燃料化学学报（中英文）

Catalyst	S_BET^a/(m²·g⁻¹)	v_p^a/(cm³·g⁻¹)	d_p^a/nm	d_cu^b/%	S_Cu^b/(m²·g⁻¹)	Average size^c/nm	Acidic sites^d/(μmol·g⁻¹)
^a: Determined by N₂ adsorption-desorption; ^b: Determined by N₂O titration; ^c: Determined by TEM; ^d: Determined by NH₃-TPD.
Cu/SiO₂-A	146.79	0.54	14.7	1.13	48.25	5.28	10.51	6.56	17.07
Cu/SiO₂-N	155.23	0.60	15.6	0.74	46.35	5.54	5.61	4.40	10.01
Cu/SiO₂-H	132.20	0.61	18.5	0.61	35.518	6.94	4.14	5.51	9.65

Catalyst	S_BET^a/(m²·g⁻¹)	v_p^a/(cm³·g⁻¹)	d_p^a/nm	d_cu^b/%	S_Cu^b/(m²·g⁻¹)	Average size^c/nm	Acidic sites^d/(μmol·g⁻¹)
^a: Determined by N₂ adsorption-desorption; ^b: Determined by N₂O titration; ^c: Determined by TEM; ^d: Determined by NH₃-TPD.
Cu/SiO₂-A	146.79	0.54	14.7	1.13	48.25	5.28	10.51	6.56	17.07
Cu/SiO₂-N	155.23	0.60	15.6	0.74	46.35	5.54	5.61	4.40	10.01
Cu/SiO₂-H	132.20	0.61	18.5	0.61	35.518	6.94	4.14	5.51	9.65

Catalyst	Crystalline size/nm
Cu/SiO₂-A	5.1	3.6	3.6
Cu/SiO₂-N	5.3	5.1	−
Cu/SiO₂-H	6.1	3.9	6.5

Catalyst	Crystalline size/nm
Cu/SiO₂-A	5.1	3.6	3.6
Cu/SiO₂-N	5.3	5.1	−
Cu/SiO₂-H	6.1	3.9	6.5

焙烧气氛精准调控的Cu/SiO₂催化剂用于高效催化丁二酸二甲酯加氢制1,4-丁二醇

PDF下载

邵旭浩 ¹ , 张旭妍 ¹ , 陈晓荣 ¹ , 杜嘉欣 ¹ , 艾培培 ²^,^* , 谭明慧 ³ , 高志华 ¹^,^* , 黄伟 ¹

燃料化学学报（中英文） | 2026,54(8): 20250326-1708-20250326-1718

收起

燃料化学学报（中英文） 2026 , 54 (8) : 20250326-1708 -20250326-1718

焙烧气氛精准调控的Cu/SiO₂催化剂用于高效催化丁二酸二甲酯加氢制1,4-丁二醇

全屏

邵旭浩¹, 张旭妍¹, 陈晓荣¹, 杜嘉欣¹, 艾培培²^,^*, 谭明慧³, 高志华¹^,^*, 黄伟¹

作者信息

¹太原理工大学化学与化工学院省部共建煤基能源清洁高效利用国家重点实验室, 山西太原 030024

²青岛科技大学材料科学与工程学院, 山东青岛 266042

³青岛科技大学化工学院, 山东青岛 266042

通讯作者:

艾培培, 高志华

Calcination atmosphere-engineered Cu/SiO₂ catalysts for efficient hydrogenation of dimethyl succinate to 1,4-butanediol

Xuhao SHAO¹, Xuyan ZHANG¹, Xiaorong CHEN¹, Jiaxin DU¹, Peipei AI²^,^*, Minghui TAN³, Zhihua GAO¹^,^*, Wei HUANG¹

Affiliations

¹State Key Laboratory of Clean and Efficient Coal Utilization, College of Chemistry and Chemical Engineering, Taiyuan University of Technology, Taiyuan 030024, China

²College of Materials Science and Engineering, Qingdao University of Science and Technology, Qingdao 266042, China

³College of Chemical Engineering, Qingdao University of Science and Technology, Qingdao 266042, China

Corresponding Author:

E-mail: aipeipei@qust.edu.cn

gaozhihua@tyut.edu.cn

出版时间: 2026-08-10 doi: 10.1016/S1872-5813(26)60663-9

文章导航

摘要

收起

生物质衍生的丁二酸二甲酯催化加氢制备1,4-丁二醇，是绿色化学背景下生产高附加值C4化学品的一条关键路径。Cu/SiO₂催化剂虽以酯加氢高选择性著称，但其性能本质上与铜物种的微观结构密切相关。尽管焙烧是形成催化剂活性结构的关键步骤，但焙烧气氛对其影响的系统性研究尚不充分。本研究采用尿素辅助水热法制备了Cu/SiO₂催化剂，并在不同气氛下进行焙烧，以阐明焙烧气氛对催化剂理化性质及其后续加氢性能的影响。通过N₂物理吸脱附、FT-IR、H₂-TRR、XRD、TEM、N₂O化学吸附、XPS和NH₃-TPD表征发现，焙烧气氛能显著改变金属-载体间相互作用，进而有效调控负载铜物种的分散度和化学状态。尤其是，在空气中焙烧后的催化剂，其金属-载体间相互作用较强，有效提高了铜物种的分散度，并增加了关键活性位Cu⁺的占比。在优化的反应条件下，Cu/SiO₂-A催化剂展现了优异的催化性能，丁二酸二甲酯转化率达92.37%，1,4-丁二醇收率达64.15%。本工作证实了焙烧气氛工程是一种优化多相催化剂中金属-载体相互作用，从而实现高效加氢过程的强效策略。

