Bi<sup>3+</sup>-activated dual-wavelength emitting phosphors toward effective optical thermometry

Bi³⁺-activated dual-wavelength emitting phosphors toward effective optical thermometry

PDF

Yu Xue^a, Yuqi Chen^a, Guixian Li^a, Weixi Xia^a, Qinan Mao^a, Lang Pei^a, Meijiao Liu^c, Liang Chu^b^,^*, Jiasong Zhong^a^,^*

Chinese Chemical Letters | 2024, 35(3) : 108447

Less

Chinese Chemical Letters | 2024, 35(3): 108447

• Communication •

Bi³⁺-activated dual-wavelength emitting phosphors toward effective optical thermometry

Full

Yu Xue^a, Yuqi Chen^a, Guixian Li^a, Weixi Xia^a, Qinan Mao^a, Lang Pei^a, Meijiao Liu^c, Liang Chu^b^,^*, Jiasong Zhong^a^,^*

Affiliations

^aCenter of Advanced Optoelectronic Materials, College of Materials and Environmental Engineering, Hangzhou Dianzi University, Hangzhou 310018, China

^bCollege of Electronics and Information, Hangzhou Dianzi University, Hangzhou 310018, China

^cDepartment of Chemistry, Zhejiang Sci-Tech University, Hangzhou 310018, China

Published: 2024-03-15 doi: 10.1016/j.cclet.2023.108447

Outline

Abstract

Less

Optical thermometry as an important local temperature-sensing technique, has received increasing attention in scientific and industrial areas. However, it is still a big challenge to develop luminescent materials with self-activated dual-wavelength emissions toward high-sensitivity optical thermometers. Herein, a novel ratiometric thermometric strategy of Bi³⁺-activated dual-wavelength emission band was realized in the same lattice position with two local electronic states of La₃Sb_1-xTa_xO₇:Bi³⁺(0 ≤ x ≤ 1.0) materials based on the different temperature-dependent emission behaviors, benefiting from the highly-sensitive and regulable emission to the coordination environment of Bi³⁺. The structural and spectral results demonstrate that the emission tremendously shifted from green to blue with 68 nm and the intensity was enhanced 2.6 times. Especially, the visual dual-wavelength emitting from two emission centers was presented by increasing the Ta⁵⁺substitution concentration to 20% or 25%, mainly originating from the two local electronic states around the Bi³⁺ emission center. Significantly, the dual-wavelength with different thermal-quenching performance provided high-temperature sensitivity and good discrimination signals for optical thermometry in the range between 303 and 493 K. The maximum relative sensitivity reached 2.64%/K (La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺@383 K) and 1.91%/K (La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺@388 K). This work reveals a rational design strategy of different local electronic states around the single-doping multiple emission centers towards practical applications, such as luminescence thermometry and white LED lighting.

Key words

Dual-wavelength emitting / Cationic substitution / Two local electronic states / Optical thermometry / Bi³⁺-doped phosphor

Cite this Article

Yu Xue, Yuqi Chen, Guixian Li, Weixi Xia, Qinan Mao, Lang Pei, Meijiao Liu, Liang Chu, Jiasong Zhong. Bi³⁺-activated dual-wavelength emitting phosphors toward effective optical thermometry[J]. Chinese Chemical Letters, 2024 , 35 (3) : 108447 - . DOI: 10.1016/j.cclet.2023.108447

Full Text

Less

With the development of science and technology, temperature detection accuracy is highly demanded [1,2]. Luminescence thermometry possesses obvious advantages, such as non-contact, rapid response, noninvasive operation, excellent spatial and temperature resolution [3]. Importantly, this technology can be applied in a complex environment, micro/nano system, and strong electronic/magnetic field [4–7]. Fluorescence intensity ratio (FIR), luminescence lifetime, and emission peak/bandwidth are the main three paradigms of luminescence thermometry [8–11]. In FIR, the calibration curve is determined by the relative ratio of emission peaks or integrated intensity at a certain temperature [12], which is not easily disturbed by non-temperature parameters. The method of the relative ratio of the emission intensities can reduce the systemic error from the fluctuation of the excitation light source to enhance accuracy and repeatability [13,14]. In general, the relative emission peaks are managed by co-doping temperature-sensitive transition metal (TM) and thermally-stable rare earth ions [15]. Besides, the thermal quenching can be tuned by changing the TM crystal field. However, the two-type ions have different excitation wavelengths, weakening the efficiency of temperature detection. To date, it is desired to explore single-doped based dual-wavelength emission phosphor for effective luminescence thermometry [16].

