. Here, we report one-pot wet chemical method to synthesize two polymorphs of Au₁₉Ag₄(S-Adm)₁₅ nanocluster protected by 1-adamantanethiol (HS-Adm), which adopt P-1 and P2₁/c space group respectively. The crystal structures of two polymorphs were determined by X-ray crystallography. Compared to the previously reported Au₁₉Ag₄(S-Adm)₁₅ nanocluster adopting P2₁/n space group, polymorphs of Au₁₉Ag₄(S-Adm)₁₅ with P-1 and P2₁/c space group show the different optical properties. Moreover, Au₁₉Ag₄(S-Adm)₁₅ with P-1 space group exhibits good thermal stability. Meanwhile, we investigated the effect of solvent and molar ratio of metal precursors on the polymorphs. This work provides an insight to polymorphs of metal nanoclusters.

Key words

Au₁₉Ag₄(S-Adm)₁₅ / Alloy nanocluster / Polymorph / Fluorescence / Thermal stability

Cite this Article

Xuemei Fu, Xinzhang Lin, Xiuqing Ren, Hengjiang Cong, Chao Liu, Jiahui Huang. Synthesis and structure of Au₁₉Ag₄(S-Adm)₁₅ nanocluster: Polymorphs and optical properties[J]. Chinese Chemical Letters, 2021 , 32 (1) : 565 -568 . DOI: 10.1016/j.cclet.2020.02.041

Full Text

Less

Nobel metal nanoclusters have attracted significant attentions for decades in virtue of the potential applications in many fields, such as sensor [1-3], biochemistry [4-7], catalysis [8-11] and optics [12-14]. A series of atomically precise Au nanoclusters have been successfully synthesized and their crystal structures have been determined by X-ray crystallography. In recent years, most work concentrated on developing novel methods to design and synthesize special crystal structures of Au nanoclusters with enhanced properties. It has been found that Au-M alloy nanoclusters could exhibit synergistic effects on the physical and chemical properties due to the foreign atoms doping into Au nanoclusters [15, 16]. Therefore, design, preparation and application in different fields of Au-M alloy nanoclusters have been a hot spot [17-23].

As doping foreign atoms can influence the electronic structure of Au nanoclusters, different metal atoms are brought into Au nanoclusters in order to tune the chemical and physical properties of Au nanoclusters. Fields-Zinna et al. successfully doped Pd into Au₂₅(SR)₁₈ nanocluster and obtained PdAu₂₄(SR)₁₈ alloy nanocluster via ligand exchange method [24]. After that, many foreign metal atoms, such as Ag [25-31], Pt [32, 33], Cu [34-36], Hg [37, 38] and Cd [37, 38], were doped into thiolate protected Au nanoclusters. Wang et al. doped Cu, Ag, Cd and Hg into Au₂₅ nanocluster via using Au₂₅ nanocluster as template, as a result, a series of alloy nanoclusters Cu_xAu_25-x(SR)₁₈, Ag_xAu_25-x(SR)₁₈, Cd₁Au₂₄(SR)₁₈ and Hg₁Au₂₄(SR)₁₈ were obtained [37, 38]. Nair et al. reported that Pd atom could replace the central atom of Au₁₃ icosahedrons in [Au₂₄Pd(PPh₃)₁₀(SC₂H₄Ph)₅C_l2]⁺, which led to the dipole moment and excellent stability [39]. Meanwhile, Tlahuice-Flores et al. [40] carried out TD-DFT calculation to study a series of Ag doped Au₁₈ nanoclusters. And it was found that Au_18-xAg_x nanocluster shows enhanced oscillator strength of HOMO-LOMO due to Ag doping. In addition, Au_18-xAg_x nanocluster exhibited different optical properties and Circular Dichroism in comparison with Au18 nanocluster. Wang et al. [22] reported Ag atoms substituted Au₂₅ nanocluster displaying a 200-fold photoluminescence quantum yield than parent Au₂₅ nanocluster. DFT theory indicated that Ag atom in the central site of Au_25-xAg_x nanocluster could stabilize the charges on LUMO orbit and improve its rigidity [41]. Additionally, Ag doped Au₂₃-xAg_x (x = 4–7) nanocluster was observed to show a distinctly higher catalytic activity than Au₂₃ in the photocatalytic degradation of organic pollutants [31]. Unitl now, although many types of foreign atoms have been doped into Au nanoclusters, the synthesis and determination of Au alloy nanoclusters with novel crystal structures are still a huge challenge.

