燃料化学学报（中英文）

Formula	Melting temperature/°C	Melting enthalpy/(J·g⁻¹)	Thermal conductivity/(W·m⁻¹·K⁻¹)
C₁₄H₃₀	5.5	228	0.129
C₁₆H₃₄	16.7	237	0.130
C₁₈H₃₈	28.0	244	0.138
C₂₀H₄₂	36.7	246	0.137
C₂₂H₄₆	44	249	0.164
C₂₄H₅₀	50.6	255	0.156
C₂₆H₅₄	56.3	256	0.146
C₂₈H₅₈	61.6	253	0.147

Formula	Melting temperature/°C	Melting enthalpy/(J·g⁻¹)	Thermal conductivity/(W·m⁻¹·K⁻¹)
C₁₄H₃₀	5.5	228	0.129
C₁₆H₃₄	16.7	237	0.130
C₁₈H₃₈	28.0	244	0.138
C₂₀H₄₂	36.7	246	0.137
C₂₂H₄₆	44	249	0.164
C₂₄H₅₀	50.6	255	0.156
C₂₆H₅₄	56.3	256	0.146
C₂₈H₅₈	61.6	253	0.147

Classification	Formula	Melting temperature/°C	Melting enthalpy/(J·g⁻¹)	Volumetric energy density/(kW·h·m⁻³)
Erythritol	C₄H₁₀O₄	118.9	332.3	133.9
Xylitol	C₅H₁₂O₅	93.4	237.5	100.2
Inositol	C₆H₁₂O₆	224.3	256.3	124.6
Mannitol	C₆H₁₄O₆	166.1	281.1	124.5
Sorbitol	C₆H₁₄O₆	99.4	184.4	34.9
Galactitol	C₆H₁₄O₆	186-187	330.0	117.5

Classification	Formula	Melting temperature/°C	Melting enthalpy/(J·g⁻¹)	Volumetric energy density/(kW·h·m⁻³)
Erythritol	C₄H₁₀O₄	118.9	332.3	133.9
Xylitol	C₅H₁₂O₅	93.4	237.5	100.2
Inositol	C₆H₁₂O₆	224.3	256.3	124.6
Mannitol	C₆H₁₄O₆	166.1	281.1	124.5
Sorbitol	C₆H₁₄O₆	99.4	184.4	34.9
Galactitol	C₆H₁₄O₆	186-187	330.0	117.5

Formula	Melting temperature/°C	Melting enthalpy/(J·g⁻¹)	Thermal conductivity/(W·m⁻¹·K⁻¹)	Maximum operational temperature/°C
C₈H₁₆O₂	16.2	154.1	0.1872	153.6
C₁₀H₂₀O₂	28.8	172.9	0.2133	163.7
C₁₂H₂₄O₂	43.1	192.9	0.2388	180.7
C₁₄H₂₈O₂	53.6	213.3	0.2662	203.5
C₁₆H₃₂O₂	61.4	222.9	0.2881	208.2
C₁₈H₃₆O₂	68.2	229.4	0.3079	224.2

Formula	Melting temperature/°C	Melting enthalpy/(J·g⁻¹)	Thermal conductivity/(W·m⁻¹·K⁻¹)	Maximum operational temperature/°C
C₈H₁₆O₂	16.2	154.1	0.1872	153.6
C₁₀H₂₀O₂	28.8	172.9	0.2133	163.7
C₁₂H₂₄O₂	43.1	192.9	0.2388	180.7
C₁₄H₂₈O₂	53.6	213.3	0.2662	203.5
C₁₆H₃₂O₂	61.4	222.9	0.2881	208.2
C₁₈H₃₆O₂	68.2	229.4	0.3079	224.2

Classification	Example	Mechanism	Advantage	Disadvantage
Halogenated flame retardants	Chlorinated paraffins (CP), polybrominated diphenyl ethers (PBDEs), hexabromocyclododecane (HBCD)	Halogen free radicals are generated during combustion, which can rapidly capture ·H and ·OH	Efficiency, good thermal stability, and good compatibility	Produces corrosive and toxic fumes
Nitrogen flame retardants	Triazine compounds melamine, dicyandiamide, guanidine salts and melamine cyanurate	Releasing non-flammable gases, absorbing heat, diluting oxygen	Safe, non-toxic, and broadly applicable	Inefficiency when used alone, synergistic with N-/P-based flame retardants
Silicon flame retardant	SiO₂, Halloysite nanotubes (HNT), Oxidized montmorillonite (OMT), silicone resin (SR) and polysiloxane (PSO)	Promoting polymer degradation forms a protective layer based on Si−O and Si−C bonds, suppressing the diffusion of heat and oxygen	Processability and environment- friendly	Poor dispersion, high cost, susceptible to moisture and heat
Phosphorus flame retardant	Red phosphorus, phosphorus oxychloride (POCl₃) and phosphorus black (PB)	·PO and ·PO₂ radicals were generated during combustion, and ·H and ·OH were captured	Low smoke, high process stability and good thermal stability	High cost, low degradation rate and environmentally unfriendly
Metal hydroxide	Mg(OH)₂, Al(OH)₃	It aecomposes to absorb heat and releases water vapor, forming a metal oxide protective layer that reduces heat transfer	Lower price, non-toxic and environmental protection	Poor compatibility and inefficiency
Intumescent flame retardant	Ammonium polyphosphate (APP), pentaerythritol (PER) and melamine	Form foam and Carbonization layer on the surface to prevent the underlying material from further exposure to ignition	Low smoke, non-toxic and efficient	Poor compatibility, affecting mechanical properties

Classification	Example	Mechanism	Advantage	Disadvantage
Halogenated flame retardants	Chlorinated paraffins (CP), polybrominated diphenyl ethers (PBDEs), hexabromocyclododecane (HBCD)	Halogen free radicals are generated during combustion, which can rapidly capture ·H and ·OH	Efficiency, good thermal stability, and good compatibility	Produces corrosive and toxic fumes
Nitrogen flame retardants	Triazine compounds melamine, dicyandiamide, guanidine salts and melamine cyanurate	Releasing non-flammable gases, absorbing heat, diluting oxygen	Safe, non-toxic, and broadly applicable	Inefficiency when used alone, synergistic with N-/P-based flame retardants
Silicon flame retardant	SiO₂, Halloysite nanotubes (HNT), Oxidized montmorillonite (OMT), silicone resin (SR) and polysiloxane (PSO)	Promoting polymer degradation forms a protective layer based on Si−O and Si−C bonds, suppressing the diffusion of heat and oxygen	Processability and environment- friendly	Poor dispersion, high cost, susceptible to moisture and heat
Phosphorus flame retardant	Red phosphorus, phosphorus oxychloride (POCl₃) and phosphorus black (PB)	·PO and ·PO₂ radicals were generated during combustion, and ·H and ·OH were captured	Low smoke, high process stability and good thermal stability	High cost, low degradation rate and environmentally unfriendly
Metal hydroxide	Mg(OH)₂, Al(OH)₃	It aecomposes to absorb heat and releases water vapor, forming a metal oxide protective layer that reduces heat transfer	Lower price, non-toxic and environmental protection	Poor compatibility and inefficiency
Intumescent flame retardant	Ammonium polyphosphate (APP), pentaerythritol (PER) and melamine	Form foam and Carbonization layer on the surface to prevent the underlying material from further exposure to ignition	Low smoke, non-toxic and efficient	Poor compatibility, affecting mechanical properties

有机相变储能材料性能优化研究进展

PDF下载

杨瑞豪 ¹ , 陈晓燕 ² , 梁林锋 ¹ , 张伟 ² , 石利红 ¹ , 陈从标 ² , 王永钊 ¹ , 王俊刚 ² , 赵江红 ¹ , 侯博 ²^,^* , 周玮 ¹^,^*

燃料化学学报（中英文） | 综合评述 2026,54(9): 20250351-1788-20250351-1805

收起

燃料化学学报（中英文） |综合评述 2026 , 54 (9) : 20250351-1788 -20250351-1805

有机相变储能材料性能优化研究进展

全屏

杨瑞豪¹, 陈晓燕², 梁林锋¹, 张伟², 石利红¹, 陈从标², 王永钊¹, 王俊刚², 赵江红¹, 侯博²^,^*, 周玮¹^,^*

作者信息

¹山西大学化学化工学院, 山西太原 030006

²中国科学院山西煤炭化学研究所煤炭高效低碳利用全国重点实验室, 山西太原 030001

通讯作者:

侯博, 周玮

Research progress on performance optimization of organic phase change materials

Ruihao YANG¹, Xiaoyan CHEN², Linfeng LIANG¹, Wei ZHANG², Lihong SHI¹, Congbiao CHEN², Yongzhao WANG¹, Jungang WANG², Jianghong ZHAO¹, Bo HOU²^,^*, Wei ZHOU¹^,^*

Affiliations

¹College of Chemistry and Chemical Engineering, Shanxi University, Taiyuan 030006, China

²State Key Laboratory of Coal Conversion, Institute of Coal Chemistry, Chinese Academy of Sciences, Taiyuan 030001, China

Corresponding Author:

E-mail: houbo@sxicc.ac.cn

zhouwei@sxu.edu.cn

出版时间: 2026-09-10 doi: 10.3724/2097-213X.2025.JFCT.0038

文章导航

摘要

收起

有机相变材料（PCMs）因其优异的能量存储特性，在热管理和能源存储领域具有广泛应用。本工作综述了有机PCMs的主要类型及其性能优化策略。在热物性调控方面，介绍了通过构建共晶体系、调控分子结构及添加纳米颗粒等方式调节相变温度与潜热。在导热增强方面，总结了与零维、一维、二维及三维结构高导热材料复合的策略。还针对有机PCMs存在的过冷现象和易燃性问题，分析了相应的抑制过冷方法与阻燃改性技术。展望了有机相变材料的发展方向，随着技术的突破，有机相变材料将在能源存储和热管理等领域得到更广泛应用。

关键词

有机相变材料 / 潜热 / 导热性能 / 阻燃性

Abstract

收起

Organic phase change materials (PCMs), known for their excellent energy storage properties, have been widely applied in thermal management and energy storage fields. This review summarizes the main types and performance optimization strategies of organic PCMs. In terms of thermophysical property regulation, methods such as constructing eutectic systems, modifying molecular structures and incorporating nanoparticles to adjust phase change temperature and latent heat are introduced. For thermal conductivity enhancement, strategies involving composites with zero-, one-, two- and three-dimensional high thermal conductivity materials are reviewed. Additionally, countermeasures for common issues like supercooling and flammability of organic PCMs are analyzed, including methods to suppress supercooling and flame-retardant modification techniques. Finally, future development directions of organic PCMs are discussed, highlighting their broader application prospects in energy storage and thermal management as technology advances.