Bismuth (Bi), an important TM element, has attracted increasing attention due to the flexible optical properties of the intimate interaction with the coordination environment [17,18]. Meanwhile, the outside electrons of Bi ([Xe]4f¹⁴5d¹⁰6s²6p³) are sensitive to the crystal structure and local electronic states [19,20]. Thus, the emission of Bi³⁺-doped phosphors has wide-range color engineering from ultraviolet (UV) to blue, green, yellow, and even red, by managing the hosts or ligands [21–23]. The PL spectra tunability of Bi³⁺ ions in a single host can be realized through the following two strategies, cationic substitution to regulate the crystal structure and co-doping activator ions to form the energy transfer [24,25]. However, co-doping is usually complex. And the cationic substitution can manage the crystal field strength of the host to change the luminescence properties [3,26]. In fact, the local electronic states around the luminescent center are affected by the crystal field strength and further influence the emission performance of Bi³⁺ ions. Therefore, the local electronic state modulation around the different emission centers may realize the single-doped Bi³⁺ dual-emitting [27,28].

In this work, an alternative strategy is designed for luminescence thermometry via dual-emitting of a single Bi³⁺ vital activator-doped La₃Sb_1-xTa_xO₇ (0 ≤ x ≤ 1.0) matrix. By managing the substitution concentration as 20% and 25%, the Bi³⁺-doped La₃Sb_1-xTa_xO₇ phosphors have obvious two emission peaks at 452 nm and 530 nm under the 303 nm excitation, due to the two emission centers from the corresponding local electronic states. The thermal quenching behaviors can be indicated in the temperature-dependence PL spectra operating from 303 K to 493 K. Based on the fluorescence intensity ratio, the maximum S are determined as 2.64%/K (La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺@383 K) and 1.91%/K (La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺@388 K), respectively, which illustrate the potential for luminescence temperature measurement.

Series of La₃SbO₇:yBi³⁺(0.02 ≤ y ≤ 0.12) and La₃Sb_1-xTa_xO₇:0.04Bi³⁺ (0 ≤ x ≤ 1.0) phosphors were synthesized by a conventional solid-state reaction method. The raw materials of La₂O₃ (99.99%), Sb₂O₅ (99.5%), Ta₂O₅ (99.99%) and Bi₂O₃ (99.99%) were weighed according to the designed stoichiometric ratio, mixed thoroughly in an agate mortar by grounding, and then sintered in a furnace at 1450 ℃ for 4 h with a heating rate of 5 ℃/min in air. After the reaction was cooled to room temperature naturally, the as-prepared phosphors were crushed into tiny powders.

The crystal structure and composition of the phosphors were characterized by X-ray diffraction (XRD) on a Bruker D8 Advance diffractometer (40 kV, 30 mA). Rietveld refinement was performed by the Maud 2.94 program. The morphology and elemental mapping were conducted by scanning electron microscope (SEM, FEI ApreoHiVac) equipped with an energy-dispersive X-ray spectrometer (EDX). The photoluminescence (PL), and photoluminescence excitation (PLE) spectra were characterized using a fluorescence spectrometer (Edinburgh Instrument FS5) with a 150 W continuous xenon lamp. The decay curves were measured by another fluorescence spectrometer (Horiba Fluorolog-3 with a 340 nm laser device). Temperature-dependent PL spectra were measured using an FS5 spectrometer equipped with a homemade temperature controller from 303 K to 493 K. The diffuse reflectance was performed by a UV-3600 spectrophotometer (Shimadzu Corporation, Tokyo, Japan), using the BaSO₄ standard reference. X-ray photoelectronic spectroscopy (XPS) spectra were performed on Thermo Scientific K-Alpha.

The fluorite-related structure of the compound (La₃SbO₇, La₃Sb_1-xTa_xO₇) belongs to the orthorhombic crystal. There are two sites of La³⁺ with coordinates of [La1O₈] and [La2O₇] (Fig. 1). Based on the same coordination number and similar radius of Bi³⁺ (r = 1.17 Å) and La³⁺(r = 1.16 Å), Bi³⁺ is supposed to replace the site of [La1O₈] rather than the sites of [La2O₇] and [SbO₆], because Bi ions cannot be doped into structures with seven coordination number. [29] The similar crystal structure of La₃SbO₇ and La₃TaO₇ makes the possibility of Ta/Sb cationic substitution. In general, the ion terms spilled into several sub-levels with large energy differences due to the nephelauxetic effect of doping Bi³⁺ ions into the host lattice. And the cationic substitution greatly affects the crystal field (CF) splitting of Bi³⁺ ions to adjust the luminescence performance of Bi³⁺. As the Ta⁵⁺ (r = 0.64 Å) substitutes for Sb⁵⁺ (r = 0.60 Å) in [MO₆]⁷⁻, the lattice can expanse due to the bigger ionic radius of Ta⁵⁺. Meanwhile, the modulation of the crystal field and nephelauxetic effect can change the peak position and intensity in the PL spectra.