With respect to metal nanoclusters with the same molecular formula, there are twotypical phenomena: structuralisomerism and polymorphism. Structural isomerism is observed in gold and silver nanoclusters, which is beneficial to understand the structureproperty relationship due to the different properties among isomers [42-44]. In recent work, a few reports focused on the structural isomers because the synthesis and structural determination were difficult. Tian et al. [45] reported two Au₃₈ isomers and found that Au38T isomer is composed of Au₂₅ inner core and exhibited much better catalytic activity in the hydrogenation of 4-nitrophenol. Besides, Pt doping Ag₂₉ isomers showed different symmetries and optical properties [46]. In term of polymorphism, atomic packing mode are almost the same apart from different bond lengths and bond angles. However, there are few reports on polymorphism in gold, silver and alloy nanoclusters [47].

Previously, Jin et al. synthesized Au₁₉Ag₄(S-Adm)₁₅ nanocluster with P2₁/n space group in tetrahydrofuran (named as NC-P2₁/n) [25]. We changed reaction solvent and molar ratio of metal precursors to obtain two polymorphic Au₁₉Ag₄(S-Adm)₁₅ nanoclusters. It is the first time to observe polymorphism in AuAg alloy nanoclusters. In this work, two polymorphs of Au₁₉Ag₄(S-Adm)₁₅ were determined by X-ray crystallography.And they adoped P-1 and P2₁/c space group (named as NC-P-1 and NC-P2₁/c, respectively). The optical properties of the Au₁₉Ag₄(S-Adm)₁₅ polymorphs were analyzed by ultra-visible (UV–vis) absorption and fluorescence.

NC-P-1 was synthesized by a simple wet chemical method: HAuCl₄·4H₂O (40.9 mg, 0.099 mmol) was dissolved in 5 mL H₂O and 10 mL dichloromethane in the presence of TOAB (63.0 mg, 0.115 mmol). After reaction for 30 min, the aqueous phase in the upper layer was removed. AgNO₃ (2.5 mg, 0.015 mmol, molar ratio of Au: Ag = 1:0.15) was dissolved in 1 mL methanol and then poured into above solution. Subsequently, HS-Adm (83.4 mg, 0.496 mmol) was added as thiol. After stirring for 1 h, NaBH₄ (37.6 mg, 0.994 mmol, dissolved in 5 mL cold water) was used to reduce the M-SR (M: Au, Ag) polymer. After stirring for four days, the reaction was stopped and the solution was dried with vacuum rotary evaporator. The crude product was washed with methanol for four times and extracted by acetone. Finally, the product was collected by evaporating acetone under vacuum condition. The final dark red crystals were obtained by a vapor diffusion of methanol to toluene at room temperature. The yield of NC-P-1 was ~11% (based on HAuCl4). Synthesis of NC-P2₁/c was followed by the synthetic process of NC-P-1, except for the molar ratio of metal precursors molar ratio of (Au: Ag = 1:0.125). The crude product was washed with methanol for several times and extracted by acetone. To obtain the pure NC-P2₁/c nanocluster, the crude product was kept in the solvent of methanol and toluene (1:1, v: v) for a week. The NC-P2₁/c was dissolved in the mixture solvent of methanol and toluene. At last, the pure NC-P2₁/c was obtained by evaporating the solvent of methanol and toluene. The final crystals were grown up by diffusing methanol to toluene at room temperature. The yield of NC-P2₁/c was ~18% (based on HAuCl4). Crystallographic data of NC-P-1 and NC-P2₁/c is submitted to the Cambridge Crystallographic Data Centre under Nos.1954872 and 1954873 respectively.