Key words

organic phase change materials / latent heat / thermal conductivity / flame retardancy

引用本文

杨瑞豪, 陈晓燕, 梁林锋, 张伟, 石利红, 陈从标, 王永钊, 王俊刚, 赵江红, 侯博, 周玮. 有机相变储能材料性能优化研究进展. 燃料化学学报（中英文）, 2026 , 54 (9) : 20250351-1788 -20250351-1805 . DOI: 10.3724/2097-213X.2025.JFCT.0038

Ruihao YANG, Xiaoyan CHEN, Linfeng LIANG, Wei ZHANG, Lihong SHI, Congbiao CHEN, Yongzhao WANG, Jungang WANG, Jianghong ZHAO, Bo HOU, Wei ZHOU. Research progress on performance optimization of organic phase change materials[J]. Journal of Fuel Chemistry and Technology, 2026 , 54 (9) : 20250351-1788 -20250351-1805 . DOI: 10.3724/2097-213X.2025.JFCT.0038

正文

收起

Phase change materials (PCMs) are a type of materials that store and release energy by absorbing or releasing heat when a substance undergoes a phase change at a specific temperature. Unlike sensible heat storage materials that rely on temperature gradients for energy accumulation, PCMs facilitate high-density energy management through nearly isothermal processes, thereby enabling more efficient thermal buffering and regulation^[1−2]. Generally, PCMs are categorized into organic and inorganic variants. Compared to the inorganic counterparts, organic PCMs possess exceptional chemical inertness, non-corrosivity and long-term cycling robustness^[3]. Crucially, organic PCMs exhibit minimal subcooling and are inherently free from phase segregation—common bottlenecks for inorganic systems. Furthermore, organic PCMs align with green chemistry principles due to their low toxicity and biodegradability, while offering modular tunability of phase transition temperatures across a broad spectrum through eutectic or mixture engineering^[4].

This review provides a comprehensive synthesis of the classifications, fundamental properties, and key performance metrics of organic PCMs, with a particular focus on recent paradigms for their performance optimization.

1　Types of organic PCMs

收起

Organic PCMs exhibit extensive application potential in thermal energy storage and temperature regulation due to their diverse compositions, tunable phase change temperature ranges and high latent heat. However, the significant differences in molecular structure, phase change behavior and thermophysical properties among different organic PCMs have greatly influenced their performance and applicability. Therefore, it is essential to systematically categorize these materials and outline their characteristics. Based on their chemical compositions, organic PCMs are classified into three categories: paraffins, polyols and fatty acids. The fundamental features of each category are summarized.

1.1　Paraffins

Based on their chemical composition, paraffin PCMs can be divided into two categories: pure linear alkanes with the general formula C_nH_2n+2, and hydrocarbon mixtures^[5]. The latter is more cost-effective than pure alkanes and is widely utilized for energy storage, as its melting point can be tailored by blending alkanes with varying chain lengths^[6]. As the number of carbon atoms increases, the melting temperature of paraffin exhibits an upward trend, providing a highly flexible phase change temperature range^[7]. Furthermore, paraffins with self-nucleating behavior can resistant to severe supercooling or phase separation, making them as ideal PCMs. However, their intrinsically low thermal conductivity severely restricts the rates of thermal energy absorption and release^[8−10]. The performance parameters of representative linear alkane PCMs are summarized in Table 1^[11].

Paraffin-based PCMs play a crucial role across various sectors due to their efficient heat storage capabilities. In the construction industry, they are integrated into building materials to regulate indoor temperatures and reduce heating energy consumption. In solar energy utilization, they serve as heat storage media in solar water heating or space heating systems, storing surplus solar energy during the day for the utilization at night or on cloudy days, thereby enhancing overall solar utilization efficiency^[12]. Regarding the thermal management of electronic devices, paraffins can rapidly absorb transient peak heat generated by electronic components (e.g., CPUs, batteries), effectively preventing thermal runaway^[13]. Additionally, paraffin PCMs are employed in cold chain logistics to maintain stable low-temperature environments in cold storage or insulated containers^[14]. Kahwaji et al.^[6] evaluated six paraffin PCMs with melting points ranging from 30 to 60 °C highlighting their potential for building applications, solar thermal storage, and passive cooling-by investigating their thermophysical properties, thermal stability and chemical compatibility. The results demonstrated high latent heats of fusion across all materials, ranging from 150–200 J/g for commercial paraffins and exceeding 200 J/g for pure alkanes. Long-term cycling tests revealed that both pure paraffins and mixtures maintained excellent thermal stability after 3000 melt-freeze cycles, with no significant degradation in melting point or latent heat. Chemical compatibility with nine metal alloys and seven plastics was assessed via corrosion immersion tests. While all tested metals exhibited good compatibility with paraffin, Cu 101 and Mg AZ91D samples displayed oxidation after 12 weeks of immersion at 75 °C. Certain plastics (e.g., polycarbonate, Type I PVC, and ABS) demonstrated good compatibility at 75 °C, whereas silicone rubber and polypropylene were deemed unsuitable due to excessive PCM absorption.

1.2　Polyols

Polyols are compounds containing two or more hydroxyl groups per molecule. Due to the unique molecular structures, polyols exhibit excellent thermal stability, environmental friendliness, and high phase change heat capacity. Common polyol PCMs include polyethylene glycol (PEG), neopentyl glycol (NPG), pentaerythritol (PE), tris(hydroxymethyl)aminomethane (TAM) and sugar alcohols (SAs).

As an organic PCM, PEG holds the characterization of high phase change enthalpy, chemical and thermal stability, biodegradability, non-toxicity, non-corrosiveness and low vapor pressure. Notably, its properties can be precisely tailored by controlling its molecular weight^[15]. Xu et al.^[16] prepared bio-based composite PCMs (CPCMs) by using diatomite as the supporting matrix, expanded graphite (EG) as an additive and PEG as the phase change medium. With an additive mass fraction (w) of 10%, the composite exhibited a melting enthalpy of 116.81 J/g and a crystallization enthalpy of 118.44 J/g. Gao et al.^[17] fabricated shape-stabilized PCMs via vacuum impregnation, using PEG as the energy storage material to yield sunflower stem carbon/PEG (SS-PEG) and sunflower receptacle carbon/PEG (SR-PEG) composites. The melting enthalpies of SS-PEG and SR-PEG were 153.4 and 171.5 J/g, with initial thermal decomposition temperatures of 344 and 368 °C, respectively.

NPG, PE and TAM are typically preferred as solid-solid PCMs. During the solid-solid phase change, they exhibit high enthalpies of transition and possess inherent advantages, including minimal volume variation, absence of liquid or gas generation, zero leakage risk and the ability to be molded into desired shapes^[18]. Wang et al.^[19] fabricated composite PCMs by integrating NPG with compressed expanded natural graphite (CENG) of varying densities. DSC results indicated that the latent heat of the NPG/CENG composites increased proportionally with the NPG mass ratio, achieving values between 75 and 106 J/g. Wang et al.^[20] pioneered the encapsulation of PE by using silicon dioxide (SiO₂) as a shell material via sol-gel technology to form a spherical core-shell structure. The PE-SiO₂ composite presented an average size of 0.3 μm, an encapsulation efficiency exceeding 77.8% and a latent heat reaching 255 kJ/kg. After 100 heating-cooling cycles, the latent heat degraded by less than 5%.

The history of sugar alcohols as PCMs is relatively brief, with the first application in thermal energy storage dating back to 1981^[21]. Compared to conventional PCMs (e.g., paraffins), sugar alcohols possess higher volumetric latent heat. Derived from natural sources, they are non-flammable, non-toxic, non-corrosive, and cost-effective. As a new generation of PCMs^[22], they demonstrate great potential. Despite their favorable thermal properties, certain sugar alcohols exhibit severe supercooling during crystallization. Shao et al.^[23] utilized DSC to measure the degree of supercooling for erythritol, d-mannitol, d-dulcitol and myo-inositol, recording values of 89, 48, 66 and 38 °C, respectively. This pronounced supercooling phenomenon prevents the timely release of stored latent heat, causing temperature mismatch during the charge-discharge cycles and subsequently reducing thermal energy utilization efficiency^[24]. Regarding thermal stability, Kaizawa et al.^[25] employed thermogravimetric analysis to determine the thermal decomposition points of erythritol, mannitol, xylitol, and sorbitol, which were 160, 280, 200 and 240 °C, respectively. Tomassetti et al.^[26] reviewed the thermophysical properties and thermal stability of six SAs (xylitol, sorbitol, erythritol, mannitol, inositol, and dulcitol). Literature provides several thermal stability analyses for erythritol and mannitol, revealing that erythritol exhibits the highest thermal stability, whereas mannitol remains unstable even under an inert atmosphere. The evaluation of other SAs remains highly limited, and existing literature reports inconsistent findings regarding their thermal stability. The phase change parameters of selected sugar alcohols are detailed in Table 2^[27].

1.3　Fatty acids

Fatty acids, with the general formula C_nH_2n+1COOH, can be extracted from biomass or synthesized chemically. Their amphiphilic molecular structure facilitates excellent interfacial interactions with most functional fillers. They possess moderate latent heats of fusion, and their phase change temperatures can be systematically adjusted by altering the fatty acid composition. The presence of polar functional groups in fatty acid PCMs promotes hydrogen bond formation, enhancing their compatibility with other materials and thereby improving their performance in composite systems^[28]. Common PCMs within the fatty acid family include capric acid, myristic acid, lauric acid, palmitic acid and stearic acid. Their primary advantages include high latent heat, robust thermal stability, zero supercooling, and low cost^[29]. Xie et al.^[30] measured the phase change parameters, thermal stability, and thermal conductivity of a series of fatty acids (octanoic, decanoic, dodecanoic, tetradecanoic, hexadecanoic, and octadecanoic acids). The corresponding results are presented in Table 3.