To verify the phase and crystal structure of La₃SbO₇:yBi³⁺ (0.02 ≤ y ≤ 0.12) and La₃Sb_1-xTa_xO₇:0.04Bi³⁺ (0 ≤ x ≤ 1.0) phosphors, XRD and Rietveld refinements are demonstrated in Figs. 2a and b. All the diffraction peaks of the obtained Bi³⁺-doped phosphors are consistent well with the standard cards of La₃SbO₇ (PDF#23–1138) or La₃TaO₇ (PDF#38–1418) without any impurity phases. As presented in Fig. 2b, the diffraction pattern gradually shifts from the crystal structure of La₃SbO₇ to La₃TaO₇ one with increasing the substitution in La₃Sb_1-xTa_xO₇:0.04Bi³⁺ (0 ≤ x ≤ 1.0). Meanwhile, the substitution process produces no other phases or impurities. Besides, the diffraction peaks gradually shift to a lower degree with increasing Ta⁵⁺ substitution, due to the lattice expansion from the different ionic sizes (Sb⁵⁺:0.60 Å, Ta⁵⁺:0.64 Å). Moreover, XRD rietveld refinements elucidate the detailed crystal structure data of La₃Sb_1-xTa_xO₇:0.04Bi³⁺ (0 ≤ x ≤ 1.0) (Figs. 2c-f, Figs. S1-S4 and Table S1 in Supporting information). Following Vegard's law, the crystal structural parameters present a linear incremental with Ta⁵⁺ substitution increasing, agreeing with the lattice expansion.

The SEM image and related elemental mapping diagrams of La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺ phosphors are demonstrated in Fig. 2g. The mean particle size is about 5 μm. The elemental mapping further confirms the element La, Sb, Ta, O and Bi are homogeneously scattered in the selected region. All the coherent elements are displayed in the EDX spectrum (Fig. S5 in Supporting information), and the element mass proportion in accordance with the chemical formula, further proves the uniform distribution of Ta⁵⁺ ions as the partial substitution for Sb⁵⁺ ions.

Diffuse reflection spectra are evaluated in Fig. 3a. Notably, the Bi³⁺-doped samples have obvious absorption peaks between 290 nm and 380 nm, in good agreement with the excitation peak of PLE spectra. In addition, the bandgaps can be estimated through the Kubelka-Munk functions [30]:

(1)

(2)

where F (R) is the absorption, R is the reflectance (%), hv is the photon energy, and E is the bandgap. The E_g values of La₃SbO₇, La₃Sb_0.75Ta_0.25O₇ and La₃TaO₇ are calculated as 4.86, 4.92 and 5.03 eV, respectively, stemming from the linear part of the absorption curve (Fig. S6 in Supporting information). Obviously, the bandgaps gradually enhanced with increasing substitution of Ta⁵⁺ in La₃SbO₇ host. Bismuth cations could easily exist with different valence states in solid compounds, which greatly affect the luminescent properties. The X-ray photoelectron spectroscopy confirms the Bi³⁺ state in La₃SbO₇:0.04Bi³⁺, La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺ and La₃TaO₇:0.04Bi³⁺. The two characteristic peaks of Bi³⁺ at 164 eV and 159 eV come from the respective 4f_5/2 and 4f_7/2 of Bi³⁺ in the phosphors (Fig. 3b). Additionally, the peak of the 4f orbit shifts to lower energy, with the same trend as the characteristic peak of the O 1s orbital (Figs. 3b and c). The peak shift can be ascribed to the transformation of the local electronic state, resulting from the cationic substitution [31,32].