The NC-P-1 nanocluster adopts P-1 space group and it has an icosahedral Au₁₀Ag₃ kernel (Fig. 1a). The details of crystallographic data were seen in Table S1 (Supporting information). In this nanocluster, three silver atoms doping in the M₁₃ kernel form a triangle on the top of the icosahedron. The other doping silver atom binds with three sulfur atoms to form a AgS₃ motif at the bottom of nanocluster. The kernel is capped by three trimeric Au₃(SR)₄ motifs and a AgS₃ motif. There is no silver atom doping into the Au₃(SR)₄ motifs (Fig. 1b). In the structural diagram of NC-P-1 nanocluster, it can be seen that the three Ag atoms forming a triangle locate on the top of kernel, and the simple motif AgS₃ is binding at the bottom of the kernel. The Au-Ag bond length of silver atom in the AgS₃ motif and the neighboring three gold atoms is 2.96 Å, 2.97 Å and 3.01 Å respectively. NC-P2₁/c is composed of the same kernel and motifs. The detailed crystallographic data of NC-P2₁/c nanocluster was shown in Fig. S1 and Table S2 (Supporting information).

The molecular structures of NC-P-1 and NC-P2₁/c are similar to that of the previously reported NC-P2₁/n [25]. To further explain the relationship of three nanoclusters, we distinguished the difference of synthetic method and structures. The reported NCP2₁/n was synthesized in tetrahydrofuran with 1:0.125 molar ratio of gold to silver precursors (Fig. 2a) [25]. NC-P2₁/c was obtained when we changed the reaction solvent from tetrahydrofuran to dichloromethane (Fig. 2b). Based on synthetic method of NC-P2₁/n, NC-P-1 was synthesized via modulating molar ratio of gold to silver precursors from 1:0.125 to 1:0.15 (Fig. 2c). Crystallographic data of three polymorphs were displayed in Fig. 2d. The crystal system of NC-P-1 is triclinic with the space group P-1. However, NC-P2₁/c and NC-P2₁/n were packed in monoclinic lattice with P2₁/c and P2₁/n space group respectively. In details, unit cell parameters of NC-P-1 are: a = 17.831(4) Å, b = 20.925(4) Å, c = 29.277(6) Å, α = 83.33(3)°, β = 81.97(3)°, γ = 68.35(3)°. Unit cell parameters of NC-P2₁/c are: a = 17.1868(2) Å, b = 21.2527(2) Å, c = 58.8533(7) Å, α = 90°, β = 93.378(1)°, γ = 90° and the unit cell parameters of NC-P2₁/n are: a = 17.4011(6) Å, b = 44.214(2) Å, c = 30.3350(13) Å, α = 90°, β = 93.106(3)°, γ = 90°. The number of molecules per unit cell (Z), volume and density of the three polymorphs are also showed in Fig. 2d, indicating the distinct difference among these unit cell parameters.

To further understand the difference of the three polymorphs, typical bond lengths of NC-P-1, NC-P2₁/c and NC-P2₁/n were compared (Fig. S2 in Supporting information). The average Au-Ag bond length in the Au₁₀Ag₃ kernel of NC-P2₁/c is 2.903 Å, shorter than that of NC-P-1 (2.913 Å) and NC-P2₁/n (2.915 Å). In term of the average Ag-Ag bond length in the kernel, that of NC-P-1 is the shortest (2.868 Å) compared to NC-P2₁/n (2.888 Å) and NC-P2₁/c (2.931 Å). However, the average Au-Au bond length in the kernel of NC-P2₁/n is longer (2.8547 Å) than that of NC-P2₁/c (2.8461 Å) and NC-P-1 (2.8462 Å). In addition, in NC-P-1 nanocluster, the average Ag-Au bond length from kernel to Au3S4 motif is 2.988 Å, which is shorter than that in NC-P2₁/c (2.993 Å) and NC-P2₁/n (3.027 Å). However, the average Au-Au bond length from kernel to Au3S4 motif of NC-P2₁/c is 3.097 Å, shorter than that of NC-P-1(3.098 Å) and NC-P2₁/n (3.132 Å). More details of the differences in bond lengths of NC-P-1, NC-P2₁/c and NC-P2₁/n are showed in Tables S3- S5 (Supporting information).