2　Performance optimization of organic PCMs

收起

Organic PCMs (including paraffins, polyols and fatty acids) with distinct characteristics in chemical composition, phase change mechanisms, and thermophysical properties enable them to fulfill diverse application requirements ranging from low-temperature energy storage to medium-temperature thermal management. However, the practical implementation is hindered by several limitations, such as inflexible phase change temperatures, insufficient latent heat, inherently low thermal conductivity, pronounced supercooling and safety risks associated with flammability. Consequently, utilizing these materials in their pristine state is insufficient for engineering applications. It is imperative to systematically enhance their performance through multi-scale material design strategies. This section reviews current primary performance optimization strategies for organic PCMs, focusing on phase change behavior regulation, thermal conductive network construction, nucleation site introduction and flame-retardant technology optimization.

2.1　Phase transition temperature and latent heat regulation

The most critical parameters of a PCM are phase change temperature and latent heat. The phase change temperature dictates the applicable scenarios for the PCMs, such as cold storage (7−15 °C), space heating equipment (40−50 °C), and solar cooling and heating (80−90 °C)^[31]. High latent heat means that the material can store or release substantial amounts of thermal energy without undergoing significant temperature fluctuations^[32]. Modulating the phase change temperature and latent heat is essential to adapt PCMs for diverse practical applications.

2.1.1　Eutectic PCMs

Eutectic PCMs are mixtures of two or more component PCMs that melt at a single, congruent temperature lower than the melting point of any individual constituent. This unique characteristic makes eutectic PCMs exceptionally suitable for targeting specific phase change temperature ranges that are unattainable by single-component PCMs^[33]. By fabricating various eutectic systems of organic PCMs, both the phase change temperature and latent heat can be easily manipulated. The phase transition process of a eutectic PCM complies with the second law of thermodynamics and phase equilibrium theory. The liquidus line of a binary PCM system can be described by the following equation^[34]:

$ \begin{matrix}-\dfrac{{H}_{{\mathrm{A}}}}{{T}_{{\mathrm{A}}}}\left({T}_{{\mathrm{m}}}-{T}_{{\mathrm{A}}}\right)+R{T}_{{\mathrm{m}}}\ln\left({X}_{{\mathrm{A}}}\right)+{G}_{{\mathrm{A,ex}}}=0 \end{matrix} $

(1)

$ \begin{matrix}-\dfrac{H_{\mathrm{B}}}{T_{\mathrm{B}}}\left(T_{\mathrm{m}}-T_{\mathrm{B}}\right)+RT_{\mathrm{m}}\ln\left(X_{\mathrm{B}}\right)+G_{\mathrm{B,ex}}=0\end{matrix} $

(2)

where H_A and H_B represent the enthalpies of components A and B (kJ/kg), respectively; T_A, T_B and T_m denote the melting points of components A, B and the mixture (K); X_A and X_B are the mole fractions of components A and B; G_A,ex and G_B,ex are the excess enthalpies of components A and B (kJ/kg); R is the universal gas constant (J/(mol·K)).

For organic compounds such as alkanes or alkanoic acids, it can be reasonably assumed that ideal mixing occurs, wherein G_A,ex = G_B,ex = 0. The aforementioned equation can thus be simplified to^[35−36]:

$\begin{matrix}{T}_{{\mathrm{m}}}={\left(\dfrac{1}{{T}_{{\mathrm{m}}}}-\dfrac{R \ln {X}_{i}}{{H}_{i}}\right)}^{-1}\left(i={\mathrm{A,B}}\right) \end{matrix}$

(3)

By utilizing this simplified equation, the phase diagram can be plotted, and the eutectic point of the binary system can be mathematically determined. The latent heat of the binary system can be calculated using the following theoretical formulation:

$\begin{matrix}{H}_{{\mathrm{m}}}={T}_{{\mathrm{m}}}\left(\dfrac{{X}_{{\mathrm{A}}}{H}_{{\mathrm{A}}}}{{T}_{{\mathrm{A}}}}+\dfrac{{X}_{{\mathrm{B}}}{H}_{{\mathrm{B}}}}{{T}_{{\mathrm{B}}}}\right)\end{matrix} $

(4)

By solving these thermodynamic equations simultaneously, the eutectic point and the theoretical latent heat of the eutectic system can be determined.

Sari et al.^[37] prepared eutectic PCMs using n-alkanes including heptadecane (C₁₇), octadecane (C₁₈), nonadecane (C₁₉) and tetracosane (C₂₄). The formulated eutectic PCMs, with compositions and mass percentages of C₁₇−C₂₄ (90%−10%), C₁₉−C₁₈ (5%−95%), C₁₉−C₂₄ (95%−5%) and C₂₀−C₂₄ (90%−10%), exhibited DSC-measured melting points of 19.24, 25.15, 32.20 and 35.80 °C, respectively, alongside latent heats of fusion of 171.14, 180.25, 187.90 and 265.60 J/g. Duraipandi et al.^[38] developed a novel eutectic PCM composed of palmitic acid and sebacic acid (PA-SA). DSC analysis determined the melting point and latent heat of the PA-SA eutectic PCM to be 61.10 °C and 161.14 J/g, respectively. Baran et al.^[39] synthesized a binary eutectic system by blending palmitic acid and stearic acid at a mass ratio of 64.2∶35.8. The resultant eutectic mixture demonstrated a phase change temperature of 52.3 °C and a latent heat of 181.7 J/g.

2.1.2　Molecular structure regulation

Modifying materials at the molecular level by chemical methodologies is an effective strategy to intrinsically control phase change temperature and latent heat. During the phase transition process, parameters such as molecular weight and the dynamics of hydrogen bond formation and dissociation are paramount; they dictate intermolecular forces, which subsequently govern the thermal properties^[40]. By systematically tuning chain lengths, molecular weights, and the types of grafted moieties, the phase change parameters of PCMs can be precisely engineered to meet specific application demands. For instance, the phase change performance of a PCM can be tailored by grafting alkyl chains or utilizing PEG of varying molecular weights^[41].

Liu et al.^[42] synthesized a series of polypropylene-g-maleic anhydride-g-C_nH_2n+1OH (PMCn, n = 18, 22, 26) comb-like polymeric solid-solid phase change materials (CPCMs) via a solvent-free esterification reaction between polypropylene-grafted maleic anhydride (PP-g-MAH) and normal alkanols with side chain lengths of n=18, 22 and 26. The synthesis process of the CPCMs is illustrated in Figure 1. The pendant alkyl side chains distributed along the PP-g-MAH backbone exhibited distinct side-chain crystallization behavior. As the side-chain length increased, the phase change temperature of PMCn escalated from 60.0 to 82.2 °C, while the phase change enthalpy increased from 53.6 to 118.4 J/g.

Kong et al.^[43] successfully grafted acrylic acid onto starch to fabricate a superabsorbent resin (SAR). At a starch addition level of 10% (w/w), the latent heat reached 330.4 J/g, approximately 1.1 times higher than that of the pristine sample without starch. Liu et al.^[44] synthesized two azo compounds (T-Azo and F-Azo) appended with different alkyl chains. Following trans-to-cis isomerization, the short-chain T-Azo exhibited a drastically reduced crystallization temperature of −6.3 °C, compared to 8.2 °C for F-Azo. Furthermore, the combined photothermal energy release and phase change enthalpy of F-Azo achieved a high energy density of 198.4 J/g, outperforming T-Azo (170.5 J/g) by 16%.

2.1.3　Adding nanoparticles

Recent studies have revealed that incorporating specific quantities of nanoparticles (such as nanocarbon materials or metal oxide nanoparticles) into PCMs can paradoxically induce an elevation in the phase change enthalpy of the resulting composites. This influence of nanoparticles on phase change enthalpy can be fundamentally understood as a competitive interplay between enhanced interfacial interactions and the adverse effects of mass substitution and crystallization disruption. The introduction of nanoparticles alters the interfacial molecular interaction network within the PCM, thereby impacting its solid-liquid phase change enthalpy. Upon nanoparticle incorporation, novel interfacial interactions emerge between the nanoparticle surface and the PCM molecular chains. Under conditions of strong interfacial affinity and excellent particle dispersion, the system must absorb supplementary energy during the melting process to overcome these interfacial constraints. When this surplus energy exceeds the enthalpy contribution lost by the fraction of PCM replaced by the nanomaterials, the overall system manifests an enhanced phase change enthalpy^[45−46].

Emeema et al.^[9] uniformly dispersed carbon quantum dots (CQDs) into paraffin to formulate composite PCMs. Compared to pristine paraffin, the latent heat of the composite PCMs was consistently augmented. Notably, at a CQD mass fraction of 1%, the latent heat experienced a remarkable 65.1% enhancement. Sahan et al.^[47] fabricated paraffin nanocomposites by embedding Fe₃O₄ nanoparticles into a paraffin matrix. At a Fe₃O₄ loading of w = 10%, the latent heat of the paraffin increased by 27%. This enhancement was primarily attributed to the intensified intermolecular forces induced by the high specific surface area of the nanomaterials. Furthermore, X-ray diffraction analysis indicated the presence of defect sites on the Fe₃O₄ surface, which likely generated supplementary interfacial interactions between the nanoparticles and the paraffin, thereby elevating the overall enthalpy. Jacob et al.^[48] dispersed TiO₂ into a eutectic system composed of paraffin and palmitic acid to fabricate nano-enhanced eutectic PCMs (NeUPCMs). Compared to the pure matrix, the latent heat of the NeUPCMs improved by 17%.

2.2　Thermal conductivity

For non-metallic PCMs, thermal conduction predominantly relies on lattice vibrations, specifically via phonons. As illustrated in Figure 2, the material lattice can be conceptualized as a system of atoms interconnected by spring-like interaction forces, where the interatomic forces are approximated by elastic potential energy. Upon heating, the atoms undergo thermal vibrations, deviating from their equilibrium positions. Phonons, functioning as the quantized carriers of lattice vibrations, transport thermal energy from the heated surface atoms to adjacent atoms, thereby facilitating thermal diffusion through the lattice and establishing a temperature gradient^[49]. In an ideal and entirely defect-free crystal lattice, phonon propagation occurs without scattering limits, theoretically yielding infinite thermal conductivity. However, in practical materials, phonons inevitably encounter various scattering mechanisms. These scattering events perturb the phonon propagation paths, altering their momentum and energy, which significantly curtails their mean free path and consequently degrades the macroscopic thermal conduction efficiency^[50].