关键词

铜基催化剂 / 焙烧气氛 / 金属-载体相互作用 / 加氢

Abstract

收起

The catalytic hydrogenation of biomass-derived dimethyl succinate (DMS) to 1,4-butanediol (BDO) represents a pivotal route for producing high-value C4 chemicals in the context of green chemistry. Cu/SiO₂ catalysts are known for their high selectivity in hydrogenating ester groups, and their performance is correlated with the microstructure of the copper species. Although calcination is a critical step in defining this active structure, the systematic influence of the calcination atmosphere remains underexplored. In this study, Cu/SiO₂ catalysts were prepared via a urea-assisted hydrothermal method and calcined under different atmospheres to elucidate their effects on catalyst physicochemical properties and subsequent hydrogenation performance. A comprehensive characterization suite (N₂ physisorption, FT-IR, H₂-TPR, XRD, TEM, N₂O pulse chemisorption, XPS and NH₃-TPD) revealed that the calcination atmosphere profoundly alters the metal-support interaction, thereby regulating the dispersion and chemical state of the loaded copper species. Specifically, calcination in air promoted a stronger metal-support interaction, effectively enhancing the dispersion of copper species and increasing the proportion of key active Cu⁺ species. Consequently, the air-calcined catalyst demonstrated superior performance, achieving 92.37% DMS conversion and 64.15% BDO yield under optimized conditions (210 °C, 5.0 MPa, WHSV of 0.6 h⁻¹, H₂/DMS molar ratio of 100). This work underscores calcination atmosphere engineering as a potent strategy for optimizing metal-support interactions in heterogeneous catalysts for efficient hydrogenation processes.

Key words

copper-based catalyst / calcination atmosphere / metal-support interaction / hydrogenation

引用本文

邵旭浩, 张旭妍, 陈晓荣, 杜嘉欣, 艾培培, 谭明慧, 高志华, 黄伟. 焙烧气氛精准调控的Cu/SiO₂催化剂用于高效催化丁二酸二甲酯加氢制1,4-丁二醇. 燃料化学学报（中英文）, 2026 , 54 (8) : 20250326-1708 -20250326-1718 . DOI: 10.1016/S1872-5813(26)60663-9

Xuhao SHAO, Xuyan ZHANG, Xiaorong CHEN, Jiaxin DU, Peipei AI, Minghui TAN, Zhihua GAO, Wei HUANG. Calcination atmosphere-engineered Cu/SiO₂ catalysts for efficient hydrogenation of dimethyl succinate to 1,4-butanediol[J]. Journal of Fuel Chemistry and Technology, 2026 , 54 (8) : 20250326-1708 -20250326-1718 . DOI: 10.1016/S1872-5813(26)60663-9

正文

收起

The global energy and chemical feedstock systems are undergoing a profound transition from fossil-based to renewable resources. This shift represents not only a necessary response to the depletion of fossil fuels but also a critical pathway to mitigating the greenhouse effect and environmental pollution, thereby facilitating the transition toward green, low-carbon development. Against this backdrop, biomass, as the only renewable organic carbon source in nature, has attracted widespread attention from both academia and industry for its valorization^[1−2]. The catalytic conversion of biomass-derived platform molecules into high-value-added chemicals is widely regarded as a cornerstone of sustainable chemical production. Among these molecules, dimethyl succinate (DMS), produced from biomass through fermentation and esterification, serves as an ideal precursor toward this end. DMS can be catalytically hydrogenated to high-value C4 chemicals such as γ-butyrolactone (GBL), 1,4-butanediol (BDO) and tetrahydrofuran (THF), thereby establishing an integrated green value chain from “biomass to platform molecules to high-value chemicals”. This route substantially reduces dependence on traditional petroleum-based pathways (e.g., hydrogenation of maleic anhydride) and significantly lowers overall carbon emissions^[3].

The hydrogenation of DMS to BDO involves a complex tandem reaction network comprising multiple sequential, parallel, and competitive steps^[4]. The generally accepted reaction pathway begins with the stepwise hydrogenation of DMS, accompanied by methanol removal, to form GBL, which subsequently undergoes ring-opening hydrogenation to produce BDO^[5]. However, BDO can be reversibly dehydrogenated back to GBL or dehydrated over acid sites to form the undesired THF by-product^[6−8]. A central challenge in this network is designing an efficient catalyst that steers the reaction pathway toward high DMS conversion and high BDO selectivity. An ideal catalyst should exhibit synergistic bifunctionality: it must efficiently activate and hydrogenate the C=O bond while suppressing over-hydrogenation, and it should also possess suitably moderated acidity to avoid side reactions such as BDO dehydration^[9].

Among various catalytic systems, noble metals (e.g., Pd, Pt, Ru) exhibit high intrinsic activity but are costly and prone to over-hydrogenation, leading to poor economic viability and selectivity. In contrast, non-noble copper-based catalysts have emerged as promising candidates for the selective hydrogenation of DMS, owing to their unique ability to adsorb moderately and selectively hydrogenate carbonyl (C=O) groups, coupled with low activity toward C−C bond hydrogenolysis^[10−11]. In particular, Cu/SiO₂ catalysts have shown exceptional promise. Their performance is strongly influenced by the microstructure of copper species, including nanoparticle size, dispersion, valence distribution (Cu⁰, Cu⁺), and the strength of metal-support interactions^[12−13]. These structural parameters are, in turn, dictated by the catalyst preparation process^[14]. Therefore, refining preparation procedures to optimize the microstructure of Cu/SiO₂ represents a key research direction for enhancing intrinsic activity and selectivity^[15].