In addition, these polymorphs show different bond angles. The three bond angles (∠S-Ag-S) in AgS3 motif of NC-P-1 are 118.37°, 119.54° and 120.72° respectively, indicating the atoms of AgS3 motif are not in the same plane (Fig. S3 in Supporting information). The average bond angle (∠S-Ag-S) in AgS3 motif of NC-P-1 is 119.54°, which is larger than that of NC-P2₁/c (119.22°) and NC-P2₁/n (119.18°). The average bond angle (ffAu-S-Au) in Au₃S₄ motif (Fig. S4a in Supporting information) of NC-P-1 (94.51°) is also larger than that of NC-P2₁/c (94.08°) and NC-P2₁/n (93.61°). In Fig. S4b (Supporting information), for the M₁₃ core, the average bond angle (∠Ag-Au_c-Au) of NC-P-1, NC-P2₁/c and NC-P2₁/n are 134.67°, 134.66° and 134.63°, showing the slight difference among NC-P-1, NC-P2₁/c and NC-P2₁/n. More details of the bond lengths and bond angles of NC-P-1, NC-P2₁/c and NC-P2₁/n were showed in Tables S6-S11 (Supporting information). Of note, it was the first time to find the polymorphs in AuAg alloy nanoclusters.

Many factors influence the synthesis of alloy nanoclusters, such as solvent, molar ratio of metal precursors. It is important to explore the influence factors on the formation of polymorphs. Firstly, we investigated the effect of solvents on the polymorphs. When the dichloromethane was used as solvent instead of tetrahydrofuran, the NC-P2₁/c with P2₁/c space group was obtained. In previous work, reaction solvent has important effect on the size of gold nanoclusters [48]. In our case, it also indicated reaction solvent may lead to the formation of polymorphs. Recently, Jin et al. [25] reported a series of AuAg alloy nanoclusters via changing the molar ratio of HAuC_l4 to AgNO₃ precursors. Therefore, we further studied the effect of the molar ratio of Ag to Au on polymorphs. Interestingly, the tuning of molar ratio of AgNO₃ to HAuC_l4 gives rise to the polymorphs of NC-P-1 in dichloromethane solvent. This demonstrated that molar ratio of metal precursors plays an important role in preparing polymorphs of Au-Ag alloy nanoclusters.

The optical properties of metal nanoclusters are sensitive to the structures. To investigate optical properties of the polymorphs, we carried out UV–vis spectrometry and fluorescence. In Fig. 3a, the NC-P-1 shows the prominent absorption peaks at 730 nm, 580 nm, 460 nm and 440 nm. All the absorption peaks of NC-P-1 display the obvious blue shift by 20 nm than those of NC-P2₁/n [25]. However, NC-P2₁/c shows UV–vis absorption peaks at 490 nm and 580 nm with a shoulder at 380 nm. It further indicates that the three polymorphs exhibit different optical properties, which may result of their structures.

To further test the difference of optical properties, we studied the fluorescence of the three polymorphs. Fig. 3b demonstrated that NC-P2₁/n exhibits a weak emission at 800 nm and 720 nm. NCP2₁/c only shows a peak at 680 nm. However, the NC-P-1 exhibits the enhanced fluorescence at 800 nm. By comparison, it was found that the fluorescence of NC-P-1 is almost close to near infrared range. It can be inferred that the structures of Au-Ag alloy nanoclusters have a significant effect on the optical properties.

