Under an external electric field, the polarization response within a material determines its dielectric constant, which is one of the crucial performance metrics for dielectrics [
1–
4]. For polymers, their complex hierarchical structures lead to diverse and often unpredictable polarization behaviors [
5–
7]. In particular, semicrystalline polymers are typically composed of both crystalline and amorphous regions, which exhibit intrinsically different responses to external electric fields [
8–
10]. In the crystalline domains, molecular chains are highly ordered and constrained within the lattice, and dielectric constant is limited by constrained dipole orientation [
11–
16]. In contrast, in the disordered regions, the chain-segmental motion is enabled, enhancing polarization [
17–
19]. This disparity between the two phases not only leads to pronounced frequency-dependent dielectric responses but also makes the dielectric performance of polymers highly sensitive to materials batch, processing methods, and post-treatment conditions [
8,
9,
20–
24].
Therefore, effectively decoupling the dielectric behaviors of crystalline and amorphous structures within such hierarchical systems and elucidating their respective contributions to the macroscopic dielectric properties constitute a key scientific challenge in understanding the origins and even the limits of performance in polymer dielectric materials. Generally, this disparity was often assessed through the frequency-dependent differences in dielectric constants between crystalline and amorphous phases, where the crystalline component was usually approximated using the value measured at high frequencies or low temperatures [
19,
25,
26]. While these qualitative insights provide empirical guidance, the evolution from qualitative observation to quantitative understanding of the origin of the materials properties has long been a fundamental driving force behind the advancement of materials science. This need has become more pronounced today, as the development of materials has been greatly accelerated by the application of data-driven and AI-assisted approaches, where physically interpretable and quantitatively reliable parameters as meaningful input for predictive modeling is required.
To address these challenges, polymer lamellar single crystals (PLSCs), serving as the basic building blocks of semicrystalline polymers [
27–
29], provide an ideal model system for isolating and characterizing the intrinsic dielectric response of the crystalline region.
The availability of large-area polymer single crystals is paramount to probing their intrinsic dielectric characteristics. However, the realization of these large-sized polymer single crystals has remained a persistent challenge. Although “self-seeding” crystallization technique enabled the production of lamellar polymer crystals with dimensions reaching tens of micrometers [
30,
31], sometimes with the largest size of one hundred micrometer through precise manipulation of crystallization parameters [
14], these crystals were typically too small for common dielectric characterization strategies. Furthermore, this method usually yields polymer crystals dispersed in solution, requiring additional transfer steps for device fabrication, which often causes damage to the ultrathin polymer crystals and complicates the vertical metal–insulator–metal (MIM) device construction. To address these challenges, in the present work, we developed a controlled solvent evaporation method that enables the direct deposition of large-area PLSCs onto the substrate.
Fundamentally, achieving large-area single crystals necessitates refined control of both nucleation and crystal growth kinetics. The conventional “self-seeding” method relies on precise temperature control to modulate the degree of supercooling, determining the thermodynamic driving force for crystallization and thereby influencing both nucleation and crystal growth processes. Solvent evaporation crystallization, in contrast, modulates supersaturation through leveraging increasing solute concentration driven by controlled solvent evaporation [
32–
35]. Then, the concentration profile of the crystal growth front can be precisely tuned by the evaporation rates. To achieve precise control over solvent evaporation, we designed a custom solution evaporation apparatus providing precise control over solvent evaporation (
Fig. 1a). The chamber atmosphere can be modulated
via a variable-force lid, applying greater force enhances the chamber’s sealing and thereby suppresses the evaporation rate.
Fig. S1 (Supporting information) summarized isotactic poly(1-butene) (iPB-1) lamellar single crystal morphologies at different total evaporation time (
tevap), with corresponding crystal number density (
N) and average lateral size (
l) data presented in
Figs. 1b and c respectively. Following solvent evaporation, the substrate was consistently covered in lozenge-shaped crystals. And the increasing
tevap from 4 h to 12 h resulted in
N gradually decreasing from 2.5 × 10
−4 µm
−2 to 2.9 × 10
−5 µm
−2, while average
l (long axis of lozenge-shaped crystals) increased from 32 µm to 183 µm, demonstrating that slower evaporation tends to reduce nucleation density and yield larger crystals.
Although further reducing the evaporation rate to achieve a
tevap of 16 h resulted in a larger average crystal size exceeding 200 µm, the prolonged crystallization time promotes competition between lateral growth and the formation of stacked layers [
32]. This multi-layer growth (Fig. S2 in Supporting information), along with the presence of screw dislocations, is not expected for the device fabrication and dielectric performance measurement. Therefore, to achieve both large size and uniformity, we optimized the evaporation time to 12 h, which yielded iPB-1 PLSCs with a maximum lateral size over 200 µm (
Fig. 2a). Atomic force microscopy (AFM) revealed that the large iPB-1 PLSCs possessed a uniform thickness of 9.91 nm (
Fig. 2b), with an average thickness of 10.15 ± 0.31 nm based on measurements of 10 crystals (Fig. S3 in Supporting information), consistent with previously reported values [
36]. As shown in
Fig. 2c, the crystallographic features of the obtained crystals were further investigated using selected area electron diffraction (SAED) analysis. The resulting SAED patterns were consistent with the [001] zone axis diffraction pattern of the form Ⅲ crystalline phase of iPB-1, characterized by a 4/1 helical conformation packed in an orthorhombic lattice (
Fig. 2d) [
37,
38]. The SAED data also indicated that the
c-axis (corresponding to the polymer chain direction) of these crystals was oriented perpendicular to the substrate. Form Ⅲ is a special metastable phase exhibiting a looser packed structure than the most common form Ⅰ, yet it is significantly more stable than the other metastable phase of form Ⅱ [
39–
41].