When nanofillers are introduced into a PCM, beyond providing supplementary thermal conduction pathways, interfacial phonon transport emerges as the decisive factor dictating the overall thermal performance. The heterogeneous interface formed between the PCM and the nanofillers induces acoustic impedance mismatch and severe scattering effects. This causes a fraction of high-frequency phonons to be reflected or randomly scattered, manifesting as substantial interfacial thermal resistance (Kapitza resistance)^[51]. This bottleneck is particularly pronounced in low-dimensional nanofiller systems (e.g., 0D or 1D fillers). The construction of a continuous thermally conductive pathway often necessitates heat to traverse the filler/matrix interface repeatedly. The cumulative superimposition of this interfacial thermal resistance severely restricts the effective enhancement of thermal conductivity^[52]. Conversely, as the dimensionality of the nano-additives increases, the fillers more readily form direct contacts, overlaps, or interconnected networks. This architectural shift enables thermal energy to propagate continuously over extended distances within the highly conductive fillers, drastically minimizing cross-interfacial phonon transport and thereby mitigating interfacial thermal resistance^[53]. The heat transfer mechanisms between PCMs and nano-additives of varying dimensions are schematically depicted in Figure 3. As the dimensionality of the nano-additives increases, the total interfacial area diminishes, resulting in a heat transfer efficiency that follows the trend: 3D > 2D > 1D > 0D^[54]. While excessive filler loadings inherently compromise the energy density of the PCM, insufficient loadings fail to establish continuous phonon transmission pathways. Therefore, engineering highly efficient, network-type (e.g., 3D interconnected) nano-additive architectures remains the ultimate objective for achieving superior thermal conductivity enhancement in PCMs^[55].

2.2.1　Compositing with zero-dimensional (0D) materials

0D structural particles possessing high intrinsic thermal conductivity play a pivotal role in augmenting the thermal transport of PCMs. They primarily enhance heat flux by uniformly dispersing within the PCM to form local thermal conduction chains, which incrementally elevate the phonon group velocity and mean free path^[56]. However, during solution processing, nanoparticles are highly susceptible to sedimentation and agglomeration. This aggregation obstructs phonon transmission, detrimentally impacting the heat transfer characteristics of the phase change composite. Consequently, achieving adequate dispersion often necessitates the assistance of barrier or functionalization materials^[54]. Commonly employed 0D nanomaterials predominantly include metallic nanoparticles, metal oxides, and specific nanocarbon derivatives.

Liu et al.^[57] engineered a highly thermally conductive nano-ZnO functionalized paraffin/diatomite PCM (PA/F-DE/ZnO) via a facile melt-blending and physical adsorption approach. Compared to PA/F-DE, the integration of ZnO (w = 10%) boosted the thermal conductivity of PA/F-DE/ZnO by 87.73%. Ezhumalai et al.^[58] utilized CuO nanoparticles to amplify the thermal conductivity of palmitic acid. Compared to pure palmitic acid, composite PCMs loaded with CuO mass fractions of 0.1%, 0.2% and 0.3% exhibited thermal conductivity enhancements of 19.87%, 45.61% and 66.08%, respectively^[59]. When the TiO₂ nanoparticles were dispersed into palmitic acid to formulate nano-enhanced PCMs (PA/TiO₂) with TiO₂ mass fractions of 0.5%, 1%, 3% and 5%, the thermal conductivity of the palmitic acid was elevated by 12.7%, 20.6%, 46.6% and 80%, respectively.

2.2.2　Compositing with one-dimensional (1D) materials

1D materials, such as nanowires, carbon fibers and carbon nanotubes (CNTs), possess distinct advantages including inherently high thermal conductivity, low density, and robust chemical stability, rendering them highly effective for phonon transport. When these 1D materials reach a critical percolation threshold and are uniformly dispersed within the PCM matrix, their large aspect ratios facilitate mutual contact and overlapping. This spatial arrangement naturally constructs an interconnected thermally conductive network, drastically enhancing the thermal transport capabilities of the composite^[55].

Nomura et al.^[60] fabricated composite PCMs (PCCs) utilizing erythritol as the phase change matrix and carbon fibers as the highly conductive filler, employing both melt-dispersion and hot-pressing techniques. As illustrated in Figure 4, compared to pristine erythritol (thermal conductivity of 0.76 W/(m·K)), both preparation methods successfully elevated the effective thermal conductivity of the PCCs. Notably, the hot-pressing method yielded a significantly more pronounced enhancement than melt-dispersion. In the hot-pressed PCCs, the carbon fibers preferentially aligned within the plane perpendicular to the applied pressing stress. Given the highly anisotropic thermal conductivity of carbon fibers, this highly oriented architecture critically accelerated the dramatic improvement in the effective thermal conductivity of the PCM.

Zhang et al.^[61] prepared phase change composites (PCCs) utilizing an erythritol matrix filled with short carbon fibers (SCFs) of two distinct lengths. The SEM images of the SCFs and PCCs, shown in Figure 5, confirm the uniform dispersion of the SCFs within the phase change matrix. The thermal conductivity of the PCCs escalated concurrently with the SCF loading. The composite containing 10% of the longer SCFs achieved the highest thermal conductivity at 3.92 W/(m·K), representing a staggering 407.8% enhancement over pure erythritol (0.77 W/(m·K)).

Salyan et al.^[62] dispersed multi-walled carbon nanotubes (MWCNTs) into D-mannitol to prepare thermally enhanced nanocomposite PCMs at weight fractions of 0.1% and 0.5%, which generated maximum thermal conductivity enhancements of 7% and 32%, respectively.

2.2.3　Compositing with two-dimensional (2D) materials

2D materials, prominently represented by graphene, are atomically thin carbon monolayers. Owing to the robust sp² covalent bonds between carbon atoms and its planar architecture, graphene exhibits extraordinary thermal conductivity, permitting near-ballistic phonon transport with minimal scattering and yielding an intrinsic thermal conductivity of up to 5000 W/(m·K)^[63]. 2D graphene is frequently combined with 1D fillers to introduce supplementary thermal conduction pathways, thereby amplifying the overall thermal conductivity of the PCM. The 2D structure efficiently establishes thermal percolating networks within the PCM matrix and acts as a bridging element between localized clusters of 1D fillers, synergistically enhancing heat transfer^[55,64].

Zhong et al.^[65] incorporated four types of graphene nanoplatelets (GNPs) (Figure 6) with varying lateral dimensions and thicknesses into n-eicosane to formulate nano-enhanced PCMs (NePCMs). Compared to pristine n-eicosane, all GNP-loaded samples exhibited augmented thermal conductivity, with a maximum enhancement of 2.1-fold. Experimental results confirmed that the aspect ratio of GNPs significantly dictates the thermophysical properties of NePCMs; a smaller aspect ratio facilitates the more seamless establishment of a thermally conductive network, thereby optimizing thermal conductivity.

As shown in Figure 7(a), Zhang et al.^[66] utilized hyperbolic graphene aerogels (HGAs) (Figure 7(c)) as highly conductive scaffolds to encapsulate paraffin, fabricating paraffin-graphene composites (PGCs) (Figure 7(d)) specifically tailored for lithium-ion battery (LIB) thermal management. At a filler mass fraction of 12.5%, the PGC retained a high latent heat of 200 J/g, only a 9.1% reduction compared to pure paraffin, while achieving an exceptional thermal conductivity of 30.75 W/(m·K). Regarding LIB thermal management, the PGC effectively suppressed thermal runaway. Even after 10000 rapid charge-discharge cycles, the system strictly maintained the battery temperature at 42 °C, ensuring stable capacity and Coulombic efficiency.

Badakhsh et al.^[67] employed a synergistic mixture of CNTs and GNPs to enhance the thermal performance of paraffin. While all composite PCMs exhibited higher thermal conductivities than pure paraffin, an increasing ratio of CNTs to GNPs resulted in a declining trend in thermal conductivity. The findings indicated that the planar 2D structure of GNPs more effectively bridges the isolated CNT clusters, as depicted in Figure 8, thereby forging superior thermal conduction pathways throughout the matrix.

2.2.4　Compositing with three-dimensional (3D) materials

3D structural additives inherently form interconnected porous networks, which provide continuous, long-range thermal conduction pathways within the PCM matrix. A highly porous network can accommodate and retain a maximal volume of the PCM^[68]. Furthermore, the robust capillary forces and surface tension provided by the micro-pores effectively confine the liquid PCM, preventing leakage during the solid-liquid phase transition^[69]. Commonly utilized porous materials include metal foams, porous carbons, and inorganic minerals^[70].

Xiao et al.^[71] prepared paraffin/nickel foam and paraffin/copper foam composite PCMs via vacuum impregnation. Figure 9(a) and (c) display the morphologies of the pristine nickel and copper foams with distinct pore sizes, while Figure 9(b) and (d) present the resultant paraffin/nickel and paraffin/copper foam composites. It is evident that pure paraffin uniformly infiltrates the metal foam pores, demonstrating excellent interfacial compatibility. Experimental measurements revealed that the thermal conductivity of the paraffin/nickel foam composite was three times that of pure paraffin, whereas the paraffin/copper foam composite achieved a 15-fold enhancement.

Yuan et al.^[72] developed a shape-stabilized erythritol/EG composite PCM for medium-temperature thermal energy storage via a facile “impregnation-compression-sintering” three-step strategy, with SEM images shown in Figure 10(a)−(i). The evolution of the latent heat and thermal conductivity as a function of EG content is plotted in Figure 10(j). As the EG mass fraction increased, the latent heat decreased while the thermal conductivity exhibited an almost linear escalation. Balancing thermal storage capacity and conductivity, the composite with an EG mass fraction of 10% demonstrated optimal performance, yielding a latent heat of 212.5 J/g and a thermal conductivity of 12.51 W/(m·K), which is 17.38 times higher than that of pristine erythritol.