Among the various steps in catalyst synthesis, calcination serves as a critical bridge between the precursor and the final active structure, playing a decisive role in defining catalytic performance. The calcination atmosphere is a powerful yet easily adjustable synthesis parameter that directly influences precursor decomposition, copper speciation, and the metal-support interface, enabling precise engineering of metal-support interaction strength. Nevertheless, systematic studies examining the effect of calcination atmosphere on the structure and performance of Cu/SiO₂ catalysts in DMS hydrogenation remain scarce. This gap presents a clear research opportunity: by using calcination atmosphere (oxidizing, inert, reducing) as a “precision switch” powerful and tunable synthesis parameter, it is possible to directionally tailor metal-support interactions strength, optimize copper dispersion and valence distribution, and synergistically modulate surface acidity, thereby significantly enhancing catalytic performance.

In this study, Cu/SiO₂ catalyst precursors were synthesized via a urea-assisted hydrothermal method and calcined under different calcination atmospheres (air, N₂, H₂) to systematically investigate their physicochemical properties and performance in DMS hydrogenation. A combination of characterization techniques, including N₂ physisorption, FT-IR, H₂-TPR, XRD, TEM, N₂O pulse chemisorption, XPS and NH₃-TPD, was employed to elucidate the structure-performance relationships linking the calcination atmosphere to metal-support interaction and catalytic performance. This work aims to provide new insights and effective synthesis strategies for the rational design of high-performance copper-based catalysts for DMS hydrogenation to BDO.

1　Experimental

收起

1.1　Experimental reagents and materials

Cu(NO₃)₂·3H₂O (w≥99.5%) was purchased from Shanghai Macklin Biochemical Co., Ltd. Urea (w≥99%) was purchased from Sigma-Aldrich. Methanol (φ≥99.5%) and ethanol (φ≥99.7%) were obtained from Sinopod Chemical Reagent Co., Ltd. All materials were used as received without further purification.

1.2　Preparation of Cu/SiO₂ catalysts with different calcination atmospheres

Copper nitrate trihydrate (2.31 g) was dissolved in 100 mL of distilled water. Urea was then added under stirring with a urea-to-copper molar ratio of 3∶1. Subsequently, 13.5 g of silica sol was introduced, and the mixture was stirred continuously for 4 h. The resulting mixture was transferred into a Teflon-lined stainless-steel autoclave and subjected to hydrothermal treatment at 200 °C for 24 h. After the hydrothermal treatment, the solid product was collected by centrifugation and washed with deionized water until the supernatant reached a pH value of 7. The obtained solid was then dried overnight in an oven at 100 °C. The dried precursor was calcined at 450 °C for 4 h in a muffle furnace or tube furnace to obtain the final Cu/SiO₂ catalyst with a Cu mass fraction of 15% (Cu/SiO₂=15%). The resulting catalysts were designated based on their calcination atmosphere: Cu/SiO₂-A (calcined in air), Cu/SiO₂-N (calcined in nitrogen) and Cu/SiO₂-H (calcined in a 40% H₂/Ar stream).

1.3　Catalyst activity test

Catalyst performance was evaluated using a fixed-bed reactor and a dual-channel reactor system. The system comprised a vaporizer, a three-stage reactor (upper, middle, and lower sections), a back-pressure valve, a gas-liquid separator, a product collection tank, and a quartz reaction tube (6 mm inner diameter). Specifically, 0.2 g of catalyst (40–60 mesh) was loaded into the quartz tube and positioned in the reactor. The system was sealed and pressurized to 5.0 MPa with H₂ using the back-pressure valve. The temperature was then raised to 300 °C at a ramp rate of 2 °C/min and maintained for 3 h for reduction. Finally, the temperature was adjusted to the reaction temperature of 210 °C. Subsequently, the feedstock—a 20% solution of DMS in methanol—was vaporized and introduced into the system at a flow rate of 0.01 mL/min, with a concurrent H₂ flow of 64.00 mL/min. This corresponds to a H₂/DMS molar ratio of 100 and a weight hourly space velocity (WHSV) of 0.6 h⁻¹. The system was stabilized under these conditions for 10 h, during which the liquid products were discarded. After the stabilization period, the reaction products passed through a gas-liquid separator. The liquid phase was directed to a collection tank and sampled at 2−4 h intervals. The main hydrogenation products of DMS were GBL, BDO and THF. For analysis, an internal standard (hexanol) was added to the liquid samples, which were then analyzed by gas chromatography (GC, Shimadzu GC-2014) equipped with a KB-5 column and a flame ionization detector (FID). The GC oven temperature was set at 260 °C, and the injection volume was 0.2 μL.

1.4　Catalyst characterization

N₂ physisorption measurements were performed on a Quantachrome QDS-30 analyzer. A 200 mg sample, prepared by compressing the powder into a tablet at 10 MPa for 1 min and then crushing it, was placed in a degassing tube. The sample was outgassed under vacuum at 200 °C for 4 h. After cooling to room temperature, the sample was transferred to the analyzer for N₂ adsorption-desorption analysis at liquid nitrogen.

X-ray diffraction (XRD) analysis was performed on a Rigaku Smart Lab diffractometer to determine the phase composition of the samples. The catalyst was reduced with the same reduction conditions as before the reaction. Data were collected using Cu Kα radiation (40 kV, 40 mA) over a 2θ range of 5° to 85° at a scanning rate of 4(°)/min.

H₂-temperature-programmed reduction (H₂-TPR) analysis was conducted using a TP-5080 instrument (Tianjin Xianquan). Approximately 50 mg of the prepared sample was loaded into the reactor. Prior to analysis, the sample was purged with a N₂ stream at 150 °C for 60 min. After cooling to 50 °C under N₂, the gas was switched to a 5% H₂/Ar mixture. The temperature was then raised from 50 to 700 °C at a heating rate of 10 °C/min. Hydrogen consumption was monitored online using a thermal conductivity detector.