To explore the doping concentration on the luminescence properties, PL spectra are demonstrated in Fig. 3d. According to the emission spectrum and intensity integration, the optimum concentration of Bi³⁺ can be estimated as 0.04. The emission intensity decreases as increasing of Bi³⁺ concentration due to the concentration quenching, which is mainly originated from the shortened distance between Bi³⁺ ions to increase the possibility of non-radiative energy transfer. The emission spectra of La₃TaO₇:0.04Bi³⁺ and La₃SbO₇:0.04Bi³⁺ exhibits a profile of broadband, while their excitation spectra are slightly different (Fig. 3e). By replacing Sb⁵⁺ with Ta⁵⁺, the PL spectra have an obvious blue shift from 530 nm to 462 nm. Interestingly, the emission intensity of La₃TaO₇:0.04Bi³⁺ has increased about 2.6 times than that of La₃SbO₇:0.04Bi³⁺. As shown in Fig. 3g, the emission intensity slightly decreased initially and then rapidly increased with increasing Ta⁵⁺ concentration. The peak position showed a rapid blue shift trend followed by a slow redshift, which approaches the peak position of La₃TaO₇:0.04Bi³⁺. From Fig. 3f, the designed phosphors will appear dual-emission only as the substitution of Ta⁵⁺ range from 10% to 25%. When the substitution of Ta⁵⁺ is 20% or 25%, the emission spectra present obvious bimodal emission (Fig. S8 in Supporting information). Besides, the emission intensity locates in the blue-light area demonstrates an increased tendency, as shown in Fig. 3h, which further confirms the effect of Ta⁵⁺ ions on the local electronic states. Furthermore, the tunable emission of the La₃Sb_1-xTa_xO₇:0.04Bi³⁺ sample can be realized by modulating the Ta⁵⁺ content. Fig. 3i displays the CIE chromaticity coordinate diagram of La₃Sb_1-xTa_xO₇:0.04Bi³⁺ samples under 303 nm excitation. The CIE coordinate of the La₃Sb_1-xTa_xO₇:0.04Bi³⁺ samples shift from (0.2927, 0.5488) to (0.16619, 0.18315) with the value of x increase from 0 to 1.0. The corresponding luminescence photographs are also presented, which evidently presents the emission color tuning.

Furthermore, the two-wavelength emission may be attributed to two aspects, including the same Bi³⁺ emission center with two radiative decay channels of the excited state and from two Bi³⁺ centers with different local electronic states, which can be further clarified by the PL decay kinetic process. The luminescence lifetime curves of La₃SbO₇:yBi³⁺ (0.02 ≤ y ≤ 0.12) with different Bi³⁺ contents are measured at room temperature, as displayed in Fig. 4a, which can be fitted with a bi-exponential equation [33]:

(3)

And the average lifetime can be calculated as the following equation:

(4)

where I₀ and I represent the emission intensity at initial t₀ and time t, A₁ and A₂ denote pre-exponential factors, τ₁ and τ₂ are lifetime components, respectively. As summarized in Table S2 (Supporting information), the average lifetimes of La₃SbO₇:yBi³⁺ monotonously decreased from 296.02 ns to 151.38 ns with increasing y from 0.02 to 0.12.

From the Gaussian fitting of emission spectra, the broad emission band of La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺ and La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺ are both exactly deconvoluted into two peaks at 444 and 535 nm, and at 445 and 530 nm, respectively. Obviously, the PL patterns have changed and the position of the PL peak appears blue-shifted with the substitution of Ta⁵⁺ ion increased. In general, luminescence lifetime decay is also influenced by the local environment of the emission center. Thus, the luminescence decay curves monitored at 530 and 462 nm with different concentrations of Ta⁵⁺ ions are presented in Fig. 4d. As the substitution concentration of Ta⁵⁺ is 20%, the lifetime is calculated to be 41.79 and 182.24 ns monitored at 462 and 530 nm, respectively (Table S3 in Supporting information). While the concentration of Ta⁵⁺ is 25%, the lifetime is 55.09 and 172.14 ns. These results can be explained by the different local environments of the Bi³⁺ emission centers. From the lifetimes based on different Ta⁵⁺ concentrations, the substitution of Ta⁵⁺ for Sb⁵⁺ enhanced the blue-light emission and weaken the green light emission, which further certifies that the substitution of Ta⁵⁺ ion can affect the local electronic state around the emission center. In order to confirm the above speculation, two emission peaks with response to different excitation wavelengths are displayed in Figs. 4e and f. As seen from the 3D contour maps of two samples, the long-wavelength emission intensity has a better response to low energy excitation than that of short-wavelength emission intensity with the increase of the excitation wavelength from 290 nm to 380 nm, which is attributed to the different local electronic states around the emission centers.

In general, the PL spectrum of the s-p (Bi³⁺) transition is related to the crystal field strength, depending on the crystal structure of the host. A new solid solution is created by the substitution of Ta⁵⁺ to Sb⁵⁺ with bigger electronegativity and a smaller formal charge, leading to lower polarizability and weaker covalence. That produces a slighter nephelauxetic effect and a weaker crystal field for Bi³⁺ activators. Compared to the original host, the weakening of energy level splitting results in the increase of emission energy, which appears as a blue shift in the spectrum. The crystal field splitting refers to the energy difference between the highest and lowest energy levels, which strongly depends on the coordination situation of activator ions. There is a great influence on the crystal field strength from the bond lengths between activator ions and ligands, the molecular overlap and covalent degree between an activator and its ligands, the coordination environment, and the symmetry of activator-ion sites. In general, the crystal field strength (D_q) in the host can be evaluated by the expression [34]:

(5)

where Z is the valence of the anion, e is the electron charge, r is the wave-function radius, and R is the bond length between the central cation and ligands. As the expression shows, the D_q value is proportional to 1/R⁵, D_q decreases with the increase of R value or polyhedral volume and thus resulting in the emission blue-shift becoming larger. Any change in the composition of the host will change the strength of D_q, which in turn affects the luminescence efficiency, emission peak position, emission color, and PL intensity. These properties provide ideas and schemes for the regulation of Bi³⁺ ions, which makes it possible to tune the emission wavelength by changing the host lattice composition and designing the structure. In the series hosts of La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺, the homogeneously scattered Ta⁵⁺ ions have a great influence on the local electronic states, especially around the emission centers. From the specific analysis of fluorescence properties and XPS spectra of Bi³⁺ and O²⁻, it can be concluded that the substituted Ta⁵⁺ ion has changed the local electronic states of emission centers, resulting in dual-wavelength emission.

The two emission centers have a great influence on thermal quenching behaviors. Thus, the luminescence spectra of La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺ and La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺ with the temperature-dependent from 303 K to 493 K under the 303 nm excitation are studied and illustrated in Figs. 6a-d. The emission intensities from the two emission centers decrease with the temperature rising, owing to the gradually stronger non-radiative effects. Both the blue-light and green-light emissions display decreased intensity with increasing temperature; thus, no obvious correlation is observed between the temperature-dependent behavior of the two emissions. On the contrary, the two emissions display different thermal stability. The thermal stability of green-light emission is obviously better than that of blue-light emission, which further evidences the two emissions from different emission centers. Due to the lower emission intensity and the poorer thermal stability, the blue-light emission of La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺ completely disappears when the temperature reaches 443 K. Meanwhile, because of the higher emission intensity, La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺ could hold on to higher temperature (Figs. 6e and f). The thermal quenching mechanism of Bi³⁺ with two local electronic states is illustrated and presented in Figs. 6g and h. The thermal quenching of Bi³⁺ ion occurs through the energy level cross-relaxation (ELCR) between ¹S₀ and ³P₁ states. With increasing the temperature, the electron-phonon coupling is enhanced, and some electrons relax to the intersection of ¹S₀ and ³P₁ states to return to the ground state without radiative transition. The thermal activation energy (E_a) is the difference between the minimum energy of the ³P₁ and the intersection [35,36]. The E_a value of blue-light emitting is 0.42 eV, which is smaller than that of green-light emitting. Because Ta⁵⁺-substituted influences the energy levels to change the intersection of the two corresponding levels, leading to the two types of thermal quenching behavior. Besides, compared to the blue-light emission center surrounded by bigger [TaO₆], the green-light emission center surrounded by smaller [SbO₆] has tighter cell packing and fewer lattice defects, resulting in higher thermal stability.

Through the peak fitting analysis of the temperature-dependence PL spectra (Figs. S9 and S10 in Supporting information), it is appropriate to adopt a ratio of the integrated emission intensities of the blue-light and green-light energy emission peaks, which can be calculated using as following:

(6)

where I_blue and I_green represent the integrated emission intensities of the two emission peaks, respectively. The integration range is the data after Gaussian fitting analysis. As shown in Figs. 6c and f, the trend of the integrated intensity of the emission peak and good discrimination dual-wavelengths illustrate the possibility for optical temperature sensing based on FIR strategy. Herein, the visual dual-wavelength emitting La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺ and La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺ materials are chosen to further test the temperature-dependent property. A ratiometric fluorescence sensor can detect temperature based on the dual wavelength with different thermal-quenching performances.

The relationship of the FIR (I_blue/I_green) and temperature can be described as follows [37]:

(7)

where T refers to the absolute temperature; A, B and C denote the related constant parameters. In the field of luminescence thermometry, the absolute sensitivity (S_a) and relative sensitivity (S_r) are requisite parameters to measure the temperature performance, which can be calculated by the following equations:

(8)

(9)

As presented in Fig. 7a, the relation between FIR and temperature of La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺ can be expressed by the following formula:

(10)

Furthermore, as displayed in Fig. 7c, in the sample of La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺, the relation can between FIR and temperature is expressed by the following formula:

(11)

As demonstrated in Figs. 6b and d, the value of S_a and S_r increase initially and then reduce with the temperature increasing from 303 to 493 K. The maximum S_a value of La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺ reaches 0.00297 K^-1 at 330 K, while the S_r is 2.64%/K at 383 K. In contrast, the maximum S_a value of La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺ achieves 0.00361 K^-1 at 330 K, and the S_r reaches the maximum of 1.91%/K at 388 K. Based on the analysis of temperature performance and thermal stability, the designed La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺ phosphor has a higher S_r, but a narrower temperature measurement interval, compared with that of La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺.