The thermal stability of nanocluster is related to their structures [49, 50]. To study the thermal stability of the three polymorphs, the samples were heated at different temperatures. The NC-P-1 nanocluster showed pretty well stability at 60 ℃. After heating at 60 ℃ for 18 h, the absorption peaks intensity was kept very well, similar to those before heating. When heating at 60 ℃ for 50 h, the absorption peaks became weak. The peak at 750 nm disappeared after reaction for 72 h, which means that the NC-P-1 nanocluster collapsed (Fig. 4a). The stability of NC-P-1 was also tested at 80 ℃. It showed the NC-P-1 could keep stable at 80 ℃ for 22 h. However, after reaction for 39 h, the UV–vis spectrum shows there is no prominent absorption peak (Fig. S5 in Supporting information). We also carried out the heat treatment of the NC-P2₁/c. When heating at 60 ℃ for 10 min, the peaks at 760 nm rapidly faded away (Fig. 4b). Even at room temperature, NC-P2₁/c only kept stable for 1 h in toluene (Fig. S6 in Supporting information). Thermal stability of NC-P2₁/n was also tested at 80 ℃ and it broke down after 2 h [25]. On the basis of the experimental data, it is clear that NC-P-1 possesses much better thermal stability than NC-P2₁/c and NCP2₁/n, and this clear difference in thermal stability should be caused by their different structures.

In summary, we synthesized two polymorphs of Au₁₉Ag₄(SAdm)₁₅ nanoclusters via changing the reaction solvent and molar ratio of AgNO₃ to HAuCl₄. In our work, it was found that solvent and molar ration of metal precursor have great effect on the synthesis of polymorphs. The two Au-Ag nanoclusters adopt P-1 and P2₁/c space group respectively. The structures of Au-Ag alloy nanoclusters were determined by X-ray crystallography, which is composed of an icosahedral Au₁₀Ag₃ kernel, three Au₃S₄ motifs and a AgS₃ motif. The three polymorphs showed different optical properties and thermal stability. NC-P-1 showed the enhanced fluorescence and exhibited well thermal stability. It can keep stable even heating at high temperature of 80 ℃ for 22 h. This study opens a new way for exploring chemical and physical properties of polymorphs in metal nanoclusters and providing the insight into understanding their structure-property relationship in the future.

Declaration of competing interest

Less

The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.

Acknowledgments

Less

We acknowledge the National Natural Science Foundation of China (No. 21601178). We sincerely thank Yingwei Li and Rongchao Jin from Department of Chemistry, Carnegie Mellon University. We thank staffs at the Shanghai Synchrotron Radiation Facility for assistance during the crystallographic data collection.

Appendix A. Supplementary data

Less

Supplementary material related to this article canbefound, in the online version, at doi:https://doi.org/10.1016/j.cclet.2020.02.041

References

Less

[1]

Q. Yu, P.L. Gao, K.Y. Zhang, et al., Light-Sci Appl. 6 (2017) e17107.

[2]

D.H. Tian, Z.S. Qian, Y.S. Xia, C.Q. Zhu, Langmuir 28 (2012) 3945-3951.

[3]

K. Saha, S.S. Agasti, C. Kim, X.N. Li, V.M. Rotello, Chem. Rev. 112 (2012) 2739-2779.

[4]

X. Yang, M.X. Yang, B. Pang, M. Vara, Y.N. Xia, Chem. Rev. 115 (2015) 10410-10488.

[5]

Z.T. Luo, K.Y. Zheng, J.P. Xie, Chem. Commun. 50 (2014) 5143-5155.

[6]

J. Xu, L. Shang, Chin. Chem. Lett. 29 (2018) 1436-1444.

[7]

H.D. Cui, D.H. Hu, J.N. Zhang, et al., Chin. Chem. Lett. 28 (2017) 1391-1398.

[8]

Z. Wu, D.R. Mullins, L.F. Allard, Q. Zhang, L. Wang, Chin. Chem. Lett. 29 (2018) 795-799.

[9]

Y. Tan, X.Y. Liu, L. Li, et al., J. Catal. 364 (2018) 174-182.

[10]

G. Li, H. Abroshan, C. Liu, et al., ACS Nano 10 (2016) 7998-8005.

[11]

B. Yoon, H. Hakkinen, U. Landman, et al., Science 307 (2005) 403-407.

[12]

H. Zhu, N. Goswami, Q. Yao, et al., J. Mater. Chem. A 6 (2018) 1102-1108.

[13]

F. Xu, J. Chen, S. Kalytchuk, et al., J. Catal. 354 (2017) 1-12.

[14]

X. Yuan, Z.T. Luo, Y. Yu, Q.F. Yao, J.P. Xie, Chem. Asian J. 8 (2013) 858-871.

[15]

H.F. Qian, D.E. Jiang, G. Li, et al., J. Am. Chem. Soc. 134 (2012) 16159-16162.