NH₃ temperature-programmed desorption mass spectrometry (NH₃-TPD-MS) was performed using a fully automated TP-5080 multifunctional adsorption apparatus (Tianjin Xianquan). The catalyst was reduced with the same reduction conditions as before the reaction. Approximately 100 mg of the sample was first purged with a He stream at 150 °C for 60 min. After cooling to 50 °C, the sample was exposed to NH₃ until saturation adsorption was achieved. Subsequently, physically adsorbed NH₃ was removed by purging with He. Finally, the temperature was programmed to increase from 50 to 600 °C at a rate of 10 °C/min under He flow. The desorbed NH₃ was monitored online by mass spectrometry.

Fourier-transform infrared (FT-IR) spectra of the samples were recorded on a Bruker INVENION S spectrometer. The potassium bromide (KBr) used for tablet pressing was dried in an oven at 150 °C overnight to remove moisture and minimize its interference with the measurements. Subsequently, approximately 0.1 g of dried KBr was thoroughly mixed and ground with a small amount of the sample in an agate mortar. The mixture was then pressed into a transparent flake at 10 MPa for 1 min. The resulting KBr flake was placed in the spectrometer, and the spectrum was acquired by averaging 32 scans over a wavenumber range of 4000 to 400 cm⁻¹ with a resolution of 4 cm⁻¹.

X-ray photoelectron spectroscopy (XPS) analysis was performed using a Shimadzu AXIS SUPRA instrument. The catalyst was reduced with the same reduction conditions as before the reaction. The analysis utilized an Al Kα X-ray source. The binding energy scale was calibrated by setting the C 1s peak to 284.8 eV. The surface elemental composition (Cu, Si, O) was analyzed and Cu LMM Auger spectra were collected to facilitate the quantification of different copper valence states (Cu⁰, Cu⁺).

TEM characterization was performed using a JEOL JEM-2000F high-resolution transmission electron microscope at 200 kV during the tests. The catalyst was reduced with the same reduction conditions as before the reaction. The samples were first pretreated by dispersing in ethanol, then placed in an ultrasonic bath for 5 min. Finally, the mixtures were placed on a microgrid for detection using a transmission electron microscope. The histogram statistics are 209 for Cu/SiO₂-A, 205 for Cu/SiO₂-N and 223 for Cu/SiO₂-H.

The copper surface area and dispersion were determined by N₂O pulse chemisorption using a TP-5080 analyzer (Tianjin Xianquan). Approximately 50 mg of catalyst was loaded into a U-shaped quartz tube. The sample was first purged with N₂ (30 mL/min) at 150 °C for 30 min. After cooling to 50 °C under N₂, the gas was switched to a 10% H₂/N₂ mixture (30 mL/min). The temperature was then ramped to 500 °C at 10 °C/min and held for 15 min for reduction. After reduction, the sample was purged with Ar and cooled to 50 °C. It was then exposed to a 10% N₂O/Ar flow (30 mL/min) at 50 °C for 30 min to oxidize surface Cu⁰ atoms. Subsequently, the system was purged with N₂ for 30 min to remove physisorbed species. Finally, the gas was switched to a 10% H₂/Ar mixture (30 mL/min), and the temperature was increased to 500 °C at 10 °C/min, then maintained for 15 min to reduce surface-oxidized copper.

2　Results and discussion

收起

2.1　Characterization of Cu/SiO₂ with different calcination atmospheres

Metal-support interaction is a critical factor governing catalytic performance, as it regulates the anchoring of metal species on the support surface, thereby directly dictating their dispersion and thermal stability. The calcination atmosphere serves as a powerful synthetic parameter for establishing initial metal-support interactions, as it controls precursor decomposition and the chemical state of the support surface. To elucidate the structure-property-performance relationships, Cu/SiO₂ catalyst precursors were calcined under three distinct atmospheres: oxidizing (Air), inert (N₂) and reducing (H₂). This approach enabled precise tuning of the metal-support interactions, ultimately leading to the development of a highly active and selective catalyst for DMS hydrogenation.

Initially, N₂ physisorption was used to assess whether the calcination atmosphere significantly altered the catalysts’ physical structure. As shown in Figure 1, all catalysts exhibited type Ⅳ isotherms with HⅡ(b)-type hysteresis loops, suggesting the presence of similar mesoporous structures. The textual properties summarized in Table 1 further demonstrate only marginal variations across catalysts prepared under different calcination atmospheres, confirming that the calcination atmosphere has a negligible impact on the catalyst’s physical structure.

As shown in Figure 2(a), all catalysts exhibit absorption bands at approximately 800 and 1110 cm⁻¹, corresponding to the symmetric and asymmetric stretching vibrations of Si–O bonds, respectively, confirming the presence of the amorphous SiO₂ support^[16−18]. The band around 500 cm⁻¹ is associated with the Si–O bending vibration. A noticeable shift in this band is observed for the Cu/SiO₂-A and Cu/SiO₂-N catalysts compared to pure SiO₂ (466 cm⁻¹), providing direct evidence for the formation of strong metal-support interactions between copper species and the silica support. H₂-TPR results further corroborate this finding. The Cu/SiO₂-H catalyst exhibits a single symmetric reduction peak at 181 °C, assigned to the reduction of Cu⁺ species to Cu^0[19−20]. In contrast, the Cu/SiO₂-A and Cu/SiO₂-N catalysts display asymmetric reduction profiles, indicating the presence of multiple copper species with distinct reducibility. For these catalysts, the lower-temperature reduction peaks (252 and 259 °C, respectively) are attributed to the highly dispersed CuO nanoparticles. In comparison, the higher-temperature peaks (298 and 311 °C) correspond to copper species strongly interacting with the SiO₂ support, likely in a Cu-O-Si structure^[21−24].