Qian et al.^[73] fabricated a composite PCM by infiltrating paraffin into a hexagonal boron nitride (h-BN) porous scaffold featuring continuous thermal conductive pathways. The resulting PCM, containing an h-BN mass fraction of 18%, exhibited a melting latent heat of 165.4 and an impressive thermal conductivity of 0.85 W/(m·K), representing a ~600% enhancement over pure paraffin.

2.3　Supercooling

Supercooling refers to the phenomenon where a material remains in a liquid state below its thermodynamic melting point. In short-term energy storage applications, supercooling can severely degrade the thermal efficiency of a PCM system. For instance, in building applications, solidification typically occurs within a limited nocturnal timeframe. If the PCM experiences severe supercooling instead of timely crystallization, it fails to release its stored thermal energy^[74]. Whether a PCM smoothly transitions into the solidification phase during cooling is intricately linked to the dominant nucleation mechanism within the system. If the system relies on homogeneous nucleation, the crystal nucleus must form spontaneously within a perfectly uniform liquid phase. Because this process must overcome a substantial interfacial energy barrier, requiring significant energy fluctuations, it generally necessitates deep supercooling to achieve stable nuclei formation. High-purity PCMs devoid of solid interfaces or nucleation sites typically exhibit this mechanism, making them prone to pronounced supercooling^[75].

Conversely, heterogeneous nucleation occurs at solid-liquid interfaces, such as container walls, trace impurities, dispersed nanoparticles, porous scaffolds, or rough topological surfaces. The presence of these interfaces drastically reduces the effective interfacial energy required for nucleus formation, lowering the critical nucleation energy barrier and enabling the system to initiate crystallization at minimal supercooling degrees^[74,76]. For organic PCMs plagued by high supercooling, such as sugar alcohols, the introduction of nucleating agents, porous frameworks, or encapsulation shell materials serves as a highly effective mitigation strategy.

Cheng et al.^[77] introduced sodium carboxymethyl cellulose (CMC-Na) and hexagonal boron nitride (h-BN) to regulate the supercooling and thermal properties of erythritol. The supercooling degree and solidification stability of erythritol were suppressed by 93% and 84%, respectively, while the melting latent heat experienced a controlled reduction from 335.1 to 294.1 J/g. Shao et al.^[24] uniformly dispersed polyvinylpyrrolidone (PVP) in erythritol to mitigate supercooling. The results demonstrated that a PVP addition (w = 1.0%) plummeted the supercooling degree from over 64 °C down to approximately 21 °C. The composite retained a melting latent heat of 301 J/g, merely a 9.3% decrease compared to pure erythritol. Yuan et al.^[78] investigated the supercooling behavior of pure erythritol versus an erythritol/EG composite (w = 15%). Their findings indicated that the incorporation of EG suppressed the supercooling degree by 25 °C and tightened the solidification stability margin to 10 °C.

2.4　Flame retardancy

Organic PCMs, composed primarily of carbon, hydrogen and oxygen, are highly susceptible to ignition upon exposure to high temperatures or direct flames, posing a severe threat to life and property. Resolving the inherent flammability of organic PCMs is of paramount importance for advancing their practical engineering applications and commercialization. Xiao et al.^[79] comprehensively enumerated various classes of flame retardants, elucidating their underlying flame-retardant mechanisms alongside their respective advantages and limitations, as summarized in Table 4. Current flame-retardant strategies for organic PCMs primarily encompass physical blending, chemical modification, microencapsulation and surface coating.

2.4.1　Physical blending of flame retardants

Dispersing flame retardants into PCMs via physical blending is highly favored for its simplicity and operational ease. However, this approach presents distinct drawbacks. Poor interfacial compatibility between the flame retardant and the PCM often compromises the mechanical properties and long-term stability of the composite. Furthermore, achieving satisfactory flame retardancy typically necessitates high loading concentrations, which detrimentally dilutes the thermal storage density of the PCM.

Li et al.^[80] fabricated a composite PCM using n-octadecane, rice husk char (RHC), ammonium polyphosphate (APP), epoxy resin (EP) and EG. The composite containing an APP mass fraction of 15% exhibited exceptional flame retardancy, achieving a UL-94 V-0 rating. The limiting oxygen index (LOI) increased from 18.3% to 23.7% and the total heat release (THR) measured via cone calorimetry decreased by 20%. DSC analysis confirmed a melting peak temperature of 27.0 °C and a latent heat of 128 J/g. Li et al.^[81] introduced a novel triazine charring foaming agent (CFA) and APP into a shape-stabilized PCM, utilizing paraffin as the thermal storage medium and polypropylene (PP) as the supporting matrix. At an APP/CFA loading of w = 30%, the composite passed the UL-94 V-0 rating and achieved an LOI value of 32.8%. Fang et al.^[82] prepared a flame-retardant n-hexadecane/silica (SiO₂) composite for thermal energy storage, further augmenting its flame retardancy by incorporating EG. At an n-hexadecane mass fraction of 73.3%, the melting and solidification latent heats were 147.58 and 145.10 kJ/kg, respectively. Microstructural analysis of the post-combustion char residues revealed that a uniform, continuous, and dense char layer effectively barricaded heat and mass transfer, thereby enhancing the composite’s flame resistance.

2.4.2　Chemical modification

Covalently bonding flame-retardant functional groups to the molecular structure of PCMs ensures uniform dispersion at the molecular level, fundamentally eradicating the poor compatibility issues inherent to physical blending. This chemical modification strategy not only significantly suppresses the migration and phase separation of flame retardants but also bolsters the flame-retardant efficacy while preserving the PCM's thermal storage capacity.

Qian et al.^[83] synthesized a novel halogen-free, flame-retardant hybrid phase change composite via an in situ sol-gel method, utilizing paraffin as the core medium and tris(triethoxysilylpropyl) phosphoramide as the sol-gel precursor. The synergistic interaction between the paraffin and the hybrid silsesquioxane network substantially enhanced the char-forming capability of the paraffin. Compared to pure paraffin, the peak heat release rate (PHRR) was drastically reduced by 62.1%.

Jiang et al.^[84] engineered a series of novel shape-stabilized PCMs enriched with phosphorus and silica via the transesterification of diethyl phosphite with 1-tetradecanol, 1-hexadecanol, and 1-octadecanol, followed by a ring-opening reaction and the hydrolytic condensation of 2,3-epoxypropoxy propyltrimethoxysilane (silane coupler KH-560). The synthesis route is detailed in Figure 11. SEM imaging and EDS spectroscopy corroborated that the dual incorporation of phosphorus and silicon accelerated protective char formation, thereby elevating both thermal stability and fire resistance.

Zhang et al.^[85] synthesized boron-modified octadecanol PCMs with varying molecular architectures by systematically adjusting the stoichiometric ratio of boric acid to octadecanol (Figure 12). The boron modification remarkably elevated the thermal stability and flame retardancy of octadecanol, yielding a 70.9% reduction in the heat release rate (HRR) and a 77.8% decrease in the smoke production rate (SPR).

2.4.3　Flame-retardant microencapsulation

Phase change microencapsulation involves enveloping PCMs within a protective microscopic shell. This architecture prevents direct material contact and leakage during the phase transition while simultaneously enhancing heat transfer area^[86]. Flame retardancy in microcapsules is typically achieved via two routes: directly encapsulating the flame retardant within the core alongside the PCM, or chemically/physically modifying the polymer shell to be intrinsically flame-retardant.

Hu et al.^[87] formulated silica-shelled microcapsules (SiO₂-MCs) and poly(urea-formaldehyde)-shelled microcapsules (PUF-MCs), utilizing a hybrid core of octadecane and tributyl phosphate (TBP). The pHRR of the SiO₂-MCs was suppressed by 26.7%, significantly outperforming the 11.5% reduction observed in PUF-MCs. The rigid SiO₂ shell provided superior thermal stability and a robust flame-retardant barrier, slowing the combustion rate and shortening the burning duration. The flame-retardant mechanism of these microcapsules is schematically illustrated in Figure 13.

Liao et al.^[88] fabricated flame-retardant PCMs (FRPCMs) utilizing octadecane as the core and bio-based magnesium phytate (PAMg) as the intrinsically flame-retardant shell (Figure 14). DSC measurements indicated a melting latent heat of 117–158 J/g. LOI and cone calorimetry assessments demonstrated an LOI increase from 18.5% to 21.6% and a 39.5% reduction in total heat release (THR).

Du et al.^[89] synthesized nanoencapsulated PCMs (NanoPCMs) featuring an n-octadecane core and a poly(methyl methacrylate) (PMMA) shell, prepared via the condensation reaction between diethyl bis(2-hydroxyethyl) aminomethylphosphonate (DEAMP) and acryloyl chloride. The incorporation of the phosphorus-containing DEAMP into the NanoPCMs significantly stifled heat and smoke release in EP/NanoPCM composites, concurrently enhancing their residual char mass and LOI values.

2.4.4　Surface coating

The coating method involves applying a flame-retardant layer directly onto the surface of macroscopic, shape-stabilized PCMs to fortify fire resistance. Because the flame-retardant barrier is confined to the exterior, the phase change dynamics and intrinsic thermal storage capacity of the internal PCM are largely preserved without disruptive chemical or physical interference.

Xu et al.^[90] fabricated shape-stabilized PCMs (SSPCMs) comprising styrene-butadiene-styrene block copolymer (SBS)/HDPE/paraffin/OMMT. Three distinct intumescent coatings—acrylic resin/EG, alkyd resin/EG and epoxy resin/EG—were applied to the SSPCM surfaces. Once the EG content surpassed a critical threshold, all surface-coated SSPCMs exhibited outstanding flame retardancy. The horizontal burning time was substantially prolonged, achieving a UL-94 V-0 rating, while the LOI values surged from 17.4% to over 30%. Additionally, the PHRR plummeted by 62%–84%, the overall heat release process was remarkably delayed, and total smoke production was minimized. The flame-retardant mechanism of the coated SSPCMs is depicted in Figure 15.