Moreover, the temperature resolution (δ) is a thermometric parameter to evaluate the accuracy of the designed phosphors, which can be calculated by the following formula [38,39]:

(12)

where δ_FIR is determined to be the standard deviation for 30 circulations at room temperature, and δ_FIR/FIR refers to the relative error in the determination of the thermometric parameter (Figs. S11 and S12 in Supporting information). Results demonstrate that both temperature resolution of the developed La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺ and La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺ samples are below 0.005 K in the temperature range from 273 K to 383 K, and the maximum resolution is up to 0.023 K and 0.0119 K, respectively.

The emission spectral of the La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺ covered the blue-and-green area, which matches the demand of w-LED (white light-emitting diode). Therefore, we constructed a w-LED device using commercial red phosphors on an n-UV LED chip to evaluate the potential application [40,41]. A continuous broad emission from blue to red and emit warm lights can be obtained (Fig. S13 in Supporting information). The CCT and CRI of the fabricated w-LED are found to be 3482 K and 87.8, respectively. The photoelectric performance reveals the designed phosphors have potential application towards w-LED.

In summary, a series of blue-green color-tunable La₃Sb_1-xTa_xO₇:Bi³⁺ (0 ≤ x ≤ 1.0) phosphors were designed by the cationic substitution strategy. With the replacement of Ta⁵⁺ to Sb⁵⁺, the emission tremendously shifted from green to blue with 68 nm and the intensity was enhanced 2.6 times. Besides, as the Ta⁵⁺ substation concentration at 20% or 25%, a novel dual-wavelength emitting phosphor was achieved for optical temperature sensing based on the two emission centers with two local electronic states from Bi³⁺-doped La₃Sb_1-xTa_xO₇ (0 ≤ x ≤ 1.0) solid solution. The two local electronic states corresponding to the emission centers were managed via cationic substitution for realizing the dual-wavelength emitting of Bi³⁺ ions in the single host. The two emission peaks from their emission centers have distinguished thermal-quenching behaviors, which were further applied in the FIR optical temperature sensing. The dual-wavelength emitting peaks of La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺ and La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺ phosphors have different temperature-dependent emission characteristics, where the S_a and S_r were both discussed in the temperature range from 303 K to 483 K. The maximum values of S_r reach 2.64%/K (La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺@383 K) and 1.91%/K (La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺@388 K), relatively. The design of local electronic state modulation will provide a new strategy for developing novel multifunctional phosphors.

Declaration of competing interest

Less

The authors declare that they have no known competing financial interests or personal relationships that could have appeared to influence the work reported in this paper.

Acknowledgments

Less

This work was supported by the National Natural Science Foundation of China (Nos. 52072101, 51972088, 52172205), the Fundamental Research Funds for the Provincial Universities of Zhejiang (No. GK229909299001-003), the Postgraduate Research Innovation Fund of Hangzhou Dianzi University (No. CXJJ2022032).

Supplementary materials

Less

Supplementary material associated with this article can be found, in the online version, at doi:10.1016/j.cclet.2023.108447.

References

Less

[1]

C.D.S. Brites, S. Balabhadra, L.D. Carlos, Adv. Opt. Mater. 7 (2019) 1801239.

[2]

G. Kucsko, P.C. Maurer, N.Y. Yao, et al., Nature 500 (2013) 54–58.

[3]

G. Li, G. Li, Q. Mao, et al., Chem. Eng. J. 430 (2022) 132923.

[4]

B. Deng, S. Liu, C. Zhou, et al., Chem. Eur. J. 24 (2018) 11627.

[5]

P. Du, J. Tang, W. Li, L. Luo, Chem. Eng. J. 406 (2021) 127165.

[6]

Y. Gao, Y. Bando, Nature 415 (2002) 599.

[7]

G. Bao, K.L. Wong, D. Jin, P.A. Tanner, Light Sci. Appl. 7 (2018) 96.

[8]

X. Qiu, Q. Zhou, X. Zhu, et al., Nat. Commun. 11 (2020) 4.

[9]

J.R. Shakirova, N.N. Shevchenko, V.A. Baigildin, et al., ACS Appl. Polym. Mater. 2 (2020) 537–547.

[10]

M. Xu, X. Zou, Q. Su, et al., Nat. Commun. 9 (2018) 2698.

[11]

M.A. Hernández-Rodríguez, A.D. Lozano-Gorrín, I.R. Martín, U.R. Rodríguez-Mendoza, V. Lavín, Sens. Actuators B 255 (2018) 970–976.

[12]

G. Li, Y. Xue, Q. Mao, et al., Dalton Trans. 51 (2022) 4685–4694.

[13]

W. Liu, X. Wang, Q. Zhu, et al., Sci. Technol. Adv. Mater. 20 (2019) 949–963.

[14]

S.W. Long, S.P. Lin, D.C. Ma, et al., Photonics Res. 8 (2020) 135–142.