[16]

Y. Niihori, W. Kurashige, M. Matsuzaki, Y. Negishi, Nanoscale 5 (2013) 508-512.

[17]

T. Chen, S. Yang, J. Chai, et al., Sci. Adv. 3 (2017) e1700956.

[18]

M.A. Tofanelli, T.W. Ni, B.D. Phillips, C.J. Ackerson, Inorg. Chem. 55 (2016) 999-1001.

[19]

G. Soldan, M.A. Aljuhani, M.S. Bootharaju, et al., Angew. Chem. Int. Ed. 55 (2016) 5749-5753.

[20]

Y.B. Song, S. Jin, X. Kang, et al., Chem. Mater. 28 (2016) 2609-2617.

[21]

T. Cesca, B. Kalinic, N. Michieli, et al., Phys. Chem. Chem. Phys. 17 (2015) 28262-28269.

[22]

S. Wang, X. Meng, A. Das, et al., Angew. Chem. Int. Ed. 53 (2014) 2376-2380.

[23]

Y. Negishi, M. Mizuno, M. Hirayama, et al., Nanoscale 5 (2013) 7188-7192.

[24]

C.A. Fields-Zinna, M.C. Crowe, A. Dass, J.E.F. Weaver, R.W. Murray, Langmuir 25 (2009) 7704-7710.

[25]

Y. Li, T.Y. Luo, M. Zhou, et al., J. Am. Chem. Soc. 140 (2018) 14235-14243.

[26]

X. Kang, L. Xiong, S. Wang, Y. Pei, M. Zhu, Inorg. Chem. 57 (2018) 335-342.

[27]

C. Kumara, C. M. Aikens, A. Dass, J. Phys, Chem. Lett. 5 (2014) 461-466.

[28]

V.R. Jupally, A. Dass, Phys. Chem. Chem. Phys. 16 (2014) 10473-10479.

[29]

C. Kumara, A. Dass, Nanoscale 4 (2012) 4084-4086.

[30]

S. Malola, H. Hakkinen, J. Phys. Chem. Lett. 2 (2011) 2316-2321.

[31]

C. Liu, X.Q. Ren, F. Lin, et al., Angew. Chem. Int. Ed. 58 (2019) 11335-11339.

[32]

X. Kang, M. Zhou, S. Wang, et al., Chem. Sci. 8 (2017) 2581-2587.

[33]

S. Tian, L. Liao, J. Yuan, et al., Chem. Commun. 52 (2016) 9873-9876.

[34]

S. Wang, Y. Song, S. Jin, et al., J. Am. Chem. Soc. 137 (2015) 4018-4021.

[35]

E. Gottlieb, H.F. Qian, R.C. Jin, Chem: Eur J. 19 (2013) 4238-4243.

[36]

Y. Negishi, K. Munakata, W. Ohgake, K. Nobusada, J. Phys, Chem. Lett. 3 (2012) 2209-2214.

[37]

C. Yao, Yj. Lin, J. Yuan, et al., J. Am. Chem. Soc. 137 (2015) 15350-15353.

[38]

L.W. Liao, S.M. Zhou, Y.F. Dai, et al., J. Am. Chem. Soc. 137 (2015) 9511-9514.

[39]

L.V. Nair, S. Hossain, S. Takagi, et al., Nanoscale 10 (2018) 18969-18979.

[40]

B. Molina, A. Tlahuice-Flores, Phys. Chem. Chem. Phys. 18 (2016) 1397-1403.

[41]

M. Zhou, J. Zhong, S. Wang, et al., J. Phys. Chem. C 119 (2015) 18790-18797.

[42]

L.Q. Wang, X.Q. Chai, X.L. Cheng, Y. Zhu, ChemistrySelect 3 (2018) 6165-6169.

