Sodium-ion batteries (SIBs) are considered the most promising large-scale energy storage technology, attributed to their abundant resources and low cost [
1,
2]. Hard carbon (HC) with low-cost and high-performance has been widely used as anodes materials [
3,
4]. However, HC still suffers from low initial Coulombic efficiency (ICE) and poor cycling stability, which are crucial for practical application [
5-
7]. Simply tuning the structure of HC anodes is insufficient to enhance their performance [
8-
10]. Notably, optimizing electrode/electrolyte interface
via constructing appropriate SEI is effective to improve HC performance [
11,
12].
Many studies have demonstrated that SEI has a significant impact on electrode performance [
13,
14]. During the SEI formation process, organic and inorganic components are generated. The organic SEI is relatively thick and uneven, which is broken and reconstructed during cycling process with SEI thickness increasing [
15,
16].
In situ interfacial characterization techniques revealed that the organic-dominated structure of the solid electrolyte interphase (SEI) leads to inferior mechanical strength. Furthermore, the dissolution of organic species causes the embedded inorganic components to lose structural support and subsequently detach, ultimately compromising the structural integrity of the entire SEI and rendering it unstable within the electrolyte environment [
17]. Thereby sodium ion transporting rate and cycling life decreases a lot. Constructed inorganic rich SEI can effectively improve the sodium storage performance and cycling stability of HC [
18,
19].
The composition and structure of SEI are often regulated by adjusting electrolyte components (such as high concentration electrolyte [
20], localized high-concentration electrolytes [
21]), however, the crucial role of electrode materials in SEI formation is neglected. The SEI composition can also be regulated by tuning intrinsic properties of material [
22,
23] and electronic properties of anodes [
24], which were linked with SEI composition [
25]. Gong
et al. reported an anion-reduction-catalysis strategy to obtain a inorganic rich SEI through coating tellurium nanosheets [
26]. Nonetheless, it is still very sticky to precisely regulate and achieve the targeted SEI in hard carbon.
Herein, we have designed a sp2 hybridized carbon rich (sp2–C) interface to suppress excessive adsorption and decomposition of solvents during the formation of SEI, thereby, inorganic-rich SEI is obtained successfully. The sp2–C delivers a low adsorption energy to solvent molecules forming anion rich interface structure. Consequently, the optimized anodes exhibit excellent performance with a high ICE of 91% and favorable sodium storage capacity of 346 mAh/g. The reaction kinetics and SEI structure are also illustrated carefully to understand the electrochemical processes.
The hard carbon (BHC) was purchased from Best Carbon Co., Ltd. Pitch powder was dissolved in an
N-methylpyrrolidone (NMP) solvent to prepare a 2 wt% solution. Subsequently, the hard carbon was mixed with varying masses of the pitch solution. After drying and carbonization, a surface-rich sp
2 carbon product (PHC) was obtained.
Fig. 1a illustrates the influence of orbital hybridization on distribution of solvent molecules and anions at interface. The sp
2/sp
3 carbon with abundant defects exhibits higher adsorption energy toward solvent molecules, leading to a greater concentration of solvent molecules at interface. More solvent decomposition forms an SEI film with a high organic content. In contrast, sp
2-rich carbon demonstrates weaker adsorption energy to solvent molecules, resulting in predominant anion accumulation at the interface, which corresponds to an SEI film characterized by elevated inorganic content. The formation of a thin and uniform inorganic-rich SEI film significantly enhances the interfacial stability of hard carbon anodes, thereby achieving superior initial coulombic efficiency and long-term cycling stability.