[15]

Miroslav D. Dramićanin, J. Appl. Phys. 128 (2020) 040902.

[16]

D. Liu, X. Yun, P. Dang, et al., Chem. Mater. 7 (2020) 3065–3077.

[17]

R.M. Friedman, J.D. Corbett, Inorg. Chem. 12 (1973) 1134–1139.

[18]

Y. Wang, J. Ding, Y. Wang, J. Am. Ceram. Soc. 100 (2017) 2612–2620.

[19]

L. Seijo, Z. Barandiaran, Phys. Chem. Chem. Phys. 16 (2014) 17305–17314.

[20]

F. Kang, M. Peng, D. Lei, Q. Zhang, Chem. Mater. 28 (2016) 7807–7815.

[21]

M. Zhao, H. Liao, M. Molokeev, et al., Light Sci. Appl. 8 (2019) 38.

[22]

F. Kang, G. Sun, P. Boutinaud, et al., J. Mater. Chem. C 7 (2019) 9865–9877.

[23]

Y. Wei, Z. Gao, X. Yun, et al., Chem. Mater. 32 (2020) 8747–8753.

[24]

P. Dang, D. Liu, G. Li, A. Kheraif, J. Lin, Adv. Opt. Mater. 8 (2020) 1901993–1902005.

[25]

D. Liu, P. Dang, X. Yun, et al., J. Mater. Chem. C 7 (2019) 13536–13547.

[26]

X. Shi, Y. Xue, Q. Mao, et al., Inorg. Chem. 62 (2023) 893–903.

[27]

M. Jain, P. Rajput, A. Vij, A. Thakur, J. Mater. Chem. C 10 (2022) 11379–11387.

[28]

F. Massee, Y.K. Huang, M. Aprili, Science 367 (2020) 6473.

[29]

P. Gao, Q. Li, C. Zhou, et al., Inorg. Chem. 61 (2022) 13104–13114.

[30]

Y. Wei, L. Cao, L. Lv, et al., Chem. Mater. 30 (2018) 2389–2399.

[31]

Q. Ma, G. Ning, Y. Xin, B. Shao, Inorg. Chem. Front. 8 (2021) 4072–4085.

[32]

B. Li, Z. Li, X. Wu, Z. Zhu, Nano Res. Energy 1 (2022) 9120011.

[33]

X. Shi, M. Zhang, X. Lu, et al., Mater. Today Chem. 27 (2023) 101264.

[34]

G. Li, Y. Zhao, Y. Wei, et al., Chem. Commun. 52 (2016) 3376–3379.

[35]

B. Zhao, Y. Chen, Y. Xue, et al., Mater. Des. 227 (2023) 111802.

[36]

Y. Ding, N. Guo, M. Zhu, et al., Mater. Res. Bull. 129 (2020) 110869.

[37]

J. Jin, J. Lin, Y. Huang, et al., Chin. Chem. Lett. 33 (2022) 4798–4802.

[38]

Y. Wang, Y. Sun, Z. Xia, J. Phys. Chem. Lett. 14 (2023) 178–182.

[39]

T. Hu, Y. Gao, M. Molokeev, Z. Xia, Q. Zhang, Sci. China Mater. 62 (2019) 1807–1814.

[40]

T. Li, Y. Zheng, C. Wu, et al., Chin. Chem. Lett. 33 (2022) 4238–4242.

[41]

J. Yang, C. Lei, X. Liu, et al., Acta Phys. Chim. Sin. 38 (2022) 2111020.

Appendix

Less

Year 2024 volume 35 Issue 3

PDF

Cite this Article

BibTeX

Article Info

doi: 10.1016/j.cclet.2023.108447

Receive Date：2023-02-21
Online Date：2025-11-20
Published：2024-03-15

Article Data

Affiliations

History

Received：2023-02-21
Revised：2023-03-08
Accepted：2023-04-12

Affiliations

^aCenter of Advanced Optoelectronic Materials, College of Materials and Environmental Engineering, Hangzhou Dianzi University, Hangzhou 310018, China

^bCollege of Electronics and Information, Hangzhou Dianzi University, Hangzhou 310018, China