[43]

M. Zhou, S.B. Tian, C.J. Zeng, et al., J. Phys. Chem. C 121 (2017) 10686-10693.

[44]

R. Juarez-Mosqueda, S. Malola, H. Hakkinen, Eur. Phys. J. D 73 (2019) 62-68.

[45]

S. Tian, Y.Z. Li, M.B. Li, et al., Nat. Commun. 6 (2015) 8667.

[46]

X. Lin, C. Liu, K. Sun, et al., Nano Res. 12 (2019) 309-314.

[47]

A. Nag, P. Chakraborty, M. Bodiuzzaman, et al., Nanoscale 10 (2018) 9851-9855.

[48]

C. Liu, G. Li, G. Pang, R. Jin, RSC Adv. 3 (2013) 9778-9784.

[49]

X. Kang, C. Silalai, Y. Lv, et al., Eur. J. Inorg. Chem. 2017 (2017) 1414-1419.

[50]

Q. Tang, R.H. Ouyang, Z.Q. Tian, D.E. Jiang, Nanoscale 7 (2015) 2225-2229.

Appendix

Less

Year 2021 volume 32 Issue 1

PDF

Cite this Article

BibTeX

Article Info

doi: 10.1016/j.cclet.2020.02.041

Receive Date：2019-12-23
Online Date：2026-01-04
Published：2021-01-15

Article Data

Affiliations

History

Received：2019-12-23
Revised：2020-02-14
Accepted：2020-02-20

Affiliations

^a Gold Catalysis Research Center, State Key Laboratory of Catalysis, Dalian Institute of Chemical Physics, Chinese Academy of Sciences, Dalian 116023, China

^b University of Chinese Academy of Sciences, Beijing 100049, China

^c College of Chemistry and Molecular Sciences, Engineering Research Center of Organosilicon Compounds & Materials, Ministry of Education, Wuhan University, Wuhan 430072, China

References

Share

https://castjournals.cast.org.cn/joweb/ccl/EN/10.1016/j.cclet.2020.02.041

Share to

Scan QR to access full text

Cite this article

BibTeX

Citations

表12种不同金属材料的力学参数

科 Family	属数 Number of genus	种数 Number of species	占总种数比例 Percentage of total species (%)	属 Genus	种数 Number of species	占总种数比例 Percentage of total species (%)
鹅膏菌科Amanitaceae	2	11	5.26	鹅膏菌属 Amanita	10	4.78
小菇科 Mycenaceae	2	12	5.74	丝盖伞属 Inocybe	5	2.39
多孔菌科 Polyporaceae	8	14	6.70	蜡蘑属 Laccaria	5	2.39
红菇科 Russulaceae	3	23	11.00	小皮伞属 Marasmius	6	2.87
				小菇属 Mycena	11	5.26
				光柄菇属 Pluteus	5	2.39
				红菇属 Russula	17	8.13
				栓菌属 Trametes	5	2.39

关闭全屏

BibTeX
EndNote
RefWorks
TxT

Fig. 1 (a) The total crystal structure of NC-P-1 without hydrogen atoms for clarity. (b) Anatomy of NC-P-1 structure. Color code: yellow, Au; purple, Ag; green, S; grey, C.

Fig. 2 Unit cell of (a) NC-P2₁/n; (b) NC-P2₁/c; (c) NC-P-1. (d) Table of parameters of the three polymorphs. Color code: yellow, Au; purple, Ag; green, S; grey, C.

Fig. 3 (a) UV–vis absorption spectrum of NC-P-1, NC-P2₁/c and NC-P2₁/n [25] and (b) Fluorescence spectra of the NC-P-1, NC-P2₁/c and NC-P2₁/n (dissolved in dichloromethane).

Fig. 4 Thermal stability test of (a) NC-P-1 and (b) NC-P2₁/c nanoclusters at 60 ℃ in toluene.

Articles: Latest Articles; Most Read; Collections

Updates: Events; News; Multimedia

About: About Us

Contact

No. 86 Xueyuan South Road, Haidian District, Beijing

100081

010-62199257

qkjq@cast.org.cn

Copyright © 2025 China Association for Science and Technology. All rights reserved. For all open access content, the relevant licensing terms apply.
Sponsored by the Office of the Leading Group for Cybersecurity and Informatization of CAST, and supported by Science and Technology Review Publishing House