The significantly higher reduction temperatures for Cu/SiO₂-A and Cu/SiO₂-N underscore their stronger metal-support interactions compared to Cu/SiO₂-H. Such strong interactions are known to enhance catalytic activity and stability by anchoring metal species and inhibiting sintering. Furthermore, deconvolution of the TPR profiles reveals that the high-temperature reduction peak constitutes 33.65% of the total area for Cu/SiO₂-A, substantially greater than the 15.09% for Cu/SiO₂-N. This quantitative difference indicates a higher population of strongly interacting copper species in the Cu/SiO₂-A catalyst.

The distinct metal-support interactions induced by different calcination atmospheres critically govern the dispersion and valence distribution of the loaded copper species, which are decisive factors for the catalytic activity, selectivity, and stability. XRD analysis was used to determine the phase composition of the catalysts. As shown in Figure 3(a), all catalysts exhibit a broad diffraction peak at approximately 21.5°, characteristic of amorphous SiO₂^[25−26]. For catalysts calcined under inert (N₂) and oxidative (Air) atmospheres, weak diffraction peaks appear around 35.04°, corresponding to CuO species. This observation, combined with the low intensity of these peaks, suggests a strong metal-support interaction that promotes the uniform dispersion of copper. In contrast, the Cu/SiO₂-H catalyst displays distinct diffraction peaks assignable to Cu₂O and Cu⁰ species. This indicates that precursor decomposition and its simultaneous reduction to metallic and cationic copper occurred during H₂ calcination. Consequently, the opportunity for forming a strong Cu-O-Si interaction with the support was diminished, leading to significant copper agglomeration, as evidenced by the relatively sharp and intense copper diffraction peaks in Cu/SiO₂-H^[24].

After hydrogen reduction, the XRD pattern of the Cu/SiO₂-H catalyst remained unchanged, whereas significant transformations were observed for the Cu/SiO₂-N and Cu/SiO₂-A catalysts. The CuO diffraction peaks disappeared, and new characteristic peaks for Cu₂O and Cu⁰ emerged, confirming the complete reduction of CuO to lower-valence species, accompanied by particle agglomeration. The broad nature of the Cu₂O diffraction peaks implies a high dispersion of Cu₂O species. The stability of these Cu₂O species is attributed to strong metal-support interactions, which effectively stabilize the cationic copper and suppress its over-reduction and aggregation into large metallic particles^[27−29]. The crystallite sizes of the copper species in the reduced catalysts were estimated using the Scherrer equation (Table 2), yielding values between 3−7 nm. The reduced Cu/SiO₂-A catalyst possessed the smallest crystallite size, indicating superior copper dispersion. TEM analysis (Figure 4) showed that the average copper particle sizes followed the order: Cu/SiO₂-A (5.28 nm) < Cu/SiO₂-N (5.54 nm) < Cu/SiO₂-H (6.94 nm). This consistent trend from both techniques conclusively demonstrates that calcination in air achieves the highest metal dispersion, followed by nitrogen and hydrogen atmospheres.

The copper dispersion and surface area were further quantified by N₂O chemisorption. As summarized in Table 1, the Cu/SiO₂-A catalyst exhibits superior copper dispersion and a larger copper surface area than its N₂- and H₂-calcined counterparts.

These results, collectively with the XRD and TEM findings, confirm that the strength of the metal-support interaction directly governs the dispersion of the loaded metal. Enhanced copper dispersion provides a higher population of accessible active sites, which is crucial for the hydrogenation of DMS to BDO. These abundant sites facilitate efficient hydrogen activation and reactant adsorption, while precisely regulating the hydrogenation depth to suppress over-hydrogenation and undesired side reactions, thereby leading to superior catalytic activity.

The metal-support interactions govern not only the dispersion of the loaded metal but also its chemical state. Since the surface chemical state of the reduced catalysts is critical to hydrogenation performance, the catalysts were analyzed by X-ray photoelectron spectroscopy (XPS) and X-ray excited Auger electron spectroscopy (XAES). The survey spectra confirm that all catalysts consist of Cu, Si and O, indicating a consistent bulk composition. In the high-resolution Cu 2p spectra (Figure 5(b)), all catalysts exhibit only two characteristic peaks at approximately 932.6 eV (Cu 2p_3/2) and 952.5 eV (Cu 2p_1/2) with no satellite features in the 941−945 eV region that are characteristic of Cu²⁺ species. This confirms the complete reduction of Cu²⁺ to Cu⁰ and/or Cu⁺, consistent with the XRD results. Notably, the Cu 2p peaks for Cu/SiO₂-A and Cu/SiO₂-N are slightly shifted to lower binding energies compared to those of Cu/SiO₂-H, with the shift being most pronounced for the Cu/SiO₂-A catalyst^[30]. This suggests the strongest metal-support interaction in Cu/SiO₂-A, aligning with the H₂-TPR and FT-IR findings.

Due to the nearly overlapping binding energies of Cu⁺ and Cu⁰ in the Cu 2p spectra, Cu LMM Auger spectroscopy was employed to distinguish these species. The deconvoluted Cu LMM spectra confirm the coexistence of both Cu⁺ and Cu⁰ in all reduced catalysts, with binding energy typically around 572 and 568 eV, respectively. Quantitative analysis reveals that the relative proportion of Cu⁺ (Cu⁺/(Cu⁺+Cu⁰)) follows the order: Cu/SiO₂-A (47.18%) > Cu/SiO₂-N (32.45%) > Cu/SiO₂-H (26.41%). The observed order of Cu⁺ proportion (Cu⁺/(Cu⁺+Cu⁰)) can be attributed to the varying strength of the metal-support interaction, as indicated by H₂-TPR and FT-IR results. Specifically, the Cu/SiO₂-A catalyst exhibits the strongest Cu-O-Si interaction, which helps stabilize Cu⁺ species and allows more Cu₂O to remain after reduction. Although Cu/SiO₂-N shows the most intense Cu₂O diffraction peak in Figure 3(b), this likely reflects the presence of larger and better-crystallized Cu₂O particles in its bulk phase. In contrast, the weaker diffraction signal from Cu/SiO₂-A does not imply a lower amount of Cu₂O, but instead suggests that Cu₂O is highly dispersed on the support surface, which is consistent with its higher Cu⁺ proportion derived from XPS analysis. This quantitative trend is significant, as a synergistic interaction between Cu⁺ and Cu⁰ sites is crucial for the hydrogenation reaction. The Cu⁺ sites are primarily responsible for activating and adsorbing the carbonyl group of DMS, while also contributing to the catalyst’s thermal stability. Consequently, a higher concentration of Cu⁺ sites enhances both the activity and stability of copper-based catalysts.