The dielectric constant (k) can be reliably determined through capacitance of vertical MIM parallel-plate capacitors. To realize MIM devices, we need to fabricate electrodes on both the top and bottom surfaces of the lamellar crystal, which was challenging for fragile, small-sized crystals (<100 µm) suspended in solvent that obtained through conventional “self-seeding” methods. Here, within controlled solvent evaporation method, large-area iPB-1 single crystals with lateral dimensions spanning several hundred micrometers were obtained. Furthermore, this controlled evaporation approach enabled direct deposition of the as-grown single crystals onto conductive substrates, thereby simplifying the fabrication of MIM capacitors.
As shown in
Fig. 3a, the MIM vertical parallel-plate capacitors were fabricated by first depositing a uniform 25 nm layer of gold onto silicon wafers
via thermal vapor deposition, which served as the conductive bottom electrode. Subsequently, iPB-1 PLSCs were grown directly on this gold electrode using a controlled solvent evaporation method. This
in-situ growth approach minimized the risk of transfer-induced damage and ensured intimate interfacial contact. The large iPB-1 PLSCs further enabled facile capacitor fabrication
via direct transfer of gold top electrodes onto selected regions.
And then the dielectric constant
k was determined by analyzing capacitor parameters from impedance measurements and applying the equation:
, where
C denotes the capacitance,
t is the thickness of the dielectric layer,
εn is the vacuum permittivity, and
A is the effective device area (
i.e., the overlap area between the top and bottom electrodes). The extracted dielectric constant
versus frequency from 25 capacitors were plotted in
Fig. 4a. The dielectric constant
k is approximately constant over a wide range of frequencies and has an average value of 1.82 ± 0.05 at 100 kHz. This astonishing value is much lower than the reported values of 2.10–2.53 for iPB-1 based materials [
26,
42–
44] and is also lower than most dense polymer dielectrics with a dielectric constant exceeding 2.0 [
7,
10,
45–
47]. To mitigate potential errors in dielectric constant determination arising from the small device area, we performed capacitance measurements on a series of devices with varying electrode areas (Figs. S4 and S5 in Supporting information) [
48]. As shown in
Fig. 4b, the proportional relationship between capacitance and area indicates that the
k value we derived is independent of device area and unaffected by area measurement errors. According to slope of
C-
A,
k was determined with the value of 1.79, consistent with the average value of 1.82 ± 0.05, confirming the validity of our method and the derived
k value of 1.82 ± 0.05 as the intrinsic dielectric constant of the iPB-1 PLSCs.
The dielectric constant quantifies a material’s ability to be polarized by an electric field. According to the Clausius-Mossotti relationship [
49], the dielectric constant
k of nonpolar dielectrics can be expressed as:
, where
α is the electronic polarizability,
N is the number of molecules per unit volume, and
εn is the vacuum permittivity. The Clausius-Mossotti equation dictates that
k decreases with decreasing polarizability (
α) or the number of molecules per unit volume (
N). As discussed previously, the highly ordered and densely packed polymer chains within the crystal lattice of PLSCs can significantly suppress chain segment motion and dipole orientation, reducing the dielectric’s polarizability (
α) and resulting in a lower
k. Furthermore, the unique crystal structure and molecular packing of form Ⅲ iPB-1 also contribute to its low
k. Form Ⅲ, a metastable phase with a more loosely packed arrangement of polymer chains than the commonly observed form Ⅰ, exhibits a Kitaigorodskii packing coefficient [
50] of 0.64 (compared to 0.68 for form Ⅰ) [
37], resulting in a corresponding density of 0.894 g/cm
3, approaching that of amorphous iPB-1 (0.868 g/cm
3) and significantly lower than form Ⅰ crystals (0.950 g/cm
3) [
51]. This difference in packing coefficients and densities suggests a higher void fraction within form Ⅲ crystals compared to form Ⅰ, leading to a lower
N and further reducing the dielectric constant. The synergistic effect of decreased polarizability and reduced molecular density therefore results in the characteristically low dielectric constant observed in form Ⅲ iPB-1 lamellar single crystals.
In summary, with the precise control over the solvent evaporation rate, we have successfully implemented a controlled solvent evaporation method to achieve the growth of large-area (over 200 µm lateral dimension), high-quality form Ⅲ iPB-1 PLSCs directly onto conductive substrates, which then simplified fabrication of MIM capacitors. Based on these MIM capacitors, the surprisingly low dielectric constant of 1.82 ± 0.05 at 100 kHz for the form Ⅲ iPB-1 single crystals was revealed. This exceptionally low value was attributed to a synergistic effect resulting from reduced molecular packing density of the special form Ⅲ polymorph and suppressed chain segment motion in the highly ordered crystalline structure. This work not only demonstrates a robust and efficient method for directly probing these intrinsic structure-property relationships via solvent evaporation crystallization and facile MIM capacitor fabrication but also indicates the critical role of crystal structure in governing the dielectric properties of semicrystalline polymers. These findings presented here holds great promise for the preparation and characterization of other polymeric single crystals, providing a valuable tool for mapping the relationship between crystal structure and dielectric properties in a wide variety of semicrystalline polymer dielectrics.
PDF
Full
78
43
关闭全屏
No. 86 Xueyuan South Road, Haidian District, Beijing
010-62662699(Operation and Technical Support)
qkjq@cast.org.cn