^cDepartment of Chemistry, Zhejiang Sci-Tech University, Hangzhou 310018, China

References

Share

https://castjournals.cast.org.cn/joweb/ccl/EN/10.1016/j.cclet.2023.108447

Share to

Scan QR to access full text

Cite this article

BibTeX

Citations

表12种不同金属材料的力学参数

科 Family	属数 Number of genus	种数 Number of species	占总种数比例 Percentage of total species (%)	属 Genus	种数 Number of species	占总种数比例 Percentage of total species (%)
鹅膏菌科Amanitaceae	2	11	5.26	鹅膏菌属 Amanita	10	4.78
小菇科 Mycenaceae	2	12	5.74	丝盖伞属 Inocybe	5	2.39
多孔菌科 Polyporaceae	8	14	6.70	蜡蘑属 Laccaria	5	2.39
红菇科 Russulaceae	3	23	11.00	小皮伞属 Marasmius	6	2.87
				小菇属 Mycena	11	5.26
				光柄菇属 Pluteus	5	2.39
				红菇属 Russula	17	8.13
				栓菌属 Trametes	5	2.39

关闭全屏

BibTeX
EndNote
RefWorks
TxT

Fig. 1 Crystal-structural of La₃SbO₇:Bi³⁺. (a) Unit cell structures of La₃SbO₇ and La₃TaO₇. (b) Schematic diagram of Bi³⁺ doping in La1 position. (c) Schematic diagram of the substitution process.

Fig. 2 Crystal phase of La₃SbO₇:Bi³⁺. (a, b) XRD patterns of La₃SbO₇:yBi³⁺ (0.02 ≤ y ≤ 0.12) and La₃Sb_1-xTa_xO₇:0.04Bi³⁺ (0 ≤ x ≤ 1.0). (c-e) XRD Rietveld refinements of La₃SbO₇:0.04Bi³⁺ and La₃TaO₇:0.04Bi³⁺ and La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺. (f) Summary of cell parameters. (g) SEM and corresponding elemental mapping images of La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺.

Fig. 3 Optical properties and XPS spectra. (a) The diffuse reflection spectra of the La₃SbO₇, La₃TaO₇, La₃Sb_0.75Ta_0.25O₇ hosts, and the representative Bi³⁺ doped phosphors. (b, c) XPS spectra of the La₃SbO₇:0.04Bi³⁺, La₃TaO₇:0.04Bi³⁺ and La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺ samples. (d) PL spectra of the La₃SbO₇:yBi³⁺(0.02 ≤ y ≤ 0.12). (e) Normalized PL and PLE spectra of the La₃SbO₇:0.04Bi³⁺ and La₃TaO₇:0.04Bi³⁺. (f) PL spectra of La₃Sb_1-xTa_xO₇:0.04Bi³⁺ (0 ≤ x ≤ 1.0). (g) Normalized PL intensity and the peak position with various Ta⁵⁺ concentrations. (h) Normalized PL intensity of La₃Sb_1-xTa_xO₇:0.04Bi³⁺(0.05 ≤ x ≤ 0.25). (i) CIE chromaticity coordinates and luminescence photograph of La₃Sb_1-xTa_xO₇:0.04Bi³⁺ (0 ≤ x ≤ 1.0).

Fig. 4 Properties of bimodal emission. (a) Photoluminescence decay curve of the La₃SbO₇:yBi³⁺ (0.02 ≤ y ≤ 0.12) under 340 nm excitation. (b, c) Gaussian fitting of PL spectra of La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺ and La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺. (d) PL decay curve of the La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺, La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺, La₃SbO₇:0.04Bi³⁺ and La₃TaO₇:0.04Bi³⁺ samples under 340 nm excitation. (e, f) 3D contour map of PL spectra of the La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺ and La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺ under different excitation wavelengths.

Fig. 5 Schematic energy levels of free Bi³⁺ ion and emission tuning mechanism by changing crystal structure.

Fig. 6 Temperature-dependent characteristics of La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺ and La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺. (a, b) PL spectra from 303 K to 493 K, and (c, d) the corresponding two-dimension images. (e, f) Normalized emission intensity. (g, h) The quenching mechanism for the Bi³⁺ activator with blue-light and green-light emitting.

Fig. 7 Temperature measurement performance. (a) FIR (I_blue /I_green) of La₃Sb_0.8Ta_0.2O₇:0.04Bi³⁺between 303 K and 443 K. (b) The corresponding S_a and S_r values. (c) FIR (I_blue /I_green) of La₃Sb_0.75Ta_0.25O₇:0.04Bi³⁺ between 303 K and 483 K. (d) The corresponding S_a and S_r values are calculated between 303 K and 483 K.

Articles: Latest Articles; Most Read; Collections

Updates: Events; News; Multimedia

About: About Us

Contact

No. 86 Xueyuan South Road, Haidian District, Beijing

100081

010-62199257

qkjq@cast.org.cn

Copyright © 2025 China Association for Science and Technology. All rights reserved. For all open access content, the relevant licensing terms apply.
Sponsored by the Office of the Leading Group for Cybersecurity and Informatization of CAST, and supported by Science and Technology Review Publishing House