Niu et al.^[91] compounded ammonium polyphosphate (APP) and dipentaerythritol (DEPR) as flame retardants (APP∶DEPR = 3∶1) with polyurethane (PU) to formulate an intumescent flame-retardant coating. Initially, a composite PCM (CPCM) was prepared using paraffin and silica aerogel (SA). By applying the flame-retardant coating onto the CPCM, an FR-CPCM was obtained. The FR-CPCM achieved an exceptional LOI of 56.31%, and due to the formation of a dense, intumescent carbonized layer at elevated temperatures, its flame-retardant rating escalated to V-0 in the UL-94 vertical burning test.

3　Conclusion and outlook

收起

Organic PCMs possess distinct advantages such as high phase change enthalpy, tunable phase change temperatures, excellent chemical stability, minimal supercooling, relative cost-effectiveness, and abundant raw material sources. Therefore, they have emerged as indispensable candidates in the domains of thermal energy storage and thermal management. This review has comprehensively summarized several mainstream organic PCMs, detailing their phase transition characteristics (temperature, enthalpy), intrinsic merits, and limitations. Furthermore, grounded in the physicochemical properties of these materials, recent advancements in performance optimization strategies for organic PCMs have been systematically evaluated.

Despite the broad application prospects of organic PCMs, the large-scale engineering deployment remains bottlenecked by critical challenges, including inherently low thermal conductivity, compromised long-term cycling stability, and elevated overall cost. To propel this field forward, future research should strategically pivot towards the following pivotal directions.

(1) Intrinsic Enhancement of Material Properties: Future studies should focus on the precise matching of phase change temperatures and latent heats through molecular architectural design, the construction of tailored eutectic systems, and targeted functionalization. Concurrently, it is crucial to fundamentally elucidate the mechanisms governing intermolecular forces, crystal growth behavior, and nucleation kinetics following the introduction of nanoparticles, thereby enabling the predictive modulation of latent heat variations and the targeted suppression of supercooling.

(2) Efficient Heat Transfer and Interfacial Engineering: By rationally designing the dimensionality, spatial distribution and interfacial coupling of thermally conductive fillers—while stringently preserving high latent heat density—researchers must construct composite PCM architectures characterized by minimized interfacial thermal resistance and continuous phonon transmission pathways. This is essential to decisively overcome the limited thermal response rates of organic PCMs.

(3) Structuralization and Multifunctional Integration: The continuous development of spatial confinement technologies—such as porous framework infiltration, micro- and nano-encapsulation and 3D skeleton supporting structures—is imperative for elevating the morphological stability and cyclic reliability of PCMs. Moreover, the seamless integration of functional units capable of photothermal, electrothermal, or electromagnetic-responsive conversion into the phase change matrix will yield multifunctional phase change materials, satisfying the stringent demands of complex operational environments.

(4) Engineering Application and Sustainable Development: Finally, the trajectory of organic PCM research must shift towards cost reduction, green chemistry, and scalable manufacturing. Enhanced efforts should be directed towards developing bio-based, industrial by-product-derived and renewable resource-based PCMs to simultaneously mitigate material costs and alleviate the environmental footprint.

参考文献

收起

文献

收起

参考文献引证文献

排序方式：

XIAO L, WANG J. Research progress and applications of inorganic hydrated salt phase change materials for energy storage[J]. Appl Chem Ind, 2021, 50(6): 1653−1657.

SHARMA A, TYAGI V V, CHEN C R, et al. Review on thermal energy storage with phase change materials and applications[J]. Renewable Sustainable Energy Rev, 2009, 13(2): 318−345.

MAGENDRAN S S, KHAN F S A, MUBARAK N M, et al. Synthesis of organic phase change materials (PCM) for energy storage applications: A review[J]. Nano-Struct Nano-Objects, 2019, 20: 100399.

YANG J, WANG X. Preparation and thermal properties of organic phase change energy storage materials[J]. Chin J Anal Chem, 2025, 53(6): 100491.

HIMRAN S, SUWONO A, MANSOORI G A. Characterization of alkanes and paraffin waxes for application as phase change energy storage medium[J]. Energy sources, 1994, 16(1): 117−128.

KAHWAJI S, JOHNSON M B, KHEIRABADI A C, et al. A comprehensive study of properties of paraffin phase change materials for solar thermal energy storage and thermal management applications[J]. Energy, 2018, 162: 1169−1182.

AKGÜN M, AYDıN O, KAYGUSUZ K. Experimental study on melting/solidification characteristics of a paraffin as PCM[J]. Energy Convers Manag, 2007, 48(2): 669−678.

GEORGE M, PANDEY A K, ABD RAHIM N, et al. A novel polyaniline (PANI)/paraffin wax nano composite phase change material: Superior transition heat storage capacity, thermal conductivity and thermal reliability[J]. Sol Energy, 2020, 204: 448−458.

EMEEMA J, MURALI G, REDDI B V, et al. Investigations on paraffin wax/CQD composite phase change material-Improved latent heat and thermal stability[J]. J Energy Storage, 2024, 85: 111056.

PAUL A, BAUMHÖGGER E, DEWERTH M O, et al. Thermal conductivity of solid paraffins and several n-docosane compounds with graphite[J]. J Therm Anal Calorim, 2023, 148(12): 5687−5694.

LIU L. Preparation and performance study of SiO₂-based broad-spectrum photothermal conversion phase change energy storage nanocapsules[D]. Beijing: University of Science and Technology Beijing, 2022.

BHARATHIRAJA R, RAMKUMAR T, SELVAKUMAR M, et al. Advancements in paraffin wax phase change materials: A comprehensive review of enhancement techniques and thermal storage applications[J]. Thermochim Acta, 2025, 753: 180129.

WANG Y, YU J, HUANG W, et al. Anti-overload performance in micro-nanocavity graphene/paraffin phase change energy storage materials for electronic thermal management[J]. Compost Sci Technol, 2025, 270: 111322.

CHEN Y, ZHANG X, JI J, et al. Cold chain transportation energy conservation and emission reduction based on phase change materials under dual-carbon background: A review[J]. J Energy Storage, 2024, 86: 111258.

SHARWAN S, SIKARWAR P, MAZUMDAR B. Recent innovations in support materials for shape-stable organic composite phase change materials: A comprehensive review[J]. Sol Energy Mater Sol Cells, 2024, 272: 112910.

XU W, YANG W, SU J, et al. Diatom-based biomass composites phase change materials with high thermal conductivity for battery thermal management[J]. J Energy Storage, 2024, 96: 112737.

GAO N, DU J, YANG W, et al. Bio-based sunflower carbon/polyethylene glycol shape-stabilized phase change materials for thermal energy storage[J]. RSC Adv, 2024, 14(33): 24141−24151.

PRAVEEN B, SURESH S. Experimental study on heat transfer performance of neopentyl glycol/CuO composite solid-solid PCM in TES based heat sink[J]. Eng Sci Technol Int J, 2018, 21(5): 1086−1094.

WANG X, GUO Q, ZHONG Y, et al. Heat transfer enhancement of neopentyl glycol using compressed expanded natural graphite for thermal energy storage[J]. Renew Energy, 2013, 51: 241−246.

WANG X, WU Y, LI C, et al. Preparation and thermal properties investigation of pentaerythritol based phase change microcapsules for low and medium temperature thermal energy storage[J]. J Energy Storage, 2024, 100: 113704.

SHAO X, YANG S, FAN L, et al. Sugar alcohol phase change materials for low-to-medium temperature thermal energy storage: A comprehensive review[J]. J Energy Storage, 2023, 68: 107848.

DEL BARRIO E P, GODIN A, DUQUESNE M, et al. Characterization of different sugar alcohols as phase change materials for thermal energy storage applications[J]. Sol Energy Mater Sol Cells, 2017, 159: 560−569.

SHAO X F, WANG C, YANG Y J, et al. Screening of sugar alcohols and their binary eutectic mixtures as phase change materials for low-to-medium temperature latent heat storage. (Ⅰ): Non-isothermal melting and crystallization behaviors[J]. Energy, 2018, 160: 1078−1090.

SHAO X F, YANG S, LIN J C, et al. Polyvinylpyrrolidone (PVP)-enabled significant suppression of supercooling of erythritol for medium-temperature thermal energy storage[J]. J Energy Storage, 2022, 46: 103915.

KAIZAWA A, MARUOKA N, KAWAI A, et al. Thermophysical and heat transfer properties of phase change material candidate for waste heat transportation system[J]. Heat Mass Transfer, 2008, 44(7): 763−769.

TOMASSETTI S, AQUILANTI A, MUCIACCIA P F, et al. A review on thermophysical properties and thermal stability of sugar alcohols as phase change materials[J]. J Energy Storage, 2022, 55: 105456.

LIU H, JING J, LIU J, et al. Sugar alcohol-based phase change materials for thermal energy storage: Optimization design and applications[J]. Renewable Sustainable Energy Rev, 2024, 199: 114528.

LEE W, KIM J A comprehensive review of research on organic-based phase-change thermal interface materials for thermal management of electric devices: Methods, performance, and applications[J]. Polym Test, 2025, 142: 108677.

ZHANG Q, LIU J, ZHANG J, et al. A review of composite phase change materials based on biomass materials[J]. Polymers, 2022, 14(19): 4089.

XIE Z, YAN H, DAI H, et al. Heat capacity study of fatty acids as phase change materials for thermal energy storage[J]. J Chem Thermodyn, 2024, 197: 107338.

SARBU I, DORCA A. Review on heat transfer analysis in thermal energy storage using latent heat storage systems and phase change materials[J]. Int J Energy Res, 2019, 43(1): 29−64.

LUO S, BAI T, GUO M, et al. Impact of freeze–thaw cycles on the long-term performance of concrete pavement and related improvement measures: A review[J]. Materials, 2022, 15(13): 4568.

ANAND A, MANSOR M, SHARMA K, et al. A comprehensive review on eutectic phase change materials: Development, thermophysical properties, thermal stability, reliability, and applications[J]. Alexandria Eng J, 2025, 112: 254−280.

YANG Y, WU W, FU S, et al. Study of a novel ceramsite-based shape-stabilized composite phase change material (PCM) for energy conservation in buildings[J]. Constr Build Mater, 2020, 246: 118479.

YANPING Y, WENQUAN T, XIAOLING C, et al. Theoretic prediction of melting temperature and latent heat for a fatty acid eutectic mixture[J]. J Chem Eng Data, 2011, 56(6): 2889−2891.