The surface acidity of the catalysts calcined under different atmospheres was characterized by NH₃-TPD. As shown in Figure 6, all reduced catalysts exhibit NH₃ desorption peaks in the range of 150−400 °C, corresponding to the presence of both weak and medium-strong acid sites. Quantitative analysis via peak deconvolution reveals that the total acid amounts of the Cu/SiO₂-N and Cu/SiO₂-H catalysts are similar, whereas the Cu/SiO₂-A catalyst exhibits a significantly higher total acid amount. Specifically, the weak acid amount reaches 10.51 μmol/g for Cu/SiO₂-A, which is considerably higher than that of Cu/SiO₂-N (5.61 μmol/g) and Cu/SiO₂-H (4.14 μmol/g). In the hydrogenation of DMS to BDO, weak acid sites are believed to facilitate the reaction by adsorbing and polarizing the carbonyl oxygen atom of the ester group. This polarization weakens the C=O bond, thereby enhancing its reactivity toward nucleophilic attack by hydrogen species activated on adjacent metallic copper sites^[31]. In contrast, medium-strength acid sites catalyze the intramolecular dehydration and cyclization of BDO, leading to the formation of the THF by-product.

Compared with Cu/SiO₂-N and Cu/SiO₂-H, the Cu/SiO₂-A catalyst possesses a notably higher density of medium-strength acid sites. Therefore, while the highest density of weak acid sites in Cu/SiO₂-A contributes to its superior DMS conversion, the concurrent high density of medium-strength acid sites also promotes THF formation.

2.2　Performance evaluation of catalysts with different calcination atmospheres

The catalytic performance of the Cu/SiO₂ catalysts calcined under different atmospheres was evaluated for DMS hydrogenation to BDO at 210 °C, 5.0 MPa, a WHSV of 0.6 h⁻¹ and an H₂/DMS molar ratio of 100. As summarized in Figure 7(a), the Cu/SiO₂-A catalyst demonstrated superior activity, achieving a DMS conversion of 92.37%, which is substantially higher than that of the Cu/SiO₂-N (57.67%) and Cu/SiO₂-H (29.86%) catalysts. Notably, the Cu/SiO₂-A catalyst also exhibited the highest BDO selectivity of 69.45% at this high conversion level. In contrast, the Cu/SiO₂-N catalyst showed moderate conversion with comparable BDO selectivity, while the Cu/SiO₂-H catalyst performed poorly in both activity and selectivity.

To further elucidate the key active sites in the catalyst that influence activity and selectivity, we correlated the yield of BDO with both the Cu⁺/(Cu⁰+Cu⁺) ratio and the weak acid site density, and separately linked the formation of the THF to the medium-strong acid site density. As shown in Figure 7(b) and (c), the BDO yield exhibits a positive correlation with both the Cu⁺/(Cu⁰+Cu⁺) ratio and the weak acid amount. This suggests that achieving a high BDO yield is governed by a synergistic and competitive interplay among different types of active sites on the catalyst surface. Specifically, the Cu⁺-Cu⁰ dual site serves as the core active center for the sequential hydrogenation of DMS to BDO, with Cu⁺ activating the carbonyl group and Cu⁰ facilitating H₂ dissociation. Their proximity ensures efficient hydrogenation. Meanwhile, weak acid sites stabilize polar intermediates through weak adsorption, aiding the hydrogenation process and thereby enhancing the BDO yield.

Conversely, once formed, BDO molecules can interact with medium-strong acid sites, where intramolecular dehydration and cyclization occur, leading to the formation of the THF. Thus, the high performance of the optimal catalyst, Cu/SiO₂-A, stems from its combination of a high density of Cu⁺-Cu⁰ dual sites and a suitable weak-acid environment, which together maximize BDO production efficiency. However, its relatively higher density of medium-strong acid sites also results in increased THF selectivity. Notably, Cu/SiO₂-A possesses the highest density of weak acid sites and the largest Cu⁺/(Cu⁰+Cu⁺) ratio. This optimized configuration delivers outstanding performance, achieving a DMS conversion of 92.37% and a BDO selectivity of 69.45%.

Based on the characterization results and catalytic performance data, we propose a potential synergistic mechanism between Cu⁺ and Cu⁰ species. Specifically, Cu⁺ sites tend to adsorb and activate the C=O bond of dimethyl succinate (DMS), thereby polarizing it, while Cu⁰ sites facilitate the dissociation of H₂ to provide active hydrogen species (H*). Building on this, a plausible reaction pathway for the hydrogenation of DMS to BDO is proposed (Figure 8). H₂ first undergoes dissociative adsorption on Cu⁰ sites, forming surface adsorbed H atoms. With the cooperative assistance of acidic sites, Cu⁺ then adsorbs and activates the C–O/C=O bonds of DMS. Then, C–O bond cleavage occurs, after which the activated C=O bond reacts with H*, breaking the double bond to yield the intermediate methyl 4-hydroxybutyrate (4-HBM) and methanol. Subsequently, 4-HBM undergoes intramolecular transesterification to form GBL, releasing another methanol molecule^[32]. Next, GBL undergoes ring-opening in the presence of H* to form the intermediate 4-hydroxybutyraldehyde (4-HB), whose C=O bond is then activated by Cu⁺ and further hydrogenated to produce the target product BDO. Furthermore, when medium-strength acid sites are present on the catalyst, BDO can undergo intramolecular cyclodehydration to form THF as a byproduct.