The Raman spectra of different samples are presented in
Fig. 1b and Fig. S1a (Supporting information). The G band corresponds to in-plane stretching vibration mode of carbon bonds, which is associated with graphitization degree [
27,
28], while D band originates from disorder-induced boundary vibration modes in hexagonal Brillouin zone and serves as an indicator of defects [
29]. The calculated intensity ratio A
G/A
D of based hard carbon (BHC) is 0.376, whereas pitch coated hard carbon (PHC) exhibits an increased value of 0.52, suggesting a higher content of surface sp
2 hybridized carbon. Further analysis
via X-ray photoelectron spectroscopy (XPS) elucidates surface chemical states of hard carbon. Deconvolution results (
Figs. 1c and
d) confirm a marked increase in sp
2 hybridized carbon content and a decrease in sp
3 hybridized carbon on the surface of PHC. While BHC exhibits more sp
3–C because of surface defects and irregular arrangement of carbon. The peak deconvolution results of O 1s XPS spectra for BHC and PHC samples are shown in Figs. S1b and c (Supporting information). Quantitative analysis reveals that the C=O peak area in PHC (4.75%) is lower than that in BHC (6.69%), while the C–O–C content increases from 52.37% (BHC) to 55.47% (PHC). These results indicate a reduction of C=O groups and an increase in C–O–C content on the PHC surface, which could weaken the adsorption of electrolyte solvent molecules and thereby enhance the ICE. Nitrogen adsorption-desorption isotherms (
Fig. 1e) reveal a specific surface area of 8.845 m
2/g for BHC, which decreases to 2.948 m
2/g for PHC because of less exposed micropores. The corresponding pore size distribution curves (Fig. S1d in Supporting information) demonstrate a significant reduction in larger open pores within PHC, effectively suppressing irreversible electrolyte decomposition, thereby enhancing the initial coulombic efficiency [
30]. The XRD patterns of samples (Fig. S1e in Supporting information) indicate no notable changes in their crystalline structures, only the surface chemistry was modulated.
The structural models of BHC and PHC systems are constructed as depicted in Figs. S2a and b (Supporting information) respectively. Differential charge density maps of Na
+-G2 group adsorbed on carbon layers (Figs. S2c and d in Supporting information) illustrate the electron transfer between Na
+-G2 and carbon. Notably, a critical comparison of adsorption energy is presented in
Fig. 1f, where BHC exhibits an adsorption energy of −0.29 eV and PHC demonstrates a reduced value of −0.08 eV. This indicates that sp
2-rich carbon effectively suppresses the adsorption quantity of solvent molecules at electrode-electrolyte interface, thereby mitigating excessive electrolyte decomposition and enhancing the ICE [
31]. As shown in Figs. S3a and b (Supporting information), for the ester-based solvent molecule ethylene carbonate (EC) and dimethyl carbonate (DMC), PHC still exhibits a relatively low adsorption energy than BHC. Fig. S3c (Supporting information) displays the first discharge curves of half-cells using 1 mol/L NaPF
6 in EC/DMC (1:1, v/v) electrolyte, showing an improvement in the ICE from 82.2% to 86.8%. Furthermore, contact angle measurements conducted on both electrodes (
Figs. 1g and
h). It reveals that the electrolyte exhibits a contact angle of 11.53° on BHC electrode surface, which increases to 17.24° on PHC electrode surface. Although contact angle is enlarged, the electrode can still maintain good wettability with electrolyte. This observation indicates that sp
2-rich carbon interface exhibits reduced adsorption energy toward electrolyte molecules, avoiding excessive decomposition of electrolyte.
The cyclic voltammetry (CV) curves of hard carbon/sodium half-cell (
Figs. 2a and
b) exhibit an irreversible reduction peak near 0.8 V, corresponding to decomposition of electrolyte at hard carbon surface to form a SEI film [
32-
34]. A pair of characteristic redox peaks appeared around 0.1 V, attributing to intercalation/deintercalation behavior of Na
+ within hard carbon layers [
35,
36]. In
Fig. 2b, the irreversible reduction peak near 0.8 V diminishes significantly, indicating suppressed irreversible electrolyte decomposition during the first discharge process, which contributes to improved ICE. The first discharge curve of hard carbon electrode (
Fig. 2c) comprises a typical sloping region and a plateau region. The BHC electrode delivers an ICE of 85% and a reversible discharge capacity of 323 mAh/g, while the PHC electrode demonstrates enhanced performance with an ICE of 91% and a reversible capacity of 346 mAh/g. Other samples were also tested by half cells and GCD curves were shown in Fig. S4 (Supporting information). When the coating layer is thin, the sp
2 carbon can effectively reduce the adsorption energy of solvent molecules, thus preventing excessive solvent decomposition and improving the initial coulombic efficiency. However, when the coating layer becomes excessively thick, the surface forms pitch-derived hard carbon with narrow interlayer spacing, which may lead to irreversible sodium ion intercalation, thereby reducing the ICE [
37]. Rate capability tests across various current densities (
Fig. 2d) reveal that PHC consistently exhibits higher discharge capacity than BHC. As shown in
Fig. 2e, the cycling performance at 0.3 A/g demonstrates a capacity retention of 98.9% for PHC after 200 cycles, surpassing the 94% retention of BHC. Compared with literature-reported values (
Fig. 2f), PHC achieves a superior combination of ICE and reversible capacity. To further evaluate cycling stability, long-term tests at 1 A/g reveal a capacity retention of 90.7% for PHC after 700 cycles, significantly higher than 83.8% retention observed for BHC (
Fig. 2g).