ZHANG Y, SU Y, GE X. Theoretical prediction of melting points and latent heats of (quasi-) eutectic phase change materials[J]. Univ Sci Technol China, 1995(4): 474−478.

SARı A, ALKAN C, BILGIN C. Micro/nano encapsulation of some paraffin eutectic mixtures with poly (methyl methacrylate) shell: Preparation, characterization and latent heat thermal energy storage properties[J]. Appl Energy, 2014, 136: 217−227.

DURAIPANDI S, SREEKUMAR A. Investigation on the performance of a natural convection solar dryer with novel palmitic and sebacic acid eutectic phase change material for thermal energy storage applications[J]. J Energy Storage, 2024, 77: 109908.

BARAN G, SARI A. Phase change and heat transfer characteristics of a eutectic mixture of palmitic and stearic acids as PCM in a latent heat storage system[J]. Energy Convers Manag, 2003, 44(20): 3227−3246.

LIU Y, LI A, XU S, et al. Reversible luminescent switching in an organic cocrystal: Multi-stimuli-induced crystal-to-crystal phase transformation[J]. Angew Chem Int Ed, 2020, 59(35): 15098−15103.

GENG L, CUI J, ZHANG C, et al. Chemistry in phase change energy storage: Properties regulation on organic phase change materials by covalent bond modification[J]. Chem Eng J, 2024, 495: 153359.

LIU L, WANG H, LIU X, et al. Thermal properties and shape-stabilization of poly (propylene-graft-maleic anhydride)-g-alkyl alcohol comb-like polymeric phase change thermal energy storage materials[J]. J Energy Storage, 2024, 97: 112845.

KONG Q, MU H, HAN Y, et al. Biodegradable phase change materials with high latent heat: Preparation and application on Lentinus edodes storage[J]. Food Chem, 2021, 364: 130391.

LIU H, FENG Y, FENG W. Alkyl-grafted azobenzene molecules for photo-induced heat storage and release via integration function of phase change and photoisomerization[J]. Compos Commun, 2020, 21: 100402.

SHAIKH S, LAFDI K, HALLINAN K. Carbon nanoadditives to enhance latent energy storage of phase change materials[J]. J Appl Phys, 2008, 103(9): 094302.

BAHIRAEI F, FARTAJ A, NAZRI G A. Experimental and numerical investigation on the performance of carbon-based nanoenhanced phase change materials for thermal management applications[J]. Energy Convers Manag, 2017, 153: 115−128.

SAHAN N, PAKSOY H O. Thermal enhancement of paraffin as a phase change material with nanomagnetite[J]. Sol Energy Mater Sol Cells, 2014, 126: 56−61.

JACOB J, PANDEY A K, ABD RAHIM N, et al. Quantifying thermophysical properties, characterization, and thermal cycle testing of nano-enhanced organic eutectic phase change materials for thermal energy storage applications[J]. Sol Energy Mater Sol Cells, 2022, 248: 112008.

BURGER N, LAACHACHI A, FERRIOL M, et al. Review of thermal conductivity in composites: Mechanisms, parameters and theory[J]. Prog Polym Sci, 2016, 61: 1−28.

LI J, MO S, ZHOU Z, et al. Nanoparticle-enhanced phase change materials for thermal energy storage: A critical review[J]. Renewable Sustainable Energy Rev, 2025, 223: 116040.

SWARTZ E T, POHL R O. Thermal boundary resistance[J]. Rev Mod Phys, 1989, 61(3): 605.

Cahill D G, Ford W K, Goodson K E, et al. Nanoscale thermal transport[J]. J Appl Phys, 2003, 93(2): 793−818.

Yu W, Xie H. A review on nanofluids: Preparation, stability mechanisms, and applications[J]. J Nanomater, 2012, 2012(1): 435873.

CHENG P, CHEN X, GAO H, et al. Different dimensional nanoadditives for thermal conductivity enhancement of phase change materials: fundamentals and applications[J]. Nano Energy, 2021, 85: 105948.

WANG S, DU R, LI T. Progress and perspective on thermal conductivity enhancement of phase change materials[J]. Sci Bull, 2024, 69(20): 3176−3179.

WU S, YAN T, KUAI Z, et al. Thermal conductivity enhancement on phase change materials for thermal energy storage: A review[J]. Energy Storage Mater, 2020, 25: 251−295.

LIU X, HOU X, YAN L, et al. ZnO functionalized paraffin/diatomite phase change material and its thermal management mechanism in PDMS coatings[J]. RSC Adv, 2025, 15(8): 6032−6042.

EZHUMALAI D S, SRIHARAN G, HARIKRISHNAN S. Improved thermal energy storage behavior of CuO/palmitic acid composite as phase change material[J]. Mater Today Proc, 2018, 5(6): 14618−14627.

SHARMA R K, GANESAN P, TYAGI V V, et al. Thermal properties and heat storage analysis of palmitic acid-TiO₂ composite as nano-enhanced organic phase change material (NEOPCM)[J]. Appl Therm Eng, 2016, 99: 1254−1262.

NOMURA T, TABUCHI K, ZHU C, et al. High thermal conductivity phase change composite with percolating carbon fiber network[J]. Appl Energy, 2015, 154: 678−685.

ZHANG Q, LUO Z, GUO Q, et al. Preparation and thermal properties of short carbon fibers/erythritol phase change materials[J]. Energy Convers Manag, 2017, 136: 220−228.

SALYAN S, SURESH S. Multi-walled carbon nanotube laden with D-Mannitol as phase change material: Characterization and experimental investigation[J]. Adv Powder Technol, 2018, 29(12): 3183−3191.

SINGH H, BUDIARTO H A, SINGH B, et al. Graphene for Next-Generation Technologies: Advances in Properties, Applications, and Industrial Integration[J]. Results Eng, 2025: 106865.

WU K, LEI C, HUANG R, et al. Design and preparation of a unique segregated double network with excellent thermal conductive property[J]. ACS Appl Mater Interfaces, 2017, 9(8): 7637−7647.

ZHONG Y, ZHANG J, LI W, et al. The influences of graphene nanoplatelets dimension on the thermophysical properties of nanocomposite phase change materials[J]. Mater Today Commun, 2025, 47: 113089.

ZHANG C, MAO Y, LI K, et al. High power and energy density graphene phase change composite materials for efficient thermal management of Li-ion batteries[J]. Energy Storage Mater, 2025, 75: 104003.

BADAKHSH A, LEE Y M, RHEE K Y, et al. Improvement of thermal, electrical and mechanical properties of composites using a synergistic network of length controlled-CNTs and graphene nanoplatelets[J]. Compos Part B Eng, 2019, 175: 107075.

HUANG X, CHEN X, LI A, et al. Shape-stabilized phase change materials based on porous supports for thermal energy storage applications[J]. Chem Eng J, 2019, 356: 641−661.

UMAIR M M, ZHANG Y, IQBAL K, et al. Novel strategies and supporting materials applied to shape-stabilize organic phase change materials for thermal energy storage–A review[J]. Appl Energy, 2019, 235: 846−873.

YU S, LI X, ZHANG T, et al. Improving the shape stability and photothermal conversion performance of phase change materials through three-dimensional metal-organic network[J]. Mater Today Commun, 2024, 38: 108194.

XIAO X, ZHANG P, LI M. Preparation and thermal characterization of paraffin/metal foam composite phase change material[J]. Appl Energy, 2013, 112: 1357−1366.

YUAN M, REN Y, XU C, et al. Characterization and stability study of a form-stable erythritol/expanded graphite composite phase change material for thermal energy storage[J]. Renewable Energy, 2019, 136: 211−222.

QIAN Z, SHEN H, FANG X, et al. Phase change materials of paraffin in h-BN porous scaffolds with enhanced thermal conductivity and form stability[J]. Energy Build, 2018, 158: 1184−1188.

SHAMSEDDINE I, PENNEC F, BIWOLE P, et al. Supercooling of phase change materials: A review[J]. Renewable Sustainable Energy Rev, 2022, 158: 112172.

LIU C, CHENG Q, LI B, et al. Recent advances of sugar alcohols phase change materials for thermal energy storage[J]. Renewable Sustainable Energy Rev, 2023, 188: 113805.

ZHAO Y, ZHANG X, XU X, et al. Research progress in nucleation and supercooling induced by phase change materials[J]. J Energy Storage, 2020, 27: 101156.

CHENG Q, CHENG X, WANG X, et al. Supercooling regulation and thermal property optimization of erythritol as phase change material for thermal energy storage[J]. J Energy Storage, 2022, 52: 105000.

YUAN M, YE F, XU C. Supercooling study of erythritol/EG composite phase change materials[J]. Energy Procedia, 2019, 158: 4629−4634.

XIAO Y, LI T, YANG Y, et al. Exploring flame-retardant, shape-stabilized multi-functional composite phase change materials[J]. Sol Energy Mater Sol Cells, 2025, 282: 113369.

LI C, SUN Z, SHAO J J, et al. A novel biochar supported dual-flame-retardant composite phase change material (PCM) for building energy saving[J]. Constr Build Mater, 2025, 485: 141953.

LI L, WANG G, GUO C. Influence of intumescent flame retardant on thermal and flame retardancy of eutectic mixed paraffin/polypropylene form-stable phase change materials[J]. Appl Energy, 2016, 162: 428−434.

FANG G, LI H, CHEN Z, et al. Preparation and characterization of flame retardant n-hexadecane/silicon dioxide composites as thermal energy storage materials[J]. J Hazard Mater, 2010, 181(1/3): 1004−1009.

QIAN Y, WEI P, JIANG P, et al. Preparation of halogen-free flame retardant hybrid paraffin composites as thermal energy storage materials by in-situ sol–gel process[J]. Sol Energy Mater Sol Cells, 2012, 107: 13−19.

JIANG Y, YAN P, WANG Y, et al. Form-stable phase change materials with enhanced thermal stability and fire resistance via the incorporation of phosphorus and silicon[J]. Mater Des, 2018, 160: 763−771.

ZHENG R, CHEN R, WU F, et al. Boron-modified form stable phase change materials with high energy storage, flame retardancy, and smoke suppression for advanced photo-to-heat conversion[J]. Polym Test, 2025, 147: 108804.