3　Conclusion

收起

In summary, the calcination atmosphere is demonstrated to be an effective strategy for engineering the properties of Cu/SiO₂ catalysts, precisely tuning the metal-support interaction and surface acidity. The catalyst calcined in air (Cu/SiO₂-A) exhibited optimal characteristics, including the strongest metal-support interactions, the highest copper dispersion, an abundant surface acidity, and the largest population of stabilized Cu⁺ species. These properties synergistically contributed to its superior performance in the hydrogenation of DMS to BDO. The high dispersion and Cu⁺ sites facilitated hydrogen activation and carbonyl adsorption, while the acid sites promoted C=O polarization. This synergistic cooperation resulted in outstanding catalytic metrics under optimal conditions (210 °C, 5.0 MPa, WHSV of 0.6 h⁻¹, H₂/DMS molar ratio of 100), achieving a DMS conversion of 92.37% and a BDO yield of 64.15%. This work highlights calcination atmosphere engineering as a pivotal strategy for designing efficient heterogeneous catalysts reliant on metal-acid synergy.

参考文献

收起

文献

收起

参考文献引证文献

排序方式：

CHEN L-F, GUO P-J, ZHU L-J, et al. Preparation of Cu/SBA-15 catalysts by different methods for the hydrogenolysis of dimethyl maleate to 1, 4-butanediol[J]. Appl Catal A: Gen, 2009, 356(2): 129−136.

HAAS T, JAEGER B, WEBER R, et al. New diol processes: 1, 3-propanediol and 1, 4-butanediol[J]. Appl Catal A: Gen, 2005, 280(1): 83−88.

CHOCARRO-WRONA C, DE VICENTE J, ANTICH C, et al. Validation of the 1, 4-butanediol thermoplastic polyurethane as a novel material for 3D bioprinting applications[J]. Bioeng Transl Med, 2021, 6(1): e10192.

ZHANG D, YIN H, GE C, et al. Selective hydrogenation of maleic anhydride to γ-butyrolactone and tetrahydrofuran by Cu–Zn–Zr catalyst in the presence of ethanol[J]. J Ind Eng Chem, 2009, 15(4): 537−543.

NORHAFINI H, THINAGARAN L, SHANTINI K, et al. Synthesis of poly(3-hydroxybutyrate-co-4-hydroxybutyrate) with high 4HB composition and PHA content using 1, 4-butanediol and 1, 6-hexanediol for medical application[J]. J Polym Res, 2017, 24: 189.

THAKUR S, CHAUDHARY J, SINGH P, et al. Synthesis of Bio-based monomers and polymers using microbes for a sustainable bioeconomy[J]. Bioresour Technol, 2022, 344 (Pt A): 126156.

KÖSEOĞLU Y. Fuel aided rapid synthesis and room temperature ferromagnetism of M_0.1Co_0.1Zn_0.8O (M=Mn, Ni, Fe and Cu) DMS nanoparticles[J]. Ceram Int, 2016, 42 (7); 9190−9195.

NAUREEN B, HASEEB A, BASIRUN W J, et al. Recent advances in tissue engineering scaffolds based on polyurethane and modified polyurethane[J]. Mater Sci Eng, C, 2021, 118: 111228.

COK B, TSIROPOULOS I, ROES A L, et al. Succinic acid production derived from carbohydrates: An energy and greenhouse gas assessment of a platform chemical toward a bio-based economy[J]. Biofuels Bioprod Biorefin, 2013, 8(1): 16−29.

QIN Y-L, ZHU P, OUYANG C-X, et al. Chain extender-induced hydrogen bonding organization determines the morphology and properties of thermoplastic polycarbonate polyurethane[J]. Chin J Polym Sci, 2023, 42(1): 87−96.

NGHIEM N, KLEFF, S, SCHWEGMANN S. Succinic acid: Technology development and commercialization[J]. Fermentation, 2017, 3(6): 26.

ZHU Y, YANG J, MEI F, et al. Bio-based 1, 4-butanediol and tetrahydrofuran synthesis: Perspective[J]. Green Chem, 2022, 24(17): 6450−6466.

DI X, LI C, ZHANG B, et al. Role of Re and Ru in Re–Ru/C bimetallic catalysts for the aqueous hydrogenation of succinic acid[J]. Ind Eng Chem Res, 2017, 56(16): 4672−4683.

BUDRONI G, CORMA A. Gold and gold–platinum as active and selective catalyst for biomass conversion: Synthesis of γ-butyrolactone and one-pot synthesis of pyrrolidone[J]. J Catal, 2008, 257(2): 403−408.

UTSUNOMIA C, REN Q, ZINN M. Poly(4-Hydroxybutyrate): Current state and perspectives[J]. Front Bioeng Biotechnol, 2020, 8: 257.

CHEN C-S, CHENG W-H, LIN S-S. Study of iron-promoted Cu/SiO₂ catalyst on high temperature reverse water gas shift reaction[J]. Appl Catal A: Gen, 2004, 257(1): 97−106.

SMITH M L, KUMAR N, SPIVEY J J. CO adsorption behavior of Cu/SiO₂, Co/SiO₂, and CuCo/SiO₂ catalysts studied by in situ DRIFTS[J]. J Phys Chem C, 2012, 116(14): 7931−7939.