The cyclic voltammetry profiles at various scan rates are presented in
Fig. 3a. The CV peaks near 0.1 V exhibit minimal polarization voltage, suggesting favorable electrochemical behavior of Na
+. As calculated in
Fig. 3b, the capacitive contribution of PHC electrode accounts for 64.2% achieving better rate performance. Quantitative analysis of capacitive contribution at different scan rates (
Fig. 3c) reveals a gradual increase in capacitive dominance with elevated scan rates. Concurrently, the PHC electrode demonstrates significantly lower electrochemical impedance compared to BHC (
Fig. 3d). As shown in
Figs. 3e and
f, activation energy calculations derived from temperature-dependent impedance measurements indicate that Na
+ transfer through SEI activation energy for PHC (0.042 eV) is lower than that of BHC (0.062 eV), while electrochemical reaction activation energy of PHC (0.462 eV) is also reduced relative to BHC (0.478 eV). Lower activation energy is beneficial to accelerate sodium ions transfer, corresponding to better electrochemical performance. The galvanostatic intermittent titration technique (GITT) voltage-time profiles and corresponding diffusion coefficient profiles are depicted in
Figs. 3g and
h. The
DNa+ demonstrates a gradual decline in diffusion coefficients as the voltage decreases, reaching a minimum near 0.1 V, followed by a slight recovery at lower voltages under 0.1 V. While PHC delivers a analogous diffusion coefficient trend to BHC but higher values. Therefore, PHC electrode delivers a higher Na
+ transport rate, revealing a better sodium storage capacity in high current density.
X-ray photoelectron spectroscopy measurements were conducted on cycled electrodes to characterize the composition and structural features of SEI. As shown in
Figs. 4a and
d, the C–O and C=O peaks in C 1s spectrum of BHC electrodes exhibit greater intensity compared to those in PHC electrode, indicating a higher proportion of organic species within SEI [
14,
26]. The reduced sp
2–C content in BHC enhances its adsorption energy to solvent molecules, resulting in excessive decomposition of solvent (
Figs. 4b and
e). The F 1s profiles in
Figs. 4c and
f reveal that PHC contains a higher NaF content than BHC. This elevated inorganic component facilitates the formation of a favorable SEI layer, which is beneficial for long-term cycling stability. Figs. S5a and b (Supporting information) further demonstrate that SEI on PHC electrode contains a greater amount of NaF inorganic constituent. Specifically, the BHC surface exhibits a higher organic content and lower inorganic content in its SEI compared to PHC. More inorganic constituent can form a thin and firm SEI, keeping stable during cycles. While SEI with more organic component usually undergoes multiple crushing and rebuilding during cycle, resulting poor cycle life.
The PHC electrode was further assembled to be coin full-cell after cycling three times in HC/Na half-cell. The cathode material employed Na
2/3Ni
1/3Fe
1/3Mn
1/3O
2 (P2-NFM), while
Fig. 4g demonstrates half-cell performance of P2-NFM/Na and PHC/Na. Notably, the cathode exhibits a reversible capacity of 103 mAh/g. The charge-discharge profiles of full-cell presented in
Fig. 4h deliver a reversible capacity of 100 mAh/g at a current density of 0.1 C (1 C = 120 mA/g). As depicted in
Fig. 4i, P2-NFM/PHC full-cell demonstrates stable cycling performance at 0.2 C, maintaining a capacity retention rate of 84.1% after 250 cycles.
In summary, we propose a carbon orbital hybridization modulation strategy to regulate the hard carbon properties and design an interface layer enriched with sp2–C. Owing to lower adsorption energy of sp2–C toward solvent molecules compared to sp3–C, the interfacial region exhibits reduced solvent accumulation and enhanced anion enrichment. This interface effectively modulates the composition of SEI, forming an inorganic-rich SEI layer, which significantly improves ICE of hard carbon. Optimized PHC demonstrates a high ICE of 91% and a sodium storage capacity of 346 mAh/g. This work elucidates the critical role of carbon hybridization states in governing hard carbon performance, offering a novel design principle for high-performance hard carbon materials with substantial commercial potential.
PDF
Full
66
37
关闭全屏
No. 86 Xueyuan South Road, Haidian District, Beijing
010-62662699(Operation and Technical Support)
qkjq@cast.org.cn