PNG Z M, SOO X Y D, CHUA M H, et al. Strategies to reduce the flammability of organic phase change materials: A review[J]. Sol Energy, 2022, 231: 115−128.

HU Z T, REINACK V H, AN J, et al. Ecofriendly microencapsulated phase-change materials with hybrid core materials for thermal energy storage and flame retardancy[J]. Langmuir, 2021, 37(21): 6380−6387.

LIAO H, DUAN W, LIU Y, et al. Flame retardant and leaking preventable phase change materials for thermal energy storage and thermal regulation[J]. J Energy Storage, 2021, 35: 102248.

DU X, WANG S, DU Z, et al. Preparation and characterization of flame-retardant nanoencapsulated phase change materials with poly (methylmethacrylate) shells for thermal energy storage[J]. J Mater Chem A, 2018, 6(36): 17519−17529.

XU L, LIU X, YANG R. Flame retardant paraffin-based shape-stabilized phase change material via expandable graphite-based flame-retardant coating[J]. Molecules, 2020, 25(10): 2408.

NIU J, DENG S, GAO X, et al. Experimental study on low thermal conductive and flame retardant phase change composite material for mitigating battery thermal runaway propagation[J]. J Energy Storage, 2022, 47: 103557.

2026年第54卷第9期

PDF下载

183

引用本文

BibTeX

文章信息

doi: 10.3724/2097-213X.2025.JFCT.0038

接收时间：2025-11-07
首发时间：2026-09-23
出版时间：2026-09-10

补充材料

相关文章

文章信息

作者

出版历史

收稿日期：2025-11-07
修回日期：2025-12-16
录用日期：2025-12-26

基金

作者信息

¹山西大学化学化工学院, 山西太原 030006

²中国科学院山西煤炭化学研究所煤炭高效低碳利用全国重点实验室, 山西太原 030001

通讯作者:

参考文献

分享链接

https://castjournals.cast.org.cn/joweb/rlhxxb/CN/10.3724/2097-213X.2025.JFCT.0038

分享至

全文二维码

扫描看全文

引用本文

BibTeX

本文的引用情况

2种不同金属材料的力学参数

科 Family	属数 Number of genus	种数 Number of species	占总种数比例 Percentage of total species (%)	属 Genus	种数 Number of species	占总种数比例 Percentage of total species (%)
鹅膏菌科Amanitaceae	2	11	5.26	鹅膏菌属 Amanita	10	4.78
小菇科 Mycenaceae	2	12	5.74	丝盖伞属 Inocybe	5	2.39
多孔菌科 Polyporaceae	8	14	6.70	蜡蘑属 Laccaria	5	2.39
红菇科 Russulaceae	3	23	11.00	小皮伞属 Marasmius	6	2.87
				小菇属 Mycena	11	5.26
				光柄菇属 Pluteus	5	2.39
				红菇属 Russula	17	8.13
				栓菌属 Trametes	5	2.39

关闭全屏

BibTeX
EndNote
RefWorks
TxT

Formula	Melting temperature/°C	Melting enthalpy/(J·g⁻¹)	Thermal conductivity/(W·m⁻¹·K⁻¹)
C₁₄H₃₀	5.5	228	0.129
C₁₆H₃₄	16.7	237	0.130
C₁₈H₃₈	28.0	244	0.138
C₂₀H₄₂	36.7	246	0.137
C₂₂H₄₆	44	249	0.164
C₂₄H₅₀	50.6	255	0.156
C₂₆H₅₄	56.3	256	0.146
C₂₈H₅₈	61.6	253	0.147

Formula

Melting temperature/°C

Melting enthalpy/(J·g⁻¹)

Thermal conductivity/(W·m⁻¹·K⁻¹)

C₁₄H₃₀

5.5

228

0.129

C₁₆H₃₄

16.7

237

0.130

C₁₈H₃₈

28.0

244

0.138

C₂₀H₄₂

36.7

246

0.137

C₂₂H₄₆

249

0.164

C₂₄H₅₀

50.6

255

0.156

C₂₆H₅₄

56.3

256

0.146

C₂₈H₅₈

61.6

253

0.147

Classification	Formula	Melting temperature/°C	Melting enthalpy/(J·g⁻¹)	Volumetric energy density/(kW·h·m⁻³)
Erythritol	C₄H₁₀O₄	118.9	332.3	133.9
Xylitol	C₅H₁₂O₅	93.4	237.5	100.2
Inositol	C₆H₁₂O₆	224.3	256.3	124.6
Mannitol	C₆H₁₄O₆	166.1	281.1	124.5
Sorbitol	C₆H₁₄O₆	99.4	184.4	34.9
Galactitol	C₆H₁₄O₆	186-187	330.0	117.5

Classification

Formula

Melting temperature/°C

Melting enthalpy/(J·g⁻¹)

Volumetric energy density/(kW·h·m⁻³)

Erythritol

C₄H₁₀O₄

118.9

332.3

133.9

Xylitol

C₅H₁₂O₅

93.4

237.5

100.2

Inositol

C₆H₁₂O₆

224.3

256.3

124.6

Mannitol

C₆H₁₄O₆

166.1

281.1

124.5

Sorbitol

C₆H₁₄O₆

99.4

184.4

34.9

Galactitol

C₆H₁₄O₆

186-187

330.0

117.5

Formula	Melting temperature/°C	Melting enthalpy/(J·g⁻¹)	Thermal conductivity/(W·m⁻¹·K⁻¹)	Maximum operational temperature/°C
C₈H₁₆O₂	16.2	154.1	0.1872	153.6
C₁₀H₂₀O₂	28.8	172.9	0.2133	163.7
C₁₂H₂₄O₂	43.1	192.9	0.2388	180.7
C₁₄H₂₈O₂	53.6	213.3	0.2662	203.5
C₁₆H₃₂O₂	61.4	222.9	0.2881	208.2
C₁₈H₃₆O₂	68.2	229.4	0.3079	224.2

Formula

Melting temperature/°C

Melting enthalpy/(J·g⁻¹)

Thermal conductivity/(W·m⁻¹·K⁻¹)

Maximum operational temperature/°C

C₈H₁₆O₂

16.2

154.1

0.1872

153.6

C₁₀H₂₀O₂

28.8

172.9

0.2133

163.7

C₁₂H₂₄O₂

43.1

192.9

0.2388

180.7

C₁₄H₂₈O₂

53.6

213.3

0.2662

203.5

C₁₆H₃₂O₂

61.4

222.9

0.2881

208.2

C₁₈H₃₆O₂

68.2

229.4

0.3079

224.2

Classification	Example	Mechanism	Advantage	Disadvantage
Halogenated flame retardants	Chlorinated paraffins (CP), polybrominated diphenyl ethers (PBDEs), hexabromocyclododecane (HBCD)	Halogen free radicals are generated during combustion, which can rapidly capture ·H and ·OH	Efficiency, good thermal stability, and good compatibility	Produces corrosive and toxic fumes
Nitrogen flame retardants	Triazine compounds melamine, dicyandiamide, guanidine salts and melamine cyanurate	Releasing non-flammable gases, absorbing heat, diluting oxygen	Safe, non-toxic, and broadly applicable	Inefficiency when used alone, synergistic with N-/P-based flame retardants
Silicon flame retardant	SiO₂, Halloysite nanotubes (HNT), Oxidized montmorillonite (OMT), silicone resin (SR) and polysiloxane (PSO)	Promoting polymer degradation forms a protective layer based on Si−O and Si−C bonds, suppressing the diffusion of heat and oxygen	Processability and environment- friendly	Poor dispersion, high cost, susceptible to moisture and heat
Phosphorus flame retardant	Red phosphorus, phosphorus oxychloride (POCl₃) and phosphorus black (PB)	·PO and ·PO₂ radicals were generated during combustion, and ·H and ·OH were captured	Low smoke, high process stability and good thermal stability	High cost, low degradation rate and environmentally unfriendly
Metal hydroxide	Mg(OH)₂, Al(OH)₃	It aecomposes to absorb heat and releases water vapor, forming a metal oxide protective layer that reduces heat transfer	Lower price, non-toxic and environmental protection	Poor compatibility and inefficiency
Intumescent flame retardant	Ammonium polyphosphate (APP), pentaerythritol (PER) and melamine	Form foam and Carbonization layer on the surface to prevent the underlying material from further exposure to ignition	Low smoke, non-toxic and efficient	Poor compatibility, affecting mechanical properties

Classification

Example

Mechanism

Advantage

Disadvantage

Halogenated flame retardants

Chlorinated paraffins (CP), polybrominated diphenyl ethers (PBDEs), hexabromocyclododecane (HBCD)

Halogen free radicals are generated during combustion, which can rapidly capture ·H and ·OH

Efficiency, good thermal stability, and good compatibility

Produces corrosive and toxic fumes

Nitrogen flame retardants

Triazine compounds melamine, dicyandiamide, guanidine salts and melamine cyanurate

Releasing non-flammable gases, absorbing heat, diluting oxygen

Safe, non-toxic, and broadly applicable

Inefficiency when used alone, synergistic with N-/P-based flame retardants

Silicon flame retardant

SiO₂, Halloysite nanotubes (HNT), Oxidized montmorillonite (OMT), silicone resin (SR) and polysiloxane (PSO)

Promoting polymer degradation forms a protective layer based on Si−O and Si−C bonds, suppressing the diffusion of heat and oxygen

Processability and environment- friendly

Poor dispersion, high cost, susceptible to moisture and heat

Phosphorus flame retardant

Red phosphorus, phosphorus oxychloride (POCl₃) and phosphorus black (PB)

·PO and ·PO₂ radicals were generated during combustion, and ·H and ·OH were captured

Low smoke, high process stability and good thermal stability

High cost, low degradation rate and environmentally unfriendly

Metal hydroxide

Mg(OH)₂, Al(OH)₃

It aecomposes to absorb heat and releases water vapor, forming a metal oxide protective layer that reduces heat transfer

Lower price, non-toxic and environmental protection

Poor compatibility and inefficiency

Intumescent flame retardant

Ammonium polyphosphate (APP), pentaerythritol (PER) and melamine

Form foam and Carbonization layer on the surface to prevent the underlying material from further exposure to ignition

Low smoke, non-toxic and efficient

Poor compatibility, affecting mechanical properties