SU J, ZHANG Z, FU D, et al. Higher alcohols synthesis from syngas over CoCu/SiO₂ catalysts: dynamic structure and the role of Cu[J]. J Catal, 2016, 336: 94−106.

LI F, LU C-S, LI X-N. The effect of the amount of ammonia on the Cu⁰/Cu⁺ ratio of Cu/SiO₂ catalyst for the hydrogenation of dimethyl oxalate to ethylene glycol[J]. Chin Chem Lett, 2014, 25(11): 1461−1465.

CHEN H, TAN J, CUI J, et al. Promoting effect of boron oxide on Ag/SiO₂ catalyst for the hydrogenation of dimethyl oxalate to methyl glycolate[J]. Mol Catal, 2017, 433: 346−353.

ZHANG C, WANG D, ZHU M, et al. Plasma-enhanced copper dispersion and activity performance of Cu-Ni/ZrO₂ catalyst for dimethyl oxalate hydrogenation[J]. Catal Commun, 2017, 102: 31−34.

QI W, LING Q, DING D, et al. Performance enhancement of Cu/SiO₂ catalyst for hydrogenation of dimethyl oxalate to ethylene glycol through zinc incorporation[J]. Catal Commun, 2018, 108: 68−72.

WANG X, CHEN M, CHEN X, et al. Constructing copper-zinc interface for selective hydrogenation of dimethyl oxalate[J]. J Catal, 2020, 383: 254−263.

ZHAO Y, ZHANG H, XU Y, et al. Interface tuning of Cu⁺/Cu⁰ by zirconia for dimethyl oxalate hydrogenation to ethylene glycol over Cu/SiO₂ catalyst[J]. J Energy Chem, 2020, 49: 248−256.

SEPÚLVEDA C, DELGADO, L, GARCÍA R, et al. Effect of phosphorus on the activity of Cu/SiO₂ catalysts in the hydrogenolysis of glycerol[J]. Catal Today, 2017, 279: 217−223.

MO L, SAW E-T, KATHIRASER Y, et al. Preparation of highly dispersed Cu/SiO₂ doped with CeO₂ and its application for high temperature water gas shift reaction[J]. Int J Hydrogen Energy, 2018, 43(33): 15891−15897.

GIORGIANNI G, MEBRAHTU C, PERATHONER S, et al. Hydrogenation of dimethyl oxalate to ethylene glycol on Cu/SiO₂ catalysts prepared by a deposition-decomposition method: Optimization of the operating conditions and pre-reduction procedure[J]. Catal Today, 2022, 390−391: 343−353.

LI Z, MA Z, LI Y, et al. Tuning the product selectivity of dimethyl oxalate hydrogenation over WO modified Cu/SiO₂ catalysts[J]. J Energy Chem, 2024, 97: 128−138.

LI Z, LI Y, WANG X, et al. Hydrogenation of dimethyl oxalate to ethanol over Mo-doped Cu/SiO₂ catalyst[J]. Chem Eng J, 2023, 454: 140001.

WANG S, FENG K, ZHANG D, et al. Stable Cu catalysts supported by two-dimensional SiO₂ with strong metal-support interaction[J]. Adv Sci, 2022, 9(9): e2104972.

YE R-P, LIN L, WANG L-C, et al. Perspectives on the active sites and catalyst design for the hydrogenation of dimethyl oxalate[J]. ACS Catal, 2020, 10(8): 4465−4490.

SUN F, HUANG, H, CAO S, et al. Synthesis of 1, 4-butanediol via one-step esterification–hydrogenation of succinic anhydride over Cu-ZnO catalysts: A mechanism study of reaction and deactivation[J]. ACS Catal, 2025, 15(18): 16052−16069.

2026年第54卷第8期

PDF下载

176

引用本文

BibTeX

文章信息

doi: 10.1016/S1872-5813(26)60663-9

接收时间：2025-10-30
首发时间：2026-09-23
出版时间：2026-08-10

补充材料

相关文章

文章信息

作者

出版历史

收稿日期：2025-10-30
修回日期：2025-12-07
录用日期：2025-12-16

基金

作者信息

¹太原理工大学化学与化工学院省部共建煤基能源清洁高效利用国家重点实验室, 山西太原 030024

²青岛科技大学材料科学与工程学院, 山东青岛 266042

³青岛科技大学化工学院, 山东青岛 266042

通讯作者:

参考文献

分享链接

https://castjournals.cast.org.cn/joweb/rlhxxb/CN/10.1016/S1872-5813(26)60663-9

分享至

全文二维码

扫描看全文

引用本文

BibTeX

本文的引用情况

2种不同金属材料的力学参数

科 Family	属数 Number of genus	种数 Number of species	占总种数比例 Percentage of total species (%)	属 Genus	种数 Number of species	占总种数比例 Percentage of total species (%)
鹅膏菌科Amanitaceae	2	11	5.26	鹅膏菌属 Amanita	10	4.78
小菇科 Mycenaceae	2	12	5.74	丝盖伞属 Inocybe	5	2.39
多孔菌科 Polyporaceae	8	14	6.70	蜡蘑属 Laccaria	5	2.39
红菇科 Russulaceae	3	23	11.00	小皮伞属 Marasmius	6	2.87
				小菇属 Mycena	11	5.26
				光柄菇属 Pluteus	5	2.39
				红菇属 Russula	17	8.13
				栓菌属 Trametes	5	2.39

关闭全屏

BibTeX
EndNote
RefWorks
TxT

Catalyst	Crystalline size/nm
Catalyst	Cu(111)	Cu₂O(111)	Cu(200)
Cu/SiO₂-A	5.1	3.6	3.6
Cu/SiO₂-N	5.3	5.1	−
Cu/SiO₂-H	6.1	3.9	6.5